http://www.iaeme.com/IJMET/index.asp 197 [email protected]
International Journal of Mechanical Engineering and Technology (IJMET) Volume 8, Issue 12, December 2017, pp. 197–205, Article ID: IJMET_08_12_020 Available online at http://www.iaeme.com/IJMET/issues.asp?JType=IJMET&VType=8&IType=12 ISSN Print: 0976-6340 and ISSN Online: 0976-6359
© IAEME Publication Scopus Indexed
FINITE ELEMENT ANALYSIS OF KNEE
IMPLANT AND PROTOTYPE FABRICATION
USING RPT PROCESS
B.Rajesh, L.Radhakrishna and K.Venkata Reddy
Assistant Professor, Department of Mechanical Engineering, S R Engineering College, Warangal, Telangana, India
ABSTRACT
The aim of this research work is to do finite element analysis of patient specific
knee implant and compare the stress analysis results with commercially available
knee implant and Fabrication of prototypes of Patient Specific knee implant and
commercially available knee implant are done using FDM additive manufacturing
process.
In this research, it is proposed to develop a three-dimensional model of knee
implant from .stl file of knee joint using software’s like meshlab, NetFabb and CATIA
software’s. The data is obtained from Sunshine Hospital, Secunderabad. Based on the
dimensions of knee joint, it is proposed to Design a Knee implant in Catia software.
Once the 3D CAD model is designed in Catia software, it is meshed in ANSYS and
finite element analysis is performed for varying loads (500N-5000N). The obtained
results are compared with the commercially available knee implant. According to
walking condition the patient specific knee implant is analyzed for different flexion
angles (15, 45, 60 degrees). Fabrication of prototypes of patient Specific knee implant
and commercial available knee implants are done using FDM additive manufacturing
process.
Keywords: finite element, knee implant, RPT
Cite this Article: B.Rajesh, L.Radhakrishna and K.Venkata Reddy, Finite Element Analysis of Knee Implant and Prototype Fabrication using Rpt Process, International Journal of Mechanical Engineering and Technology 8(12), 2017, pp. 197–205. http://www.iaeme.com/IJMET/issues.asp?JType=IJMET&VType=8&IType=12
1. INTRODUCTION
1.1 KNEE JOINT
The knee is one of the largest and most complex joint in the human body. The knee joins the thigh bone (femur) to the shin bone (tibia). The smaller bone runs alongside the tibia (fibula) and the knee-cap (patella) and the other bones that make the knee joint. Tendons connect the knee bones to the leg muscles that move the knee joint. Ligaments join the knee bones and provide stability to the knee joint:
Finite Element Analysis of Knee Implant and Prototype Fabrication using Rpt Process
http://www.iaeme.com/IJMET/index.asp 198 [email protected]
• The anterior cruciate ligament prevents the femur from sliding backward on the tibia (or the tibia sliding forward on the femur).
• The posterior cruciate ligament prevents the femur from sliding forward on the tibia (or the tibia from sliding backward on the femur).
• The medial and lateral collateral ligaments prevent the femur from sliding side to side.
Two C-shaped pieces of cartilage called the medial and lateral menisci act as shock absorbers between the femur and tibia. Numerous bursae, or fluid-filled sacs, help the knee move smoothly.
Figure 1 Knee Implant
Reasons for damage of Knee Implant: the main reasons for the damage of the knee joint are as follows:
• Wear and loosening: Friction caused by joint surfaces rubbing against each other wears away the surface of the implant causing bone loss and loosening of the implants.
• Infection: Large metal and plastic implants can serve as a surface onto which bacteria can latch.
• Fracture: Fractures around the knee implant that disrupt its stability may require revision surgery.
• Instability: A sensation of the knee "giving away" may mean that the soft-tissue surrounding the knee is too weak to support standing and walking. Improperly placed implants may also cause instability.
