Physical Properties - Propiedades Fisicas
Inve
stm
ents
HIGH-CAST
CROWNS AND BRIDGES
CHROME COBALT DENTURES
SPECIAL INVESTIMENT
CROMACAST
SILCA-VEST
CROMOVEST
CROMOVEST SF
PIN-CAST
Bonding Material
Type: Class ISO
15912:2006
Phosphate
Material
salmon
green
PLASTER
1:2
2 2 45 60 7 13 0,23 2500(18)
4600(32)-
24 60 4-6- 25-306 -7 - 2.0 - 1.2 700-900ºC high.cast
Phosphate2:1 13 30 13-1760 604 -5 35 1,2-1,2 900-1080ºC cromacastexpansor
expansor
A&BPolysil& Alc
2:1 14-18 - 760 608 -10 30-45 1,4 900-1050ºC
Polysil& Alc
2:1 18-20 - 760 608 -10 30-45 1,4 900-1050ºC A&B
A&BPolysil& Alc
2:1 18-20 - 760 608 -10 30-45 1,4 900-1050ºC
Gypsum1:1 30 30 560 606 -8 - 0,4 700-720ºC distilledwather
Consistency (ml.)
Mechanical Mixing (sec.)
ManualMixing (sec.)
Working Time (min.)
Model Ready (min.)
Ready for burnout (min.)
Expansion ( % / Setting - Themal)
Compressive stregth 2h. (Mpa)
Final Temperature
Mixing Liquid
green
Gyps
ums
Labox
Gypsums - Yesos
ISO 6873: TIPO IV DIE-ROCK
yellow
1102-0111102-351
1102-0131102-353
1102-0151102-354
ivory
Consistency: 20ml/100g; | Working Time: 9 min. | Setting Time: 12 min. | Expansion: 0.13% | Comp. Streight: 17.000 Psi
High strengh die stone.
1 Kg.25 Kg.
ADA: TIPO V
PouchBag
white
Yeso para troqueles de máxima compresión.
ISO 6873: TIPO IV RESIN-STONE
peach
1107-012 1107-011
ivory
Consistency: 20ml/100g; | Working Time: 7 min. | Setting Time: 10 min. | Expansion: 0.08% | Comp. Streight: 11.000 Psi
Resin fortified, low expansion die stone.
1 Kg.
ADA: TIPO IV
Pouch1107-352 1107-351 25 Kg.Bag
Yeso extra duro aditivado con resina. De baja expansión.
ISO 6873: TIPO IV MIX-ROCK
pink
1120-0111120-351
1120-0121120-352
1120-0131120-353
Consistency: 23ml / 100g | Working Time: 9 min. | Setting Time: 13 min. | Expansion: 0.09% | Comp. Streight: 13.000 Psi
Low-expansion die stone.
1 Kg.25 Kg.
ADA: TIPO IV
PouchBag
yellowwhite
Yeso para troqueles de baja expansión.
SPECIALITY STONE - YESOS PARA ESPECIALIDADES
DIE STONES - YESOS PARA MODELOS
ISO 6873: TIPO III MOUNTING-ROCK
1160-005
white
Consistency: 30ml/100g | Working Time: 1-2 min. | Setting Time: 3 min. | Expansion: 0.06% | Comp. Streight: 6.500 Psi
Gypsum for mounting to articulators. Low-expansion fast-setting stone.
500 g.Pouch1160-350 25 Kg.Bag
Yeso especial para impresión y montaje en articulador. Freguado rápìdo. Baja expansión.
ISO 6873: TIPO IV ADA: TIPO IV SCAN-ROCK
golden salmon
1112-0111112-012
Consistency: 20ml/100g; | Working Time: 9 min. | Setting Time: 12 min. | Expansion: 0.09% | Comp. Streight: 17.000 Psi
Elite Gypsum. Extra hard high density die stone. CAD-CAM compatible. Yeso Premium. De baja expansión y alta compresión. Compatible CAD-CAM.
Pouch 1 Kg.1112-3511112-352 Bag 25 Kg.
white
ISO 6873: TIPO IV FLOW-ROCK
deep bluedeep buff
1130-0111130-351
1130-0121130-352
1130-0131130-353
Consistency: 22-24ml/100g | Working Time: 6-9 min. | Setting Time: 11 min. | Expansion: 0.08% | Comp. Streight: 12.000 Psi
Fluid, low-expansion base stone.
