Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
CONTENTS
SR. No.
Description Page No.
1 INTRODUCTION
1.1 Overview of composites
1.2 Merits & Demerits of Composite
1.3. Scope of the project
2 LITERATURE SURVEY
2.1 Objectives of the Present Work
3 MATERIALS AND METHODS
3.1. Introduction
3.2. Characterization of the Composites
3.3. Processing of the Composites
4 RESULTS & ANALYSIS
4.1 Result & Discussion
4.2. Design Parameter for Composite Leaf Spring
4.3. Design of experiments
6 CONCLUSIONS
6.1. Scope for Future Work
REFERENCES
1
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
ABSTRACT
LIST OF ABBREVIATIONS
FEM – Finite Element Method
FEA –Finite Element Analysis
GFRP – Glass Fiber Reinforced Polymer
E – Modulus of Elasticity
G – Modulus of Rigidity
σ – Stress
µ – Poissons Ration
e – Strain
P – Applied load
M – Material
2
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
CHAPTER-1
INTRODUCTION
1.1 General
In order to conserve natural resources and economize energy, weight reduction has been
the main focus of automobile manufacturers in the present scenario. Weight reduction can be
achieved primarily by the introduction of better material, design optimization and better
manufacturing processes. The suspension leaf spring is one of the potential items for weight
reduction in automobiles as it accounts for 10% - 20% of the unsprung weight. This achieves the
vehicle with more fuel efficiency and improved riding qualities. The introduction of composite
materials was made it possible to reduce the weight of leaf spring without any reduction on load
carrying capacity and stiffness. Since, the composite materials have more elastic strain energy
storage capacity and high strength to weight ratio as compared with those of steel, multi-leaf
steel springs are being replaced by mono-leaf composite springs. The composite material offer
opportunities for substantial weight saving but not always be cost-effective over their steel
counterparts.
Fiber-reinforced polymers have been vigorously developed for many applications, mainly
because of the potential for weight savings. Other advantages of using fiber-reinforced polymers
instead of steel are: (a) the possibility of reducing noise, vibrations and ride harshness due to
their high damping factors; (b) the absence of corrosion problems, which means lower
maintenance costs; and (c) lower tooling costs, which has favorable impact on the manufacturing
costs [1]. Springs are crucial suspension elements in cars, necessary to minimize the vertical
vibrations, impacts and bumps due to road regularities[2]. The functions of the suspension
springs for an automobile are to maintain a good control stability and to improve riding comfort
due to composite design and manufacturing, complications arise; for example, the change from
relatively isotropic-homogeneous steel alloys to anisotropic in homogeneous fiber reinforcement
plastic has not yet been achieved [3 & 4]. The behavior of steel leaf spring is non linear,
relatively high weight, and change in solid axle angle due to weight transfer specially during
cornering of vehicle, that will lead to over steer and directional instability under such situation it
is very difficult for driver to control vehicle, these are some defect of metallic leaf spring so
considering automobile development and importance of relative aspect such as fuel consumption,
3
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
weight, riding quality, and handling, so development of new material is necessary in the
automobile industry. Recently, graphite and carbon fiber demonstrate its superiority over other
composite material however due to cost and availability limitation the present work restricted to
leaf spring made up of glass fiber and Epoxy resin.
Many papers were devoted to find spring geometry. The recently vehicle such as Ford,
and Volvo buses are using leaf spring made up of carbon fiber as it gives good advantage but
costly. So in this select glass fiber and general purpose resin for spring material on the basis of
cost factor and strength.
1.1. Overview of composites
Composite materials (or composites for short) are engineering materials made from two
or more constituent materials that remain separate and distinct on a macroscopic level while
forming a single component. There are two categories of constituent materials: matrix and
reinforcement. At least one portion of each type is required. The matrix material surrounds and
supports the reinforcement materials by maintaining their relative positions. The reinforcements
impart their special mechanical and physical properties to enhance the matrix properties. The
primary functions of the matrix are to transfer stresses between the reinforcing fibers/particles
and to protect them from mechanical and/or environmental damage whereas the presence of
fibers/particles in a composite improves its mechanical properties such as strength, stiffness etc.
A composite is therefore a synergistic combination of two or more micro-constituents that differ
in physical form and chemical composition and which are insoluble in each other. The objective
is to take advantage of the superior properties of both materials without compromising on the
weakness of either. The synergism produces material properties unavailable from the individual
constituent materials. Due to the wide variety of matrix and reinforcement materials available,
the design potentials are incredible. Composite materials have successfully substituted the
traditional materials in several light weight and high strength applications. The reasons why
composites are selected for such applications are mainly their high strength-toweight ratio, high
tensile strength at elevated temperatures, high creep resistance and high toughness. Typically, in
a composite, the reinforcing materials are strong with low densities while the matrix is usually a
ductile or tough material. If the composite is designed and fabricated correctly it combines the
strength of the reinforcement with the toughness of the matrix to achieve a combination of
desirable properties not available in any single 3 conventional material. The strength of the
4
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
composites depends primarily on the amount, arrangement and type of fiber and /or particle
reinforcement in the resin.
