IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10...
-
Upload
blaze-blake -
Category
Documents
-
view
236 -
download
6
Transcript of IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10...
![Page 1: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/1.jpg)
IE 337: Materials & Manufacturing Processes
Lectures 7&8: Introduction to Metal Casting
Chapters 10 & 6
![Page 2: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/2.jpg)
Assignment
HW 2 due today CH 21,22 and 24 Problems In Assignments folder
2
![Page 3: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/3.jpg)
3
This Time
Basic Process Casting Terminology Heating Pouring Phase diagrams Solidification
![Page 4: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/4.jpg)
4
Flow of Molten Liquid Requires Heating
Heat Transfer of Liquid in Mold Cavity During and After Pouring
Solidification into Component
Casting
Common process attributes:
![Page 5: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/5.jpg)
5
Metal Casting Processes Categories
1. Expendable mold processes - mold is sacrificed to remove part Advantage: more complex shapes possible Disadvantage: production rates often limited by
time to make mold rather than casting itself
2. Permanent mold processes - mold is made of metal and can be used to make many castings Advantage: higher production rates Disadvantage: geometries limited by need to open
mold
![Page 6: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/6.jpg)
6
Overview of Sand Casting
Most widely used casting process, accounting for a significant majority of total tonnage cast
Nearly all alloys can be sand cast, including metals with high melting temperatures, such as steel, nickel, and titanium
Parts ranging in size from small to very large Production quantities from one to millions
![Page 7: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/7.jpg)
7Sand casting mold
Sand Casting
![Page 8: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/8.jpg)
8
Gating System
Channel through which molten metal flows into cavity from outside of mold
Consists of a downsprue, through which metal enters a runner leading to the main cavity
At top of downsprue, a pouring cup is often used to minimize splash and turbulence as the metal flows into downsprue
![Page 9: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/9.jpg)
9
Riser
Reservoir in the mold which is a source of liquid metal to compensate for shrinkage during solidification
The riser must be designed to freeze after the main casting in order to satisfy its function
![Page 10: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/10.jpg)
10
Heating the Metal
Heating furnaces are used to heat the metal to molten temperature sufficient for casting
The heat required is the sum of: 1. Heat to raise temperature to melting point
2. Heat of fusion to convert from solid to liquid
3. Heat to raise molten metal to desired temperature for pouring
![Page 11: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/11.jpg)
11
Heating the Metal
1. Heat to melting point: VCs(Tm-To)
2. Heat of fusion to convert from solid to liquid: VHf
3. Heat molten metal to pouring temp.: VCl(Tp-Tm)
density, V = volume, Cs = specific heat,
Hf = latent heat of fusion, T = temperature
• Properties vary with temperature and phase• Melting may occur over a temperature range• Heat loss to the ambient
![Page 12: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/12.jpg)
12
Pouring the Molten Metal
For this step to be successful, metal must flow into all regions of the mold, most importantly the main cavity, before solidifying
Factors that determine success: Pouring temperature Pouring rate Turbulence
![Page 13: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/13.jpg)
13
Pouring Calculations 1
Minimum mold filling time, MFT
MFT =V/Q
Q: volumetric flow rate, cm3/s
V: mold cavity volume, cm3
![Page 14: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/14.jpg)
14
Pouring Calculations 2
Volumetric flow rate remains constant
Q =v1A1 = v2A2
Q: volume rate of flow cm3/s
v: velocity of the liquid metal
A: cross-sectional area, cm2
CONTINUITY EQUATION
Increase in area results in decrease in velocity
![Page 15: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/15.jpg)
15
Pouring Calculations 3
Flow of liquid metal through gating system & mold
v = (2gh)1/2
v: velocity of the liquid metal at base of sprue
g = gravitational acceleration, 981 cm/s2
h = height of sprue, cm
![Page 16: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/16.jpg)
16
Example 1
The downsprue leading into the runner of a certain mold has a length = 175 mm.
The cross-sectional area at the base of the sprue is 400 mm2.
The mold cavity has a volume = 0.001 m3. Determine: (a) the velocity of the molten metal
flowing through the base of the downsprue, (b) the volumetric flow rate, and (c) the time required to fill the mold cavity.