1 Kg.Pouch25 Kg.Bag
Yeso fluido autonivelante especial para zócalos.
PULICROM
7880-010
Líquido electrolítico para el pulido de estructuras de Cr. Co.
Liquid for electrolytic polishing of Cr.Co.
1l.
POLI-GEL
Gel para pulir metales preciosos y resinas.Polishing paste for resins.
150 g.7881-150
ALUMINUM OXIDE
Óxido de aluminio para arenado.
Special corundum grit comprising 99,6% aluminum oxide.
1 k.Pouch
RUBBER WHEELS
7710-100 size: 24 x 6,3 mm.box x 100 u.
Goma rueda negra para pulir Cromo Cobalto y metales duros.Black rubber for finishing and polishing Cr. Co. metals.
PUMICE
7882-010 1 k.Piedra pómez en polvo.Pumice powder.
RUBBER CYLINDERS
Goma punta negra para pulir Cromo Cobalto y metales duros.7710-101 box x 100 u. size: 22 x 3,1 mm.
Black rubber for finishing and polishing Cr. Co. metals.
ACRYLIC POLISHERS
7720-250 25u.
Goma de silicona para el pulido de Acrílico.Silicone polishers for acrylic materials.
Casting Alloy - Aleaciones para colado
LABOX Co. Cr. ISO: 22674: TIPO V
4010-100
Aleación de cromo cobalto para prótesis esquelética.Cr. Co. frame work casting alloy.
1 k.
SURFACE FINISHING - ACABADO DE LA SUPERFICIE
PHYSICAL AND MECHANICAL FEATURES:Solidus-Liquidus temperature: 1340-1400ºCDensity: 8,3 g/cm3.Vickers hardness: 390 Hv10.Elongation at fracture: 6,2 %Yield load strenght (Rp0.2): 609 Mpa.Modulus of elasticity: 200 Gpa.
Composition: Cobalto (Co): 62% Cromo (Cr): 31% Molibdeno (Mo): 5% Others: C, Fe, Si, Mn.
ISO 6873: TIPO III ORTHO-GIPS
1150-010
snow white
Consistency: 28ml/100g | Working Time: 6 min. | Setting Time: 10 min. | Expansion: 0.09% | Comp. Streight: 8.500 Psi
Yeso de baja expansión especial para modelos de ortodoncia. Special stone for study models and orthodontic.
1 Kg.
ADA: TIPO III
Pouch1150-350 25 Kg.Bag
ISO 6873: TIPO III ECO-GIPS
1170-0101170-350
1170-0111170-351
1141-0121141-352
1170-0121170-350
green blue yellow white
Consistency: 35ml/100g | Working Time: 5 min. | Setting Time: 12 min. | Expansion: 0.18% | Comp. Streight: 8.000 Psi
Yeso piedra para modelos y antagonistas.Hard stone for models and antagonist.
1 Kg.Pouch25 Kg.Bag
ISO 6873: TIPO II PLASTER
1171-010
white yellow
Consistency: 45 ml / 100g | Working Time: 7 min. | Setting Time: 13 min. | Expansion: 0.23% | Comp. Streight: 4.600 Psi
Yeso taller para laboratorio.Plaster for laboratory.
1 Kg.Pouch1171-010
1171-0111171-351 25 Kg.Bag
ISO 6873: TIPO II LABOR-PLASTER
1182-010
white
Consistency: 50ml / 100g | Working Time: 7 min. | Setting Time: 13 min. | Expansion: 0.29% | Comp. Streight: 3.300 Psi
Yeso Taller Para Laboratorio.De fácil recortado.Plaster for laboratory. Easy to cut.
1 Kg.Pouch1182-350 25 Kg.Bag
ISO 6873: TIPO II ORTHO-PLASTER
1151-010
snow white
Consistency: 37-38ml / 100g | Working Time: 9 min. | Setting Time: 13 min. | Expansion: 0.20% | Comp. Streight: 6.500 Psi
Yeso para modelos de ortodoncia. De facil recortado.Plaster for models in orthodontics, easy to cut.
