FIBERGLASS

MARKETING PROJECT:

Name: Hemali J Shah

1 | P a g e

1

2

3

4

EXAMPLES OF FIBERGLASS PRODUCTS:

1) Fiberglass Chairs

2) Fiber glass cloth sheets

3) Fibreglass ladders

4) Fibreglass Moulded Containers

Enrolment no: 11BSP1398

Roll NO: 46

2 | P a g e

CONTENTS

PARTICULARS PAGE NO.1) What is Fiberglass? 32) Production 43) Sizing 44) Characteristics 55) Composition 66) Applications 77) Construction Methods 108) Examples of Fiberglass use 139) Global Fiberglass Market. 1410) Problems in the Production and Processing 1511) Demand for Fiberglass 1612) The Future 1713)

3 | P a g e

What is Fiber Glass?Fiberglass (also called glass-reinforced plastic, GRP, glass fiber-reinforced plastic, or GFRP), is a fiber reinforced polymer made of a plastic matrix reinforced by fine fibers of glass. It is also known as GFK (for German: Glasfaserverstärkter Kunststoff).

Fiberglass is a lightweight, extremely strong, and robust material. Although strength properties are somewhat lower than carbon fiber and it is less stiff, the material is typically far less brittle, and the raw materials are much less expensive. Its bulk strength and weight properties are also very favorable when compared to metals, and it can be easily formed using molding processes.

The plastic matrix may be epoxy, a thermosetting plastic (most often polyester or vinylester) or thermoplastic.

Common uses of fiber glass include boats, automobiles, baths, hot tubs, water tanks, roofing, pipes, cladding and external door skins.

Fiber Glass being lightweight, durable, anti corrosive, efficient carrier and a versatile material, is used in both traditional and high-tech industries. The major industries in which fiberglass products are used include:

Aerospace Construction Transportation Corrosion Resistant Equipment Manufacturing

4 | P a g e

ProductionThe manufacturing process for glass fibers suitable for reinforcement uses large furnaces to gradually melt the sand/chemical mix to liquid form, and then it is extruded through bundles of very small orifices (typically 17-25 micrometres in diameter for E-Glass, 9 micrometres for S-Glass). These filaments are then sized with a chemical solution. The individual filaments are now bundled together in large numbers to provide a roving. The diameter of the filaments, as well as the number of filaments in the roving determines its weight. This is typically expressed in yield-yards per pound (how many yards of fiber in one pound of material, thus a smaller number means a heavier roving, example of standard yields are 225yield, 450yield, 675yield) or in tex-grams per km (how many grams 1 km of roving weighs, this is inverted from yield, thus a smaller number means a lighter roving, examples of standard tex are 750tex, 1100tex, 2200tex).

These roving’s are then either used directly in a composite application such as pultrusion, filament winding (pipe), gun roving (automated gun chops the glass into short lengths and drops it into a jet of resin, projected onto the surface of a mold), or used in an intermediary step, to manufacture fabrics such as chopped strand mat (CSM) (made of randomly oriented small cut lengths of fiber all bonded together), woven fabrics, knit fabrics or uni-directional fabrics.

SizingA sort of coating, or primer, is used which both helps protect the glass filaments for processing/manipulation as well as ensure proper bonding to the resin matrix, thus allowing for transfer of shear loads from the glass fibers to the thermo set plastic, without this bonding, the fibers can 'slip' in the matrix and localised failure would ensue.

5 | P a g e

CharacteristicsAn individual structural glass fiber is both stiff and strong in tension and compression—that is, along its axis. Although it might be assumed that the fiber is weak in compression, it is actually only the long aspect ratio of the fiber which makes it seem so; i.e., because a typical fiber is long and narrow, it buckles easily. On the other hand, the glass fiber is unstiff and unstrong in shear—that is, across its axis. Therefore if a collection of fibers can be arranged permanently in a preferred direction within a material, and if the fibers can be prevented from buckling in compression, then that material will become preferentially strong in that direction.