They are:
a) Metal Matrix Composites (MMC)
b) Ceramic Matrix Composites (CMC)
c) Polymer Matrix Composites (PMC)
a) Metal Matrix Composites
Metal Matrix Composites have many advantages over monolithic metals like higher
specific modulus, higher specific strength, better properties at elevated temperatures, and lower
coefficient of thermal expansion. Because of these attributes metal matrix composites are under
consideration for wide range of applications viz. combustion chamber nozzle (in rocket, space
shuttle), housings, tubing, cables, heat exchangers, structural members etc.
b) Ceramic matrix Composites
One of the main objectives in producing ceramic matrix composites is to increase the
toughness. Naturally it is hoped and indeed often found that there is a concomitant improvement
in strength and stiffness of ceramic matrix composites.
c) Polymer Matrix Composites
Most commonly used matrix materials are polymeric. The reason for this are twofold. In
general the mechanical properties of polymers are inadequate for many structural purposes. In
particular their strength and stiffness are low compared to metals and ceramics. These difficulties
are overcome by reinforcing other materials with polymers. Secondly the processing of polymer
matrix composites need not involve high pressure and doesn’t require high temperature. Also
equipments required for manufacturing polymer matrix composites are simpler. For this reason
polymer matrix composites developed rapidly and soon became popular for structural
applications. Composites are used because overall properties of the composites are superior to
those of the individual components for example polymer/ceramic. Composites have a greater
modulus than the polymer component but are not as brittle as ceramics.
Two types of polymer composites are:
• Fiber reinforced polymer (FRP)
• Particle reinforced polymer (PRP)
Fiber Reinforced Polymer
5
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
Common fiber reinforced composites are composed of fibers and a matrix. Fibers are the
reinforcement and the main source of strength while matrix glues all the fibers together in shape
and transfers stresses between the reinforcing fibers. The fibers carry the loads along their
longitudinal directions. Sometimes, filler might be added to smooth the manufacturing process,
impact special properties to the composites, and reduce the product cost. Common fiber
reinforcing agents include asbestos, carbon / graphite fibers,
beryllium, beryllium carbide, beryllium oxide, molybdenum, aluminium oxide, glass fibers,
polyamide, natural fibers etc. Similarly common matrix materials include epoxy, phenolic,
polyester, polyurethane, polyetherethrketone (PEEK), vinyl ester etc. Among these resin
materials, PEEK is most widely used. Epoxy, which has higher adhesion and less shrinkage than
PEEK, comes in second for its high cost.
Particle Reinforced Polymer
Particles used for reinforcing include ceramics and glasses such as small mineral
particles, metal particles such as aluminium and amorphous materials, including polymers and
carbon black. Particles are used to increase the modules of the matrix and to decrease the
ductility of the matrix. Particles are also used to reduce the cost of the composites.
Reinforcements and matrices can be common, inexpensive materials and are easily processed.
Some of the useful properties of ceramics and glasses include high melting temp., low density,
high strength, stiffness; wear resistance, and corrosion resistance. Many ceramics are good
electrical and thermal insulators. Some ceramics have special properties; some ceramics are
magnetic materials; some are piezoelectric materials; and a few special ceramics are even
superconductors at very low temperatures. Ceramics and glasses have one major drawback: they
are brittle. An example of particle reinforced composites is an automobile tire, which has carbon
black particles in a matrix of poly-isobutylene elastomeric polymer. Polymer composite
materials have generated wide interest in various engineering fields, particularly in aerospace
applications. Research is underway worldwide to develop newer composites with varied
combinations of fibers and fillers so as to make them useable under different operational
conditions. Against this backdrop, the present work has been taken up to develop a series of
PEEK based composites with glass fiber reinforcement and with ceramic fillers and to study their
response to solid particle erosion.
6
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
The composite materials have got a widely applications in all cutting-edge ranges of
advanced materials as aeronautics, automotives, boats, sports parts and medical devices. As a
general definition, the composite material has more versions, and ones of them can be as a
material composed by the combination of two or more materials: a reinforcing element and a
compatible resin binder (matrix) to obtain specific characteristics and properties.
The roles of matrix in composite materials are to give shape to the composite part, protect
the reinforcements to the environment, transfer loads to reinforcements and toughness of
material, together with reinforcements. The aims of reinforcements in composites are to get
strength, stiffness and other mechanical properties, dominate other properties as coefficient of
thermal extension, conductivity and thermal transport.
1.2. Merits & Demerits of Composites
Advantages of composites over their conventional counterparts are the ability to meet
diverse design requirements with significant weight savings as well as strength-to-weight ratio.
Some advantages of composite materials over conventional are as follows: -
Tensile strength of composites is four to six times greater than that of steel.
Improved torsional stiffness and impact properties.
Lower embedded energy compared to other structural metallic materials like steel,
aluminum etc.
Composites are less noisy while in operation and provide lower vibration transmission
than metals.
Composites are more versatile than metals and can be tailored to meet performance needs
and complex design requirements.
Long life offer excellent fatigue, impact, environmental resistance and reduce
maintenance.
Composites enjoy reduced life cycle cost compared to metals. Composites exhibit
excellent corrosion resistance and fire retardancy.
Improved appearance with smooth surfaces and readily incorporable integral decorative
melamine are other characteristics of composites.
Composite parts can eliminate joints / fasteners, providing part simplification and
integrated design compared to conventional metallic parts.
7
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
Broadly, composite materials can be classified into three groups on the basis of matrix
material.