1 Kg.Pouch1151-350 25 Kg.Bag
MODEL STONES - YESOS PARA MODELOS
PLASTERS - YESOS LIGEROS
ISO 6873: TIPO III DUR-GIPS
yellow
1140-0111140-351
blue
1140-0101140-350
Consistency: 28-30ml/100g | Working Time: 5 min. | Setting Time: 12 min. | Expansion: 0.16% | Comp. Streight: 8.500 Psi
Hard stone for models antagonist and flexible denture.
1 Kg.25 Kg.
1140-0121140-352
pink
PouchBag
Yeso tipo III para modelos antagonistas y prótesis flexibles.
ISO 6873: TIPO II MUFLA-STONE
1184-010
white
Consistency: 35-40ml / 100g | Working Time: 3-4 min. | Setting Time: 8 min. | Expansion: 0.30% | Comp. Streight: 3.500 Psi
Yeso líquido para el enmuflado de Acrílico. Sin necesidad de vibración.Special flow plaster to muffle pouring without vibration.
1 Kg.Pouch1184-200 20 Kg.Bag
Gypsums - Yesos
LABOWAX-PALADAR
8548-100
Paladares de cera preformados.Palatine wax preformed.
Pink 10 u.
CROWNS AND BRIDGES - CORONAS Y PUENTES
LABOWAX - CASTING WAX
8504-7018504-7018504-703
Cera para colado en la técnica de coronas y puentes.Casting wax for crowns and bridges technique.
StickStickStick
RedBlueGreen
150 g.150 g.150 g.
8501-1318501-1328501-133
TabletTablet Tablet
RedBlueGreen
113 g.113 g.113 g.
8504-7018504-7028504-703
RedBlueGreen
CanCanCan
70 g.70 g.70 u.
LABOWAX-DIPPING WAX
8582-500
Cera de inmersión elástica. En escamas.Dipping wax, elastic.
Orange 100 g.
LABOWAX-OPACA
8503-7018503-7028503-7038503-704
Cera para esculpir. OpacaSculpturing wax. Opaque.
MintLight BlueIvoryGray
70 g.70 g.70 g.70 g.
LABOWAX-STICKY
8548-075
Cera adhesiva para reparaciones.Sticky wax for fixing.
Stick 35 u.70g.
PLASTIC SPRUES
GreenBlue
HardSoft
1000 u.1000 u.
LABOWAX-WAX WIRE
Hilo de cera en carrete para la confección de bebederos.Wax wire round on spools, for sprues.
2.5 - 3.0 - 3.5 - 4.0 - 5.0 mmGreen 250 g.
CR. CO.
8525-150
Cera para modelado en revestimiento. Wax for blocking out.
blue 500 g.8525-152 green 500 g.
RETENTIONS
8560-1508561-1508564-250
Cera para retenciones. En TirasWax performed retentions.
RoundOval Alternating
25 u.25 u.25 u.
CLASPS
8590-1008590-1108590-200
Ganchos preformados de cera.Wax preform clasps.
PremolarsMolars Bonyhard clasps
10 x 20 u.10 x 20 u.10 x 20 u.
STIPPLED CASTING WAX
8530-5008531-5008533-500
Cera grabada en planchas.Calibrated stippled wax.
FineCoarseExtra Coarse
15 u.15 u.15 u.
0,5 mm.0,5 mm.0,5 mm.
SMOOTH CASTING WAX
8510-500
Cera lisa calibrada en planchas. Calibrated smooth WAX.
0.5mm.smooth 15 u.
WAX PROFILES LINGUAL BARS CONTINUOS CLASPS BEADING WIRE
4.3 x 2.0 mm1,5x 1,0 mm 1.0 mm
FRAME WORK TECHNIQUE - TÉCNICA ESQUELÉTICA
MESH
8540-0018540-002
Cera para retención. Rejillas. Mesh wax of retentions.
SquareRound
20 u.20 u.
ACRYLIC WORK - TÉCNICA ACRÍLICA SPRUES - BEBEDEROS
Waxes - LABOWAX
LABOWAX
ISO 15912: 2006HIGH-CASTBonding Material: Phosphate Consistency: 24 ml. Working Time: 6-7 min. Ready for Burnout: 25-30 min. Final Temperature: 700-900ºC Mixing Liquid: High-cast expansor.
