WI>f9{H'UBt1CATI0tH)R-fQR ftrfCRQijCg-
NATIONAL BUREAU OF STANDARDS REPORT
10 655
SPECIFICATIONS FOR RESINOUS FLOORING -
REQUIREMENTS AND TEST METHODS
U.S. DEPARTMENT OF COMMERCE
NATIONAL BUREAU OF STANDARDS
-
NATIONAL BUREAU OF STANDARDS
The National Bureau of Standards ' was established by an act of Congress March 3, 1901. Today,
in addition to serving as the Nation’s central measurement laboratory, the Bureau is a principal
focal point in the Federal Government for assuring maximum application of the physical andengineering sciences to the advancement of technology in industry and commerce. To this endthe Bureau conducts research and provides central national services in four broad program
areas. These are; (1) basic measurements and standards, (2) materials measurements and
standards, (3) technological measurements and standards, and (4) transfer of technology.
The Bureau comprises the Institute for Basic Standards, the Institute for Materials Research, the
Institute for Applied Technology, the Center for Radiation Research, the Center for Computer
Sciences and Technology, and the Office for Information Programs.
THE INSTITUTE FOR BASIC STANDARDS provides the central basis within the UnitedStates of a complete and consistent system of physical measurement; coordinates that system with
measurement systems of other nations; and furnishes essential services leading to accurate and
uniform physical measurements throughout the Nation’s scientific community, industry, and com-
merce. The Institute consists of an Office of Measurement Services and the following technical
divisions:
Applied Mathematics—Electricity—Metrology—Mechanics—Heat—Atomic and Molec-ular Physics—Radio Physics -—Radio Engineering -—Time and Frequency -
—
Astro-
physics -—Cryogenics.-THE INSTITUTE FOR MATERIALS RESEARCH conducts materials research leading to im-proved methods of measurement standards, and data on the properties of well-characterized
materials needed by industry, commerce, educational institutions, and Government; develops,
produces, and distributes standard reference materials; relates the physical and chemical prop-
erties of materials to their behavior and their interaction with their environments; and provides
advisory and research services to other Government agencies. The Institute consists of an Office
of Standard Reference Materials and the following divisions:
Analytical Chemistry—Polymers—Metallurgy—Inorganic Materials—Physical Chemistry.THE INSTITUTE FOR APPLIED TECHNOLOGY provides technical services to promotethe use of available technology and to facilitate technological innovation in industry and Gov-
ernment; cooperates with public and private organizations in the development of technological
standards, and test methodologies; and provides advisory and research services for Federal, state,
and local government agencies. The Institute consists of the following technical divisions and
offices:
Engineering Standards—Weights and Measures— Invention and Innovation — VehicleSystems Research—Product Evaluation—Building Research—Instrument Shops—Meas-urement Engineering—Electronic Technology—Technical Analysis.
THE CENTER FOR RADIATION RESEARCH engages in research, measurement, and ap-plication of radiation to the solution of Bureau mission problems and the problems of other agen-
cies and institutions. The Center consists of the following divisions:
Reactor Radiation—Linac Radiation—Nuclear Radiation—Applied Radiation.THE CENTER FOR COMPUTER SCIENCES AND TECHNOLOGY conducts research andprovides technical services designed to aid Government agencies in the selection, acquisition,
and effective use of automatic data processing equipment; and serves as the principal focus
for the development of Federal standards for automatic data processing equipment, techniques,
and computer languages. The Center consists of the following offices and divisions:
Information Processing Standards—Computer Information— Computer Services— Sys-tems Development—Information Processing Technology.
THE OFFICE FOR INFORMATION PROGRAMS promotes optimum dissemination andaccessibility of scientific information generated within NBS and other agencies of the Federalgovernment; promotes the development of the National Standard Reference Data System and a
system of information analysis centers dealing with the broader aspects of the National Measure-
ment System, and provides appropriate services to ensure that the NBS staff has optimum ac-cessibility to the scientific information of the world. The Office consists of the following
organizational units;
Office of Standard Reference Data—Clearinghouse for Federal Scientific and TechnicalInformation ‘—Office of Technical Information and Publications—Library—Office ofPublic Information—Office of International Relations.
’ Headquarters and Laboratories at Gaithersburg. Maryland, unless otherwise noted: mailing address Washington, D.C. 20234.- Located at Boulder, Colorado 80302.
“ Located at 5285 Port Royal Road, Springfield, Virginia 22151.
-
NATIONAL BUREAU OF STANDARDS REPORT
NBS PROJECT4216448 December 7, 1971
NBS REPORT
10 655
SPECIFICATIONS FOR RESINOUS FLOORING -
REQUIREMENTS AND TEST METHODS
by
Winthrop C. Wolfe
Materials Durability and Analysis Section
Building Research Division
National Bureau of Standards
Washington, D.C. 20234
Sponsored by
Office of the Chief of Engineers, U. S. Army
Directorate of Civil Engineering, U. S. Air Force
Naval Facilities Engineering Command, U. S. Navy
NATIONAL BUREAU OF STANfor use within the Government. Bel
and review. For this reason, the pi
whole or in part, is not authorizec
Bureau of Standards, Washington, !
the Report has been specifically prt
IMPORTANT NOTICE
Approved for public release by thedirector of the National Institute ofStandards and Technology (NIST)
on October 9, 2015
jccounting documents intended
)jected to additional evaluation
ting of this Report, either in
iffice of the Director, National
he Government agency for which
es for its own use.
U.S. DEPARTMENT OF COMMERCE
NATIONAL BUREAU OF STANDARDS
-
» :,v' Ill' ^im
^ '.biViiki' . v.'-';^
. ^tlut-0 qQnl’rii'^,
nnit3i)2 ai'^^lsriA bofi vtiHdBtuO
norBtviQ ri?'!£^295^ gmblioS‘ EbrBb/t6r2 lo ue^'iijB
ftesOt '.b.Q1 f.
;' ' ' -'.
* ‘
!';.
.„•..
•'> V
'.'
'
'..
«'f
•
,
'
'I
yd b&ioanoqE j
jj^ol uk,Z A\ ,^nnp$n*j^n3 ilviOlO blB)Ol:>9i!Q•
fZ .y ,'b;fl6if;{r»qPlEVcii :**>
.F" ' ;*ATVV2DIT&W r^AT»0
-
TABLE OF CONTENTSPage
INTRODUCTION 1
1.0 Corps of Engineers Guide Specifications forResinous Floors. First Drafts 1
1.1 Comments on Corps of Engineers Draft Guide Specifications. 2
1.2 Review of Guide Specification by ASTM 3
1.3 Guide Specifications issued by the Corps of Engineers .... 4
1.3.1 OCE Guide Specification GE 244.02,RESINOUS TERRAZZO FLOORING 4
1.3.2 OCE Guide Specification 244.03,INDUSTRIAL RESINOUS FLOORING 5
1.3.3 OCE Guide Specification CE 244.04,CONDUCTIVE RESINOUS TERRAZZO FLOORING 6
1.3.4 OCE Guide Specification CE 244.05,CONDUCTIVE SPARKPROOF INDUSTRIAL RESINOUS FLOORING 6
2.0 National Terrazzo and Mosaic Association (NTMA)Specifications 7
2.1 NTMA Specification for Conductive Epoxy Resin Terrazzo.... 8
2.1.1 NTMA 1.10 PERFORMANCE AND PROPERTIES OF CONDUCTIVEEPOXY MATRIX 8
2.1.2 NTMA 1.11 PERFORMANCE AND PROPERTIES OF CONDUCTIVEEPOXY TERRAZZO 9
2.2 NTMA Specification for Conductive Polyester Resin Terrazzo 9
2.2.1 NTMA 1.10 PERFORMANCE AND PROPERTIES 9
2.3 NTMA Specification for Epoxy Resin Terrazzo 11
2.3.1 NTMA 1.10 PERFORMANCE AND PROPERTIES OF EPOXY MATRIX 11
2.3.2 NTMA 1.11 PERFORMANCE AND PROPERTIES OF EPOXYRESIN TERRAZZO 11
2.4 NTMA Specification for Polyester Resin Terrazzo 11
2.5 NTMA Specification for Latex Matrix Terrazzo 11
2.5.1 NTMA 1.10 PERFORMANCE AND PROPERTIES 11
3.0 Tentative Specification for Resinous ChemicalResistant Monolithic Surfacings of ASTM Committee C-3 16
-
TABLE OF CONTENTS - continued
Page
4.0 Measurement by Building Research Division ofPhysical Properties of Resin Mixes 28
4.1 Compressive strength 29
4.2 Shrinkage on curing and coefficient of thermal expansion.. 31
4.3 Flexural strength and Flexural modulus of elasticity 34
4.4 Tensile strength 36
4.5 Comparison of BRD values with values of physicalproperties in ASTM specification 36
5.0 Conclusions and recommendations 41
ii
-
SPECIFICATIONS FOR RESINOUS FLOORING - REQUIREMENTS AND TEST METHODS
INTRODUCTION
At the request of the U. S. Army, Office of the Chief of
Engineers (OCE),The Building Research Division (BRD) reviewed the
Guide Specifications for Military Construction dealing with resinousflooring, described in Part 1 of the report. Since the BuildingResearch Division had not investigated the properties of the resinoussystems covered by these specifications, BRD requested a review by atechnical committee of the American Society for Testing and Materials(ASTM) . This is Committee C-3 on CHEMICAL-RES 1STANT NONMETALLICMATERIALS and includes Subcommittee S-4 on Monolithic Surfacings. Sub-committee S-4 has prepared TENTATIVE SPECIFICATION FOR RESINOUSCHEMICAL RESISTANT MONOLITHIC SURFACINGS, in the process of letterballot for adoption as a Tentative Standard by the Committee. ThisTentative Specification is described in Part 3 of this report. The OCEGuide Specifications are based on specifications by The NationalTerrazzo and Mosaic Association, Inc. (NTMA) , described in Part 2 of thisreport. These NTMA specifications are based in turn on ASTM Standards,Federal Test Method Standard No. 406, military specifications, andprivate sources. The NTMA specifications for polyester terrazzo arebased largely on Military Specification MIL-F-52505, while the LatexTerrazzo specification is derived from MIL-D-3134F.
The review of the OCE Guide Specifications by the ASTM C-3Committee, Section 1.2 of this report, cited differences between valuesfor physical properties in the Guide Specifications and those in theirown Tentative Specification. In an attempt to resolve this conflict,BRD measured some of the important physical properties of two mixes ofstandard Ottawa sand and two flooring resins. One of these resins isan epoxy resin or prepolymer and a curing agent, a combination recom-mended by the manufacturer for monolithic surfacings. The manufactureris one of the most important in petrochemicals and in epoxy resinsand curing agents in particular. The other resin is a polyester resinwith peroxide catalyst, also recommended by the manufacturer formonolithic surfacings.
1.0 Corps of Engineers Guide Specifications forResinous Flooring. First Drafts
Drafts of four such specifications were sent to BRD 22 July 1970with a letter explaining that these are used as a basis for preparingcontract specifications for military construction projects. Comments onthese specifications were submitted in a letter to Mr. Nyal Nelson, OCT,
12 August 1970. After the specifications had been reviewed by ASTMCommittee C-3, their comments were transmitted in a letter to Mr. William
Darnell 23 September 1970. The four OCE Guide Specificatons were approved
April 1971 with minor changes but with the same references for physical
properties
.