Such as Demerits of composites are the followings:
Cost of materials
Long development time
Low ductility
Temperature limits
Solvent or moister attack
Hidden damages and damage susceptibility
1.2.3 E-Glass/Epoxy Data Sheet
Key Characteristics Test Method Units - English (SI) Typical Values
Specific Gravity -- lb./in. (g/cc) 0.064 (1.77)
Rockwell Hardness (.50”) -- M Scale 99
Tensile Strength (.125”) LW CW ASTM D-638 psi (MPa)
43,000 (296) 39,000 (269)
Compressive Strength, Flatwise (.50”)
ASTM D-695 psi (MPa) 44,000 (303)
Flexural Strength (.062”) LW CW ASTM D-790 psi (MPa) 66,000 (455) 60,000 (413)
Flexural Modulus (.062”) LW CW ASTM D-790 ksi (MPa)
3,400 (23,442) 3,300 (22,753)
Shear Strength, Perpendicular (.062”)
ASTM D-732 psi (MPa) 19,000 (130)
IZOD Impact Strength LW CW ASTM D-256 ft.-lbs./in. Notched 9.5 7.5
Dielectric Strength (.062”) Condition A D-48/50 ASTM D-149 V/mil 960 1,000
Breakdown Voltage (.062”) Condition A D-48/50 ASTM D-149 kV 66 65
1.3 Composites Applications
The advanced composite materials can be used for applications demand high strength,
high stiffness, or low thermal conductivity, which substituted many aerospace , aircrafts,
automotives, marines, constructions parts by metal with these composites .
Advanced composites contained materials such as carbon/graphite, boron or aramid
fibers in an organic resin matrix used by aerospace’s industries. The special properties of these
materials, examples lightweight, stiffness and strong materials are used from aircraft structures to
8
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
automotive and trucks parts, from spacecraft to printed circuit boards, sports equipment, such as:
the gamut for boat hulls and hokey shine guards, advanced composite hinge for retractable arm
of space shuttle.
Carbon/graphite-reinforced composites are used in many applications, which required
thermal stability, high temperature strength, good ablation characteristics and insulating
capability.
Graphite fibers are used in place where required greater strength and higher thermal
conductivity, have six times the tensile strength of carbon fibers.
Carbon fibers are used in rocket nozzle thoughts and ablation chambers, because of them
physically stability and elevated temperature.
In generally, the composite materials can change with success the metal parts in diverse
application, for example will be analysis the altering of slide bearing of bimetallic material from
machine tools with bearing of composites, by used the finite element analysis (FEA).
1.4. Scope of the project
1. The basic aim of the present work is to develop and characterize a new class of composites
material with a polymer called epoxy-Resin as the matrix and glass fiber as the reinforcing
material.
2. Their physical and mechanical characterization is done.
3. Vibrational behavior of this new class of composites is investigated in this project work.
Deflection is performed on the composites material for leaf spring application.
4. This work is expected to introduce a new class of functional polymer composites suitable for
tribological & suspension applications.
1.3.1 Historical background
9
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
CHAPTER 2
LITERATURE SURVEY
This chapter outlines some of the recent reports published in literature on composites
with special emphasis on erosion wear behavior of glass fiber reinforced polymer composites.
Polymers have generated wide interest in various engineering fields including tribological
applications, in view of their good strength and low density as compared to monolithic metal
alloys. Being lightweight they are the most suitable materials for weight sensitive uses, but their
high cost sometimes becomes the limiting factor for commercial applications. Use of low cost,
easily available fillers is therefore useful to bring down the cost of component. Study of the
effect of such filler addition is necessary to ensure that the mechanical properties of the
composites are not affected adversely by such addition. Available references suggest a large
number of materials to be used as fillers in polymers [5]. The purpose of use of fillers can
therefore be divided into two basic categories; first, to improve the mechanical, thermal or
tribological properties and second, to reduce the cost of the component. There have been various
reports on use of materials such as minerals and inorganic oxides, such as alumina and silica
mixed into widely employed thermoplastic polymers like polypropylene [6,7] and polyethylene
[8,9]. But very few attempts have indeed been made to utilize cheap materials like industrial
wastes in preparing particle-reinforced polymer composites. A key feature of particulate
reinforced polymer composites that makes them so promising as engineering materials is the
opportunity to tailor the materials properties through the control of filler content and matrix
combinations and the selection of processing techniques. A judicious selection of matrix and the
reinforcing solid particulate phase can lead to a composite with a combination of strength and
modulus comparable to or even better than those of conventional metallic materials [10]. Hard
particulate fillers consisting of ceramic or metal particles and fiber fillers made of glass are being
used these days to dramatically improve the wear resistance of composites, even up to 9 three
orders of magnitude [11]. The improved performance of polymers and their composites in
automobile applications by the addition of particulate fillers has shown a great promise and so
has lately been a subject of considerable interest. Various kinds of polymers and polymer matrix
composites reinforced with metal particles have a wide range of industrial applications such as
10
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
heaters, electrodes [12], composites with thermal durability at high temperature [13] etc. These
engineering composites are desired due to their low density, high corrosion resistance, ease of
fabrication, and low cost [14, 15]. Similarly, ceramic filled polymer composites have been the
subject of extensive research in last two decades.
According to Roberts and M. INST B.E.(1954), there is no exaggeration to say that
springs are the life blood of modern civilized life, for without springs the great development
which has taken place in engineering and mechanical science would have been impossible.
Simple everyday actions, such as the latching or locking of a door, or turning on an electric light,
are controlled by springs. Springs are essential for working of clocks, watches, gramophone,
wireless, the intricate mechanism of automatic telephone, and the gigantic printing presses and
weaving looms. Modern travel would be impossible without springs, many thousands of different
types being used in bicycles, motor cycles, cars and aircraft.