Revestimiento fosfático universal para todo tipo de aleaciones. Calentamiento convencional o rápido.
Universal investment for all alloys and pressable ceramics. Normal or rapid burnout technique (speed)
Mixing liquid6636-200 box 2 x 1Kg.6636-050
2 Kg.500 ml.
CHROME COBALT DENTURES - TÉCNICA ESQUELÉTICA.
PIN-CAST
6660-100
Revestimiento para colado de pernos.Investment for pins casting.
Bag1 Kg.
6660-100Pouch
25 Kg.
ISO 15912: 2006Bonding Material: Gypsum Consistency: 30 ml. Working Time: 6-8 min. Ready for Burnout: 60 min. Final Temperature: 700-720ºC Mixing Liquid: Distilled Wather.
SPECIAL INVESTMENT - REVESTIMIENTOS PARA PERNOS
CROMACAST
6622-2006622-100
Revestimiento a base de fosfatos para colados en CR.CO.Phosphate - based precision investment for CR.CO. casting.
20 Kg.1 L.
box 50 Pouch x 400g.Mixing liquid
ISO 15912: 2006Bonding Material: Phosphate Consistency: 13 ml. Working Time: 4-5 min. Ready for Burnout: 60 min. Final Temperature: 900-1080ºC Mixing Liquid: Cromacast expansion.
Investments - Revestimientos
CROWNS AND BRIDGES - CORONAS Y PUENTES
CROMOVEST
6632-0506632-1006632-250
Revestimiento a base de polisilicatos de alcohol para colados en CR.COPolisilicate alcohol based investment for CR.CO. casting.
bag + mixing liquidbag + mixing liquidbag + mixing liquid
5 Kg.10 Kg.25Kg.
ISO 15912: 2006Bonding Material: Polysil & ALC Consistency: 18-20 ml. Working Time: 8-10 min. Ready for Burnout: 60 min. Final Temperature: 900-1050ºC Mixing Liquid: A&B.
SILCA-VEST
6630-1006630-200
Revestimiento a base de polisilicatos y alcohol para colados en CR.COPolisilicate alcohol based investment for CR.CO. casting.
bag + mixing liquidbag + mixing liquid
10 Kg.20 Kg.
ISO 15912: 2006Bonding Material: Polysil & Alc Consistency: 14-18 ml. Working Time: 8-10 min. Ready for Burnout: 60 min. Final Temperature: 900-1050ºC Mixing Liquid: A&B.
TENSION REDUCER
3270-1253270-2503270-060
Reductor de tensión para patrones de cera.Surface tension-reducing agent for wax patterns.
SprayRefill Spray
60 ml125 ml250 ml
OKKLU-SPRAY
3245-5013245-502
Spray de oclusión para la visualización de puntos de contacto.Spray for making contact point visible.
GreenRed
50 g.50 g.
LAC-SPACER
3221-2513221-252
Laca espaciadora para muñones. Superficie lisa, resistente a los rasguños.
Lacquer for stumps. Smooth, scratch resistant surface.
Thickness: 5 µmThickness: 10 µm
25 ml.25 ml.
3221-2533221-2543220-250
Thickness: 13 µmThickness: 15 µm
BlueRed SilverGold Thinner for die spacer 25 ml.
25 ml.25 ml.
BAÑOMOL
8010-0108010-050
Líquido endurecedor de modelos.Hardener for duplicated models.
1 L.5 L.
REMO-GIPS
1191-100
Removedor de yeso y alginato.
Removing liquid for stone and alginate. Fast reaction 4hs.
1000 ml.
CERA-FILM
3205-0153205-050
Separador de Yeso-Cera. Separating fluid gypsum-wax.
PaintBrushRefill
15 ml.50 ml.
LABOXGEL
Gelatina de duplicado a base de AGAR-AGAR.
Duplicating material. Based on AGAR-AGAR reversible.
5510-0115510-010
1 Kg.5 Kg.
LABOX-SIL
Silicona para laboratorio. Policondensacion.Silicone for laboratory policondensation.
5020-200 2 Kg.+40 g.Shore 80
Complements - Complementos
Líquido separador para resinas acrílicas.Separating fluid for acrylic resins.LABO-FILM
1000 ml.3201-100
ISO 15912: 2006HIGH-CASTBonding Material: Phosphate Consistency: 24 ml. Working Time: 6-7 min. Ready for Burnout: 25-30 min. Final Temperature: 700-900ºC Mixing Liquid: High-cast expansor.