1
-
1 . 1 Comments on Corps of Engineers Draft Guide Specificatioas
Comments submitted by BRD were as follows:
(1) The needs of the Services would be best served by a perform-ance type specification for resinous floors, if such is practicable atthe present time. An effort in this direction is the enclosed DraftNo. 4, TENTATIVE SPECIFICATIONS FOR RESINOUS CHEMICAL RESISTANT MONOLITHICSURFACINGSj prepared by ASTM Committee C-3, Subcommittee S-4, hereafterreferred to as ASTM Specification.
(2) The four Corps of Engineers Specifications are redundant andshould be combined into one specification. The four types of resinousflooring could then be specified as Types I, II, III and IV.
(3) The Corps of Engineers Specifications are based on the NTMAspecifications, which give architectural and engineering detailslacking in the ASTM specification. Also, explanations are given in theNTMA specifications for procedures and tests.
(4) In both the NTMA and ASTM specifications, different tests areused and different values required for different resin systems. In aperformance specification, tests would be selected which correspond toperformance requirements and acceptable values would be those requiredin service. For example:
(a) In the NTMA SPECIFICATION FOR EPOXY RESIN TERRAZZO, section1.10 prescribes PERFORMANCE AND PROPERTIES OF EPOXY MATRIX(with no marble chips or fillers added) . In the NTMASPECIFICATION FOR POLYESTER RESIN TERRAZZO there are no suchrequirements for polyester matrix.
(b) In the NTMA SPECIFICATION FOR POLYESTER RESIN TERRAZZO, section1.10 PERFORMANCE AND PROPERTIES prescribes curing time,shrinkage resistance, chemical resistance, fumigant resistance,abrasion resistance, hardness, porosity, accelerated weatheringresistance, fungistatic and bacteriostatic resistance, ultra-violet light resistance, thermal shock resistance, and stainresistance, which are lacking in NTMA SPECIFICATION FOR EPOXYRESIN TERRAZZO, section 1.11, PERFORMANCE AND PROPERTIES OFEPOXY RESIN TERRAZZO, although some of these factors are foundin section 1.10 PERFORMANCE AND PROPERTIES OF EPOXY MATRIX.On the other hand, a bond strength test is prescribed for epoxyresin terrazzo but not for polyester resin terrazzo. The impactresistance of epoxy resin terrazzo must be 16 foot pounds whentested by a two pound falling ball, while the polyesterterrazzo is required to pass a Gardner impact test of 144 inchpounds. Why should one resin terrazzo be required to pass amore stringent or a different test than another?
2
-
(c) In the ASTM specification, compressive strength requirementsvary from 4,000 to 10,000 psi depending on the type of resin,while flexural strength requirements vary from 750 to 1,500psi
.
1
.2
Review of Guide Specification by ASTM
ASTM Committee C-3 would comment on only one of the four OCE GuideSpecifications, INDUSTRIAL RESINOUS FLOORING. The others,
DECORATIVE RESINOUS FLOORINGCONDUCTIVE RESINOUS TERRAZZO FLOORINGCONDUCTIVE SPARKPROOF INDUSTRIAL RESINOUS FLOORING
were considered to be outside the scope of the Committee, limited tochemical resistant monolithic surfacings more than 1/16- inch or 60 milsthick. Comments of the Committee on GUIDE SPECIFICATION FOR INDUSTRIALRESINOUS FIDORING were as follows, referring to numbered paragraphs orsections of the July 1970 draft:
1.1 The Subcommittee does not agree with the values for thephysical properties in the NTMA Specification Details. Values recom-mended by the Subcommittee are found in Table 1 of the enclosed DraftNo. 4, TENTATIVE SPECIFICATIONS FOR RESINOUS CHEMICAL RESISTANTMONOLITHIC SURFACINGS, March 10, 1970.
n, d 2. GENERAL. The question was raised as to temperature ofstorage but members agreed that epoxy resins, at least, are designed tobe stored at temperatures as low as 50°F. However, the temperatureshould be at least 65 °F. for installation.
2.1, 2.2, and n, d 3.5. Divider strips are not needed for in-dustrial resinous flooring and if exposed to corrosive chemicals, maybe detrimental.
3.1 Primer is not always required with epoxy flooring. Theprimer, if required, is not necessarily dry or cured before the resinsurfacing is applied.
3.2 The term "thermosetting" is unnecessary since epoxy resinsare all thermosetting. The degree of thixotropy of polyester resinsis important and epoxy resins should have a degree of thixotropy.
3.3 The terms "catalyst" and "curing agent" are better than"catalyzer". Actually, peroxides used with polyester resins areinitiators rather than catalysts, since they are not recoverable.Curing agents or hardeners used with epoxy resins are reactants, notcatalysts, and are added in stoichometric amounts. However, "catalyst"and "curing agent" are terms used by the industry.
3
-
3.4 Cellulosic materials are not commonly used as fillers inresinous flooring compositions. The size 3/16-inch for filler seemsfairly coarse. The maximum diameter of the aggregate must not be morethan half the thickness of the surfacing, which is specified in 6.2 asfrom 3/16 to 5/16 inch.
3.6 and 3.7 Sealer is not needed in industrial resinous flooringand if sealer is used the flooring will not be non-slipping or non-yellowing .
5 A curing period of 28 days is adequate but ASTM recommends ashorter period.
6.3 It is necessary to add a thickener to the mix for coving.
NOTES, No. 5. Both epoxy and polyester sur facings should besuitable in areas where there are sources of heat. Sources of heatshould be better defined, as the temperature, temperature differential,or cycling.
1 . 3 Guide Specifications Issued by the Corps of Engineers
The Corps of Engineers did not issue a Guide Specification onDECORATIVE RESINOUS FLOORING but issued an additional GuideSpecification on RESINOUS TERRAZZO FLOORING. The four GuideSpecifications issued April 1971 are:
CE 244.02, RESINOUS TERRAZZO FLOORING
CE 244.03, INDUSTRIAL RESINOUS FLOORING
CE -244.04, CONDUCTIVE RESINOUS TERRAZZO FLOORING
CE 244.05, CONDUCTIVE SPARKPROOF INDUSTRIAL RESINOUS FLOORING
Only those portions of the Guide Specifications relating torequirements and test methods will be discussed in this report.
1.3.1 OCE Guide Specification CE 244.02. RESINOUS TERRAZZO FLOORING
Reference to requirements and test methods: NTMA Specifications
Epoxy Resin Terrazzo (Section 2.3 of this report)
Polyester Resin Terrazzo (Section 2.4 of this report)
In 5.1 of CE 244.02: Epoxy flooring system : The epoxy matrixwith no chips or fillers shall conform to PERFORMANCE AND PROPERTIES OFEPOXY MATRIX of Specification for Epoxy Resin Terrazzo except that therequirements of weight loss and dimensional change on the specimenssubjected to the chemical resistance tests shall not apply. The epoxymatrix with aggregate and/or -filler shall conform to PERFORMANCE ANDPROPERTIES OF EPOXY RESIN TERRAZZO of Specification for Epoxy ResinTerrazzo.
4
-
In 5.2 of CE 244*02: Polyester flooring system shall conform toPERFORMANCE AND PROPERTIES of Specification for Polyester Resin Terrazzo .
In Section 2 of CE 244.02, storage of materials is specified atminimum temperature of 50°F. and installation temperature 60°F. Dividerstrips are specified, as this is not a specification for industrial orcorrosion resistant flooring. Primer is specified but it is not requiredto be dry before application of the topping. Catalyzer or hardener isspecified in place of catalyzer. Aggregate specified is a blend ofmarble chips consisting of a range of sizes up to and including anNTMA Standard No. 1 chip.
1.3.2 OCE Guide Specification CE 244.03 , INDUSTRIAL RESINOUS FLOORING
Review of CE 244:03: Sections 1.1 and 1.2 of this report
Reference to requirements and test methods: NTMA Specifications
Epoxy Resin Terrazzo (Section 2.3 of this report)
Polyester Resin Terrazzo (Section 2.4 of this report)
In 5.1 of CE 244.03: Epoxy flooring system . The epoxy matrixwith no chips or fillers shall conform to PERFORMANCE AND PROPERTIESOF EPOXY MATRIX of Specification for Epoxy Resin Terrazzo except thatthe requirements for weight loss and dimensional change on the specimenssubjected to the chemical resistance tests shall not apply. The epoxymatrix with filler shall conform to PERFORMANCE AND PROPERTIES OF EPOXYRESIN TERRAZZO of Specification for Epoxy Resin Terrazzo except testspecimens shall not be ground.
In 5.2 of CE 244.03: Polyester flooring system shall conform toPERFORMANCE AND PROPERTIES of Specification for Polyester ResinTerrazzo .
In Section 2 of CE 244.03, storage of materials is specified atminimum temperature of 50°F. and installation temperature 60°F. Metaldivider strips are specified but plastic strips are to be substitutedin acidic or alkaline conditions. Primer is specified but is not re-quired to be dry before application of the topping. Catalyzer orhardener is specified in place of catalyzer, as in the original draft.The filler particle size is specified as not greater than 3/16 inch asin the original draft. Sealer is also specified as in the originaldraft but the non-yellowing requirement was eliminated. Curing timefor the concrete is according to the manufacturer's recommendation.No provision for thickener appears in the requirement for cove base.
5
-
1.3.3 OCE Guide Specification CS 244.04 . CONDUCTIVE RESINOUSTERRAZZO FLOORING
Reference to requirements and test methods: NTMA Specifications
Conductive Epoxy Resin Terrazzo (Section 2.1 of this report)
Conductive Polyester Resin Terrazzo (Section 2.2 of this report)
Latex Matrix Terrazzo (Section 2.5 of this report)
In 5.1 of CE 244.04: Conductive epoxy flooring system . The epoxymatrix with no chips or fillers shall conform to PERFORMANCE ANDPROPERTIES OF CONDUCTIVE EPOXY MATRIX in NTMA Specification forConductive Epoxy Resin Terrazzo . The epoxy matrix with aggregateand/or filler shall conform to the requirements of PERFORMANCE ANDPROPERTIES OF CONDUCTIVE EPOXY TERRAZZO of Specifications for ConductiveEpoxy Resin Terrazzo .
In 5.2 of CE 244.04: Conductive polyester flooring system shallconform to PERFORMANCE AND PROPERTIES of Specification for ConductivePolyester Resin Terrazzo .
In 5.3 of CE 244.04: Conductive latex flooring system shall con-form to PERFORMANCE AND PROPERTIES of Specification for Latex MatrixTerrazzo and conductivity requirements of epoxy and polyester specifi-cations above.
In Section 2 of CE 244.04, storage of materials is specified atminimum temperature of 50°F. and installation temperature 60°F. It isspecified that plastic strips be installed "in locations indicated".Primer is specified but is not required to be dry before application ofthe topping, except for conductive latex flooring system, in which "theinterval between priming and application of topping shall be in strictaccordance with the manufacturer's recommendation". Aggregate specifiedis a blend of marble chips that consists of a range of sizes up to andincluding NTMA Standard No. 1 chip.
1.3.4 OCE Guide Specification CE 244.05 , CONDUCTIVE SPARKPROOFINDUSTRIAL RESINOUS FLOORING
Reference to requirements and tests methods: NTMA Specifications
Conductive Epoxy Resin Terrazzo (Section 2.1 of this report)
Conductive Polyester Resin Terrazzo (Section 2.2 of this report)
Latex Matrix Terrazzo (Section 2.5 of this report).