Springs are unlike other machine/structure components in that they undergo significant
deformation when loaded; their compliance enables them to store readily recoverable mechanical
energy. It is well known that springs, in general, are designed to absorb and store energy and
then release it. Hence, the strain energy of the material and the shape become a major factor in
designing the springs (Al-Qureshi, 2001). In a vehicle suspension, when the wheel meets an
obstacle, the springing allows movement of the wheel over the obstacle and thereafter returns the
wheel to its normal position (i.e. to be resilient).
The elliptic composite springs described by Mallick (1987) represents the first step in
introducing fiber reinforced composite elliptic springs for automotive applications. Mechanical
performance and failure modes of composite elliptic spring elements under static load conditions
were also reported. Key design parameters, such as spring rate and failure load were measured as
a function of spring thickness.
Nowadays, the industrial vehicles have to reduce their tare weight and to improve safety
as well as life expectancy; one solution to this is the replacement of steel springs with composite.
As stated by Sardou and Djomseu (2000), there are three ways to introduce composite on vehicle
suspension. The first is to take away a metal leaf spring and put in place a composite leaf spring.
Second is to design a composite axle doing anti roll as well as spring and guidance task. The last
one is to design a metal suspension and to use composite spring only for its vehicle properties. First
and second solutions design the composite to carry a complex job of wheel control and suspension
11
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
spring. The task is rather complex for composite and end up with a relatively small benefit in weight
and cost, on top of that suspension quality is relatively poor. However, in the field of vehicle
suspension, the industry looks for a cost effective composite spring with minimum mass capable of
resisting corrosion and possessing a high degree of durability. Therefore, the automobile industry has
shown increased interest in the replacement of steel springs with composite springs especially glass
fibre composites rather than others such as carbon fiber due to the cost factor.
Testing of Steel and Composite Mono Leaf Spring [23]
The steel and composite leaf springs are tested in the Leaf spring test rig. The experimental set
up is shown in Figs.2 (a) and (c). The leaf springs are tested following
standard procedures recommended by SAE. The spring to be tested is examined for any
defects like cracks, surface abnormalities, etc. The spring is loaded from zero to the prescribed
maximum deflection and back to zero. The load is applied at the centre of spring; the vertical
deflection of the spring centre is recorded in the load interval of 50N.
Fig.2.4 (a) Static test of steel leaf spring Fig. 2.4 (b) Static test of composite leaf spring.
The optimum values for the design variables, constraints and leaf spring weight obtained
through the GA process. The obtained GA results were compared with experimental data.
Results comparison of load, deflection and stresses are shown in Table 2. These optimum
values obtained through the GA is shown in Table 3 and illustrated in Fig. 3 to 7.
Table 2.7 Comparison results of load, deflection and stresses
12
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
The weight of the composite leaf spring can be reduced by 53.5% from 38.8 N to 18.04 N
by applying the GA optimization technique.
Composite mono leaf spring reduces the weight by 85% for E-Glass/Epoxy over
conventional leaf spring. The reduction of 93%weight is achieved by replacing
conventional steel spring with an optimally designed composite mono-leaf spring.
From the results, it is observed that the composite leaf spring is lighter and more
economical than the conventional steel spring with similar design specifications
The study demonstrated that composites can be used for leaf springs for light weight
vehicles and meet the requirements, together with substantial weight savings
As stated by Sardou and Djomseu (2000), there are three ways to introduce composite on
vehicle suspension. The first is to take away a metal leaf spring and put in place a composite leaf
spring. Second is to design a composite axle doing anti roll as well as spring and guidance task.
The last one is to design a metal suspension and to use composite spring only for its vehicle
properties. First and second solutions design the composite to carry a complex job of wheel control
and suspension spring. The task is rather complex for composite and end up with a relatively small
benefit in weight and cost, on top of that suspension quality is relatively poor. However, in the field
of vehicle suspension, the industry looks for a cost effective composite spring with minimum mass
capable of resisting corrosion and possessing a high degree of durability. Therefore, the automobile
industry has shown increased interest in the replacement of steel springs with composite springs
especially glass fibre composites rather than others such as carbon fiber due to the cost factor.
Accourding To Gulur Siddaramanna Shiva Shankar∗, Sambagam Vijayarangan Received
20 June 2005; Accepted 07 April 2006 (19)
The development of a composite mono leaf spring having constant cross sectional area,
here the stress level at any station in the leaf spring is considered constant due to the
parabolic type of the thickness of the spring, has proved to be very effective.
The study demonstrated that composites can be used for leaf springs for light weight
vehicles and meet the requirements, together with substantial weight savings.
The 3-D modeling of both steel and composite leaf spring is done and analysed using
ANSYS.
A comparative study has been made between composite and steel leaf spring with respect
to weight, cost and strength.
13
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
The analytical results were compared with FEA and the results show good agreement
with test results.
From the results, it is observed that the composite leaf spring is lighter and more
economical than the conventional steel spring with similar design specifications.
Adhesively bonded end joints enhance the performance of composite leaf spring for
delamination and stress concentration at the end in compare with bolted joints.
Composite mono leaf spring reduces the weight by 85 % for E-Glass/Epoxy, 91 % for
Graphite/Epoxy, and 90 % for Carbon/Epoxy over conventional leaf spring.
