TPE 210-S - Stratasys · ALM TPE 210-S: 02.04.2013 Advanced Laser Materials, LLC l Tel:...
1
For reference use only. Actual properties may vary significantly from those listed above based on processing parameters, operating conditions and end use applications. The above properties were based on virgin ALM TPE 210-S using normal processing parameters on a 2500+ platform as outlined in the ALM Material Processing Guide. Advanced Laser Materials, LLC makes no warranties of materials for any application, nor does it make a warranty of any type, expressed or implied, but not limited to, the warranties of merchantability for a particular purpose. TPE 210-S HIGHLIGHTS • Soft, white parts out of the machine • Extreme elongations achievable without permanent deformation • Easy to infiltrate to obtain maximum properties • 100% recyclable APPLICATIONS • Footwear prototyping • Automotive gaskets and seals • Cushioning applications MATERIAL SPECIFICATIONS TYPICAL PHYSICAL PROPERTIES - Uninfiltrated PROPERTY Color/Appearance Bulk Density Elongation at Break Flexural Modulus (-40 C) Flexural Modulus (23 C) Flexural Modulus (100 C) Initial Tear Resistance, Die C, 23 C Abrasion Resistance, Taber H-18 Wheel Shore Hardness, Shore “A” Tensile Modulus Average Particle Size (D50) Particle Size Range (D10-D90) Sintered Part Density TEST METHOD Visual ASTM D1895 ASTM D638 ASTM D790 ASTM D790 ASTM D790 ASTM D624 ASTM D4060 ASTM D2240 ASTM D638 Laser Diffraction Laser Diffraction U.S. STANDARD White 0.214 oz/in 3 110% 3,336 psi 1,885 psi 435 psi 7.4 lbf 0.012 oz 40 1,160 psi 0.003 inches 0.001 - 0.005 inches 0.595 oz/in 1.03 g/cm METRIC White 0.37 g/cm 3 110% 23 MPa 13 MPa 3 MPa 33 N 535 mg 40 8 MPa 85 microns 20 - 130 microns ALM TPE 210-S: 02.04.2013 Advanced Laser Materials, LLC l Tel: 254.773.3080 l Fax: 254.773.3084 3115 Lucius McCelvey, Temple, TX 76504 l www.alm-llc.com • Ideal for applications requiring softer parts with excellent ductility and surface finish. ASTM D792 3 3
Transcript of TPE 210-S - Stratasys · ALM TPE 210-S: 02.04.2013 Advanced Laser Materials, LLC l Tel:...
For reference use only. Actual properties may vary signi�cantly from those listed above based on processing parameters, operating conditionsand end use applications. The above properties were based on virgin ALM TPE 210-S using normal processing parameters on a 2500+ platformas outlined in the ALM Material Processing Guide. Advanced Laser Materials, LLC makes no warranties of materials for any application, nor does it make a warranty of any type, expressed or implied, but not limited to, the warranties of merchantability for a particular purpose.
TPE 210-SHIGHLIGHTS
• Soft, white parts out of the machine
• Extreme elongations achievable without permanent deformation
• Easy to infiltrate to obtain maximumproperties
• 100% recyclable
APPLICATIONS
• Footwear prototyping
• Automotive gaskets and seals
• Cushioning applications
MATERIAL SPECIFICATIONS
TYPICAL PHYSICAL PROPERTIES - Unin�ltratedPROPERTY Color/Appearance
Bulk Density
Elongation at Break
Flexural Modulus (-40 C)
Flexural Modulus (23 C)
Flexural Modulus (100 C)
Initial Tear Resistance, Die C, 23 C
Abrasion Resistance, Taber H-18 Wheel
Shore Hardness, Shore “A”
Tensile Modulus
Average Particle Size (D50) Particle Size Range (D10-D90)
Sintered Part Density
TEST METHODVisual
ASTM D1895
ASTM D638
ASTM D790
ASTM D790
ASTM D790
ASTM D624
ASTM D4060
ASTM D2240
ASTM D638
Laser DiffractionLaser Diffraction
U.S. STANDARDWhite
0.214 oz/in3
110%
3,336 psi
1,885 psi
435 psi
7.4 lbf
0.012 oz
40
1,160 psi
0.003 inches0.001 - 0.005 inches
0.595 oz/in 1.03 g/cm
METRICWhite
0.37 g/cm 3
110%
23 MPa
13 MPa
3 MPa
33 N
535 mg
40
8 MPa
85 microns20 - 130 microns
ALM TPE 210-S: 02.04.2013
Advanced Laser Materials, LLC l Tel: 254.773.3080 l Fax: 254.773.30843115 Lucius McCelvey, Temple, TX 76504 l www.alm-llc.com
• Ideal for applications requiring softerparts with excellent ductility andsurface finish.
ASTM D792 33