6
-
In 5.1 of CE 244.05: Epoxy flooring system . The epoxy matrixwith no chips or fillers shall conform to PERFORMANCE AND PROPERTIES OFCONDUCTIVE EPOXY MATRIX of Specification for Conductive Epoxy ResinTerrazzo except for the requirements for weight loss and dimensionalchange on the specimens subjected to the chemical resistance testsshall not apply. The epoxy matrix with aggregate and/or filler shallconform to PERFORMANCE AND PROPERTIES OF CONDUCTIVE EPOXY RESINTERRAZZO of Specification for Conductive Epoxy Resin Terrazzo .
In 5.2 of OCE 244.05: Polyester flooring system shall conform toPEEIFORMANCE AND PROPERTIES of Specification for Conductive PolyesterResin Terrazzo .
In 5.3 of OCE 244.05: Latex flooring systems shall conform toPERFORMANCE AND PROPERTIES of Specification for Latex Matrix Terrazzoand shall meet the conductivity requirements in the Specifications forConductive Epoxy Flooring Systems and Conductive Polyester FlooringSystems
.
2 . 0 National Terrazzo and Mosaic Association (NTMA) Specifications
The following specifications were referenced in the OCE GuideSpecifications, all from The National Terrazzo and Mosaic Association,Inc., 716 Church Street, Alexandria, Virginia 22314:
CONDUCTIVE EPOXY RESIN TERRAZZO
CONDUCTIVE POLYESTER RESIN TERRAZZO
EPOXY RESIN TERRAZZO
POLYESTER RESIN TERRAZZO
LATEX LATRIX TERRAZZO
Copies of these specifications may be obtained from the Associationbut for convenience, requirements and test methods are listed alphabet-ically under each specification. References have been corrected andupdated
.
7
-
2.1 NTMA Specification for Conductive Epoxy Resin Terrazzo
2.1.1 NTMA 1.10 PERFORMANCE AND PROPERTIES OF CONDUCTIVE EOPXY MATRIX(with no marble chips or fillers added)
Requirement
Abrasion or wear resistance (Abrasive resistance), 0.1 gram loss perASTM D968-51 (reapproved 1966), maximum
Chemical resistance,Federal Test Method
Standard No. 406, Method 7011, 7 daysimmersion
5 gals, silica sand
Reagents; Mineral oil, ASTM No. 3 oil, lard,isopropyl alcohol, ethyl alcohol, 10% hydro-chloric acid, 30% sulfuric acid, 5%, aceticacid. O'. 025%, detergent, 1%, soap solution,10%, sodium hydroxide, distilled water No effect
Compressive strength, ASTM D695-69Specimen b, cylinder, minimum, psi 14,000
Flexural strength, ASTM D790-66Flexural yield strength, minimum, psiTangent modulus of elasticity, minimum
6,500,1 X
Hardness, ASTM D1706-61 (Discontinued in 1968 butcan be found on page 564, Part 27, ASTMStandards, June 1967)Shore D DurometerBarcol Impressor
60-8555-80
Shrinkage, linear, ERF-64 (Epoxy ResinFormulators Test Method)
,maximum,
inch per inch 0.001
Tensile elongation, ASTM D638-68, C die as inASTM D4 12-68, 0.2 inch/min., minimum 5 percent
Tensile strength, ASTM D638-68, C die as inASTM D412-68, 0.2 inch/min .,minimum, psi 4,000
8
-
2.1.2 NTMA 1.11 PERFORMANCE AND PROPERTIES OF CONDUCTIVE EPOXY TERRAZZO(Epoxy resin mixed with marble chips)
Requirement
Bond strength, "Field Test for Surface Soundnessand Adhesion", Appendix, pages 1139-1141, TitleNo. 59-43, "Guide for Use of Epoxy Compoundswith Concrete", Journal of the American ConcreteInstitute, Proceedings, vol. No. 9(September 1962)
,
Minimum tensile strength with 1007o concretefailure, psi 300
Conductivity, Section 252, NFPA 56A, Standard forthe Use of Flammable Anesthetics, 1971, NationalFire Protection Association, with recentlycalibrated ohmmeter
Less than 1,000,000and more than25,000 ohms
Flammability, ASTM D635-68Extent of burning, maximum
Self extinguishingQ . 25 inch
Heat resistance (to elevated temperature),MIL-D-3134F, sections 3.10, 4.7.5
Will not slip or flowNo softening
Impact strength, two pound ball falling on a12 X 12 X 1/4 inch specimen bonded to concreteand ground to terrazzo finish, 16 ft. lbs.
No chipping ordetachmentNo indentation
Indentation, MIL-D-3134F, sections 3.9, 4.7.4,4 X 6 X 1/4 inch specimen ground toterrazzo finish No indentation
Thermal coefficient of linear expansion, ASTMD-696-70, temperature range 12 - 140°F.maximum inch per inch per degree Fahrenheit 25 X 10'^
2.2 NTMA Specification for Conductive Polyester Resin Terrazzo
2.2.1 NTMA 1.10 PERFORMANCE AND PROPERTIES
Abrasion resistance, MIL-F-52505 (MO), sections3.7, 4. 4. 2. 6, 1,000 cycles on abraser machine,loss of thickness, maximum 1 mil
Accelerated weathering resistance, MIL-F-52505 (MO),sections 3.11, 4.4.2.10, 300 hours acceleratedweathering
No cracking, peeling,blistering, or lossof adhesion. Slightchalking or fadingof color permitted
9
-
Requirement
Chemical resistance, MIL-F-52505 (MO), sections3.5, 4. 4. 2.
4
Reagents: 47o hydrochloric acid, 47o sodiumhydroxide, 5% formaldehyde, 25,000 ppmchlorine (Hypochlorite solution), 1:500mercuric chloride solution
Conductivity, section 252, NFPA 56A, Standardfor the Use of Flammable Anesthetics, 1971,National Fire Protection Association, withrecently calibrated ohmmeter
Curing time, MIL-F-52505 (MO), sections 3.3,4. 4. 2. 2, at 73±5°F, 40±10 percentrelative humidity
Flammability, Federal Test Method StandardNo. 406, Method 2021
Fumigant resistance, MIL-F-52505 (MO), sections3.6, 4. 4. 2. 5, cyclic exposure toformaldehyde or beta- propio lactone
Fungistatic and bacteriostatic resistance,MIL-F-52505 (MO), sections 3.12, 4.4.2.11
Hardness, MIL-F-52505 (MO), sections 3.8,4. 4. 2. 7, Hardness as defined, minimum
Impact resistance, MIL-F-52505 (MO), sections3.10, 4. 4. 2. 9, Impact test machine, 144inch- pounds force
Porosity, MIL-F-52505 (MO), sections 3.9,4. 4. 2. 8, submersion in distilled waterfor 24 hoursGain in weight
,maximum
Shrinkage resistance, MIL-F-52505 (MO), sections3.4, 4. 4. 2.1, 4. 4. 2. 3, dried terrazzoMaximum shrinkage
Stain resistance, MIL-F-52505 (MO), sections3.15, 4.4.2.14, exposed for 24 hours tostaining agent
No change in color;no blistering,cracking, peeling,loss of adhesion
Less than 1,000,000and no more than25,000 ohms
within 18 hours
Rating of ’’selfextinguishing"
No deterioration,as blistering,cracking, peeling,loss of adhesion
Shall not supportgrowth of fungusor bacteria
M85
No cracking,spalling, loss ofadhesion
No cracking, peeling,blistering, loss ofadhesion8 percent
No cracking, spalling,ridging1/32 inch in 12 inches
Shall not retain apermanent stain
10
-
Requirement
Thermal shock resistance, MIL-F-52505 (MO), sections
3.14j 4.4.2.13, 50 cycles immersion in chilledand boiling water at 2-minute intervals
Ultraviolet light resistance, MIL-F-525Q5 (MO),sections 3.13, 4. 4. ^.12, 48 hours exposureto 30 microwatts ultraviolet light
2.3 NTMA Specification for Epoxy Resin Terrazzo
2.3.1 NTMA 1.10 PERFORMANCE AND PROPERTIES OF EPOXYMATRIX (with no marble chips or fillers added)
Same as 2.1.1 under NTMA Specification forConductive Epoxy Resin Terrazzo with thedeletion of Conductivity and addition ofFading resistance, ASTM E188-70, Method A,48 hours exposure
2.3.2 NTMA 1.11 PERFORMANCE AND PROPERTIES OF EPOXYRESIN TERRAZZO (Epoxy resin mixedwith marble chips)
Same as 2.1.2 under NTMA Specification forConductive Epoxy Resin Terrazzo exceptConductivity requirement is deleted.
2.4 NTMA Specification for Polyester Resin Terrazzo
Same requirements as 2.2.1 under NTMA Specificationfor Conductive Polyester Resin Terrazzo exceptConductivity requirement is deleted
t
2.5 NTMA Specification for Latex Matrix Terrazzo
2.5.1 NTMA 1.10 PERFORMANCE AND PROPERTIES
Abrasion or wear resistance, MIL-D-3134F,sections 3.15, 4.7.10, Maximum wear
Shall not crack,peel, blister,spall, or lose
adhesion
No chalking,cracking, peeling,blistering, orloss of adhesion
No discolorationor other physicalqhanges
0 . 150 inch
11
-
Requirement
Accelerated light and weather agingresistance, MIL-D-3134F, sections
3.21, 4.7.16
Color, MIL-D-3134F, sections 3.5, 6.2
Corrosion resistance, MIL-D-3134F,sections 3.14, 4.7.9
Impact shock resistance, MIL-D-3134F,sections 3.18, 4.7.13
Odor, MIL-D-3134F, section 3.4, underordinary service conditions
Surface shall showno appreciablechange in color,signs of checking,cracking, or otherdeterioration
65 psi
957o of initialstrength
As specified
Shall not softenor become detachedfrom substrate
Fire retardant
Shall not constitutean undue fire hazard
.
Fumes shall not be moretoxic than those fromordinary paint.
Shall not flow or slip
in any part morethan 1/16 inch, orsoften
No visible signsof chipping, crack-ing, or detachment
No signs of chipping,cracking, or de-tachment
No signs of crack-ing or detachmentLess than 7 percentMore than 1 percent
Free from object-ionable odors
Adhesive strength, MIL-D-3134F, sections3.19, 4.7.14, Initial adhesive strength,minimum. After aging and exposure, minimum
Fire resistance, MIL-D-3134F, sections 3.164.7.11, Rating of, minimum
Fire and toxicity hazards, MIL-D-3134F,section 3.6, before and after setting
Heat resistance (to elevated temperature),MIL-D-3134F, sections 3.10, 4.7.5
Impact resistance, MIL-D-3134F, sections3.8, 4.7.3
Indentation, MIL-D-3134F, sections 3.9, 4.7.4
Initial indentation
12
-
Requirement
Oil resistance, MIL-D-3134F, sections 3.17, 4.7.12Maximum weight changeMaximum volume change
Resistance to moisture and temperaturechanges, MIL-D-3134F, sections3.12, 4.7.7
Slip resistance (non-slip properties),MIL-D-3134F, section 3.11, factorsof friction
Water (moisture) absorption, MIL-D-3134F,sections 3.13, 4.7.8, maximum based onweight under normal atmospheric conditions
Water resistance (Serviceability),MIL-D-3134F, sections 3.22, 4,7.17
Weight, MIL-D-3134F, sections 3.7, 4.7.2,in thickness of 1/4 inch, maximum
3 percent
2 percent
No signs of crack-ing, separation,or corrosion
Not less thanthose specifiedin Table 1
5 percent
No breaks, lossof adhesion, orother deficiencywhich would affectserviceability
3.0 pounds persq. ft.