Revestimiento fosfático universal para todo tipo de aleaciones. Calentamiento convencional o rápido.
Universal investment for all alloys and pressable ceramics. Normal or rapid burnout technique (speed)
Mixing liquid6636-200 box 2 x 1Kg.6636-050
2 Kg.500 ml.
CHROME COBALT DENTURES - TÉCNICA ESQUELÉTICA.
PIN-CAST
6660-100
Revestimiento para colado de pernos.Investment for pins casting.
Bag1 Kg.
6660-100Pouch
25 Kg.
ISO 15912: 2006Bonding Material: Gypsum Consistency: 30 ml. Working Time: 6-8 min. Ready for Burnout: 60 min. Final Temperature: 700-720ºC Mixing Liquid: Distilled Wather.
SPECIAL INVESTMENT - REVESTIMIENTOS PARA PERNOS
CROMACAST
6622-2006622-100
Revestimiento a base de fosfatos para colados en CR.CO.Phosphate - based precision investment for CR.CO. casting.
20 Kg.1 L.
box 50 Pouch x 400g.Mixing liquid
ISO 15912: 2006Bonding Material: Phosphate Consistency: 13 ml. Working Time: 4-5 min. Ready for Burnout: 60 min. Final Temperature: 900-1080ºC Mixing Liquid: Cromacast expansion.
Investments - Revestimientos
CROWNS AND BRIDGES - CORONAS Y PUENTES
CROMOVEST
6632-0506632-1006632-250
Revestimiento a base de polisilicatos de alcohol para colados en CR.COPolisilicate alcohol based investment for CR.CO. casting.
bag + mixing liquidbag + mixing liquidbag + mixing liquid
5 Kg.10 Kg.25Kg.
ISO 15912: 2006Bonding Material: Polysil & ALC Consistency: 18-20 ml. Working Time: 8-10 min. Ready for Burnout: 60 min. Final Temperature: 900-1050ºC Mixing Liquid: A&B.
SILCA-VEST
6630-1006630-200
Revestimiento a base de polisilicatos y alcohol para colados en CR.COPolisilicate alcohol based investment for CR.CO. casting.
bag + mixing liquidbag + mixing liquid
10 Kg.20 Kg.
ISO 15912: 2006Bonding Material: Polysil & Alc Consistency: 14-18 ml. Working Time: 8-10 min. Ready for Burnout: 60 min. Final Temperature: 900-1050ºC Mixing Liquid: A&B.
TENSION REDUCER
3270-1253270-2503270-060
Reductor de tensión para patrones de cera.Surface tension-reducing agent for wax patterns.
SprayRefill Spray
60 ml125 ml250 ml
OKKLU-SPRAY
3245-5013245-502
Spray de oclusión para la visualización de puntos de contacto.Spray for making contact point visible.
GreenRed
50 g.50 g.
LAC-SPACER
3221-2513221-252
Laca espaciadora para muñones. Superficie lisa, resistente a los rasguños.
Lacquer for stumps. Smooth, scratch resistant surface.
Thickness: 5 µmThickness: 10 µm
25 ml.25 ml.
3221-2533221-2543220-250
Thickness: 13 µmThickness: 15 µm
BlueRed SilverGold Thinner for die spacer 25 ml.
25 ml.25 ml.
BAÑOMOL
8010-0108010-050
Líquido endurecedor de modelos.Hardener for duplicated models.
1 L.5 L.
REMO-GIPS
1191-100
Removedor de yeso y alginato.
Removing liquid for stone and alginate. Fast reaction 4hs.
1000 ml.
CERA-FILM
3205-0153205-050
Separador de Yeso-Cera. Separating fluid gypsum-wax.
PaintBrushRefill
15 ml.50 ml.
LABOXGEL
Gelatina de duplicado a base de AGAR-AGAR.
Duplicating material. Based on AGAR-AGAR reversible.
5510-0115510-010
1 Kg.5 Kg.
LABOX-SIL
Silicona para laboratorio. Policondensacion.Silicone for laboratory policondensation.