![Page 17: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/17.jpg)
17
Example 1: Solution
(a) Velocity v = (2gh)0.5
= (2 x 9810 x 175)0.5 = 1853 mm/s
(b) Volume flow rate Q = vA = 1853 x 400 = 741,200 mm3/s
(c) Time to fill cavity MFT = V/Q
![Page 18: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/18.jpg)
18
Solidification of Pure Metals
A pure metal solidifies at a constant temperature equal to its freezing point (same as melting point)
![Page 19: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/19.jpg)
Solidification and Cooling
Figure 10.8 Shrinkage of a cylindrical casting during solidification and cooling: (0) starting level of molten metal immediately after pouring; (1) reduction in level caused by liquid contraction during cooling (dimensional reductions are exaggerated for clarity).
![Page 20: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/20.jpg)
20
Characteristic grain structure in a casting of a pure metal, showing randomly oriented grains of small size near the mold
wall, and large columnar grains oriented toward the center of the casting
Microstructure: I
![Page 21: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/21.jpg)
21
Most alloys freeze over a temperature range rather than at a single temperature
Solidification of Alloys
![Page 22: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/22.jpg)
22
Characteristic grain structure in an alloy casting, showing segregation of alloying components in center of casting
Microstructure: II
Micro-segregation
![Page 23: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/23.jpg)
23
Characteristic grain structure in an alloy casting, showing segregation of alloying components in center of casting
Microstructure: II
Macro-segregation
![Page 24: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/24.jpg)
Phase Diagrams
A graphical means of representing the phases of a metal alloy system as a function of composition and temperature
A phase diagram for an alloy system consisting of two elements at atmospheric pressure is called a binary phase diagram Other forms of phase diagrams are
discussed in texts on metallurgy and materials science
![Page 25: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/25.jpg)
Phase Diagrams
Composition is plotted on the horizontal axis and temperature on the vertical axis
Any point in the diagram indicates the overall composition and the phase or phases present at the given temperature under equilibrium conditions
![Page 26: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/26.jpg)
Copper-Nickel Phase Diagram
Figure 6.2 Phase diagram for the copper‑nickel alloy system.
![Page 27: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/27.jpg)
Copper‑Nickel (Cu-Ni) Alloy System
Solid solution alloy throughout entire range of compositions below the solidus
No intermediate solid phases in this alloy system
However, there is a mixture of phases (solid + liquid) in the region bounded by the solidus and liquidus
![Page 28: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/28.jpg)
Chemical Compositions of Phases
The overall composition of the alloy is given by its position along the horizontal axis
However, the compositions of liquid and solid phases are not the same These compositions can be found by
drawing a horizontal line at the temperature of interest
Where the line intersects the solidus and liquidus indicates the compositions of solid and liquid phases, respectively
![Page 29: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/29.jpg)
Example
Determine compositions of liquid and solid phases in the Cu-Ni system at an aggregate composition of 50% nickel and a temperature of 1316oC (2400oF)
![Page 30: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/30.jpg)
Inverse Lever Rule – Step 1
The phase diagram can be used to determine the amounts of each phase present at a given temperature Using the horizontal line that indicates
overall composition at a given temperature, measure the distances between the aggregate composition and the intersection points with the liquidus and solidus, identifying the distances as CL and CS, respectively
![Page 31: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/31.jpg)
Inverse Lever Rule – Step 2
The proportion of liquid phase present is given by
L phase proportion =
And the proportion of solid phase present is given by
S phase proportion =
)( CLCSCS
CLCSCL
![Page 32: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/32.jpg)
Applications of the Inverse Lever Rule
Methods for determining chemical composition of phases and amounts of each phase are applicable to the solid region of the phase diagram as well as the liquidus‑solidus region
Wherever there are regions in which two phases are present, these methods can be utilized
When only one phase is present, the composition of the phase is its aggregate composition under equilibrium conditions, and the inverse lever rule does not apply
![Page 33: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/33.jpg)
Tin-Lead Phase Diagram
Figure 6.3 Phase diagram for the tin‑lead alloy system.