13
-
Table
1.
Requirements
and
Tests
in
The
National
Terrazzo
and
Mosaic
Association
(NTMA)
Specifications
XX -HQ) ^•U 4-J
ctJ nj
injoNJ
Ncd
(U
H
H H H H H H H H H
0)
4JCO
cu
CO
t—I (UO pcj
NNcd
cu
H
H H H H H
d N!>< •p-i NO CO Cdd (U J-lw Qc:
cu
H
cu
>•r-l cu
4J 4-1 d NCJ CO •H N3 CU CO CdX cud rH do o cuo d H
d'--,cu •H r-4> CO
•r4 CU N4J NO Cd3X Xd o cuo d Hu w
S H
H H
S H
d cd4J 60 cd cd cd 44 cu cu cuCO d 60^ o s t-4 CO 1-4 54 a cu•p4 cu dvoi •r4 E cu o (U 44 d 54CO •H -d 54 cu cd' •i4 CO cd(U 4-1 f~l cu 4.) 4-» o f—l vO| 144 cu 54 o 44 44 vO
CO cu o 60 o d M4 o o cu 44 rv CO COrd d d cu cd cu -d d 44 cu •i4 •r-l 54
^4 X 4-> cd (U r—
4
4J o r\ 4-» CO cd o o CO o cd cucd d cd 4-1 5-1 cu CO d cu 60 3 44 cd cu d cu E cu cu cucu o cu CO 4J cd o d r-4 CO -D o cd 54 cu d o d:s PQ 15 •H CO •N C0\X)| 4-1 d •r4 B CO CO CO B 54 •i4 CO CO o o 44 cu r\ CO •p4
4J •H > d •p4 cu •r4 44 •r-l cu jd •r-l CO o cu •r4 COd d cd r—
1
CO •r4 o 4-> 54 CO 1-4 1-4 44 cd CO CO 54 CO 44 •r4 d 60 CO cuo o 5-1 cd CO 4-1 •r4 cu cd cd d 44 CO (U cd CO 44 cd cd cu (X•p4 •p4 (U o cu o CO 60 60 54 54 54 cd CO (U 54 44 44 44 cu •f4 44 -X 54CO CO •r4 5-4 5^ 3 o d d 3 3 •r4 d o o d 54 CO CO d dcd
-
Table
1-
continued
X(U
%N
X N•H CO
Pu uCO }-4 CNJcu
4J 4-1 d No CO •rH Nd CU CO COT3 CU Ud rH Pi Po o CUo P4 H
dcu •H> CO 1-1•H CU4-» pcj No Nd CO•d Xd o Uo a CUo w
H H
X S H X
CO
vO| T3
C3 dO N•r^ CO
CO x:d CUcO E>» o da. 4-i d oX •rJ cO •rHcu CU o 4-4 4J
o CO Cbu-l d X •rH uO cO o CO o
4J 4J CU CO4J CO u JQ
d vD| d •rH cOo CU CO d 4-1•H •pH CU cO r-S cu4J O $-1 PO CU ocO bO •rH cu •rH u dPO d M-l }-i fH d COd cu —
1
r—
1
4-> •rH Ut~4 {rt (rt •rH > 4J•H •H B B o CO u U SiCO CO tl l) •"! U cu CU POd 0) CU X 4-1 JU 4-4 •rH(U 0) ji x: o cO cO CUH H H H H X IS S
15
-
NOTES to Table 1
1. M refers to requirements under PERFORMANCE AND PROPERTIES OFCONDUCTIVE EPOXY MATRIX, section 2.1.1 of this report.
T refers to requirements under PERFORMANCE AND PROPERTIES OFCONDUCTIVE EPOXY TERRAZZO, section 2.1.2 of this report.
2. T refers to requirements under PERFORMANCE AND PROPERTIES,section 2.2.1 of this report.
3. M refers to requirements under PERFORMANCE AND PROPERTIES OF EPOXYMATRIX, section 2.3.1 of this report. These are the same asthose in Section 2.1.1 except for deletion of Conductivity andaddition of Fading resistance. See Note 1.
T refers to requirements under PERFORMANCE AND PROPERTIES OFEPOXY RESIN TERRAZZO, section 2.3.2 of this report. These arethe same as those in section 2.1.2 except that Conductivity isdeleted. See Note 1.
4. T refers to requirements in NTMA Specification for PolyesterResin Terrazzo, section 2.4 of this report. These are the sameas those in section 2.2.1 except that Conductivity is deleted.See Note 2.
5. T refers to requirements under PERFORMANCE AND PROPERTIES,section 2.5.1 of this report.
6. Requirements included in ASTM C-3 Specification, part 3.0 andTables 2 and 3 of this report.
7. Under Chemical resistance.
8. Under Serviceability.
3 . 0 Tentative Specification for Resinous Chemical ResistantMonolithic Surfacings of ASTM Committee C-3
The following is Draft No. 4 of the Tentative Specification, dated 31March 1970, drafted by Subcommittee S-4 on Monolithic Sur facings ofASTM Committee C-3 on Chemical Resistant Non-Metallic Materials.
WORKING DOCUMENT FOR ASTM COMMITTEE USE ONLY. NOT FOR PUBLICATIONEXCEPT AS EXPRESSLY APPROVED BY THE CHAIRMAN OF THE COMMITTEE OR BYTHE EXECUTIVE SECRETARY OF THE SOCIETY.
Reprinted by permission of the Chairman of ASTM Committee C-3.
16
-
SCOPE:1.
A - This specification covers the requirements for resin filledsystems suitable for use as trowel or spray applied mono-lithic surfacings in areas where chemical resistance isrequired
.
Two types are covered -
Type A - Surfacings where chemical resistance and moderateto heavy traffic are required. (Rigid systems)
Type B - Surfacings where mild chemical resistance andsevere thermal shock stability (or resistance) arerequired. (Flexible systems)
B - Monolithic surfacings utilized as vessel linings are excludedfrom this specification.
DEFINITION:
2. A - Resinous Chemical-Resistant Monolithic Surfacings:
As intimate mixture of a liquid resin-based material, hard-ening agent and filler system composed of properly selectedand graded materials. These components are mixed at tem-peratures of 65°F. to 85°F. to form a trowelable or, in somecases, a sprayable mixture that hardens after placement ofa minimum thickness of 60 mils, (approximately 1/16")
B - Monolithic
Monolithic as applied to surfacing in this usage refers toa continuous surfacing 60 mils in thickness or greaterwhich cures in place and is applied over an existing ornewly placed substrate and continuously bonded to the surface.
TYPES OF RESINS AND FILLERS:
3. A - The liquid resin base may be (1) epoxy resin, (2) polyesterresin, or (3) other resinous material capable of formingchemical resistant surfacing material when mixed with asuitable hardening agent and filler.
B - The fillers are usually of a siliceous or carbonaceousnature. The filler materials shall be selected to have ade-quate resistance to the particular chemicals to which theywill be exposed when properly combined with the resin system.
17
-
C - The hardening agent may be of the reactive or catalyst type.It is usually supplied separately to be added to the resinprior to use in accordance with the manufacturer's recom-mendation. However, in some cases it may be incorporatedin the powder in such a manner that it becomes effectivewhen mixed with the resin. The service limitations of thecured system shall be defined by the manufacturer.
PHYSICAL REQUIREMENTS:
4. Resin-based moholithic surfacings prepared from these materialsshall conform to the respective physical requirements prescribedin Table I.
GENERAL REQUIREMENTS
:
5. The resin shall have a viscosity that will permit it to be mixedwith the hardener and/or filler components by manual methods.The filler materials shall have properly graded particles thatwill permit application and finishing of the mixture to anacceptable surface at the minimum thickness prescribed by themanufacturer.
METHODS OF TESTING:
6. The properties enumerated in this specification shall be deter-mined in accordance with the following methods:
A - Working life and setting time - Methods of Test for Workingand Setting Times of Resinous Chemical-Resistant Mortars(ASTM Designation: C308)
B - Tensile Strength - Method of Test for Tensile Strength ofResinous Chemical-Resistant Mortars (ASTM Designation: C307)
C - Compressive Strength - Method of Test for Compressive Strengthof Resinous Chemical-Resistant Mortars (ASTM Designation:C579)
D - Flexural Strength and modulus of elasticity (ASTMDesignation: C580)
B - Shrinkage and coefficient of thermal expansion (ASTMDesignation: C531)
F - Absorption and apparent porosity - Tentative method of testfor absorption and apparent porosity of chemical-resistantmortars (ASTM Designation: C413)
G - Chemical Resistance (ASTM Designation: C267)
18
-
PACKAGING AND MARKING;
7. A - The hardener and/or filler shall be properly packaged toprevent deterioration in storage and shall be marked insuch a manner to indicate clearly the resin with which they(it) are (is) to be used. The resin shall be packaged insuitable containers and market in such a manner that thehardener and/or filler materials with which it is to be usedand the storage conditions required to prevent deteriorationof the resin are clearly stated.
B - In addition to the above information, packages may be markedat the discretion of the supplier and on his responsibilityindicating that the product satisfies this specification.
REJECTION:
8. The resins, hardeners and/or fillers, or all, may be rejectedif they or the surfacing mixture made therefrom fail to meetany of the requirements of this specification.
19
-
Table
2.
Physical
and
Chemical
Requirements
in
ASTM
Specification
TJ 00 r^ cr* o o X 1-H CO r".O o 1 1 1 1 o 00 00 CO CO tH X
s X
* 3 o X CO X no 54o 1 B o 00 p>- o o O X lO 1 o CM cu cuCU CO 1 ‘rl •H CM o o m X • o • 4-1 T3 CO pHa c X o LO o X CM CU CU o Cd
l-l •H CM X 4-i d d cx oHi £ O • o O o •H X •H
CU o is •H Cd cu Bcd a • CO 4J cu
X CO d 54 4-1 cu X2 rH 54 o•H CUB Cd do
o
W tH O 4-1 B 0) o< Cd X X X Cd •H X d Xi 5-4 o V CM X o
CU o 1 cu • 'd' 00 o o O X lO o O pH d to COa CO d bO CM -ct o o O X • I—
1
• CU CU cd pH X cdcu X o lO lO o X rH +J bO X dH O B X X • o o CO cd cu XO . X cv •H £ •H a.CO s d d X CU X
bO 3 •H £ CO X cuCO d £ £ •iH cd o o
•H •H d X pH XCO d CU X d •H cu Cd COcu o 54 X •H X £ s £X X d CU £ X MH £ X d cu COd CO X >> CO bO O d cu £ CJ cud " o X > r% d X £ X •H d d•H cu Cu bO cd X X cu X CO •H X X cd rHB B X •P^ cu X X X bO d X cd X d
•H cu tH X bO bO X d X cd « X d d CO cu d £ o pl^ •H
CU pH rv #> cu cu X X O COLH CU Cd o o X X cu X o X — CU • ••H CO o •H •H X X > CO £ d • d X ! 1X d •H MH LX CO CO •H cu cu C! o
B 4H IX CO X pH bO •H M •H rH CUbO X cu Cd Cd cu cu CO cd Cd cd O X cd Xd cd X 54 X o X cu X X X •H • a, o o•H *H u H H •pi •H X d d d MH d X •HX X > CO a X X •i-i MH H o £54 X X d £ cu cu X CU CO cuo d cu cu o X rH X O X X12 H CO H o pH Ph CO u c u
oo cdCM
O rH•H cu o
COc
cd
x:XI
ccd
X4-J
CU
CU CU
> XCO -TO
O X5-1 ;o
u oO XO CO
o CO4J 00
c
rX OCU
X 05XI Cd
5-1
no CUrHd cuo COXCO cu
uXI OM S
gcuX
cu Xd *x•H O
CM
CU
Xo
i
*1000
psi
for
carbon
filled
surfacings.