Furthermore, by laying multiple layers of fiber on top of one another, with each layer oriented in various preferred directions, the stiffness and strength properties of the overall material can be controlled in an efficient manner. In the case of fiberglass, it is the plastic matrix which permanently constrains the structural glass fibers to directions chosen by the designer. With chopped strand mat, this directionality is essentially an entire two dimensional plane; with woven fabrics or unidirectional layers, directionality of stiffness and strength can be more precisely controlled within the plane.

A fiberglass component is typically of a thin "shell" construction, sometimes filled on the inside with structural foam, as in the case of surfboards. The component may be of nearly arbitrary shape, limited only by the complexity and tolerances of the mold used for manufacturing the shell.

6 | P a g e

Composition

Material Specific Gravity

Tensile Strength (Mpa)

Compressive Strength (Mpa)

Polyester resin (unreinforced)[ 1.28 55 140Polyester and Chopped Strand Mat Laminate 30% E-glass

1.4 100 150

Polyester and Woven Rovings Laminate 45% E-glass

1.6 250 150

Polyester and Satin Weave Cloth Laminate 55% E-glass

1.7 300 250

Polyester and Continuous Rovings Laminate 70% E-glass[

1.9 800 350

E-Glass Epoxy composite 1.99 1770S-Glass Epoxy composite 1.95 2358

7 | P a g e

Applications

Fiberglass is an immensely versatile material which combines its light weight with an inherent strength to provide a weather resistant finish, with a variety of surface textures.

Fiberglass was developed in the UK during the Second World War as a replacement for the molded plywood used in aircraft radomes (fiberglass being transparent to microwaves). Its first main civilian application was for building of boats, where it gained acceptance in the 1950s. Its use has broadened to the automotive and sport equipment sectors as well as model aircraft, although its use there is now partly being taken over by carbon fiber which weighs less per given volume and is stronger both by volume and by weight. Fiberglass uses also include hot tubs, pipes for drinking water and sewers, office plant display containers and flat roof systems.

Advanced manufacturing techniques such as pre-pregs and fiber roving’s extend the applications and the tensile strength possible with fiber-reinforced plastics.

Fiberglass is also used in the telecommunications industry for shrouding the visual appearance of antennas, due to its RF permeability and low signal attenuation properties. It may also be used to shroud the visual appearance of other equipment where no signal permeability is required, such as equipment cabinets and steel support structures, due to the ease with which it can be molded, manufactured and painted to custom designs, to blend in with existing structures or brickwork. Other uses include sheet form made electrical insulators and other structural components commonly found in the power industries.

8 | P a g e

Storage tanks

Several large fiberglass tanks at an airport

Storage tanks can be made of fiber glass with capacities up to about 300 tonnes. The smaller tanks can be made with chopped strand mat cast over a thermoplastic inner tank which acts as a preform during construction. Much more reliable tanks are made using woven mat or filament wound fibre with the fibre orientation at right angles to the hoop stress imposed in the side wall by the contents. They tend to be used for chemical storage because the plastic liner (often polypropylene) is resistant to a wide range of strong chemicals. Fiberglass tanks are also used for septic tanks.

House building

Glass reinforced plastics are also used in the house building market for the production of roofing laminate, door surrounds, over-door canopies, window canopies and dormers, chimneys, coping systems, heads with keystones and sills. The use of fiberglass for these applications provides for a much faster installation and due to the reduced weight manual handling issues are reduced. With the advent of high volume manufacturing processes it is possible to construct fiberglass brick effect panels which can be used in the construction of composite housing. These panels can be constructed with the appropriate insulation which reduces heat loss.

9 | P a g e

Piping

GRP and GRE pipe systems can be used for a variety of applications, above and under the ground.