5020-200 2 Kg.+40 g.Shore 80
Complements - Complementos
Líquido separador para resinas acrílicas.Separating fluid for acrylic resins.LABO-FILM
1000 ml.3201-100
ISO 6873: TIPO III ORTHO-GIPS
1150-010
snow white
Consistency: 28ml/100g | Working Time: 6 min. | Setting Time: 10 min. | Expansion: 0.09% | Comp. Streight: 8.500 Psi
Yeso de baja expansión especial para modelos de ortodoncia. Special stone for study models and orthodontic.
1 Kg.
ADA: TIPO III
Pouch1150-350 25 Kg.Bag
ISO 6873: TIPO III ECO-GIPS
1170-0101170-350
1170-0111170-351
1141-0121141-352
1170-0121170-350
green blue yellow white
Consistency: 35ml/100g | Working Time: 5 min. | Setting Time: 12 min. | Expansion: 0.18% | Comp. Streight: 8.000 Psi
Yeso piedra para modelos y antagonistas.Hard stone for models and antagonist.
1 Kg.Pouch25 Kg.Bag
ISO 6873: TIPO II PLASTER
1171-010
white yellow
Consistency: 45 ml / 100g | Working Time: 7 min. | Setting Time: 13 min. | Expansion: 0.23% | Comp. Streight: 4.600 Psi
Yeso taller para laboratorio.Plaster for laboratory.
1 Kg.Pouch1171-010
1171-0111171-351 25 Kg.Bag
ISO 6873: TIPO II LABOR-PLASTER
1182-010
white
Consistency: 50ml / 100g | Working Time: 7 min. | Setting Time: 13 min. | Expansion: 0.29% | Comp. Streight: 3.300 Psi
Yeso Taller Para Laboratorio.De fácil recortado.Plaster for laboratory. Easy to cut.
1 Kg.Pouch1182-350 25 Kg.Bag
ISO 6873: TIPO II ORTHO-PLASTER
1151-010
snow white
Consistency: 37-38ml / 100g | Working Time: 9 min. | Setting Time: 13 min. | Expansion: 0.20% | Comp. Streight: 6.500 Psi
Yeso para modelos de ortodoncia. De facil recortado.Plaster for models in orthodontics, easy to cut.
1 Kg.Pouch1151-350 25 Kg.Bag
MODEL STONES - YESOS PARA MODELOS
PLASTERS - YESOS LIGEROS
ISO 6873: TIPO III DUR-GIPS
yellow
1140-0111140-351
blue
1140-0101140-350
Consistency: 28-30ml/100g | Working Time: 5 min. | Setting Time: 12 min. | Expansion: 0.16% | Comp. Streight: 8.500 Psi
Hard stone for models antagonist and flexible denture.
1 Kg.25 Kg.
1140-0121140-352
pink
PouchBag
Yeso tipo III para modelos antagonistas y prótesis flexibles.
ISO 6873: TIPO II MUFLA-STONE
1184-010
white
Consistency: 35-40ml / 100g | Working Time: 3-4 min. | Setting Time: 8 min. | Expansion: 0.30% | Comp. Streight: 3.500 Psi
Yeso líquido para el enmuflado de Acrílico. Sin necesidad de vibración.Special flow plaster to muffle pouring without vibration.
1 Kg.Pouch1184-200 20 Kg.Bag
Gypsums - Yesos
LABOWAX-PALADAR
8548-100
Paladares de cera preformados.Palatine wax preformed.
Pink 10 u.
CROWNS AND BRIDGES - CORONAS Y PUENTES
LABOWAX - CASTING WAX
8504-7018504-7018504-703
Cera para colado en la técnica de coronas y puentes.Casting wax for crowns and bridges technique.
StickStickStick
RedBlueGreen
150 g.150 g.150 g.
8501-1318501-1328501-133
TabletTablet Tablet
RedBlueGreen
113 g.113 g.113 g.
8504-7018504-7028504-703
RedBlueGreen
CanCanCan
70 g.70 g.70 u.
LABOWAX-DIPPING WAX
8582-500
Cera de inmersión elástica. En escamas.Dipping wax, elastic.
Orange 100 g.
LABOWAX-OPACA
8503-7018503-7028503-7038503-704
Cera para esculpir. OpacaSculpturing wax. Opaque.
MintLight BlueIvoryGray
70 g.70 g.70 g.70 g.
