Low VOC

Fire Resistant Coating Properties

Color

Operating Temperature

Curing Condition

Adhesion

Specific Gravity

Base

Slightly Opaque

20ºC ~ 1,000ºC

24H at 20ºC

KS F 4715:2007

1.3 ~ 1.4 g/cm

Sodium Silicate

Fire Resistant Coating PerformanceApplication

Easily applied by brush, roller and airless sprayer

Best applied in conjunction with primer and top coat

Excellent FR Performance Hard Durable Finish

Brush, Roller, Airless Sprayer Non-Toxic / Low Odour

Safety & Environment

Non-toxic

Key Benefits

JIOS AeroVa is a registered trademark of JIOS Aerogel Ltd.

© 2015 JIOS Aerogel Ltd.

JIOS AeroVa Fire Resistant Coating Technical Data Sheet

-mail

Viscosity (cPs)

Application Method

500 ~ 2,000

Brush, Roller, Airless Sprayer

JIOS AeroVa® Fire Resistant Coating is a premium quality water-based intumescent coating, which provides excellent fire resistance properties. The coating utilizes a specialized chemistry between silica aerogel and sodium silicate to create a dense fire barrier when exposed to flame.

JIOS AeroVa® FR Coating is low VOC, easy to apply and is suitable for a wide variety of applications.

3

Water-Based intumescent coating that forms a hard, glassy barrier when exposed to flame

Low heat transfer

Hard durable finish

Environmentally friendly

0 20 30 90 15060 120 (min)

80

120

160

200

Time (minute)

Tem

pera

ture

(˚C

)

(˚C)

100

140

180

220

20

0

Low odour

~~

18010 40 50

143.5

103.8

166.8173.3 169.9

174.8 175.4 181.7

27.0

* Test conducted by JIOS Aerogel in 2014-2015

Test Time (minutes)

Back-side Temperature (˚C)

0

27.0˚C

10

103.8˚C

20

143.5˚C

40

166.8˚C

90

169.9˚C

120

174.8˚C

150

175.4˚C

180

181.7˚C

* Test Description: Coating was applied to a steel substrate(4.0mm) and torched(direct flame exposure) at a temperature ranging from 700~1,000˚C. Backside temperature was measured using thermocouples in order to determine the temperature difference.