Firewater systems Cooling water systems Drinking water systems Waste water systems/Sewage systems Gas systems

Pipes made of Fiber Glass

Fiber Glass Cloth Sheets

10 | P a g e

Construction Methods

Fiberglass hand lay-up operation

Resin is mixed with a catalyst or hardener if working with epoxy, otherwise it will not cure (harden) for days/weeks. Next, the mold is wetted out with the mixture. The sheets of fiberglass are placed over the mold and rolled down into the mold using steel rollers. The material must be securely attached to the mold, air must not be trapped in between the fiberglass and the mold. Additional resin is applied and possibly additional sheets of fiberglass. Rollers are used to make sure the resin is between all the layers, the glass is wetted throughout the entire thickness of the laminate, and any air pockets are removed. The work must be done quickly enough to complete the job before the resin starts to cure. Various curing times can be achieved by altering the amount of catalyst employed. It is important to use the correct ratio of catalyst to resin to ensure the correct curing time. 1% catalyst is a slow cure, 2% is the recommended ratio, and 3% will give a fast cure. Adding more than 4% may result in the resin failing to cure at all.[6] To finish the process, a weight is applied from the top to press out any excess resin and trapped air. Stops (like coins) are used to maintain the thickness which the weight could otherwise compress beyond the desired limit.

Fiberglass spray lay-up operation

The fiberglass spray lay-up process is similar to the hand lay-up process but the difference comes from the application of the fiber and resin material to the mold. Spray-up is an open-molding composites fabrication process where resin and reinforcements are sprayed onto a mold. The resin and glass may be applied separately or simultaneously "chopped" in a combined stream from a chopper gun. Workers roll out the spray-up to compact the laminate. Wood, foam or other core material may then be added, and a secondary spray-up layer imbeds the core between the laminates. The part is then cured, cooled and removed from the reusable mold.

11 | P a g e

Pultrusion Operation

Diagram of the pultrusion process.

Pultrusion is a manufacturing method used to make strong light weight composite materials, in this case fiberglass. Fibers (the glass material) are pulled from spools through a device that coats them with a resin. They are then typically heat treated and cut to length.[7] Pultrusions can be made in a variety of shapes or cross-sections such as a W or S cross-section. The word pultrusion describes the method of moving the fibers through the machinery. It is pulled through using either a hand over hand method or a continuous roller method. This is opposed to an extrusion, which would push the material through dies.

Chopped Strand Mat

Chopped strand mat or CSM is a form of reinforcement used in fiberglass. It consists of glass-fibers laid randomly across each other and held together by a binder.

It is typically processed using the hand lay-up technique, where sheets of material are placed in a mold and brushed with resin. Because the binder dissolves in resin, the material easily conforms to different shapes when wetted out. After the resin cures, the hardened product can be taken from the mold and finished.

Using chopped strand mat gives a fiberglass with isotropic in-plane material properties.

12 | P a g e

13 | P a g e

Examples of Fiberglass Use

Kayaks made of fiberglass

Gliders, kit cars, sports cars, micro cars, karts, body shells, boats, kayaks, flat roofs, lorries, wind turbine blades.

Minesweeper hulls Pods, domes and architectural features where a light weight is necessary. Bodies for automobiles, such as the Anadol, Reliant, Quantum Coupé,

Chevrolet Corvette and Studebaker Avanti, and DeLorean DMC-12 under body.

A320 radome. FRP tanks and vessels: FRP is used extensively to manufacture chemical

equipments and tanks and vessels. BS4994 is a British standard related to this application.

UHF-broadcasting antennas are often mounted inside a fiberglass cylinder on the pinnacle of a broadcasting tower

Most commercial Velomobiles Large Commercial Wind Turbine Blades RF coils used in MRI scanners

14 | P a g e

Global Fiberglass Market

Geographically, the US is the largest market for fiber glass, both in terms of

production and consumption. Among the emerging markets, China has been the

largest producer, and in the coming years, China is expected to become the

largest consumer of fiber glass worldwide, surpassing the US.

The global fiber glass industry has consistently shown an increasing

performance for the past few years, due to its versatile performance and low

cost, and is expected to grow in the coming years as well. The growing demand

of alternate sources of energy, mainly wind energy, also tends to increase the

demand of fiber glass.

