SUBMTTED BY-
Koushik Das
1st sem,Roll no. 10
School Of Industrial Fisheries
C.U.S.A.T
MARINE CORROSION
![Page 2: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/2.jpg)
Corrosion, fouling & boring of the hulls of fishing vessels are serious problems of “high economic significance”.
Fouling in marine environment is initiated by the micro-organisms like bacteria, fungi & algae to the surface of the exposed material known as “Bioflim”.
More than 4000 species of animals and plants which are include bacteria, diatoms, algae, fungi, protozoan, etc. are recorded from fouling communities (Venkatesan et al.,2006)
Introduction
![Page 3: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/3.jpg)
Corrosion is the term used to described the conversion of a metal to a non-metallic state.
Corrosion is defined as the destruction of a metal
by chemical or electro-chemical reaction with it’s environment.
Metal + Environment Metal Compound + Free Energy
Corrosion:
(Fe; Zn) (H2 o; O2; H2S) (Metallic Oxide, Hydroxide, Sulphide) (Fe2 O3, Fe(OH)2, Fe(OH)3, ZnS)
![Page 4: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/4.jpg)
UNIFORM/ GENERAL CORROSION
GALVANIC/ TWO METAL CORROSION
CONCENTRATION CELL/ CREVICE CORROSION
PITTING CORROSION
MICRO-BIOLOGICALLY INDUCED CORROSION
STRESS CORROSION
EROSION CORROSION
FILLIFORM CORROSION
SELECTIVE CORROSION
TYPES OF CORROSION:-
![Page 5: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/5.jpg)
In this type of corrosion take place uniformly over the surface of the metals.
Uniform corrosion can be prevented by selecting corrosion resistant alloys, apply chemical inhibitors & coating cathodic protection.
Metals such as steel that do not form passive films show uniform corrosion.
Uniform corrosion:
![Page 6: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/6.jpg)
![Page 7: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/7.jpg)
Corrosion which occurs when dissimilar metals are in electric contact in presence of an electrolyte such as seawater is termed as galvanic corrosion.
Galvanic corrosion can be prevented by selecting the alloys of similar electro-chemical nature (making the area more actively corroding material ‘anode’ larger than the ‘cathode’).
Galvanic corrosion:
![Page 8: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/8.jpg)
![Page 9: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/9.jpg)
It is a localized corrosion which may occur in small areas of stagnant solution in crevice, joints & under corrosion deposits.
This can be prevented by closing the crevices with non-absorbent materials & preventing build up of scales or any solids on the surface of material.
Crevice corrosion:
![Page 10: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/10.jpg)
![Page 11: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/11.jpg)
It is a highly localized corrosion occurs on the metal surface. It occurs as a process of local anodic dissolution where metal loss is the presence of small anode & large cathode.
Pitting corrosion can be prevented by increasing the velocity of media or removal deposits of solids form exposed metal surface.
Suitable selection of alloys, chemical inhibitor & de-aeration of aerated environment will help to reduce pitting.
Pitting corrosion:
![Page 12: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/12.jpg)
Pitting corrosion
![Page 13: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/13.jpg)
In the micro-biologically induced corrosion, micro- organisms like bacteria or fungi are involved in the degradation of material.
The type of organism involved in the process depend on the substrate and the environment.
It is a severe problem in the case of cooling water & submerged pipelines in soil.
Micro-biologically induced corrosion:
![Page 14: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/14.jpg)
![Page 15: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/15.jpg)
Stress corrosion cracking may be occurs at stresses well below the yield point of the alloy.
Generally, corrosion does not lead to the mechanical failure of structures or component because the reduction in cross sectional area is controlled either by choosing a corrosion resistant alloy or by applying suitable protective coating.
Stress corrosion
![Page 16: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/16.jpg)
![Page 17: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/17.jpg)
Interaction with particulate matter present in the fluid, flow of liquids in tubes especially at bends can leads to mechanical damage of the internal surface of tubes leading to erosion corrosion.
Erosion corrosion:
![Page 18: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/18.jpg)
![Page 19: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/19.jpg)
This is a process in which one of the materials of a binary alloy selectively dissolves leaving a spongy mass behind. An example is the corrosion in brass and bronze materials.
Selective corrosion:
![Page 20: Marine corrosion koushik das](https://reader035.fdocuments.us/reader035/viewer/2022062319/55493fccb4c9050a4d8b4fe6/html5/thumbnails/20.jpg)
THERMODYNAMIC
PROTECTION
KINETIC PROTECTIO
N
BARRIER PROTECTIO
N
STRUCTURAL DESIGN
METALLURGI-CAL DESIGN
HULL PROTECTIO
N OF FISHING VESSEL
PROTECTION OF
WOODN HULL
Corrosion prevention methods: