MAXIFLOOR® MFC 200 WB EPOXY CEMENT

MAXIFLOOR® MFC 200 WB Epoxy Cement is a three component, waterborn self-smoothing epoxy flooring system for moisture barrier (2 mm thick). It is resistance to water and oil, good flow ability and can be over coated with epoxy and polyurethane flooring system.

APPLICATION DETAILS

Application Method Rubber Squeegee and spiked rollerMixing ratio (by weight) Comp.A : Comp.B : Comp.C = 1 : 3 : 16Pot Life 3 hours at 30°C.Recommended thickness Minimum 1.5 mm and Maximum 3.0 mm. Re-coating interval Minimum 24 hours (30°C) and Maximum 7 days (30°C).Substrate temperature Minimum 10°C and Maximum 30°C. Relative Air Humidity Max 80%

PRODUCT DATA

PRODUCT DESCRIPTION

MAXIFLOOR® MFC 200 WB Epoxy Cement , advantages such as:Simple application and easy to install• Good leveling properties• Can be overcoated with epoxy resin system• Waterbarrier• Permeable to water vapour• Excellent adhesion to damp and green concrete• Excellent early and final mechanical strengths• Excellent resistance to water and oil• Frost and de-icing salt resistant• Thermal expansion properties similar to concrete

Chemical Base Waterborn epoxy with selected aggregate.Color Light GreyFinishing Seamless matt and smooth finishDensity (mixture) 2.10 Kg /Liter Comp. A + B + CSurface dry 3.0 hours (30°C) Hard dry 24 hours (30°C)Full cure 7 days (30°C) Bonding strength 1.9 N/mm2 (after 7 days)Compressive strength 11.0 N/mm2 (after 7 days)Packaging 20 Kg-set (Parts A + B + C)Storage stability 6 months from the date of production, if stored in original, unopened and undamaged sealed packaging, in dry conditions at temperatures between 10°C and 30°C.

ADVANTAGES

TECHNICAL DATA

MAXIFLOOR® MFC 200 WB EPOXY CEMENT

A health and safety data sheet is available for this product on request. Please observe the precautionary notices on the container. Apply under well-ventilated conditions. Do not breathe or inhale vapour. Avoid skin contact. Spillage on skin should immediately be removed with suitable cleaner, soap and water. Eyes should be well flushed with water and medical attention sought immediately.

HEALTH AND SAFETY

If the surface preparation system used has not removed deeply penetrating contamination such as oil, blasting the substrate with hot compressed air followed by an application of a sealing compound can be considered. Consult your local MAXIFLOOR® Technical Department for further information.

CONTAMINATION

Compressive strength of concrete floor must be more than 25 N/mm2. Direct trawl finish concrete without cement render is the best surface condition for epoxy flooring. The temperature of the substrate must be at least 3°C above the current dew point temperature. Good ventilation is necessary when the paint is used in confined spaces. Correct substrate preparation is critical for optimum performance. Surfaces must be structurally sound, clean and free from loose particles, oil, grease and all other contaminants. Remove oil, grease and wax contaminants by scrubbing with industrial grade detergent or degreasing compound followed by mechanical cleaning. Cement laitance, loose particles, mould release agent, curing membrane and other contaminants must be removed from surface by shot blasting, scarifying or grit blasting followed by vacuum cleaning. After pretreatment of the substrate, the bonding strength of the substrate must be at least 1.5 N/mm2. MAXIFLOOR® MFC 200 WB Epoxy Cement should not be exposed to water, chemicals or mechanical stress for at least 24 hours.

SURFACE PREPARATION

Primer :MAXIFLOOR® MFC 200 WB Epoxy Cement (comp. A + B), approx.100 – 200 g/m2 depending on substrate condition. Self leveling floor system :MAXIFLOOR® MFC 200 WB Epoxy Cement (Comp. A + B + C ), approx. 4.5 Kg/m2 for 2 mm layer thickness.

MATERIAL CONSUMPTION

Prior to mixing, stir Part A (resin) well, then add all of Part B (hardener) and mix both liquid parts thoroughly with a lowspeed electric stirrer for a minimum of one minute until a uniform mix has been achieved. To achieve good bond of the mortar to the substrate, mixed Part A + Part B must be used as a primer. Gradually add Part C (aggregate) to the mixed resin parts in the mixer for a further 3 minutes minimum, until a uniform moist mix is obtained.Use a low speed drill (500 rpm) and a helical mixer to mix MAXIFLOOR®MFC 200 WB Epoxy Cement Part A, B and C. Pour the mixed MAXIFLOOR® MFC 200 WB Epoxy Concrete onto the substrate and spread evenly with a rubber squeegee to the required levels, achieving a flat surface. Light spike rolling should be carried out within 3 minutes of application in order to avoid interfering with the film gel time. Clean all tools and application equipment with water immediately after use. Hardened material can only be mechanically removed.

APPLICATION INSTRUCTIONS

TECHNICAL DATA

MAXIFLOOR® MFC 200 WB EPOXY CEMENT

The information in this data sheet is given to the best of our knowledge based on laboratory testing and practical experience. However, as the product is often used under conditions beyond our control, we cannot guarantee anything but the quality of the product itself. We reserve the right to change the given data without notice.

DISCLAIMER

TECHNICAL DATA