-
Table 3. Comparison of Requirements—^ Conunon to NTMAand the ASTM C-3 Specification
Chemical resistance
NTMA Specification for Conductive EpoxyResin Terrazzo 4/
NTMA Specification for Conductive PolyesterResin Terrazzo 5/
ASTM C-3 Specification
Compressive strength
NTMA Specification for Conductive EpoxyResin Terrazzo 4/
ASTM C-3 Specification
Epoxy, Type A, rigid systemsEpoxy, Type B, flexible systemsPolyester, Type APolyester, Type B
Curing Time
NTMA Specification for Conductive PolyesterResin Terrazzo 5/
ASTM C-3 Specification
Initial use time, hours, 73°F., minimum
Chemical exposureLight traffic
Epoxy, Type A or BPolyester, Type A or B
Heavy trafficEpoxy, Type A or BPolyester, Type A or B
Service strength setting time, days, maximumEpoxy, Type A or BPolyester, Type A or B
21
Specif icat ions~
Requirement
No effect
No change in colorno blistering,cracking, peeling,loss of adhesion
None given
14,000 psi
6.000 psi
4.000 psi10,000 psi
8.000 psi
within 18 hrs
.
at 73±5°F.,40±10% R.H.
72
24
16
4836
7
3
-
Table 3 - continued
Requirement
Flexural strength
NTMA Specification for Conductive EpoxyResin Terrazzo 4/ 6,500 psi
ASTM C-3 Specification, minimum, after 7 days
Epoxy, Type A 1,500 psiEpoxy
,Type B 750 psi
Polyester, Type A 1,500 psiPolyester, Type B 750 psi
Flexural modulus of elasticity
NTMA Specification for Conductive Epoxy Resin ATerrazzo 4/ 1 X 10
ASTM C-3 Specification, minimum, after 7 days
Epoxy 5 Type AEpoxy, Type BPolyester, Type APolyester, Type B
Shrinkage
NTMA Specification for Conductive EpoxyResin Terrazzo 4/
NTMA Specification for Conductive PolyesterResin Terrazzo 5/
0.5 X 10^
0.25 X 10^
1.0 X 10^
0.5 X 106
0.001 in. /in.
1/32 inch in
12 inches
ASTM C-3 Specification, percent maximum, after gelation
Epoxy, Type A or B 0.5Polyester, Type A 1.0Polyester, Type B 0.6
Tensile strength
NTMA Specification for Conductive Epoxy ResinTerrazzo ^4/ 4,000 psi
ASTM C-3 Specification, minimum, after 7 days
Epoxy, Type A 1,500 psiEpoxy, Type B 600 psiPolyester, Type A 1,500 psiPolyester, Type B 600 psi
22
-
Table 3 - continued
Thermal coefficient of linear expansion
NTMA Specification for Conductive EpoxyResin Terrazzo
ASTM C-3 Specification
Epoxy and Polyester, Types A and B, maximum
Requirement
25 X 10in. /in. /deg. F.
40 X 10"
in. /in. /deg.F.
Water absorption
7/NTMA Specification for Latex Matrix Terrazzo— 5 percent undernormal atmosphericconditions
ASTM C-3 Specification, percent maximum andapparent porosity
Epoxy, Type A 1.0Epoxy, Type B 2.0Polyester, Type A 1.0Polyester, Type B 2.0
NOTES to Table 3
1. For comparison of test methods, see Table 4.
2. See section 2.0 and Table 1 of this report.
3. See section 3.0 and Table 2 of this report. Requirements are forthe finished product with fillers.
4. For matrix with no marble chips or“ fillers, section 2.1.1 of thisreport. Also included in Epoxy Resin Terrazzo, section 2.3.1.See Table 1.
5. For terrazzo with marble chips and fillers, section 2.2.1 of thisreport. Also included in Polyester Resin Terrazzo , section 2.4.See Table 1.
6. For terrazzo with marble chips and fillers, section 2.1.2 of this re-port. Also included in Epoxy Resin Terrazzo, section 2.3.2. SeeTable 1.
7. For terrazzo with marble chips and fillers, section 2.5.1 of thisreport. See table 1.
-
1 / 2Table 4. Comparison of Test Methods— in NTMA Specificatioag~~
and the ASTM C-3 Specification _3/
Chemical resistance
4/NTMA Specification for Conductive Epoxy Resin Terrazzo—
Federal Test Method Standard No. 406, PLASTICS: METHODS OF TESTING,Method 7011, 7 days immersionReagents: Mineral oil, ASTM No. 3 oil, lard, isopropyl alcohol,ethyl alcohol, 10% hydrochloric acid, 307o sulfuric acid, 57o aceticacid, 0.0257o detergent, 1% soap solution, 107o sodium hydroxide,distilled water
NTMA Specification for Conductive Polyester Resin Terrazzo —
^
MIL-F-52505 (MO), FLOOR COATING, RESINOUS, MONOLITHIC,TROWEL TYPE (FOR WOOD AND CONCRETE FLOORS), Sections 3.5, 4. 4. 2.
4
Reagents: 4% hydrochloric acid, 4% sodium hydroxide, 57.formaldehyde, 25,000 ppm chlorine (hypochlorite solution),1:500 mercuric chloride solution
ASTM C-3 Specification
ASTM C267-65, Standard Method of Test for CHEMICAL RESISTANCE OFMORTARS. The test reagents shall consist of the reagents,solutions, or products to which the mortars are exposed inservice. No reagents are specified.
Compressive strength
ASTM D695-69, Standard Method of Test for COMPRESSIVE PROPERTIESOF RIGID PLASTICS, Specimen b, cylinder. (Size of specimen notspecified but should be)
ASTM C-3 Specification
ASTM C5 79-68, Standard Method of Test for COMPRESSIVE STRENGTHOF CHEMICAL-RESISTANT MORTARS
Curing Time
NTMA Specification for Conductive Polyester Resin Terrazzo —
^
MIL-F-52505 (MO), sections 3.3, 4. 4. 2. 2, at 73±5°F., 40±10%relative humidity. Shall cure within 18 hours.
ASTM C-3 Specification: No reference
24
-
Flexural strength and modulus of elasticity
4/NTMA Specification for Conductive Epoxy Resin Terrazzo—
ASTM D790-66, Standard Method of Test for FLEXURAL PROPERTIESOF PLASTICS (Detail specification should specify specimen size)
ASTM C-3 Specification
ASTM C580-68, Standard Method of Test for FLEXURAL STRENGTH ANDMODULUS OF ELASTICITY OF CHEMICAL-RESISTANT MORTARS
4/
Shrinkage
NTMA Specification for Conductive Epoxy Resin TerrazzO”
ERF-64 (Epoxy Resin Formulators Test Method)
5/NTMA Specification for Conductive Polyester Resin Terrazzo—
MIL-F-52505 (MO), sections 3.4, 4. 4. 2.1, 4. 4. 2. 3, dried terrazzo.Concrete panels are prepared as in Method 2051, procedure C,Federal Test Method Standard No. 141a, PAINT, VARNISH, LACQUER,AND RELATED MATERIALS : METHODS OF INSPECTION, SAMPLING, AND TESTING.The panels are cured and then cleaned, dried, primed, and a1/4- inch coating applied. After 48 hours drying the panels areexamined for shrinkage, which should not be more than 1/32 inchin length or width. (No measurement procedure is described.)
ASTM C-3 Specification
ASTM C531-68, Standard Method of Test for SHRINKAGE ANDCOEFFICIENT OF THERMAL EXPANSION OF CHEMICAL- R^ISISTANT MORTARS
Tensile strength
4/NTMA Specification for Conductive Epoxy Resin Terrazzo—
ASTM D-638, Standard Method of Test for TENSILE PROPERTIES OFPLASTICS, 0.2 inch/min., C- die as in ASTM D412-68, StandardMethod of TENSION TESTING OF VULCANIZED RUBBER .
ASTM C-3 Specification
ASTM C307-61, Standard Method of Test for TENSILE STRENGTH OFCHEMICAL-RESISTANT RESIN MORTARS (Will be discontinued in April1972 unless Committee C-3 reapprove? or revises it.)
25
-
Thermal coefficient of linear expansion
NTMA Specification for Conductive Epoxy Resin Terrazzo^^
ASTM D696-70, Standard Method of Test for COEFFICIENT OF LINEARTHERMAL EXPANSION OF PLASTICS, temperature range 12-140°F., inchper inch per degree Fahrenheit. ASTM D696 recommends the range-30 to 30°C. unless the properties of the plastic are well knpwn,as the possible change in coefficient at a certain temperature.
ASTM C-3 Specification
ASTM C531-68, Standard Method of Test for SHRINKAGE AND COEFFICIENTOF THERMAL EXPANSION OF CHEMICAL-RESISTANT MORTARS
Water absorption (Moisture absorption)
7/NTMA Specification for Latex Matrix Terrazzo—
MIL-D-3134F, DECK COVERING MATERIALS, 3.13, 4.7.8. Three specimens,2 inches square by 1/4 inch thick, shall be prepared by applyingthe deck covering to oiled surfaces of steel plate, so that ondrying the specimens will not adhere to the plates. Each specimenwithout the steel backing plate shall be weighed dry, dippedinto tap water at room temperature, lightly wiped on allsurfaces with a paper towel and again weighed to the nearest0.1 gram. Immediately after weighing, the specimens shall beimmersed in water (tap, at room temperature) for 24 hours,lightly wiped and again weighed. The percent gain in moistureshall be based on the weight of the dry specimen and the dif-ference between the weight after 24 hours immersion and theweight after dipping and wiping.
ASTM C-3 Specification
ASTM C413-66, Standard Method of Test for ABSORPTION OF CHEMICAL-RESISTANT MORTARS
26
-
NOTES to Table 4
1. For comparison of requirements, see Table 3.
2. See Section 2.0 and Table 1 of this report.
3. See Section 3.0 and Table 2 of this report. Requirements are forthe finished product with fillers.
4. For matrix with no marble chips or fillers, section 2.1.1 of thisreport. Also included in Epoxy Resin Terrazzo, section 2.3.1.See Table 1.
5. For terrazzo with marble chips and fillers, section 2.2.1 of thisreport. Also included in Polyester Resin Terrazzo, section 2.4.See Table 1.
6. For terrazzo with marble chips and fillers, section 2.1.2 of thisreport. Also included in Epoxy Resin Terrazzo, section 2.3.2.See Table 1.