![Page 34: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/34.jpg)
34
Mechanical properties of 2 identical composition samples with different cooling rates
Effect of Solidification Rate
![Page 35: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/35.jpg)
Solidification Time
Solidification takes time Total solidification time TST = time required for
casting to solidify after pouring TST depends on size and shape of casting by
relationship known as Chvorinov's Rule
35
![Page 36: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/36.jpg)
Chvorinov's Rule
where TST = total solidification time; V = volume of the casting; A = surface area of casting; n = exponent usually taken to have a value = 2; and Cm is mold constant
n
m A
VCTST
36
![Page 37: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/37.jpg)
Mold Constant in Chvorinov's Rule
Cm depends on mold material, thermal properties of casting metal, and pouring temperature relative to melting point
Value of Cm for a given casting operation can be based on experimental data from previous operations carried out using same mold material, metal, and pouring temperature, even though the shape of the part may be quite different
37
![Page 38: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/38.jpg)
Example 1
In casting experiments performed using a titanium alloy and a zircon sand mold, it took 155 s for a cube-shaped casting to solidify. The cube was 50 mm on a side.
If the same alloy and mold type were used, find the total solidification time for a cylindrical casting in which the diameter = 30 mm and length = 50 mm.
38
![Page 39: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/39.jpg)
Example 1: Solution
Cube Volume V = (50)3 = 125,000 mm3
Cube Area A = 6 x (50)2 = 15,000 mm2
Cube (V/A) = 125,000/15,000 = 8.33 mm
Cm = TST/(V/A)2
= 155/(8.33)2
= 2.23 s/mm2
Cylinder Volume V = D2L/4 = (30)2(50)/4
= 35,343 mm3
Cylinder Area A = 2D2/4 + DL = (30)2/2 + (30)(50)= 6126 mm2
Cylinder (V/A) = 35,343/6126 = 5.77 mm
TST = Cm(V/A)2
= 2.23 (5.77)2 = 74.3 s39
![Page 40: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/40.jpg)
What Chvorinov's Rule Tells Us
A casting with a higher volume‑to‑surface area ratio cools and solidifies more slowly than one with a lower ratio
Since riser and casting mold constants will be equal, design the riser to have a larger volume‑to‑area ratio so that the main casting solidifies first
40
![Page 41: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/41.jpg)
Shrinkage in Solidification and Cooling
Figure 10.8 Shrinkage of a cylindrical casting during solidification and cooling: (0) starting level of molten metal immediately after pouring; (1) reduction in level caused by liquid contraction during cooling (dimensional reductions are exaggerated for clarity).
![Page 42: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/42.jpg)
Shrinkage in Solidification and Cooling
Figure 10.8 (2) reduction in height and formation of shrinkage cavity caused by solidification shrinkage; (3) further reduction in height and diameter due to thermal contraction during cooling of solid metal (dimensional reductions are exaggerated for clarity).
![Page 43: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/43.jpg)
43
Solidification Shrinkage
Occurs in nearly all metals because the solid phase has a higher density than the liquid phase
Thus, solidification causes a reduction in volume per unit weight of metal
Exception: cast iron with high C content Graphitization during final stages of freezing causes
expansion that counteracts volumetric decrease associated with phase change
![Page 44: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/44.jpg)
44
Shrinkage Allowance
Patternmakers account for solidification shrinkage and thermal contraction by making mold cavity oversized (See Table 10.1)
Amount by which mold is made larger relative to final casting size is called pattern shrinkage allowance
![Page 45: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/45.jpg)
45
Example 2
A mold cavity has the shape of a cube, 100 mm on a side. Determine the volume and dimensions of the final cube after cooling to room temperature if the cast metal is copper.
Assume that the mold is full at the start of solidification and that shrinkage occurs uniformly in all directions.
For copper, solidification shrinkage is 4.9%, solid contraction during cooling is 7.5%.
![Page 46: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/46.jpg)
46
Example 2: Solution
Volume of cavity V = (100)3 = 106 mm3
Volume of casting V = 106(1-0.049)(1-0.075) = 879,675 mm3
Dimension on each side of cube = (879,675)0.333 = 95.82 mm
![Page 47: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/47.jpg)
47
You should have learned
Basic Process Sand Casting Terminology Heating Pouring Phase diagrams Solidification
![Page 48: IE 337: Materials & Manufacturing Processes Lectures 7&8: Introduction to Metal Casting Chapters 10 & 6.](https://reader035.fdocuments.us/reader035/viewer/2022062221/56649cd75503460f9499eab0/html5/thumbnails/48.jpg)
48
Next Class
Casting Continued Chapter 11