TECHNICAL CHARACTERISTICS CEVISAMA 2009 - GRES PORCELAIN
A.A. PEI Hardness Chemical R SLIP
RESISTANT COF SIZE SERIE ITEM ISO 10545-3
(%) ISO 10545-7
UNE 67 -101 (Mohs)
ISO 10545-13 DIN
51130:2004 ASTM C 1028
59X59 INOX Inox White E ≤ 0.5% III 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
29,4X59 Inox Brown E ≤ 0.5% III 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
29,4X29,4 Inox Black E ≤ 0.5% III 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
LAGOON Lagoon White E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Lagoon Silver Grey E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Lagoon Brown E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Lagoon Black E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
ATLANTIS Atlantis Sand E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Atlantis Beige Stone E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Atlantis Nut Stone E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
59X59 APRILIA Aprilia Sand E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
49X49 Aprilia Beige E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
29,4X59 Aprilia Grey E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
29,4X29,4 Aprilia Graphite Grey E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Aprilia Black E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Aprilia Chocolate E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
59X59 MYTHOS Mythos Tahiti White, E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
44X66 Mythos Everest Grey, E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
29,4X59 Mythos Marrakech Beige E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
29,4X29,4 Mythos Colombian Coffee E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Mythos Barcelona Red E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
59X59 KORUS Korus Ivory E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
44X66 Korus Beige E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
49X49 Korus Camel E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
29,4X59 Korus White E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
29,4X29,4 Korus Ice Grey E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Korus Grey E ≤ 0.5% IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
44X66 MARTINICA Martinica Snow Oak E ≤ 0.5% II 7 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Martinica Snow Grey E ≤ 0.5% II 7 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Martinica Snow Wenge E ≤ 0.5% II 7 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Martinica Athenea Pine E ≤ 0.5% II 7 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Martinica Athenea Cherry E ≤ 0.5% II 7 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Martinica Athenea Chesnut E ≤ 0.5% II 7 GLA acido GLA base R9 Dry 0.7
Wet 0.6
![Page 2: Technical Charact. Porcelain Mapisa 2009](https://reader037.fdocuments.us/reader037/viewer/2022100600/5571f2b349795947648cea00/html5/thumbnails/2.jpg)
TECHNICAL CHARACTERISTICS CEVISAMA 2009 - GRES PORCELAIN
A.A. PEI Hardness Chemical R SLIP
RESISTANT COF SIZE SERIE ITEM ISO 10545-3
(%) ISO 10545-7
UNE 67 -101 (Mohs)
ISO 10545-13 DIN
51130:2004 ASTM C 1028
44x66 BABYLON Babylon Praline E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Babylon Sand E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Babylon Beige E ≤ 0.5% IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
44X66 SUMATRA Sumatra Stone Marfil E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
22X66 Sumatra Stone Beige E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Sumatra Stone Brown E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Sumatra Stone Moka E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
A.A. PEI Hardness Chemical R SLIP
RESISTANT COF SIZE SERIE ITEM ISO 10545-3
(%) ISO 10545-7
UNE 67 -101 (Mohs)
ISO 10545-13 DIN
51130:2004 ASTM C 1028
49X49 CLIO Clio White E ≤ 0.5% III 6 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Clio Beige E ≤ 0.5% III 6 GLA acido GLA base R9 Dry 0.7
Wet 0.6
TAIGA Taiga Walnut E ≤ 0.5% II 6 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Taiga Cherry E ≤ 0.5% II 6 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Taiga Wenge E ≤ 0.5% II 6 GLA acido GLA base R9 Dry 0.7
Wet 0.6
TROY E ≤ 0.5% III-IV 8 GLA acido GLA base R9 Dry 0.7
Wet 0.6
SAVANNAH Savannah Dark Beige E ≤ 0.5% III-IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Savannah orange E ≤ 0.5% III-IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Savannah Cherry E ≤ 0.5% III-IV 9 GLA acido GLA base R9 Dry 0.7
Wet 0.6
SYROS Syros Stone White E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Syros Stone Emerald E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Syros Stone Moka E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Syros Stone White E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Syros Stone Ivory E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6
Syros Stone Moka E ≤ 0.5% V 10 GLA acido GLA base R9 Dry 0.7
Wet 0.6