The current report analyses the global fiber glass market and also the two main

regions, Europe and China. The current reports delve into the various

opportunities and drivers, which are expected to boost up the market. These

include increasing demand from the emerging countries, particularly BRIC

countries, and increasing energy demand.

15 | P a g e

Problems in the Production and Processing

Dust development in the processing of components made of fiberglass-reinforced plastics

Evidence of laminar air flow for the extraction and filtration of styrene vapors in a production hall for GRP

yachts

While the resins are cured styrene vapors are released. These are irritating to mucous membranes and respiratory tract. Therefore, the Hazardous Substances Ordinance in Germany dictates a maximum occupational exposure limit of 86 mg / m³. In certain concentrations may even occur a potentially explosive mixture. Further manufacture of GRP components (grinding, cutting, sawing) goes along with the emission of fine dusts and chips containing glass filaments as well as of tacky dust in substantial quantities. These affect people's health and functionality of machines and equipment. To ensure safety regulations are adhered to and efficiency can be sustained the installation of effective extraction and filtration equipment is needed.

16 | P a g e

Why is there an increase in the demand for fiberglass?At present man is mainly using the fiberglass which is the lightest but well-built substance with unlimited uses because of its toughness.

As the name suggest the very tiny filament of glass is used to manufacture the fiberglass, which are compounded as one producing a product having the characteristics of flexibility and the exceptional toughness. In this article we will see that how the powder produced from the core are used in most of the various industries,

Other metals than fiberglass do not work practically in the oil refineries industries for manufacturing machines and also form the point of workers safety because they own acidic characteristics of lubricants and other elements.

Fiberglass enjoys the qualities of fireproof, nonreactive as well as demands the modest regular protection. The shred of the fiberglass strongly bear the weight which the employees keep on it without getting oxidizes as found in metals.

Fiberglass shreds are also used at many places for making the paths as well as for sewage stuffs like the parks, zoos and museums. One can prefer fiberglass powder as the ingredient for making decomposing dock as the older get destroyed because of hurricanes. Fiberglass as having the resistance quality towards salty water can keep on appearing good for many years.

The prime requisite of constructing the water parks is the continuous outflow of water and the strong non-reactive power against the chlorine and other elements which are usually used in them. One can make vivid and result oriented effective fiberglass material to manufacture channels which also costs low price.

To meet the increasing requirements of the fiberglass substances in the market the manufacturing companies are continuously working to create the new styles and multi-growing uses.

For making the footpaths and conventional bar exterior plan the fiberglass is said to be a trendy option. Offered in the various range and dimensions it serves as the best for locating a company. In the world of manufacturing, the material has come up as the most demanding product for the upcoming time.

17 | P a g e

The FutureThe fiberglass industry faces some major challenges over the rest of the 1990s and beyond. The number of producers of fiberglass insulation has increased due to American subsidiaries of foreign companies and improvements in productivity by U.S. manufacturers. This has resulted in excess capacity, which the current and perhaps future market cannot accommodate.

In addition to excess capacity, other insulation materials will compete. Rock wool has become widely used because of recent process and product improvements. Foam insulation is another alternative to fiberglass in residential walls and commercial roofs. Another competing material is cellulose, which is used in attic insulation.

Because of the low demand for insulation due to a soft housing market, consumers are demanding lower prices. This demand is also a result of the continued trend in consolidation of retailers and contractors. In response, the fiberglass insulation industry will have to continue to cut costs in two major areas: energy and environment. More efficient furnaces will have to be used that do not rely on only one source of energy.

With landfills reaching maximum capacity, fiberglass manufacturers will have to achieve nearly zero output on solid waste without increasing costs. This will require improving manufacturing processes to reduce waste (for liquid and gas waste as well) and reusing waste wherever possible.

Such waste may require reprocessing and remelting before reusing as a raw material. Several manufacturers are already addressing these issues.

18 | P a g e