Ultra-wide planar Bragg grating detuning and 2d channel
waveguide integration through direct grating writing
G.D.Emmerson, C.B.E.Gawith, R.B.Williams and P.G.R.SmithOptoelectronics Research Centre, University of Southampton, SO17
1BJ, United Kingdom
S.G.McMeekin, J.R.Bonar and R.I.LamingAVANEX Livingston, Starlow Park, Livingston, EH54 8SF
Outline• Goals of the work• Direct UV writing
– How structures are defined
• Direct Grating Writing– Comparison with existing techniques– Method of single-step processing
• Grating detuning• Ultra-wide results• Unique features• Conclusions
Motivation
• Goal– To devise a way of writing high quality Bragg gratings
in planar waveguides
• Issues:– Number of possible solutions – based around fibre
Bragg grating techniques applied to planar channels.– Problem is the need for core uniformity – excellent in
fibre – expensive to achieve in planar.– Need constant along waveguide!
Approach
• Builds on two key techniques:– Direct UV writing into silica – particularly the
work by Mikael Svalgaard, COM, Technical University of Denmark
– Work in the ORC (and elsewhere) on writing of Bragg gratings in fibre using the phase mask stepping technique
Direct UV writing• UV laser (244nm CW)
focused down to micron order writing spot.
• Channel waveguide structures defined through relative translation between sample and writing spot.
Translation controlled via computer control, no mask or subsequent processing
required
Planar Bragg gratings
• Traditionally planar and fibre Bragg gratings fabricated in two steps:– Channel waveguide
fabrication– Superimposed grating
modulation through exposure to a UV interference pattern
Direct Grating Writing
• Writing spot formed by crossing two focused 244nm beams• Resultant spot has an inherent interference pattern• Channels waveguides defined by translation with laser
constantly on• Modulating the laser during translation results in grating
structure defined at the same time as a channel waveguide
Single-step characteristics
• The writing spot contains the grating structure
• Can define channels or channels and Bragg gratings with the same neff
• Can use the maximum grating contrast possible
• Small writing spot allows rapid variation of grating parameters
Samples• Flame Hydrolysis Deposition (FHD) silica-on-silicon samples produced by Alcatel Optronics UK
• Core layer co-doped with germanium to produce intrinsic photosensitivity• Samples Deuterium or Hydrogen loaded @150Bar for 1 week
Waveguide results
• Illustrated: three cross-coupler structures written using DGW
• ‘Strong’ waveguides as visible as etched structures to the naked eye
• NA @633nm = 0.17±0.02 from far field imaging
• Fibre-fibre loss @ 1.55µm ~2.5dB for a 30mm long channel waveguide
Grating Response
Control of the grating parameters through the writing conditions.
Low contrast and high contrast gratings can be produced with minimal effect on the effective index of the channel.
Detuned Grating Formation
• Beam modulated every 600nm (100nm different from interference pattern)
• Grating with 600nm period built up, with reduced contrast
• Detuning range inversely proportional to the number of grating plains in the spot
Example writing spot, 2.5µm wide with a Λ=500nm interference pattern
Detuning range
width of writing spot, m
0 10 20 30 40 50
0% c
ontr
ast
span
, nm
0
100
200
300
400
500
N
2
0% span
2-d Bragg grating incorporation
Entire structure written in one go, with two gratings of differing period defined through detuning.
Arm separation of 200µm, 8mm long gratings with periods of 532 and 532.4nm.
Wavelength DetuningAll gratings written with a writing spot period of 532nm
Grating period controlled only through software
Wavelength DetuningAll gratings written with a writing spot period of 532nm
Grating period controlled only through software
Material InsightThe grating response gives a direct insight into the parameters of the structures written, e.g. birefringence of 1.2x10-4.
Along with the relationship between writing conditions and the strength of the waveguide
Thermal properties
• Gratings allow assessment of material thermal characteristics and stability
Temperature / °C
0 100 200 300 400 500 600 700
1.4535
1.4540
1.4545
1.4550
1.4555
1.4560
1.4565
1.4570
34.4 KJcm -2
17.2 KJcm -2
8.6 KJcm -2
Effe
ctiv
e in
de
x
Thermal tuning of grating
Thermal annealing of grating
(30 minutes per anneal step)
Dispersion measurement
• Ultrawide detuning gives a powerful technique for measuring waveguide dispersion
• Arguably ‘non-intrusive’?
Thermal locking•One problem with Direct UV writing is H2/D2 out-diffusion
•Thermal locking (rapid heat treatment – 1200 to 1400C for a few seconds) locks the photosensitivity into the glass – lasts > 6months
•Much lower fluences are required to induce a waveguide than in the freshly loaded sample.
•The trend for lower writing powers to produce higher index changes remains but the discrepancy becomes less at lower fluences.
Unlike thermally locked samples, the loaded samples exhibit a distinct threshold effect where channels are no longer written for fluences below 10KJcm-2. This effect is not shown in the ‘locked’ samples.
Conclusions
• Simultaneous writing provides a large control over the writing conditions for the Bragg grating structures
• Grating parameters can be varied to give responses >30dB with a range of bandwidths
• Small writing spot allows for almost unparralled flexibility in the grating period defined
• The period of the gratings can be varied to give responses over the O, E, S, C, L and U bands without any change to the fabrication setup
• Gratings provide a power material characterisation tool