As per M. M. Patunkar & D. R. Dolas “Modelling and Analysis of Composite Leaf Spring under
the Static Load Condition by using FEA” (20)
Under the same static load conditions deflection and stresses of steel leaf spring and
composite leaf spring are found with the great difference. Deflection of Composite leaf
spring is less as compared to steel leaf spring with the same loading condition.
Conventional steel leaf spring was found to weigh 23 Kg. whereas E-Glass/Epoxy mono
leaf spring weighs only 3.59 Kg. Indicating reductions in weight by 84.40% same level of
performance.
Conventional Leaf spring show failure at eye end only. At maximum load condition also
Composite Leaf Spring shows the minimum deflection as compared to Steel Leaf Spring.
Composite leaf spring can be used on smooth roads with very high performance
expectations.
However on rough road conditions due to lower chipping resistance failure from chipping
of composite leaf spring is highly probable.
As per J P Hou, J-Y Cherruault, G Jeronimidis and R Mayer (25) A new design of the double-
leaf spring has been presented in this paper. Static tests show that the springs can carry safely the
specified 150 kN maximum load. The composite double-leaf spring has similar static stiffness’s
to the steel spring that it replaces. A dedicated shaker rig has been used to collect valuable
information on the dynamic response of the real system under various load conditions. Results
have shown that the system at tare load needs more damping to ensure a smoother ride. Finite
element predictions of stiffness, strain, and dynamic responses of the spring agree well with the
experimental results. This gives confidence in the use of finite element method for the design of
composite springs and for performance predictions. Results from FEA also show that the bottom
14
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
leaf can maintain the gross vehicle mass in the case where the top leaf fails by delimitation. This
mode of failure is a safe one, as the eye end remains intact. Investigation of composite leaf
spring in the early failed to yield the production facility because of inconsistent fatigue
performance and absence of strong need for mass reduction. Researches in the area of
automobile components have been receiving considerable attention now. Particularly the
automobile manufacturers and parts makers have been attempting to reduce the weight of the
vehicles in recent years. Emphasis of vehicles weight reduction in 1978 justified taking a new
look at composite springs. The development of a lite flex suspension leaf spring is first achieved.
Based on consideration of chipping resistance base part resistance and fatigue resistance, a
carbon glass fiber hybrid laminated spring is constructed. A general discussion on analysis and
design of constant width, variable thickness, and composite leaf spring is presented. Recent
developments have been achieved in the field of materials improvement and quality assured for
composite leaf springs based on microstructure mechanism. All these literature report that the
cost of composite; leaf spring is higher than that of steel leaf spring. Hence an attempt has been
made to fabricate the composite leaf spring with the same cost as that of steel leaf spring.
Material properties and design of composite structures are reported in many literatures.
Very little information are available in connection with finite element analysis of leaf spring in
the literature, than too in 2D analysis of leaf spring. At the same time, the literature available
regarding experimental stress analysis more. The experimental procedures are described in
national and international standards. Recent emphasis on mass reduction and developments in
materials synthesis and processing technology has led to proven production vehicle equipment.
A lot of research has been done on natural fiber reinforced polymer composites but
research on coconut based polymer composites is very rare. Against this background, the present
research work has been undertaken, with an objective to explore the potential of coconut fiber
polymer composites and to study the mechanical and wear characterization of different
composites.
2.1 Objectives of the Present Work
The objectives of the project are outlined below.
Fabrication of glass fibre reinforced epoxy resin based hybrid composite with filler
content. Where we change the percentage of glass fiber.
Evaluation of mechanical properties (tensile strength, flexural, hardness,
15
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
impact strength etc.)
The present work is to design, fabricate and experimental testing and analysis of
composite spring made up of E-glass fiber, epoxy resin & Hardner with constant width
and thickness throughout its length.
CHAPTER-3
. MATERIALS AND METHODS
3.1. Introduction
This chapter describes the details of processing of the composites and the experimental
procedures followed for their characterization and process evaluation. The raw materials used in
this work are
16
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
1. E-glass Fiber
2. Dubeckot 520F Epoxy resin
3. Resin hardener
3.2 Material selection
Materials constitute nearly 60%-70% of the vehicle cost and contribute to the quality and
the performance of the vehicle. Even a small amount in weight reduction of the vehicle, may
have a wider economic impact. Composite materials are proved as suitable substitutes for steel in
connection with weight reduction of the vehicle. Hence, the composite material have been
selected for leaf spring design.
3.2.1 Fibres Selection
The commonly used fibers are carbon, glass, keviar, etc.. Among these, the glass fiber
has been selected based on the cost factor and strength. The types of glass fibers are C-glass,S-
glass and E-glass. The C-glass fiber is designed to give improved surface finish.S-glass fiber is
design to give very high modular, which is used particularly in aeronautic industries. The E-glass
fiber is a high quality glass, which is used as standard reinforcement fiber for all the present
systems well complying with mechanical property requirements. Thus, E-glass fiber was found
appropriate for this application.
3.2.2 Resins Selection
In a FRP leaf spring , the inter laminar shear strengths is controlled by the matrix system
used . since these are reinforcement fibers in the thickness direction , fiber do not influence inter
laminar shear strength. Therefore, the matrix system should have good inter laminar shear
strength characteristics compatibility to the selected reinforcement fiber. Many thermo set resins
such as polyester, vinyl ester, azpoxy resin are being used for fiber reinforcement plastics(FRP)
fabrication . Among these resin systems, epoxies show better inter laminar shear strength and
good mechanical properties. Hence, epoxide is found to be the best resins that would suit this
application. different grades of epoxy resins and hardener combinations are classifieds , based on
the mechanical properties.
