Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop...
-
Upload
linda-baldwin -
Category
Documents
-
view
228 -
download
1
Transcript of Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop...
![Page 1: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/1.jpg)
Research Needs on SCC of Pipelines
Raymond R. Fessler
Stress-Corrosion Cracking (SCC) Workshop
DOT/RSPA
Houston, TX
December 2, 2003
![Page 2: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/2.jpg)
Status of SCC
• Remains an industry-wide concern
• SCC is being managed– Probability of failures is low
• Much lower than would be expected if it were not being managed
• Probably never will be zero
– Integrity of P/L can be assured
• Cost of SCC management is very high
![Page 3: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/3.jpg)
SCC Gap Analysis
• What opportunities are there to decrease the probability of SCC failures and reduce the cost of SCC management?
• What research is needed to take advantages of those opportunities?
![Page 4: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/4.jpg)
STRUCTURE FOR SCC GAP ANALYSIS
1.1. AssessRisk
1.2.1.Locate
1.2.2.Treat
1.2. LocateSCC and
treat
1.3. Changeoperatingpractices
1. Existing pipeline
2.1.1.Initiation
2.1.2.Threshold
2.1.3.Growth
2.1. Selectresistant
steel
2.2. Selecteffectivecoating
2.3. Designoperatingconditions
2. New (future) pipeline
Manage high-pH and near-neutral-pH SCC
![Page 5: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/5.jpg)
Criteria for Recommending Research
• Understanding is not high
• Probability of success is reasonable
• Potential benefits far exceed cost of research
![Page 6: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/6.jpg)
Incentives for Additional R&D
• Improve effectiveness and reduce costs of– Hydrostatic retesting– ILI– Direct Assessment
• Make future pipelines more resistant to SCC
![Page 7: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/7.jpg)
Objectives for Future R&D
• Optimize hydrotesting and ILI intervals– Justify on basis of crack growth rate– Extend intervals by reducing crack growth rate
through operating practices– Prioritize areas– Optimize procedures
• Develop ILI for gas pipelines
![Page 8: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/8.jpg)
Objectives for Future R&D (cont.)
• Validate Direct Assessment for SCC
• Develop direct-examination sizing techniques
• Develop simple-to-use ECA methods
• Validate new repair methods for SCC
• Develop resistant steels
![Page 9: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/9.jpg)
R&D Approaches
• Optimize inspection intervals– Improve crack-growth models
– Improve site-selection models
• ILI– Develop technologies
– Develop commercial tools
• Direct Assessment– Field Validation
• Sizing techniques– Develop & qualify commercial tools
• ECA methods– Develop simple tool (RSTRENG for
SCC)
• Resistant steels– Evaluate current steels
– Understand relationships between composition, structure, properties, & performance
![Page 10: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/10.jpg)
Crack-Growth Models
![Page 11: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/11.jpg)
Crack-Growth Models
• Several crack-growth models – Leis (Battelle) probabilistic model for high-pH SCC– Rainbow P/L Model for near-neutral-pH SCC– Beaver’s/Lambert’s superposition model
• All are based on simplified assumptions about growth rate of single crack
• Some consider interactions between cracks• Each has benefits and limitations• At least two should be examined and developed more
fully
![Page 12: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/12.jpg)
Site-Selection Models
![Page 13: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/13.jpg)
Site-Selection Models
• Difficult to evaluate effectiveness– Limited data– Few “control experiments”– Proprietary algorithms– Continual refinements
• Phenomenological rather than scientific
![Page 14: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/14.jpg)
Site-Selection Models (continued)
• Mixed industry experience– Geographically specific– More reliable with tape than asphalt– Interdependent factors (e.g., coating type and soil resistivity)
• Opportunities – Develop scientific basis– High pH vs. near-neutral-pH– Improved soils module
• Accelerating & Inhibiting factors– Incorporate operating history & coating– Combine industry data
![Page 15: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/15.jpg)
In-Line Inspection (ILI)
![Page 16: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/16.jpg)
In-Line Inspection (ILI)
• No satisfactory commercially available tool for gas pipelines– Liquid-coupled UT too cumbersome and expensive
– Elastic wave has inadequate discrimination
– EMAT remains to be demonstrated
• Too early to judge other technologies, but probably long shots– Circumferential MFL
– Rotating magnetic-field probe
– Gas-coupled UT
![Page 17: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/17.jpg)
In-Line Inspection (continued)
• Role of PRCI– Support field validations
– Develop/encourage/test new technologies
• Role of vendors: Develop commercial tools• Role of DOT• Protection of proprietary ideas• Assurance of adequate market
![Page 18: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/18.jpg)
SCC Direct Assessment
(Covered in other presentations)
![Page 19: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/19.jpg)
SCC Direct-Examination Sizing Techniques
(Covered in other presentations)
![Page 20: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/20.jpg)
Resistant Steels
![Page 21: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/21.jpg)
Resistant Steels: R&D Approaches & Issues
• Empirical approach– Test current and new steels
• Fundamental approach– Relate SCC susceptibility to micro-plastic behavior,
microstructure, composition, processing
• Issues– Large effort required
– Proper coatings and surface preparation provide significant benefit
![Page 22: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/22.jpg)
Speculative Budget Projections
0
200
400
600
800
1000
1200
1400
2002 2003 2004 2005 2006 2007 2008 2009
$1
00
0
Crack Growth NDE-In the Ditch ILI Site Selection DA
0
200
400
600
800
1000
1200
1400
2002 2003 2004 2005 2006 2007 2008 2009
$1
00
0
Crack Growth NDE-In the Ditch ILI Site Selection DA
![Page 23: Research Needs on SCC of Pipelines Raymond R. Fessler Stress-Corrosion Cracking (SCC) Workshop DOT/RSPA Houston, TX December 2, 2003.](https://reader035.fdocuments.us/reader035/viewer/2022062222/5697bfa21a28abf838c962d9/html5/thumbnails/23.jpg)
Summary of Opportunities for Gov’t/Industry Cooperation
• Optimize testing/inspection intervals– Crack-growth models– Site-selection models
• ILI for SCC– Practical technologies for gas lines
• Direct-examination sizing and ECA of SCC
• Resistant-steel development