7. For terrazzo with marble chips and fillers, section 2.5.1 ofthis report. See Table 1.
27
-
4
.0
Measurement by Building Research Division of Physical Propertiesof Resin Mixes ;
EPOXY RESIN MIX
750 grams epoxy resin
750 grams curing agent for same4,000
grams graded standard Ottawa sand
2 /
4,000
grams standard 20-30 Ottawa sand ~
POLYESTER RESIN MIX
1,500 grams polyester resin
25 ml catalyst for same
4,000
grams graded standard Ottawa sand
4,000
grams standard 20-30 Ottawa sand
1. Sect. 4, ASTM C109-64, Standard Method of Test for COMPRESSIVESTRENGTH OF HYDRAULIC CEMENT MORTARS (USING 2-IN. CUBE SPECIMENS)
2. Sect. 3, ASTM C190-70, Standard Method of Test for TENSILE STRENGTHOF HYDRAULIC CEMENT MORTARS.
28
-
4 . 1 Compressive strength
Compressive strength measurements were performed on the two resinmixes in 4.0 with the molds (par. 2(e)), preparation (par. 7), andtesting procedure (par. 12(c)) described in ASTM C109-64, StandardMethod of Test for COMPRESSIVE STRENGTH OF HYDRAULIC CEMENT MORTARS(USING 2-IN. CUBE SPECIMENS). The resin mixes were placed in the moldsas in ASTM C5 79-68, Standard Method of Test for COMPRESSIVE STRENGTHOF CHEMICAL-RESISTANT MORTARS. Tests were performed at the indicatedtime intervals and the values are recorded in Table 4 and Figure 1.
Table 4. Compressive Strength of Epoxy and Polyester Resin Mixes
Time, Days Compressive Strengthafter casting*
EPOXY RESIN MIX POLYESTER RESIN MIX
£Si MN/m^ £si MN/m^
1 2,194 15 , 128 5,438 37,495
2 2,881 19,864 7,500 51,713
6 3,313 22,843 8,800 60,676
30 3,877 26,732 9,225 63,606
*For time after gelation or initial set. subtract one day, as theresin.mixes set about one day after casting.
Two conclusions are obvious from examining Table 4 and Figure 1.One is that the polyester resin mix has a much higher compressivestrength than the epoxy resin mix and the other is that it takesabout 30 days for the compressive strength of either resin mix toreach equilibrium. This raises the question as to the proper curingtime at which compressive strength should be measured.
29
-
TIME,
DAYS
AFTER
CASTING
0 1000 2000 3000 4000 5000 6000 7000 8000 9000 lOOOO
COMPRESSIVE STRENGTH, PS I
Figure 1. Change in Compressive Strength of Resin Mixes on Curing
30
-
4 .2 Shrinkage on curing and coefficient of thermal expansion
Bars of resin mixes as in 4.0, 1 inch square by 10 inches betweenstuds, were made as in ASTM C531-68, Standard Method of Test forSHRINKAGE AND COEFFICIENT OF THERMAL EXPANSION OF CHEMICAL-RESISTANTMORTARS. Molds (Figure 1) and measurement equipment (Figure 3) aredescribed in ASTM C490-70, Standard Specification for APPARATUS FORUSE IN MEASUREMENT OF LENGTH CHANGE OF HARDENED CEMENT PASTE,MORTAR, AND CONCRETE. The standard bar used as an effective gagelength of 10 inches.
Lq - LPercent shrinkage = = x 100, where
Lio
L^ = Original length (length of standard bar),
in inches
L = Length as measured during or after cure, in inches
Since L =10,o *
Percent Shrinkage = 10 x (Shrinkage in inches asobserved by dial readings)
Shrinkage of the resin bars is recorded in Table 5 and Figure 2
Tab le 5 . Percent Shrinkage of Resin Mixes on Curing"1 /
Time, Daysafter Casting-
Percent Shrinkage3/
EPOXY RESIN MIX- POLYESTER RESIN MIX-4/
2 0.0189 0.0177
6 0.0322 0.0312
30 0.0469 0.0402
92 0.0547 0,0453
1. Original length is length 1 day after casting
2. For time after gelation or initial set subtract one day.
3. Average of measurements on four bars.
4.
Average of measurements on three bars. One bar showed anabnormally high shrinkage and there must have been an errorin the initial length.
31
-
88
80
72
84
58
48
40
52
24
18
8
0
EPOXYSAND MIX
OI
Figure 2
.06 .07
PERCENT SHRINKAGE
Shrinkage of Resin Mixes on Curing
32
-
There seems to be little difference between shrinkage of theepoxy and the polyester resin mix on curing. It appears thatcuring of neither resin mix was complete after 30 days, as someadditional shrinkage occurred after 92 days.
Coefficient of thermal expansion was measured on the bars usedfor the shrinkage measurements on the 92nd day. The particularstuds used were as in ASTM C490-70 Standard Specification forAPPARATUS FOR USE IN MEASUREMENT OF LENGTH CHANGE OF HARDENEDCEMENT PASTE, MORTAR, AND CONCRETE, 13/16 inch long, of AISI Type316 stainless steel. According to the Metals Handbook, vol. 1,page 423, 8th ed . , the mean coefficient of thermal expansion ofthis type of stainless steel is 9 X 10“^ in. /in. /deg. f.
As described in ASTM C531-68,
2 - Y - W
C = linear coefficient of thermal expansion, per deg. F.
Z = length of bar, including studs at elevated temperature, inches
Y = length of stud expansion, inches - X x T x k, wherek = linear coefficient of thermal expansion per deg. F.of the studs
W = length of bar, including studs at lower temperature, inches
T = temperature change, deg. F.
X = length of the two studs at the lower temperature, inches
For the measurement the bars were conditioned in the room at
22.5°C. The elevated temperature was that of the oven or 99.5°C.
The temperature change T = 77.0®C. = 138. 6®F.
33
-
The observed increase in length, average of three bars, when thepolyester bars were placed in the oven at 99.5°C. overnight.
Z - W = 0.01581 inch
X = 2 X 13/16 inch = 2 x 0.8125 = 1.625 inch for the two studs
W - X = 10.0000 - 1.6250 = 8.3750 inch (0.2127 m)
T = 138. 6°F (77°C.)
Y = 2 X 9 X 0.8125 x 138.6 x 10 ^ = 0.00203 inch
Z - Y - W = 0.01581 - 0.00203 = 0.01378 inch (0.0003500 m)
0.01378138.6 X 8.3750
= 11.87 X 10 inch/inch/deg . F.(21.37 X 10 m/m/deg. C.) polyesterresin mix.
An attempt was made to measure the coefficient of thermalexpansion of the epoxy resin mix but the epoxy resin bars shrunkconsiderably after placing in the oven overnight at 99.5°C., theshrinkage amounting to 0.160 percent, based on the length of thebars after 92 days curing (See Table 5 and Figure 2) . The observedshrinkage was at least partly due to the noticeable bending whichoccurred in the bars. Apparently the epoxy resin mix is not stableto a temperature of 100°C.
A final set of length measurements was made on the resin barsafter the measurements of thermal coefficient of expansion. Thesemeasurements were made at room temperature (22.5°C.) The averageof measurements on four bars of epoxy resin mix was calculated as0.340 percent shrinkage, based on the original length (See Table 5and Figure 2) . The corresponding value for the polyester resinmix, based on measurement of three bars, was 0.0946 percentshrinkage. The heat distortion of the epoxy bars would be expectedto be reflected in a permanent apparent shrinkage. However, thepolyester bars were not distorted by heat and expanded normally.The additional shrinkage of the polyester bars indicates that furthercuring takes place during the heating period. Apparently heat hassome effect on both resin types and this may be a characteristic ofepoxy and polyester resins when cured at room temperature, a necessityfor resin mixes used in so-called seamless floors or monolithicsurfacings. This may be a basic weakness of this type of flooring.
4 . 3 Flexural strength and Flexural modulus of elasticity
Bars of the resin mixes described in 4.0, 1 inch square by 10
inches long, were made as in ASTM C580-68, Standard Method of Testfor FLEXURAL STRENGTH AND MODULUS OF ELASTICITY OF CHEMICAL-RESISTANTMORTARS. After 19 days curing, the bars were tested using equipment
34
-
described in Figure'. 3, ASTM C348-69, Standard Method of Test forFLEXURAL STRENGTH OF HYDRAULIC CEMENT MORTARS. The span, L, ofthe test equipment is 119 mm or 4.685 inches, instead of 9 inchesor 22.86 cm as in par. 6.2 of ASTM C580-68. No equipment with9- inch span was available. Otherwise the procedure of ASTM C580-68was followed as closely as practicable. Crosshead speed was 0.5cm/min. (0.19 inch/min.).
Flexural strength was calculated from the formula
S
S
3PL2bd2’
where
stress of midspan in Ib/in2
P = load in lbs . at moment of break
L = span, inches = 4.685 inches
b = width of beam = 1 inch
d = depth of beam = 1 inch
For the epoxy resin mix, as described in 4.0, the average breakingload for four bars was 339 lbs. (1,508 N) , from which the flexuralstrength, S was calculated to be 2,383 psi. (16,431 MN/m^)
For the polyester resin mix, as in 4.0, the average breakingload for four bars was 475 lbs. (2,113 N) and the flexural strength,S was 3,338 psi. (23,016 MN/m^)
.
Flexural modulus of elasticity or tangent modulus was calculatedfrom the formula
3
= 4bd3 ’
2E = modulus of elasticity in bending, in lb. /in.B
L = span, inches
b = width of beam tested, inch
d = depth of beam tested, inch
M = slope of the tangent to the steepest initial straight-line portion of the load-deflection curve in lb . /inchof deflection
The slopes of the load- elongation curves were determinedgraphically on the original chart as the tangent of the steepestpart of the curve just before each bar broke. The average slope forfour bars of epoxy resin mix was 15,199.4 lb /inch, from which it was
35
-
calculated that the flexural modulus Eg = 0.391 x 10^ lb. /in.(2.696 X 10^ N/m^) . The average slope for four bars of polyesterresin mix was 20,756 lb. /inch, from which the calculatedEg = 0.53 X 10^ lb. /in. 2 (psi) (3.654 x 10^ N/m2)
.
4 .4 Tensile strength
Tensile strength of the epoxy and polyester re^in mixes describedin 4.0 was measured as in ASTM C307-61, Standard Method of Test forTENSILE STRENGTH OF CHEMICAL-RESISTANT RESIN MORTARS. Six specimensof each type of resin mix were tested in a load-strain testingmachine with crosshead speed of 0.5 cm/min. (0.19 in. /min.). Testswere made in each case 19 days after casting the briquets of resinmix. Based on the average values obtained from six specimens, thetensile strength of the epoxy resin mix was 1,336 Ib./in.^ (psi)(9,212 MN/m^) and the tensile strength of the polyester resin mixwas 1,905 psi (13,135 MN/m^)
.
4 .5 Comparison of BRD values with values of physical propertiesin ASTM specification
As already described in part 3.0 of this report, the TentativeSpecification for Resinous Chemical Resistant Monolithic Surfacingsof ASTM Committee C-3 covers two types of resin systems and includesepoxy and polyester resins. One resin system is called Type A andis Intended for "Rigid systems" for surfacings where chemicalresistance and moderate to heavy traffic are required. The otherresin system is called Type B and is intended for "Flexible systems"for surfacings where mild chemical resistance and severe thermalshock stability or resistance are required. Values for physicalproperties are shown in Table 2 of this report, in section 3.0,which describes the ASTM Specification.
