standar AISI-1035 steel
2
AISI 1035 Carbon Steel (UNS G10350) Topics Covered Introduction Chemical Composition Physical Properties Mechanical Properties Thermal Properties Other Designations Applications Introduction Carbon steels have carbon as the key alloying element in their composition. They also contain up to 0.4% silicon and 1.2% manganese. In addition, the residual elements such as copper, molybdenum, aluminium, chromium and nickel are present in these steels. AISI 1035 is a water resisting carbon steel whose wear resistance and hardenability are increased by the addition of small quantity of chromium. The following sections will discuss in detail about AISI 1035 carbon steel. Chemical Composition The chemical composition of AISI 1035 carbon steel is outlined in the following table. Element Content (%) Iron, Fe 98.63-99.09 Manganese, Mn 0.60-0.90 Carbon, C 0.310-0.380 Sulfur, S 0.050 Phosphorous, P 0.040 Physical Properties The physical properties of AISI 1035 carbon steel are tabulated below. Properties Metric Imperial Density 7.85 g/cm 3 0.284 lb/in 3 Mechanical Properties The following table shows mechanical properties of AISI 1035 carbon steel. Properties Metric Imperial Tensile strength, ultimate 585 MPa 84800 psi Tensile strength, yield 370 MPa 53700 psi Modulus of elasticity 190-210 GPa 29700-30458 ksi Bulk modulus (typical for steel) 140 GPa 20300 ksi Shear modulus (typical for steel) 80 GPa 11600 ksi Poissons ratio 0.27-0.30 0.27-0.30 Elongation at break (in 50 mm) 30% 30% AISI 1035 Carbon Steel (UNS G10350) Saved from URL: http://www.azom.com/article.aspx?ArticleID=6540 P /2 1
-
Upload
nurulimanpristiadi -
Category
Documents
-
view
8 -
download
0
description
standar AISI-1035 steel
Transcript of standar AISI-1035 steel
-
AISI 1035 Carbon Steel (UNS G10350)Topics CoveredIntroductionChemical CompositionPhysical PropertiesMechanical PropertiesThermal PropertiesOther DesignationsApplications
IntroductionCarbon steels have carbon as the key alloying element in their composition. They also contain up to 0.4% siliconand 1.2% manganese. In addition, the residual elements such as copper, molybdenum, aluminium, chromium andnickel are present in these steels.
AISI 1035 is a water resisting carbon steel whose wear resistance and hardenability are increased by the addition ofsmall quantity of chromium.
The following sections will discuss in detail about AISI 1035 carbon steel.
Chemical CompositionThe chemical composition of AISI 1035 carbon steel is outlined in the following table.
Element Content (%)Iron, Fe 98.63-99.09Manganese, Mn 0.60-0.90Carbon, C 0.310-0.380Sulfur, S 0.050Phosphorous, P 0.040
Physical PropertiesThe physical properties of AISI 1035 carbon steel are tabulated below.
Properties Metric ImperialDensity 7.85 g/cm3 0.284 lb/in3
Mechanical PropertiesThe following table shows mechanical properties of AISI 1035 carbon steel.
Properties Metric ImperialTensile strength, ultimate 585 MPa 84800 psiTensile strength, yield 370 MPa 53700 psiModulus of elasticity 190-210 GPa 29700-30458 ksiBulk modulus (typical for steel) 140 GPa 20300 ksiShear modulus (typical for steel) 80 GPa 11600 ksiPoissons ratio 0.27-0.30 0.27-0.30Elongation at break (in 50 mm) 30% 30%
AISI 1035 Carbon Steel (UNS G10350)
Saved from URL: http://www.azom.com/article.aspx?ArticleID=6540 P
/21
-
Reduction of area 53% 53%Hardness, Brinell 183 183Hardness, Knoop (converted from Brinell hardness) 204 204Hardness, Rockwell B (converted from Brinell hardness) 89 89Hardness, Vickers (converted from Brinell hardness) 192 192Machinability (based on AISI 1212 steel. as 100 machinability) 65 65
Thermal PropertiesThe thermal properties of AISI 1035 carbon steel are given in the following table.
Thermal Properties Metric ImperialThermal expansion co-efficient (@20C/68F) 11 m/mC 6.11 in/inFThermal conductivity 51.9 W/mK 360 BTU in/hr.ft2.F
Other DesignationsOther designations that are equivalent to AISI 1035 carbon steel include the following:
AMS 5080 ASTM A544 (1035) MIL S-19434 AFNOR CC 35 B.S. 080 A 37AMS 5082 ASTM A545 (1035) MIL S-3289 DIN 1.0501 B.S. 080 M 36ASTM A29 (1035) ASTM A546 (1035) MIL S-46070 UNI C 35 AMS 5080DASTM A510 (1035) ASTM A576 (1035) QQ S700 (C1035) SS 1550 AMS 5082AASTM A512 (1035) ASTM A682 (1035) SAE J1397 (1035) B.S. 060 A 35 ASTM A108ASTM A513 (1035) ASTM A827 SAE J403 (1035) B.S. 080 A 32 QQ S635ASTM A519 (1035) ASTM A830 SAE J412 (1035) B.S. 080 A 35
ApplicationsThe following are the major applications of AISI 1035 carbon steel:
Levers Bolts Nuts Studs
Date Added: Aug 23, 2012 | Updated: Sep 21, 2012