D. Bassler, W. Shmayda, and W. U. SchröderUniversity of RochesterLaboratory for Laser Energetics
The Use of Atomic-Layer Deposition to Study How Surface Effects Impact Tritium Uptake
1
Tritium Focus Group MeetingOak Ridge, TN
15–17 May 2018
Hydrogen Triton
180 200 220 240 260 280 300Time (s)
1.0
1.5
2.0
2.5
Pre
ssu
re (
To
rr)
E27354
2
ALD is a vehicle for exploring surface chemistry effects on tritium uptake
• Surface water layers play an important role in tritium adsorption
• Tungsten and hafnium oxide have different electronic andphysical properties than stainless steel
• ALD is a gas–surface reaction that creates thin films frommetal oxides
• An ALD system is being designed to test tungsten and hafniumoxide films
Summary
ALD: atomic-layer deposition
Isotopic exchange is a first step in tritium adsorption on metal surfaces
E25746c
3
Hydrogen
Hydroxyl layer (chemisorbed)
Triton
Metal lattice
Ice-like layers (chemisorbed)
Liquid-like layers (physisorbed)
Hydrogen isotopesOxygenMetal atomHydrogen bondFull chemical bonds
P. A. Thiel and T. E. Madey, Surf. Sci. Rep. 7, 211 (1987).
E27346d
4
Isotopic exchange is a first step in tritium adsorption on metal surfaces
Hydrogen
Hydroxyl layer (chemisorbed)
Triton
Metal lattice
Ice-like layers (chemisorbed)
Liquid-like layers (physisorbed)
Hydrogen isotopesOxygenMetal atomHydrogen bondFull chemical bonds
There is a potential to accomodate large amounts of tritium in water: /mol H m106 3.
Modifications to the metal surface alter the hydroxide concentration
E27347
5
H2O
OH1.0SS316
Pure Fe0.8
0.6
0.4
Ph
oto
elec
tro
n in
ten
sity
(arb
itra
ry u
nit
s)
0.2
0.0538 536 534
Binding energy (eV)
532 530 528 526
SS316-CRO
Y. Ozeki et al., Fusion Sci. Technol. 60, 1499 (2011).
Hydroxyl-layer alterations may correlate with different surface tritium inventories.
O1s spectra
E27348a
6
Hafnium and tungsten have differing electronic and lattice structure than iron
Hafnium Tungsten Iron
Electronic configuration [Xe] 4f14 6s2 5d2 [Xe] 4f14 6s2 5d4 [Ar] 4s2 3d6
Ionic radius (pm) 71 60 25
Activation energy (kJ/mol) 119.9 118.0 56.5
Hafnium
[Xe]
Tungsten
[Xe][Ar]
ALD grows complete films through alternating injections of reactive gases
E27349
7
• Reagents (precursors) areinjected in short pulses
180 200 220 240 260 280 300
Time (s)
1.0
1.5
2.0
2.5
Pre
ssu
re (
To
rr)
One cycle = one monolayer
ALD film growth is a self-terminating gas–surface reaction
E27352
8
180 200 220 240 260 280 300
Time (s)
1.0
1.5
2.0
2.5
Pre
ssu
re (
To
rr)
OH terminated surface
Substrate Substrate Substrate
Substrate
Nex
t AL
D c
ycle
Substrate
H2O pulseN2 purge
N2 purgeHfCl4 pulse
OH OH OH OH
OH OHOH OH OH OH
OHOH
Cl Cl Cl
Cl
Cln*(HCI)
n*(HCI)
n*
n*
Hf
Hf
Hf Hf Hf Hf
H H
Hf Hf
HfHfHf
ClCl Cl
Cl
Cl
Cl
Cl
Cl Cl
ClCl
Cl
Cl
Cl
Cl
O O O O O
O
OOO O O O O O
O OO
O
OO
O
O
ALD film growth is a self-terminating gas–surface reaction
E27352a
9
180 200 220 240 260 280 300
Time (s)
1.0
1.5
2.0
2.5
Pre
ssu
re (
To
rr)
OH terminated surface
Substrate Substrate Substrate
Substrate
Nex
t AL
D c
ycle
Substrate
H2O pulseN2 purge
N2 purgeHfCl4 pulse
OH OH OH OH
OH OHOH OH OH OH
OHOH
Cl Cl Cl
Cl
Cln*(HCI)
n*(HCI)
n*
n*
Hf
Hf
Hf Hf Hf Hf
H H
Hf Hf
HfHfHf
ClCl Cl
Cl
Cl
Cl
Cl
Cl Cl
ClCl
Cl
Cl
Cl
Cl
O O O O O
O
OOO O O O O O
O OO
O
OO
O
O
ALD film growth is a self-terminating gas–surface reaction
E27352b
10
180 200 220 240 260 280 300
Time (s)
1.0
1.5
2.0
2.5
Pre
ssu
re (
To
rr)
OH terminated surface
Substrate Substrate Substrate
Substrate
Nex
t AL
D c
ycle
Substrate
H2O pulseN2 purge
N2 purgeHfCl4 pulse
OH OH OH OH
OH OHOH OH OH OH
OHOH
Cl Cl Cl
Cl
Cln*(HCI)
n*(HCI)
n*
n*
Hf
Hf
Hf Hf Hf Hf
H H
Hf Hf
HfHfHf
ClCl Cl
Cl
Cl
Cl
Cl
Cl Cl
ClCl
Cl
Cl
Cl
Cl
O O O O O
O
OOO O O O O O
O OO
O
OO
O
O
ALD film growth is a self-terminating gas–surface reaction
E27352c
11
180 200 220 240 260 280 300
Time (s)
1.0
1.5
2.0
2.5
Pre
ssu
re (
To
rr)
OH terminated surface
Substrate Substrate Substrate
Substrate
Nex
t AL
D c
ycle
Substrate
H2O pulseN2 purge
N2 purgeHfCl4 pulse
OH OH OH OH
OH OHOH OH OH OH
OHOH
Cl Cl Cl
Cl
Cln*(HCI)
n*(HCI)
n*
n*
Hf
Hf
Hf Hf Hf Hf
H H
Hf Hf
HfHfHf
ClCl Cl
Cl
Cl
Cl
Cl
Cl Cl
ClCl
Cl
Cl
Cl
Cl
O O O O O
O
OOO O O O O O
O OO
O
OO
O
O
There is a temperature plateau for optimal film growth in ALD
E27353
12
GPC = growth per cycle
GP
C
TG independent self-saturative growth
Precursor decomposition
Low activity of precursor
Growth temperature (°C)
• Hafnium
– 275 °C
• Tungsten
– 350 °C
An ALD system is being design stages to deposit hafnium and tungsten oxide on stainless steel
E27355
13
ALD timing valves
Heated line
Nitrogen purge line20 sscm
Hafnium tetrachloride
Tungsten chloroxide
WaterHeated chamber
Nominal pressure: 1 Torr Pressure
gaugePressure
gauge
VacuumExhaustGetter
A getter is needed to remove unreacted precursors and hazardous byproducts
E27356
14
• Unreacted precursors will coat the vacuum pump
– high surface area stainless steel sponge
• In a 50 cycle process, we can produce 82 nmol of HCl(g) – CaO derivative beds can convert up to 80% efficiency
E27354
15
ALD is a vehicle for exploring surface chemistry effects on tritium uptake
Summary/Conclusions
• Surface water layers play an important role in tritium adsorption
• Tungsten and hafnium oxide have different electronic andphysical properties than stainless steel
• ALD is a gas–surface reaction that creates thin films frommetal oxides
• An ALD system is being designed to test tungsten and hafniumoxide films