• Stiffness: Loss of range of motion which causes pain and a functional deficit.[12]
Implant material
Generally Implants are manufactured with materials like metals, and ceramics. The metals used like Titanium, cobalt, chromium and stainless steel as shown in Table 1
Table 1 Common metals and properties used for implants
Material Density (g/cc) Compresive
strength (Mpa)
Elastic modulas
(Gpa)
Toughness
(Mpa)
Titanium 4.4-4.5 590-1117 55-117 55-115
Stainless steel 7.9-8.1 170-310 189-205 50-200
Co-cr-mo alloy 8.3-9.2 450-1896 200-253 100
B.Rajesh, L.Radhakrishna and K.Venkata Reddy
http://www.iaeme.com/IJMET/index.asp 199 [email protected]
2. PROBLEM STATEMENT
Knee arthritis has been a serious problem facing around 70 million patients worldwide. Total knee replacement has become an acceptable method of treating severe arthritis of the knee. The operative procedure must be performed with precise skill and accuracy. Great care and importance is given while selecting a proper and suitable biocompatible material for fabricating an implant. To make a bio-compatible implant it is important to know where it is located in the body. For the structural mechanics of human body involving bones, tissues and organs, it is almost impossible to conduct mechanical experiments. The finite element model to simulate such mechanical experiments has thus become an effective tool.
In this research, analysis of knee Implant is done which is designed according to the dimensions obtained from the STL file of knee joint and compared with the commercially available knee implant for three different bio-materials based on patient body weight acting on human body under different walking conditions. The patient specific knee implant is also analyzed for different flexion angles. Fabrication of designed and commercial knee implants is done using Fused Deposition Modeling RPT Process.
3. RESULTS AND DISCUSSIONS
This chapter presents the results obtained after adopting the research methodolgy discussed in earlier chapter. The finite element analysis of the patient specific Knee implant is done under static condition for different Flexion angles viz 0,15,45,60 degrees. The zero degres of Flexion angle represents the normal standing condition of the human being.
Analysis of patient specific Knee implant at zero degrees of three different bio-
compatible materials
Table 2 Comparison of Von-mises stress for different bio-compatible materials
Load (N) Von-mises stress (mpa)
Ti-6Al-4V Co-Cr-Mo SS 316L
500 2.65 3.08 3.07
1000 5.30 6.16 6.14
1500 7.95 9.24 9.21
2000 10.60 12.32 12.29
2500 13.25 15.41 15.36
3000 15.90 18.49 18.43
3500 18.55 21.57 21.51
4000 21.20 24.65 24.58
4500 23.85 27.74 27.65
5000 26.50 30.82 30.73
Table 3 Comparison of Total deformation for different bio-compatible materials
Load (N) Total deformation (mm)
Ti-6Al-4V Co-Cr-Mo SS 316L
500 0.0027 0.0020 0.0021
1000 0.0055 0.0040 0.0042
1500 0.0083 0.0060 0.0064
2000 0.0111 0.0080 0.0085
Finite Element Analysis of Knee Implant and Prototype Fabrication using Rpt Process
http://www.iaeme.com/IJMET/index.asp 200 [email protected]
2500 0.0139 0.010 0.0106
3000 0.0165 0.012 0.0128
3500 0.0194 0.014 0.0149
4000 0.0222 0.016 0.0170
4500 0.0250 0.018 0.0192
Analysis of patient specific Knee implant of various flexion angles
The 3D cad model of Knee implant assembly is rotated to 15,45,60 degrees in catia software, according to walking condition and are imported in ANSYS IGES format and analysis was carried out for three different materials with combination of ultra-high-molecular-weight-polyethylene (UHMWPE). The results were found out in the form of von-mises stress, total deformation and contact pressure at each degree of flexion
Table 4 Comparison of Von-mises stress and Total deformation at Titanium alloy and different flexion angles
Flexion angles (deg) Von-mises stress (Mpa) Total deformation (mm)
500N 2500N 500N 2500N
15˚ 8.97 44.876 0.005 0.02
45˚ 8.84 44.23 0.015 0.07
60˚ 7.13 35.696 0.03 0.15
Figure 2 Graph plotted between Von-mises stress and Total deformation at Ti-4Al-6V
Table 5 Comparison of Von-mises stress and Total deformation at SS 316 alloy and different flexion
angles
Flexion angles (deg) Von-mises stress(Mpa) Total deformation (mm)
500N 2500N 500N 2500N
15˚ 9.18 45.94 0.004 0.02
45˚ 9.20 46.02 0.014 0.07
60˚ 7.64 38.2 0.02 0.14
B.Rajesh, L.Radhakrishna and K.Venkata Reddy
http://www.iaeme.com/IJMET/index.asp 201 [email protected]
Table 6 Comparison of Von-mises stress and Total deformation at Co-Cr-Mo alloy and different flexion angles
Flexion angles (deg) Von-mises stress (Mpa) Total deformation (mm)
500N 2500N 500N 2500N
15˚ 9.21 46.05 0.004 0.02
45˚ 9.18 45.9 0.014 0.07
60˚ 7.72 38.64 0.02 0.13
Figure 3 graph plotted between Von-mises stress and Total deformation at SS 316L
Figure 4 graph plotted between Von-mises stress and Total deformation at Co-Cr-Mo
Comparison of Analysis Results for patient specific and Commercial Knee
Implants
The von-mises stress and total deformation values obtained for the designed and commercially available Knee implants for three different bio-compatible materials are compared as shown in tables 6.8, 6.9,6.10 and correspondingly graphs are drawn as shown in figures.
