Joint Preparation & Joint Dimensions
Transcript of Joint Preparation & Joint Dimensions
![Page 1: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/1.jpg)
1
Joint Preparation & Joint Dimensions
June 2020
![Page 2: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/2.jpg)
Joints: Definitions
• Sealant: Material used to fill or seal the joint
• Side of the joint: Area where the sealant connects to the joint
• Depth of the joint: The depth of a joint which is required to be filled with a sealant to
get a correctly performing joint.
• Width of the joint: The width between the to sides of the joint
• Backing material: PU or PE material which is used in a joint to define the depth of the
joint and to prevent 3-point adhesion
• Joint movement: Every change in the width of the joint due to
• Temperature difference
• Difference in humidity
• Movement of the building elements due to shrink/expansion
• Movement due to environmental circumstances (traffic,
earthquakes, …….)
![Page 3: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/3.jpg)
Joints: Types of joint
Static joint
• Movement of the joint between the elements is less than 7% (+/- =
expansion/contraction)
Connection Joint
• Movement of the joint between the elements is between 7% and 15% (+/- =
expansion/contraction)
Expansion joint
• Movement of the joint between the elements is between 15% and 25% (+/- =
expansion/contraction)
![Page 4: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/4.jpg)
Application of sealants
• Joints must be clean, dry, free of dust and grease
• Optimal joint dimensions
• Primer, backer rod necessary?
• Taping to protect joint sides
• Application temperature
• Do not seal in rain or frost
• Humidity should be > 35%
• Apply sealant in joint
• Tool with soapy solution, rinse with clear water (to avoid soap stains)
4
![Page 5: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/5.jpg)
Primers for Porous (absorbing) Substrates
• Primers: used on porous substrates• Primer 100: isocyanate
based, used in combination with PU sealants.
• Primer 150: synthetic resins based, used in combination with silicones and SMX Polymers.
5
![Page 6: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/6.jpg)
Primer 100: PU sealants
porous substrates:• no plasticizer
migration (on natural stone)
• limits adhesion loss due to capillary water pressure
• prevents bubble formation
6
![Page 7: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/7.jpg)
Primer 150: silicones and hybrid (SMX)
porous substrates:• no plasticizer
migration (on natural stone)
• limits adhesion loss due to capillary water pressure
7
![Page 8: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/8.jpg)
Activators for Non-Porous Substrates
Surface Activator
• Dual function: cleaner and adhesion promoter in one
• Improves adhesion to non-porous substrates like metals and plastics.
• Leaves a white haze on the substrate, So only use on the covered-area
Activator Spray 601
• UNIVERSAL aerosol applied surface activator
• For use with silicone, PU and hybrid polymer basedsealants and adhesives.
• Used to improve the adhesion on anodized, lacqueredand powder coated aluminium.
• Also suitable for most plastics and other metals
8
![Page 9: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/9.jpg)
Joint dimensions – Elastic Sealants
Silicone, Polyurethanes, Hybrid (SMX),
1) Joint Size from 5-11mmdepth = widthE.g.• 5mm wide = 5mm deep• 6mm wide = 6mm deep• Etc…
2) Joint size from 12mm to max widthdepth = half the widthE.g.• 12mm wide = 6mm deep• 24mm wide = 12mm deep• Etc…
9
Correct dimensions will ensure high sealant performance over
many years.
![Page 10: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/10.jpg)
Joint dimensions – Plasto & Plasto-elastic
Acrylics and butyl mastics,
1) All recommended joint sizesdepth = width
E.g.• 5mm wide = 5mm deep• 6mm wide = 6mm deep• Etc…
10
![Page 11: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/11.jpg)
Common Issues
11
If sealant applied too deep- Then the elastic properties are reduced. - There is too much sealant in the joint so
not freely able to flex- Resulting in adhesive failure
If sealant applied too thin- When the joint stretches there is not
enough sealant resulting in a weaker joint which can break more easily
- Resulting in cohesive failure
![Page 12: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/12.jpg)
Joint : preparation
Backing rods are used to
determine correct depth and
are available in a range of
sizes.
![Page 13: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/13.jpg)
Possible causes of cracking
3 points adhesion will lock the sealant to 3 sides not allowing free movement.- Possible solution = backing rod
If the joint movement exceeds the > max. allowed distortion, then the sealant stretch and eventually tear.- Possible solution = ensure correct
product selection
13
![Page 14: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/14.jpg)
Preparation of the joint –NEW JOINTS
• The joint surfaces need to be :
• Dustfree
• Stable (free of loose material)
• Free of grease
• Dry
• Use backing material to achieve the correct joint
dimension and prevent 3-point adhesion
• Often preparation is needed:
• Surface preparation
• Primer
• Others
![Page 15: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/15.jpg)
Preparation of the joint –PREVIOUSLY SEALED JOINTS
• The joint surfaces need to be :
• Dustfree
• Stable (free of loose material)
• Free of grease
• Dry
• Use backing material to achieve the correct joint
dimension and prevent 3 point adhesion
• Often preparation is needed:
• Cut out existing sealant
• Surface preparation (Grinding)
• Primer
• Others
![Page 16: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/16.jpg)
Acrylic Range
16
![Page 17: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/17.jpg)
Silicone Range
17
![Page 18: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/18.jpg)
Silirub+ 8800
• Migration of silicone oil into the natural stone
• Always use marble silicone: silicone oil is linked on the siloxane polymer and cannot migrate out of the silicone sealant.
18
![Page 19: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/19.jpg)
PU Sealants –Hybrid Polymer (SMX) Range
19
![Page 20: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/20.jpg)
ADHESION
• Porous and non-porous substrates
• Superior bonding to the widest range of substrates
DURABILITY
• Extended life cycle
• Crack resistant
• High UV resistance
• Non-shrinking and non-bubbling
APPLICATION
• Easy to work and tool
• Non-staining
• Faster curing
ENVIRONMENTALLY SAFE
• Solvent free
• Low VOC
• Low odour
• Isocyanate free
SMX® POLYMER ADVANTAGES
![Page 21: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/21.jpg)
POLYURETHANES contain isocyanates which is classified as a carcinogenic, some of the health effects of isocyanate exposure include:
• Cancer• Eye irritation - watering and discomfort• Irritation of the respiratory tract• Dryness of the throat• Tightness of the chest• Difficulty in breathing• Headaches• Asthma attacks• Reddening, swelling and blistering of exposed skin if not washed off• Dermatitis
Source: Guidance note Controlling isocyanate hazards at work (http://www.commerce.wa.gov.au)
WHAT ARE ISOCYANATES?
![Page 22: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/22.jpg)
UV Exposed Sealant
Polyurethane fully exposed to the elements
![Page 23: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/23.jpg)
SMX Polymer vs. PU sealant
UV-stability:result after 6 weeks in artificial climate room
23
SMX PU
![Page 24: Joint Preparation & Joint Dimensions](https://reader034.fdocuments.us/reader034/viewer/2022051915/6285167d0b69da25083fedd9/html5/thumbnails/24.jpg)