Among these grades , the grade of epoxy resin selected is Dobeckot 520 F and the grade of
hardener used for this application is 758. Dobeckot 520 F is a solvent less epoxy resin.
Which in combination with hardener 758 cures into hard resin . Hardener 758 is a low viscosity
polyamine. Dobeckot 520 F , hardener 758 combination is characterized by
17
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
Good mechanical and electrical properties
Faster curing at room temperature
Good chemical resistance properties
3.3 PROPERTIES OF E-GLASS / EPOXY COMPOSITE
By considering the property variation in the tapered system improper bonding and
improper curing, etc. some constant of property value are reduced from calculated values using
equations. The material properties for E-glass / Epoxy composite for 60% of fiber volume is
given below: -
3.3.1 PROPERTIES VALUES
Tensile modulus along X direction (Ex),MPa 14000
Tensile modulus along Y direction (Ey),MPa 6030
Tensile modulus along Z direction (Ez),MPa 1530
Tensile strength of the material,MPa 800
Compressive strength of the material,MPa 450
Shear modulus along XY direction(Gxy),MPa 2433
Shear modulus along YZ direction(Gyz),MPa 1600
Shear modulus along ZX direction(Gzx),MPa 2433
Flexural modulus of the material,MPa 40000
Flexural strength of the material,MPa 1000
Poisson ratio along XY direction(NUxy) 0.217
Poisson ratio along YZ direction(NUyz) 0.366
Poisson ratio along ZX direction(NUzx) 0.217
3.4 Characterization of the Composites
3.4.1 Density
The theoretical density of composite materials in terms of weight fraction can easily be
obtained as for the following equations given by Agarwal and Broutman [26].
Where, W and ρ represent the weight fraction and density respectively. The suffix f, m and ct
stand for the fiber, matrix and the composite materials respectively. The composites under this
18
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
investigation consists of three components namely matrix, fiber and particulate filler. Hence the
modified form of the expression for the density of the composite can be written as
Where, the suffix „p’ indicates the particulate filler materials. The actual density of the
composite, however, can be determined experimentally by simple water immersion technique.
The volume fraction of voids in the composites is calculated using the following equation:
3.4.2 Micro-hardness measurement
Micro-hardness measurement is done using a Leitz micro-hardness tester. A diamond
indenter, in the form of a right pyramid with a square base and an angle 1360 between opposite
faces, is forced into the material under a load F. The two diagonals X and Y of the indentation
left on the surface of the material after removal of the load are measured and their arithmetic
mean L is calculated. In the present study, the load considered F = 24.54N and Vickers hardness
number is calculated using the following equation.
and
Where F is the applied load (N), L is the diagonal of square impression (mm), X is the horizontal
length (mm) and Y is the vertical length (mm).
3.4.3 Tensile and flexural strength
The tensile test is generally performed on flat specimens. The commonly used specimens
for tensile test are the dog-bone type and the straight side type with 14 end tabs. During the test a
uni-axial load is applied through both the ends of the specimen. The ASTM standard test method
for tensile properties of fiber resin composites has the designation D 3039-76. The length of the
test section should be 200 mm. The tensile test is performed in the universal testing machine
(UTM) Instron 1195 and results are analyzed to calculate the tensile strength of composite
19
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
samples. The short beam shear (SBS) tests are performed on the composite samples at room
temperature to evaluate the value of flexural strength (FS). It is a 3-point bend test, which
generally promotes failure by inter-laminar shear. The SBS test is conducted as per ASTM
standard (D2344- 84) using the same UTM. Span length of 40 mm and the cross head speed of 1
mm/min are maintained. The flexural strength (F.S.) of any composite specimen is determined
using the following equation.
Where, L is the span length of the sample. P is the load applied; b and t are the width and
thickness of the specimen respectively.
3.4.4 Physical and mechanical properties
The theoretical and measured densities of all composite samples along with the
corresponding volume fraction of voids are presented in Table 3. It may be noted that the
composite density values calculated theoretically from weight fractions using Eq. (2) are not in
agreement with the experimentally determined values. The difference is a measure of voids and
pores present in the composites.
3.5 Processing of the Composites
E-glass fibers are reinforced with Dubeckot 520F Epoxy resin, chemically belonging to
the epoxide family is used as the matrix material. Its common name is Bisphenol A Diglycidyl
Ether. The low temperature curing epoxy resin and corresponding hardener are mixed in a ratio
of 10:1 by weight as recommended. The epoxy resin and the hardener are supplied by Ciba
Geigy India Ltd. E-glass fiber and epoxy resin has modulus of 72.5 GPa and 3.42GPa
respectively and possess density of 2590 kg/m3 and 1100kg/m3 respectively. weight fraction of
glass fiber in the composite) is kept at 50% for all the samples. The castings are put under load
for about 24 hours for proper curing at room temperature. Specimens of suitable dimension are
cut using a diamond cutter for physical characterization and other test.
The material used as coarsely woven E-glass fiber having density 400 gsm. and Glass
fiber chopped stand mat (175-450 gsm) which gives maximum tensile strength, toughness and
low cost. The resin selection was main factor because it influences the economy of leaf spring
for reducing prize,. The resin used as Dobeckot 520 F. The hardener 758 is used with this resin.