6.4.1. For Titanium alloy
The von-mises stress and total deformation values obtained for the patient specific and commercially available Knee implants for three different bio-compatible materials are compared as shown in tables 6.8 and graphs is plotted as shown in fig 6.20 and 6.21
Finite Element Analysis of Knee Implant and Prototype Fabrication using Rpt Process
http://www.iaeme.com/IJMET/index.asp 202 [email protected]
Table 7 Comparison of Equivalent Stress and Total Deformation for patient specific and Commercial knee Implants made of Titanium alloy.
LoadApplied (N) Equivalent Stress (MPa) Total Deformation (mm)
Patient specific Commercial Patient Specific Commercial
500 2.65 3.15 0.0027 0.0066
1000 5.30 6.31 0.0055 0.013
1500 7.95 9.46 0.0083 0.019
2000 10.60 12.62 0.0111 0.026
2500 13.25 15.77 0.0139 0.033
3000 15.90 18.93 0.0165 0.039
3500 18.55 22.09 0.0194 0.046
4000 21.20 25.24 0.0222 0.053
4500 23.85 28.40 0.0250 0.059
5000 26.50 31.55 0.0278 0.066
Figure 5 Comparison of Equivalent Stress for Designed(patient specific) and Commercial Knee
implants made of Titanium alloy.
Figure 6 Comparison of Total Deformation for Designed (patient specific) and Commercial Knee
Implants made of Titanium alloy.
B.Rajesh, L.Radhakrishna and K.Venkata Reddy
http://www.iaeme.com/IJMET/index.asp 203 [email protected]
6.4.2. For SS 316L alloy
hevon-mises stress and total deformation values obtained for the patient specific and
commercially available Knee implants for three different bio-compatible materials are compared as shown in tables 6.10 and graphs is plotted as shown in fig 6.24 and 6.25.
Table 6.10 Comparison of Equivalent Stress and Total Deformation for patient specific and
Commercial knee Implants made of SS 316L alloy.
Load Applied (N) Equivalent Stress (MPa) Total Deformation (mm)
patient specific Commercial patient specific Commercial
500 3.07 4.20 0.0021 0.005
1000 6.14 8.41 0.0042 0.01
1500 9.21 12.62 0.0064 0.016
2000 12.29 16.83 0.0085 0.021
2500 15.36 21.04 0.01 0.026
3000 18.43 25.25 0.012 0.032
3500 21.51 29.46 0.014 0.037
4000 24.58 33.66 0.017 0.043
4500 27.65 37.87 0.019 0.048
5000 30.73 42.08 0.02 0.053
Figure 7 Comparison of Von-Mises stress for Designed(patient specific) and Commercial Knee
implants made of SS 316L alloy.
Finite Element Analysis of Knee Implant and Prototype Fabrication using Rpt Process
http://www.iaeme.com/IJMET/index.asp 204 [email protected]
Figure 8 Comparison of Total Deformation for Designed (patient specific) and Commercial Knee
implants made of SS 316L alloy.