Values found by the Building Research Division (BRD) for pl^ysicalproperties of typical epoxy and polyester flooring resin mixes arerecorded in section 4.0, Tables 4,5, 6 and 7, and Figures 1 and 2.In Tables 6 and 7 these values are compared with values in the ASTMSpecification. Tables 4 and 5 and Figures 1 and 2 show the curingcharacteristics of the two resin mixes investigated by BRD. Thisis relevant to the "Service strength setting time" requirementin Table 2.
36
-
Table 6. Physical Properties of Epoxy Resin MixRecommended by ASTM and Found by BRD(In customary units. See Table 6a for SI units)
Physical Property Value specified by. .ASTM C-3 Committee—
Value found bybrdI/
3 4/Compressive strength"^',psi
Type A,Rigid
Type BFlexible
6,000 4,000 3,877
Percent shrinkage oncurlng4 ^5 / 0.5 0.5 0.0469
Coefficient of thermalexpansion 5jj6/,inch/inch/deg. F. 40 X lO'^ 40 X lO'^ Unstable—^
7 8 /Flexural Strength —^,psi 1,500 750 2,383
Flexural modulus ofelasticityZ^/, psi 0.5 X 10^ 0.25 X 10^ 0.391 X 10®
8 9/Tensile strength-- psi 1,500 600 1,336
1.
Values in Tables 2 and 3, part 3.0 of this report. These values areto be based on measurements on resin mixes which have been curedfor 7 days.
2.
Values for EPOXY RESIN MIX, described in part 4.0 of this report.
3. For BRD value see part 4.1 of this
4. BRD value based on measurements on
5. For BRD value see part 4.2 of this
6. BRD value based on measurements onments after 92 days curing.
7. For BRD value see part 4.3 of this
8. BRD value based on measurements on
9. For BRD value see part 4.4 of this
report
.
specimens cured for 30 days,
report
bars used for shrinkage measure-
report .
specimens cured for 19 days,
report
.
37
-
}
Table 6a. Physical Properties of Epoxy Resin Mix in SI Units*
(See Table 6 for customary units)
Physical Property Value specified by Value found byASTM C"3 Committee BRD
Type A, Type BRigid Flexible
Compressive strength,m/rn^ 41,370 27,580 26,732
Percent shrinkage oncuring 0.5 0.5 0.0469
Coefficient of thermalexpansion, m/m/deg. C. 72 X 10'^ 72 X lO'^ Unstable
2Flexural strength, MN/m 10,343 5,171 16,431
Flexural modulus ofelasticity, N/m^ 3.4 X 10®
91.7 X 10^ 2.696 X 10
2Tensile strength, MN/m 10,343 4,137 9.212
^Footnotes same as Table 6
38
-
Table 7. Physical Properties of Polyester Resin MixRecommended by ASTM and Found by BRD
Physical Property Value specified by -
.
ASTM C-3 Committee—Value found
brdI/
, 3.4/Compressive strengtlr^"*—
,
psi
Type A,Rigid
Type b.Flexible
10,000 8,000 9,225
Percent shrinkage oncuring 4.5/ 1.0 0.6 0.0402
Coefficient of thermalexpansion 5 .6/
^
inch/inch/deg. F. 40 X lO'^ 40 X 10*^ 11.87 X lo"
7 8 /Flexural strength ' ,psi 1,500 750 3,338
Flexural modulus ofelasticityZ^/
,psi 1.0 X 10^ 0.5 X 10^ 0.53 X 10®
8 9/Tensile strength psi 1,500 600 1,905
1. Values in Tables 2 and 3, part 3.0 of this report. These values areto be based on measurements on resin mixes which have been curedfor 7 days.
2. Values for POLYESTER RESIN MIX, described in part 4.0 of this report.
3. For BRD value see part 4.1 of this report.
4. BRD value based on measurements on specimens cured for 30 days.
5. For BRD value see part 4.2 of this report.
6. BRD value based on measurements on bars used for shrinkagemeasurements after 92 days curing.
7. For BRD value see part 4.3 of this report.
8. BRD value based on measurements on specimens cured for 19 days.
9. For BRD value see part 4.4 of this report.
39
-
Table 7a. Physical Properties of Polyester Resin Mix iq SI Uaits^(See Table 7 for customary units)
Physical Property Value sASTM C-
pecified by3 Committee
Value foundBRD
Type A,Rigid
Type B,Flexible
Compressive strength,MN/m^ 68,950 55,160 63,606
Percent shrinkage on curing 1.0 0.6 0.0402
Coefficient of thermalexpansion, m/m/deg. C. 72 X lO'^ 72 X lO'^ 21.37 X lO'^
2Flexural strength, MN/m 10,343 5,171 23,016
Flexural modulus ofelasticity, N/m^ 6.9 X 10^ 3.4 X 10®
93.7 X lO"^
2Tensile strength, MN/m 10,343 4,137 13,135
* Footnotes same as Table 7
40
I
-
5 . 0 Conclusions and recommendations
Most of the values for physical properties for the epoxy andpolyester resin mixes reported in section 4.0 were close to those inthe ASTM C-3 Specification. However, much lower values were reportedin section 4.0 for percent shrinkage and coefficient of thermalexpansion and it is hard to understand why such high values werespecified by ASTM Committee C-3. Also hard to explain is the lowvalue specified by ASTM C-3 for flexural strength, especially forthe flexible type of resins. The tensile strength values for theflexible type of resins in the ASTM Specification are also low,although this may not be of practical importance. The most seriousquestion is the lack of heat stability of the epoxy resin mixreported in 4.0 in which the epoxy resin would not withstand atemperature of 100°C. Epoxy resins are already regarded by theCorps of Engineers as being unstable to heat. Another characteristicof the resin mixes which we found, as shown in Tables 4 and 5 andFigures 1 and 2, is that curing is not complete after 7 days asinferred from the ASTM specification for "service strength settingtime" in Table 2. In Table 2 the setting time for epoxy is requiredto be 7 days and for polyester resin only 3 days. However, ourfindings, as in Tables 4 and 5 and Figures 1 and 2, indicate thatpolyester resin requires about 10 to 20 days to cure and epoxyresin about 20-40 days, depending on wehterh compressive strengthof percent shrinkage is used as the criterion.
Not only is there a lack of agreement between the ASTM C-3Specification and our measurements but the ASTM C-3 Specificationdoes not agree with the NTMA Specifications. This can be seenfrom an examination of Table 3. The test methods also differ, asshown in Table 4.
Another question about the ASTM C-3 Specification is the lackof detail for the chemical resistance requirement. Details aregiven for chemical resistance requirements and tests in the NTMAspecifications but these differ for epoxy and polyester resins.For details see Table 4. Table 4 shows other differences between theASTM C-3 specifications and the various NTMA specifications inrequirements common to ASTM and NTMA. Table 1 shows how few ofthe NTMA tests are included in the ASTM C-3 specification andthat not all the NTMA specifications include the same tests.Also NTMA requirements appear sometimes under the matrix andsometimes under the finished terrazzo.
41
-
A liaison should be established between the U. S. Army Corpsof Engineers, the National Bureau of Standards, ASTM CommitteeC-3 and The National Terrazzo and Mosaic Association. We proposethat the Building Research Division of the National Bureau ofStandards act, as the liaison and try to reach an agreement onspecifications for resinous flooring. We should like fo cooperatein making whatever tests and measurements are necessary to establishthese specifications. We should also like to base the specificationson physical properties relevant to perforr^ance or end use as muchas possible, using our field experience as a guide and performingwhatever field observations and tests are necessary for thispurpose
.
42
-
As a starting point we have drawn up and present the following:
PROPOSED SPECIFICATION FOR
RESINOUS MONOLITHIC SURFACING5
TABLE OF CONTENTS
1. SCOPE AND CLASSIFICATION
2. APPLICABLE DOCUMENTS
3. REQUIREMENTS AND TEST METHODS
4. QUALITY ASSURANCE PROVISIONS
5. PREPARATION OF CONCRETE SUBFLOOR
6. INSTALLATION
1. SCOPE AND CLASSIFICATION
1.1 Scope . This specification covers materials, requirements, surfacepreparation, and installation applying to resinous monolithic surfacesto be applied to concrete slabs.
1.2 Classification . Resinous monolithic surfacings shall be of thefollowing types and classes and with or without special requirements,in any combination as specified.
Type I - Thin-set Terrazzo Flooring
Type II - Industrial Resinous Flooring
Class 1 - Latex or Resin emulsion Matrix
Class 2 - Polymer Matrix
Subclass a - One component Polymer Matrix
Subclass b - Two component Pol3nner Matrix
Special requirement - Conductive
Special requirement - Sparkproof
43
-
1
2. APPLICABLE DOCUMENTS
2.1 The following documents of the issue in effect on data ofinvitation for bids or request for proposal, form a part of thisspecification to the extent specified herein.
SPECIFICATIONS
FEDERAL (INTERIM)
L-F-001641, FLOOR COVERING TRANSLUCENT OR TRANSPARENTVINYL SURFACE WITH BACKING
MILITARY
MIL-D-3134F, DECK COVERING MATERIALS
MIL-D-52505 (MO), FLOOR COATING, RESINOUS, MONOLITHIC,TROWEL TYPE (FOR WOOD AND CONCRETE FLOORS)
STANDARDS
FEDERAL TEST METHOD STANDARDS
No. 141a, PAINT, VARNISH, LACQUER AND RELATED MATERIALS:METHODS OF INSPECTION, SAMPLING, AND TESTING
No. 501a, FLOOR COVERINGS, RESILIENT, NONTEXTILE: SAMPLINGAND TESTING
OTHER PUBLICATIONS
National Terrazzo and Mosaic Association, Inc. (NTMA)
,
Terrazzo; Specifications, Details, Technical Data (1970)
National Fire Protection Association (NFPA),56A, Standard for
the Use of Inhalation Anesthetics, 1971
American Society for Testing and Materials (ASTM) Standards:
C307-61, Standard Method of Test for TENSILE STRENGTH OFCHEMICAL-RESISTANT RESIN MORTARS
C531-68, Standard Method of Test for SHRINKAGE AND COEFFICIENTOF THERMAL EXPANSION OF CHEMICAL-RESISTANT MORTARS
C579-68, Standard Method of Test for COMPRESSIVE STRENGTH OFCHEMICAL-RESISTANT MORTARS
C580-68, Standard Method of Test for FLEXURAL STRENGTH ANDMODULUS OF ELASTICITY OF CHEMICAL-RESISTANT MORTARS
44
-
D412-68, Standard Method of TENSION TESTING OF VULCANIZEDRUBBER
D638-68, Standard Method of Test for TENSILE PROPERTIES OFPLASTICS
E84-68, Standard Method of Test for SURFACE BURNINGCHARACTERISTICS OF BUILDING MATERIALS
E 188- 70, Recommended practice fOr OPERATING ENCLOSED CARBON-ARC TYPE APPARATUS FOR LIGHT EXPOSURE OF NONMETALLICMATERIALS
E303-69, Standard Method of Test for MEASURING SURFACEFRICTIONAL PROPERTIES USING THE BRITISH PORTABLETESTER
ASTM Special Technical Publication (STP) No. 422, "Symposium onFire Test Methods - Restraint and Smoke", Atlantic City, N.J., 1966
3. REQUIREMENTS AND TEST METHODS
3.1 Qualification . Monolithic surfacing materials furnished under thisspecification shall be a product which has been tested and passed thequalification tests specified herein.
