ZeonorFilm isotropic optical film properties · C ASTM D696 7x10-57x10 1.5x10-5 ... ZF14-188 136°C...
Transcript of ZeonorFilm isotropic optical film properties · C ASTM D696 7x10-57x10 1.5x10-5 ... ZF14-188 136°C...
100
90
80
70
60
50
40
30
20
10
0200 300 400 500 600 700 800
Wavelength (nm) Thickness: 3 mm
ZeonorFilm
PC
PET
Transmittance (%
)
HIGH TRANSPARENCY
ZeonorFilm exhibits high transparency (92% light
transmittance) and excellent turbidity (haze value <0.1%),
for enhanced brightness.
HIGH TRANSPARENCY
INERT SURFACE
ZeonorFilm is manufactured from Zeon’s cyclo olefi n
polymer (COP). COP is known for its excellent optical
properties and also for being a high-purity resin.
ZeonorFilm has an inert surface which makes it ideal
for sensitive bio-diagnostic devices.
INERT SURFACE
ItemMeasurement
methodUnit ZeonorFilm PC PET TAC
Membrane formation methodMelt
extrusion
Melt
extrusionSolvent cast
Melt
extrusionSolvent cast
Film thickness μm 100 100 100 80
Total light
transmittance
ASTMD1003
% 92 91 91 92 92
Dispersion (550nm
transmittance)% 91 90 90 89 92
Haze % <0.1 0.3 0.2 1.8 0.3
RetardationParallel Nichols
method— 3 20 10 25 3
LOW BIREFRINGENCE
ZeonorFilm® isotropic optical film properties
TYPICAL PROPERTIES OF ZEONORFILM
UnitsMeasurement
methodConditions ZeonorFilm
Heat-resistant
PCPET TAC
Physical properties
Specifi c gravity — JISK 6760 — 1.01 1.2 1.4 1.3
Waterabsorbency
% ASTM D570 — <0.01 0.3 0.4 7
Opticalproperties
Refractiveindex
— ASTM D542 D line, 25°C 1.53 1.59 1.60 —
Lighttransmittance
% JISK 7105Thickness
100μm92 91 89 92
Haze % JISK 7105Thickness
100μm<0.1 — — —
Abbe number — ASTM D542 25°C 56 — — —
Birefringence nmParallel Nicols
methodRoom
temperature3 — — —
Thermalproperties
Glass transitiontemperature
°C DSC 136°–163°C — — —
Molding shrinkage %100μ film100mm
120°CMD/TD
-0.02/0.06 0.01/0.00 0.56/0.52 0.61/0.54
150°CMD/TD
— 0.07/0.02 0.012 —
Linear expansioncoeffi cient
cm/cm°C
ASTM D696 7x10-5 7x10-5 1.5x10-5 —
Mechanicalproperties
Tensile strength MPa ASTM D638100μ
MD/TD60/59 62 210/220 130
Tensile elongation
% ASTM D638100μ
MD/TD40/30 110 150/130 40
Pencil hardness JISK 5401 B 2B H —
Electricalproperties
Dielectricbreakdown
strengthKY/mm ASTM D149 10μ film 360 — — —
Volumeresistivity
Ω • cm ASTM D257 >1016 >1016 >1016 —
Relative dielectricconstant
ASTM D150 1MHz 2.3 3 3.2 —
Dielectrictangent
ASTM S150 1MHz 0.005 0.01 0.01 0.013
Arcresistance
sec ASTM D495 3mm plate 124 — — —
ZEONORFILM IS AVAILABLE IN VARIOUS THICKNESS AND GLASS TRANSITION TEMPERATURES TO MEET A WIDE VARIETY OF APPLICATIONS.
ZeonorFilm
Grade
Glass Transition
Temperature (°C)Thickness
ZF14-040 136°C 40 μm
ZF14-050 136°C 50 μm
ZF14-060 136°C 60 μm
ZF14-100 136°C 100 μm
ZF14-188 136°C 188 μm
ZF16-100 163°C 100 μm
ZF16-188 163°C 188 μm
*Custom thicknesses are available via special order.
*Properties shown above are typical values. For specifi cation values, contact OPTES.