7. CONCLUSIONS
The aim of this research work is to do finite element analysis of patient specific knee implant and compare the stress analysis results with results of commercially available knee implant. Manufacturing of patient specfic knee implant and Commercial Knee implants Prototypes are done using FDM additive manufacturing process. Knee implant is designed by taking the dimensions from .STL file in CATIA software and analysis is performed in ansys software to determine the von-mises stress under various walking conditions. The values obtained are tabulated accordingly as mentioned in research and methodology.
Following are the conclusions made from the Research Methodology adopted.
� For Proposed patient specific Knee implant, the von-misses stresses and deformation values obtained for different bio-materials under walking condition are as follows:
• For Ti-4A-l4V alloy, the maximum von-misses stress and total deformation values obtained are 26.50 MPa and 0.0278 mm respectively.
• For SS-316L material, the maximum von-misses stress and total deformation values obtained are 30.73 MPa and 0.02 mm respectively.
� For Commercially available Knee implant, the von-misses stresses and deformation values obtained for different bio-materials under walking condition are as follows:
• For Ti-4Al46V alloy, the maximum von-misses stress and total deformation values obtained are 31.55MPa and 0.066 mm respectively.
• For SS-316L material, the maximum von-misses stress and total deformation values obtained are 42.08 MPa and 0.053 mm respectively.
• For Cr-Co-Mo alloy, the maximum von-misses stress and total deformation values obtained are 43.28MPa and 0.041mm respectively.
� From the first study (FEM analysis when knee is in normal position) it is clear that even under extreme loading conditions, the prosthesis is safe (values obtained are below allowable stress) and gives good results for all selected biomaterials - Ti-6Al-4V, Co-Cr, SS-316L, UHMWPE
B.Rajesh, L.Radhakrishna and K.Venkata Reddy
http://www.iaeme.com/IJMET/index.asp 205 [email protected]
� At applied 5000 N load, least and maximum deformation values found for Cobalt alloy is 0.020 mm and for Titanium alloy is 0.027 respectively, similarly least and maximum equivalent stresses develop were Titanium alloy is 26.50 MPa, whose allowable stress is 880 MPa and Cobalt alloy is 30.82 MPa whose allowable stress is 612 MPa respectively.
� From the finite element analysis results obtained by rotating the designed knee implant at different flexion angles (15, 45, 60 degrees), it is observed that even if maximum load is applied i.e. 2500N the von misses stress values are obtained are 44.876 MPa for Titanium Alloy and 45.94 MPa for SS 316L Alloy and 46.05 MPa for Co-Cr-Mo alloy which are less compared to maximum allowable stress of three bio-compatible materials.
� For the two designs which are analysed in the thesis work, von-mises stress values obtained indicate that , titanium alloy material is best sutible compared to Co-Cr-Mo alloy and SS 316L.
� From this study it is found that stress induced for all selected biomaterials Ti-6Al-4v,and Co-Cr-Mo alloy and SS 316 L are with in allowable limit for maximum force and least deformation among all cases was found to be for Cobalt alloy.
Fabrication of patient specific and Commercial Knee implants are done using fused deposition Modeling machine. The printing time and material consumed for patient specific and Commercial Knee implants are 25 min, 9.24 gms and 50 min, 18 gms.
REFERENCE
[1] A. Sreenivasa Rao and K Venkata Rao. A Study on Machining Characteristics in Milling of Ti-6Al-4V using Experimental and Finite Element Analysis. International Journal of Civil Engineering and Technology, 8(7), 2017, pp. 457–469.
[2] R. Deendayal, Behaviour of a Single Pile Located on Sloping Ground of a Soil Under Cyclic Loading: A Finite Element Analysis. International Journal of Civil Engineering and Technology, 8(10), 2017, pp. 925–932
[3] S. P. Chaphalkar and V. S. Byakod, Design and Analysis of Bridge with Two Ends Fixed on Vertical Wall Using Finite Element Analysis, International Journal of Civil Engineering and Technology, 7(2), 2016, pp. 34- 44.
[4] S. Jayavelu, C. Rajkumar, R. Rameshkumar and D. Surryaprakash, Design and Analysis of Vibration and Harshness Control For Automotive Structures Using Finite Element Analysis, International Journal of Civil Engineering and Technology, 8(10), 2017, pp. 1364–1370.