3.2 Materials . Monolithic surfacing materials shall consist of matrixand aggregate, corresponding to the desired type and class. Otheringredients may be added for the desired color or to fulfill specialrequirements. Dry materials other than aggregate shall be factoryblended and properly proportioned for mixing with the liquid components.Primer, sealer, and grout shall be supplied as required. Materialsshall be delivered to the job site in the manufacturer *s originalunopened package with the manufacturer *s name, brand name, and typeand class description clearly marked thereon. Materials to meetspecial requirements shall have the words CONDUCTIVE or SPARKPROOFmarked thereon. Materials shall be stored at a temperature not lowerthan 50 degrees F. for at least 24 hours before installation. Materialswhen properly mixed, installed, and cured at room temperature shallproduce a monolithic surfacing which meets the requirements of thisspecification.
Primer shall be supplied if recommended by the manufacturer of thesurfacing materials. When used according to the manufacturer's in-structions, the primer shall bond with the concrete subfloor and withthe monolithic surfacing. Sealer shall be supplied if recommended bythe manufacturer. When applied to the monolithic surfacing, sealershall dry within 18 hours and shall form the surface which shallcomply with the requirements of this specification. Grout shall besupplied for Type I, Thin- set Terrazzo Flooring, in an amount suf-ficient to fill in holes, cracks, and depressions in the floor afterthe first grinding.
45
-
3.2.1 Aggregate, Type I . The aggregate shall consist of a blend ofmarble chips of a range of sizes up to and including NTMA StandardNo. 1 chip.
3.2.2 Aggregate, Type II . The aggregate shall be of suitable size forapplication in 3/16 to 5/16 inch thickness and the maximum diametershall not be more than half the thickness of the surfacing. It shallbe capable of installation with a feather edge.
3.2.3 Finishing, Types I and II . All monolithic surfacings shall besuitable for application with a trowel and shall be capable of finish-ing by steel trowel on the day of application.
3.2.4 Finishing, Type I . Thin-set terrazzo flooring shall be suitablefor finishing with a terrazzo grinder after the specified curing period.
3.2.5 Matrix, Class 1 . Matrix shall consist of liquid syntheticrubber latex or resin emulsion and dry mix to be furnished in separatecontainers, properly proportioned and clearly labelled.
3.2.6 Matrix, Class 2, subclass a . Matrix shall consist of liquidpolymer or prepolymer with or without solvents, which shall cure whenproperly mixed with the other ingredients and installed, within thecuring time specified.
3.2.7 Matrix, Class 2. subclass b . Matrix shall consist of two com-ponents, which shall be in separate containers, properly proportionedand clearly labelled. One component shall be a liquid polymer or pre-pol3nner and the other component a curing agent, catalyst, or initiator,which shall cure the pol3rmer when properly mixed with the otheringredients and installed, within the curing time specified.
3.2 Application . Monolithic surfacings in the colors, of the typesand classes indicated, and with special requirements as specified,shall be applied to the areas shown on the drawings. A temperatureof at least 65 degrees F. shall be maintained from 48 hours beforeinstallation until one week after installation. Adequate ventilationshall be provided to remove any volatile fumes. Finished work ofother trades shall be protected from damage during installation.
3.4 Workmanship . The techniques of mixing, application, and finishingshall be of such quality that the monolithic surfacing shall meetthe requirements of this specification.
3.5 Test requirements . The finished monolithic surfacing and samplessubmitted shall meet test requirements as in Table 1.
46
-
Table 1. Test Requirements for Monolithic Surfacings^Test Method
Property of Surfacing Test Requirement Re ferei
Abrasion or WearResistance^
No break through atany point 3.6.1
Adhesion or BondStrength
300 psi minimum tensilestrength with 100 percentconcrete failure 3.6.5
Aging or AcceleratedWeathering Resistance^
No cracking, peeling,blistering, loss of adhesionafter 300 hours 3.6.7
Chemical Resistance No change in color; noblistering, cracking, peeling,loss of adhesion when testedwith specified reagents 3.7
3 4Compressive Strength ’ 4,000 psi 3. 6. 9.1
Conductivity, electrical Less than 1,000,000 andmore than 25,000 ohms 3,6.10
Curing time^ Within 18 hours 3.6.7
Defects in Appearance orSurface Defects
Shall conform to require-ments in 3.8 3.8
Fading Resistance No discoloration or otherphysical changes after 48hours exposure 3.6.6
3 4Fire Safety ’ Flame spread rating 200
Maximum specific opticaldensity of smoke generated450 (flaming test only) 3. 6. 9.
3
Flexural strength^ 2,000 psi 3 .6 . 9 .4
Flexural modulus ofelasticity^ 5^
0.5 X 10^ 3. 6. 9.
4
Hardness Hardness as defined,
minimum M85 3.6.7
Heat resistance^ No shrinkage or distortion 3. 6. 9.
5
47
-
Table 1 - continued
Property of Surfacing Test RequirementTest MethodRe ference
Impact resistance No cracking, peeling,blistering, loss ofadhesion from 144 inch-pounds force 3.6.7
Indentation Not more than 0.015 inchafter 10 minutes at 73°F. 3.6.2
Odor Free from objectionableodors 3.6.8
Resistance to microorgan-isms (Fungistatic,Bacteriostatic Resistance)
Shall not support growthof fungus or bacteria 3.6.7
3 4Shrinkage, linear ’ 0.5 percent maximum after
gelation or setting 3. 6. 9.
5
Slip Resistance More than 45 BPN units 3.9
Sparking resistance(friction)
Shall not produce a spark 3.10
Stain resistance Shall not retain apermanent stain 3.6.7
3 4Tensile elongation ’ Minimum 5 percent 3.6.4
Tensile strength^ 1,500 psi 3 . 6 . 9 .
6
Thermal coefficient ofexpansion^ j4
—6Maximum 40 x 10inch/inch/deg . F. 3. 6. 9.
5
Thermal shock resistance Shall not crack, peel,blister, spall, orlose adhesion 3.6.7
Volatility^ Loss of volatile materialsshall not exceed 1 percent 3.6.3
Water absorption Maximum 5 percent 3.6.8
Water Resistance See Chemical Resistance
-
Table 1 - continued
NOTES to Table 1
1. Tests to be performed after 30 days curing except as otherwiseindicated.
2. Note 1 does not apply.
3. Test cannot be performed on finished monolithic surface
4. Test cannot be performed on panels submitted as in section 4.
49
-
3.6
References in Table I to test methods
3.6.1 Federal Specification L-F-001641, 3. 3. 3.
4
3.6.2 Federal Test Method Standard No. 501a, Method ^211
3.6.3 Federal Test Method Standard No. 501a, Method 9211
3.6.4 NTMA Specification for Conductive Epoxy Resin Terrazzo,1.10 PERFORMANCE AND PROPERTIES OF CONDUCTIVE EPOXY MATRIX
Tensile elongation, ASTM D638-68 with C die as in ASTM D412-68
3.6.5 NTMA Specification for Conductive Epoxy Resin Terrazzo,1.11 PERFORMANCE AND PROPERTIES OF CONDUCTIVE EPOXY TERRAZZO
Adhesion or Bond Strength, Journal of the American CorjcreteInstitute, vol. No. 9, pages 1139-1141 (September 1962)
3.6.6
NTMA Specification for Epoxy Resin Terrazzo,
1.10
PERFORMANCE AND PROPERTIES OF EPOXY MATRIX
Fading Resistance, ASTM E188-70, Method A
3.6.7 NTMA Specification for Conductive Polyester Re^in Terrazzo,
1.10
PERFORMANCE AND PROPERTIES
Aging or Accelerated Weathering Resistance, MIL-F-52505 (MO),
3.11, 4.4.2.10
Curing Time, MIL-F-52505 (MO), 3.3, 4. 4. 2.
2
Hardness, MIL-F-52505 (MO), 3.8, 4. 4. 2.
7
Impact resistance, MIL-F-52505 (MO), 3.10, 4. 4. 2.
9
Resistance to microorganisms (Fungistatic and bacterio-static resistance), MIL-F-52505 (MO), 3.12, 4.4.2.11
Stain resistance, MIL-F-52505 (MO), 3.15, 4.4.2.14
Thermal shock resistance, MIL-F-52505 (MO), 3.15, 4.4.2.14
3.6.8 NTMA Specification for Latex Matrix Terrazzo,
1.10
PERFORMANCE AND PROPERTIES
Odor, MIL-D-3134F, 3.4
Water (moisture) absorption, MIL-D-3134F, 3.13, 4.7.8
3.6.9 ASTM Standards and other publications as follows:
50
-
3. 6.
9.1
ASTM C-5 79-68
3. 6. 9. 2 ASTM E84-68
3. 6. 9. 3 ASTM STP 422
3. 6. 9. 4 ASTM C580-68
3. 6. 9. 5 ASTM C531-68
3. 6. 9. 6 ASTM C307-61
3.6.10 Section 252, NFPA 56A
3.7 Chemical Resistance . The monolithic surfacing may be specifiedresistant to acid, alcohol, alkali, detergent, or oil in the invitationfor bids or request for proposals. In such cases the surfacing shallbe tested according to Method 6011, Federal Test Method Standard No.141a with reagents specified in Method 9311, Federal Test MethodStandard No. 501a
Product specified as resistant to Reagent, Method 9311paragraph
Acid. 3.6.2
Acetic acid 3.6.1
Sulfuric acid 3.6.2
Alcohol 3.6.5
Alkali 3.6.3
Detergent 3.6.4
Oil 3.6.6, 3.6.7, 3.6.8, 3.6.9, 3.6.10
3.8 Defects in Appearance or Surface Defects . The finished monolithicsurface and panel submitted shall have a smooth, level, even surfacefree from blisters, cracks, holes, protruding particles, and embeddedforeign matter. The color and finish of the surfacing shall matchthe panel submitted. The product shall be rejected for any surfacedefect which will seriously affect serviceability or appearance.
3.9 Slip Resistance . Surfacing shall be tested for slip resistanceaccording to ASTM E303-69 but with a dry surface.
3.10 Sparking Resistance . Surfacing shall be tested for sparking re-sistance by stroking the floor vigorously with a 12 inch hardenedsteel file in a 3 foot arc. The test shall be performed for each 80square feet of floor area. Tests shall be made in a darkened spaceand only when the relative humidity of the atmosphere within the spacedoes not exceed 50 percent.
51
-
4. QUALITY ASSURANCE PROVISIONS
4.1 Unless otherwise specified in the invitation for bids or requestfor proposal the supplier is responsible for the performance of alltests in 3.5. The government reserves the right to perform any ofthese tests or any inspections where such tests and inspectionsare deemed necessary to assure supplies and services conform toprescribed requirements. This applies to qualification tests,preparation of subfloor, and installation. Tests may be performedby the government on panels or unmixed ingredients submitted assamples
.
4.2 Qualification tests shall be performed at a laboratory satisfactoryto the procuring officer. Qualification tests shall consist of thetests specified in 3.0 and Table 1.
4.3 Samples and test data ; Prior to delivery of the materials tothe job site, the following samples shall be submitted for approval:
Monolithic surfacing: Two 12- by 12- inch sample panels ofeach type finish or color combination
Sufficient unmixed ingredients to providefor the application of 9 square feet inarea and one- fourth inch (approximate)in thickness
Divider strips, as required; Two 6-inch lengths of each type
Finished surfacing shall match the approved samples in color andtexture. Samples shall be accompanied by certified test reportsfrom an approved laboratory showing that the monolithic surfacinghas been tested within the last 12 months and meets the require-ments specified herein.
4.4 D