LABOWAX-STICKY
8548-075
Cera adhesiva para reparaciones.Sticky wax for fixing.
Stick 35 u.70g.
PLASTIC SPRUES
GreenBlue
HardSoft
1000 u.1000 u.
LABOWAX-WAX WIRE
Hilo de cera en carrete para la confección de bebederos.Wax wire round on spools, for sprues.
2.5 - 3.0 - 3.5 - 4.0 - 5.0 mmGreen 250 g.
CR. CO.
8525-150
Cera para modelado en revestimiento. Wax for blocking out.
blue 500 g.8525-152 green 500 g.
RETENTIONS
8560-1508561-1508564-250
Cera para retenciones. En TirasWax performed retentions.
RoundOval Alternating
25 u.25 u.25 u.
CLASPS
8590-1008590-1108590-200
Ganchos preformados de cera.Wax preform clasps.
PremolarsMolars Bonyhard clasps
10 x 20 u.10 x 20 u.10 x 20 u.
STIPPLED CASTING WAX
8530-5008531-5008533-500
Cera grabada en planchas.Calibrated stippled wax.
FineCoarseExtra Coarse
15 u.15 u.15 u.
0,5 mm.0,5 mm.0,5 mm.
SMOOTH CASTING WAX
8510-500
Cera lisa calibrada en planchas. Calibrated smooth WAX.
0.5mm.smooth 15 u.
WAX PROFILES LINGUAL BARS CONTINUOS CLASPS BEADING WIRE
4.3 x 2.0 mm1,5x 1,0 mm 1.0 mm
FRAME WORK TECHNIQUE - TÉCNICA ESQUELÉTICA
MESH
8540-0018540-002
Cera para retención. Rejillas. Mesh wax of retentions.
SquareRound
20 u.20 u.
ACRYLIC WORK - TÉCNICA ACRÍLICA SPRUES - BEBEDEROS
Waxes - LABOWAX
LABOWAX
Gypsums - Yesos
ISO 6873: TIPO IV DIE-ROCK
yellow
1102-0111102-351
1102-0131102-353
1102-0151102-354
ivory
Consistency: 20ml/100g; | Working Time: 9 min. | Setting Time: 12 min. | Expansion: 0.13% | Comp. Streight: 17.000 Psi
High strengh die stone.
1 Kg.25 Kg.
ADA: TIPO V
PouchBag
white
Yeso para troqueles de máxima compresión.
ISO 6873: TIPO IV RESIN-STONE
peach
1107-012 1107-011
ivory
Consistency: 20ml/100g; | Working Time: 7 min. | Setting Time: 10 min. | Expansion: 0.08% | Comp. Streight: 11.000 Psi
Resin fortified, low expansion die stone.
1 Kg.
ADA: TIPO IV
Pouch1107-352 1107-351 25 Kg.Bag
Yeso extra duro aditivado con resina. De baja expansión.
ISO 6873: TIPO IV MIX-ROCK
pink
1120-0111120-351
1120-0121120-352
1120-0131120-353
Consistency: 23ml / 100g | Working Time: 9 min. | Setting Time: 13 min. | Expansion: 0.09% | Comp. Streight: 13.000 Psi
Low-expansion die stone.
1 Kg.25 Kg.
ADA: TIPO IV
PouchBag
yellowwhite
Yeso para troqueles de baja expansión.
SPECIALITY STONE - YESOS PARA ESPECIALIDADES
DIE STONES - YESOS PARA MODELOS
ISO 6873: TIPO III MOUNTING-ROCK
1160-005
white
Consistency: 30ml/100g | Working Time: 1-2 min. | Setting Time: 3 min. | Expansion: 0.06% | Comp. Streight: 6.500 Psi
Gypsum for mounting to articulators. Low-expansion fast-setting stone.
500 g.Pouch1160-350 25 Kg.Bag
Yeso especial para impresión y montaje en articulador. Freguado rápìdo. Baja expansión.
ISO 6873: TIPO IV ADA: TIPO IV SCAN-ROCK
golden salmon
1112-0111112-012
Consistency: 20ml/100g; | Working Time: 9 min. | Setting Time: 12 min. | Expansion: 0.09% | Comp. Streight: 17.000 Psi
Elite Gypsum. Extra hard high density die stone. CAD-CAM compatible. Yeso Premium. De baja expansión y alta compresión. Compatible CAD-CAM.