20
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
(general purpose resin) the prepared matrix it consist of 10:1 mass ratio the mass ratio of resin to
hardener to fiber were calculated for each weight percentage composite based on size of mold,
desired thickness of composite and density of fiber and epoxy. Each. % wt prepared in separate
jar. In order to facilitate wetting of fibers and epoxy resin with pot life of 2 h is selected.
3.4 Composite fabrication
Preparation of mould:- Material used as Plywood. The mold was fabricated as per
desired dimension. Arc length = 1160mm. length of mould= 1010mm, width= 45mm, arc height
at axle=120 mm. The constant cross section design which ensures the fiber pass continuously
without interruption along length direction, which is advantageous to fiber reinforced structure.
The glass fiber were cut to desired length, so that they can be deposited on mold layer- by layer
during fabrication of composite leaf spring. Apply the wax/gel.. Prepare the solution of resin &
Place the first layer of glass fiber chopped mat on mould followed by epoxy resin solution over
mat. Wait for 5-10 min. Repeat the procedure till the desired thickness was obtained. The
duration of the process may take up to 25- 30 min. And finally remove the leaf spring from
mould.
Fig. 3.1: Prepared specimen of composite leaf spring Fig. 3.2: Graph Load vs Deflection
Testing of composite & steel leaf spring are takes place on UTM .
Various specification of UTM are as follows:- Make:- Heico New Delhi Model No.:- HL 9C:10
Capacity:- 20 ton Least weight- 10 kg. Maximum weight- 5 ton Dial gauge least count:-0.01mm
21
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
22
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
CHAPTER-4
EXPERIMENTAL METHODOLOGY
4.1 EXPERIMENTAL SETUP -
Move the plunger up to desired height so that we can fix the fixture and leaf spring for
test. Fix the position of fixture. On the fixture place the specimen. Set the universal testing
machine. Apply the loads in steps of 20 kg gradually. Note down the deflection readings.
Table-4.1 Deflection between composite and steel leaf spring
Leaf Spring Experimental Analytical [FEA]
STEEL 94 89.17 -
COMPOSITE 95 104.85 96.962
4.4 Stress analysis by using Ansys 10.0 Software
The element SHELL 99, SOLID 46 are the best suited for modeling of composite material.
SHELL 99 is an 8 – node, 3D shell element with six degree of freedom at each node. The
advantage of SOLID 46 is that we can stack several elements to model more than 250 layers.
Here selected element was SOLID 46.
Table 4.2 Stress analysis of composite and steel leaf spring
Leaf Spring Experimental Analytical [FEA]
STEEL 220.18 220.18 -
COMPOSITE 220.18 220.18 247.172
4.5 Performing a Static Analysis
The procedure for a static analysis consists of these tasks:
1. Build the Model
2. Define Parameters
The parameters for building the composite leaf spring are as follows-
Young's modulus is 11.9 GPa (EXX) value is 11900 MPa, Poison ratio is 0.217 XY(PRXY)
value is 0.217
Length of cantilever beam =505mm, Width of cantilever beam.= 45mm, Height of cantilever
beam. = 30mm
23
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
3. Stacking Sequence of Layers.
The stacking sequence of layer are shown fig having unidirectional fibre with stacking angle of
zero.
Table.4.3 Weight Comparison
Leaf Sprig Type Steel Composite
Weight 13.4 (with eye) 2.365 (without eye)
Fig. 4.1: Finite element model of composite leaf spring. Fig. 4.2: Mesh model of composite leaf spring
Fig. 4.3: Stacking sequences of layers. Fig. 4.4: Mesh model with application of load
24
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
Fig. 4.5: Deflection along y-direction Fig. 4.6: Deflection along x-direction
Fig. 4.7: Deflection along z-direction Fig. 4.8: Stresses along x-direction
25
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
CHAPTER-5
Result & Discussion
5.1 Background
Result & Discussion
The performance of existing steel leaf spring was compared with the fabricated
composite leaf spring. Testing has been done for unidirectional E-Glass/Epoxy mono composite
leaf spring. Since the composite leaf spring is able to withstand the static load, it is concluded
that there is no objection from strength point of view also, in the process of replacing the
conventional leaf spring by composite leaf spring. Since, the composite spring is designed for
same stiffness as that of steel leaf spring, both the springs are considered to be almost equal in
vehicle stability. The major disadvantages of composite leaf spring are sometimes breaking of
fibers. When composite leaf spring hit by stone then there is chances of breaking of fibers. This
may result in a loss of capability to flexural stiffness. But this depends on the condition of the
road. In normal road condition, this type of problem will not occur.
5.10 Summary:-
26
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
CHAPTER 6
CONCLUSIONS
This analytical and experimental investigation into the erosion behavior of E glass-epoxy
Resin hybrid composites leads to the following conclusions:
1. This work shows that successful fabrication of a glass fiber reinforced epoxy composites
with and without filler by simple hand lay-up technique.
2. These composites using Filler have adequate potential for tribological and Automobile
applications.
1. The composite leaf spring is designed according to constant cross-section area method.
2. The 3-D model of the composite leaf spring is analyzed using Ansys 10.0 Software.
3. Static test has been conducted to predict the stress and displacement at different locations
for various load value.
4. The results of the Analysis by ansys software are verified with the test results.
5. A comparative study has been made between composite and steel leaf springs with
respect to weight, riding quality, cost and strength.
