Technical Data Sheet -...
Transcript of Technical Data Sheet -...
Low VOC
Fire Resistant Coating Properties
Color
Operating Temperature
Curing Condition
Adhesion
Specific Gravity
Base
Slightly Opaque
20ºC ~ 1,000ºC
24H at 20ºC
KS F 4715:2007
1.3 ~ 1.4 g/cm
Sodium Silicate
Fire Resistant Coating PerformanceApplication
Easily applied by brush, roller and airless sprayer
Best applied in conjunction with primer and top coat
Excellent FR Performance Hard Durable Finish
Brush, Roller, Airless Sprayer Non-Toxic / Low Odour
Safety & Environment
Non-toxic
Key Benefits
JIOS AeroVa is a registered trademark of JIOS Aerogel Ltd.
© 2015 JIOS Aerogel Ltd.
JIOS AeroVa Fire Resistant Coating Technical Data Sheet
Viscosity (cPs)
Application Method
500 ~ 2,000
Brush, Roller, Airless Sprayer
JIOS AeroVa® Fire Resistant Coating is a premium quality water-based intumescent coating, which provides excellent fire resistance properties. The coating utilizes a specialized chemistry between silica aerogel and sodium silicate to create a dense fire barrier when exposed to flame.
JIOS AeroVa® FR Coating is low VOC, easy to apply and is suitable for a wide variety of applications.
3
Water-Based intumescent coating that forms a hard, glassy barrier when exposed to flame
Low heat transfer
Hard durable finish
Environmentally friendly
0 20 30 90 15060 120 (min)
80
120
160
200
Time (minute)
Tem
pera
ture
(˚C
)
(˚C)
100
140
180
220
20
0
Low odour
~~
18010 40 50
143.5
103.8
166.8173.3 169.9
174.8 175.4 181.7
27.0
* Test conducted by JIOS Aerogel in 2014-2015
Test Time (minutes)
Back-side Temperature (˚C)
0
27.0˚C
10
103.8˚C
20
143.5˚C
40
166.8˚C
90
169.9˚C
120
174.8˚C
150
175.4˚C
180
181.7˚C
* Test Description: Coating was applied to a steel substrate(4.0mm) and torched(direct flame exposure) at a temperature ranging from 700~1,000˚C. Backside temperature was measured using thermocouples in order to determine the temperature difference.
15642 Sand Canyon Avenue. #51537Irvine, Ca. 92619