Pouch 1 Kg.1112-3511112-352 Bag 25 Kg.
white
ISO 6873: TIPO IV FLOW-ROCK
deep bluedeep buff
1130-0111130-351
1130-0121130-352
1130-0131130-353
Consistency: 22-24ml/100g | Working Time: 6-9 min. | Setting Time: 11 min. | Expansion: 0.08% | Comp. Streight: 12.000 Psi
Fluid, low-expansion base stone.
1 Kg.Pouch25 Kg.Bag
Yeso fluido autonivelante especial para zócalos.
PULICROM
7880-010
Líquido electrolítico para el pulido de estructuras de Cr. Co.
Liquid for electrolytic polishing of Cr.Co.
1l.
POLI-GEL
Gel para pulir metales preciosos y resinas.Polishing paste for resins.
150 g.7881-150
ALUMINUM OXIDE
Óxido de aluminio para arenado.
Special corundum grit comprising 99,6% aluminum oxide.
1 k.Pouch
RUBBER WHEELS
7710-100 size: 24 x 6,3 mm.box x 100 u.
Goma rueda negra para pulir Cromo Cobalto y metales duros.Black rubber for finishing and polishing Cr. Co. metals.
PUMICE
7882-010 1 k.Piedra pómez en polvo.Pumice powder.
RUBBER CYLINDERS
Goma punta negra para pulir Cromo Cobalto y metales duros.7710-101 box x 100 u. size: 22 x 3,1 mm.
Black rubber for finishing and polishing Cr. Co. metals.
ACRYLIC POLISHERS
7720-250 25u.
Goma de silicona para el pulido de Acrílico.Silicone polishers for acrylic materials.
Casting Alloy - Aleaciones para colado
LABOX Co. Cr. ISO: 22674: TIPO V
4010-100
Aleación de cromo cobalto para prótesis esquelética.Cr. Co. frame work casting alloy.
1 k.
SURFACE FINISHING - ACABADO DE LA SUPERFICIE
PHYSICAL AND MECHANICAL FEATURES:Solidus-Liquidus temperature: 1340-1400ºCDensity: 8,3 g/cm3.Vickers hardness: 390 Hv10.Elongation at fracture: 6,2 %Yield load strenght (Rp0.2): 609 Mpa.Modulus of elasticity: 200 Gpa.
Composition: Cobalto (Co): 62% Cromo (Cr): 31% Molibdeno (Mo): 5% Others: C, Fe, Si, Mn.
+54 11 4758-9567 | +54 11 4758-9231 | [email protected] | www.laboxdental.com
Av Matienzo e Itacumbú | El Palomar | Bs. As. | Argentina
Physical Properties - Propiedades FisicasIn
vest
men
ts
HIGH-CAST
CROWNS AND BRIDGES
CHROME COBALT DENTURES
SPECIAL INVESTIMENT
CROMACAST
SILCA-VEST
CROMOVEST
CROMOVEST SF
PIN-CAST
Bonding Material
Type: Class ISO
15912:2006
Phosphate
Material
salmon
green
PLASTER
1:2
2 2 45 60 7 13 0,23 2500(18)
4600(32)-
24 60 4-6- 25-306 -7 - 2.0 - 1.2 700-900ºC high.cast
Phosphate2:1 13 30 13-1760 604 -5 35 1,2-1,2 900-1080ºC cromacastexpansor
expansor
A&BPolysil& Alc
2:1 14-18 - 760 608 -10 30-45 1,4 900-1050ºC
Polysil& Alc
2:1 18-20 - 760 608 -10 30-45 1,4 900-1050ºC A&B
A&BPolysil& Alc
2:1 18-20 - 760 608 -10 30-45 1,4 900-1050ºC
Gypsum1:1 30 30 560 606 -8 - 0,4 700-720ºC distilledwather
Consistency (ml.)
Mechanical Mixing (sec.)
ManualMixing (sec.)
Working Time (min.)
Model Ready (min.)
Ready for burnout (min.)
Expansion ( % / Setting - Themal)
Compressive stregth 2h. (Mpa)
Final Temperature
Mixing Liquid
green
Gyps
ums
Labox