6.1. Scope for Future Work
1. This study leaves wide scope for future investigations. It can be extended to newer
composites using other reinforcing phases and the resulting experimental findings can be
similarly analyzed.
2. Stress evaluation of E glass fiber reinforced epoxy resin composite has been a much less
studied area. There is a very wide scope for future scholars to explore this area of
research. Many other aspects of this problem like effect of fiber orientation, loading
pattern, weight fraction of ceramic fillers on wear response of such composites require
further investigation.
27
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
REFERENCES
1. Beardmore,P.(1986). Composite structure for automobiles. Composite Structure,5(3), Pg.
no.163-176
2. Rajendran,I.,&Vijayarangan,S.(2001). Optimal design of a composite leaf spring using genetic
algorithms. Computer & Structure, 79 (11) , Pg. no. 1121-1129
3. Mallick PK. Composite engineering handbook. New York: Marcel Dekker; 1997.
4. Sardou A, Patricia D. Light and low cost composite compression C springs for vehicle
suspension. SAE 2000:2000-01–2000-0100.
5. Katz H.S., Mileski J.V. Handbook of Fillers for Plastics, (1987), November 30, A Von
Nostrand Reihold book.
6. Mareri P. Bastide S. Binda N.; Crespy A. Mechanical Behaviour of Polypropylene Composites
Containing Fine Mineral Filler: Effect of Filler Surface Treatment, Composites Science and
Technology, 58(6), (1998) Pg. no. 747-752.
7. Järvelä, P. A. and Järvelä, P. K. Multi-component compounding of polypropylene, Journal of
Materials Science, 31(14), (1996), Pg. no. 3853-3859.
8. Rusu, M, Sofian, N, Rusu,D. Mechanical and thermal properties of zinc powder filled high
density polyethylene composites,Polymer testing, 20(44),(2001) Pg. no.409-417.
9. Stefan Barta , Jozef Bielek, Peter Dieska, Study of thermo physical and mechanical properties
of particulate composite polyethylene-CaCO3, Journal of Applied Polymer Science, 64(8) ,
(1997), Pg. no. 1525 – 1530.
10. Jang, B. Z. Advanced Polymer composites: principles and applications. ASM International,
(1994).
11. Gregory, S. W, Freudenberg K. D, Bhimaraj, P and Schadler, L.S.. A study on the friction
and wear behavior of PTFE filled with alumina nanoparticles, Wear, 254, (2003): Pg. no. 573–
580.
12. Jung-il, K., Kang, P.H and Nho, Y.C.. Positive temperature coefficient behavior of polymer
composites having a high melting temperature, J Appl Poly Sci., 92, (2004): Pg. no. 394–401.
13. Nikkeshi, S, Kudo, M and Masuko, T. Dynamic viscoelastic properties and thermal
properties of powder-epoxy resin composites, J Appl Poly Sci, 69, (1998):2593- Pg. no.8.
14. Zhu, K and Schmauder, S. Prediction of the failure properties of short fiber reinforced
composites with metal and polymer matrix, Compute Mater Sci. 28, (2003): Pg. no.743–8.34
28
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
15. Tavman, I H. Thermal and mechanical properties of copper powder filled poly (ethylene)
composites, Powder Technol, 91,(1997): Pg. no. 63–67.
16. Al-Quershi HA. Automobile leaf springs from composite materials. J Mater Process
Technology 2001; 108: Pg. no. 58–61
17. Shokrieh M, Rezaei D. Analysis and optimization of composite leaf spring. Composite
Structure 2003; 60:Pg. no.317–325.
18. Senthil kumar and Vijayarangan, “Analytical and Experimental studies on Fatigue life
Prediction of steel leaf soringand composite leaf multi leaf spring for Light passanger veicles
using life data analysis” ISSN 1392 1320 material science Vol. 13 No.2 2007.
19. Shiva Shankar and Vijayarangan “Mono Composite Leaf Spring for Light Weight Vehicle
Design, End Joint, Analysis and Testing” ISSN 1392 Material Science Vol. 12, No.3, 2006.
20. Niklas Philipson and Modelan AB “Leaf spring modelling” ideon Science Park SE-22370
Lund, Sweden
21. Zhi’an Yang and et al “Cyclic Creep and Cyclic Deformation of High-Strength Spring Steels
and the Evaluation of the Sag Effect:Part I. Cyclic Plastic Deformation Behavior” Material and
Material Transaction A Vol 32A, July 2001-Pg. No.1697
22. Muhammad Ashiqur Rahman “Inelastic deformations of stainless steel leaf springs-
experiment and nonlinear analysis” Meccanica Springer Science Business Media B.V. 2009
23. G.S.Shivashankar1, S.Vijayarangan2, D.Rajiv3, R.Pradeep3 “Genetic Algorithm Based
Optimal Design of Mono Composite Leaf Spring and Testing” PSG College of Technology,
Coimbatore-641004, India e-mail: [email protected]
24. Rajendran, I., Vijayarangan, S. Design and Analysis of a Composite Leaf Spring Journal of
Institute of Engineers India 82 2002: pp. 180 – 187.
25. J P Hou, J-Y Cherruault, G Jeronimidis and R Mayer The Journal of Strain Analysis for
Engineering Design 2005 40: 497
26. ANSYS Inc: ANSYS Users Manual, Rev. 1995, 5.2-Vol. I – IV, Houston, PA.
29
Performance Analysis Of Epoxy Resin Based Composite Leaf Spring With E-Glass Fiber
APPENDIX – A
30