Rapid Hardening Cement (Grade 42.5) Introduction General characteristics The product obtained by grinding cement clinker obtained by roasting suitable raw material, consisting essentially of anhydrous calcium sulphoaluminate and dicalcium silicate. Suitable gypsum and 0-10% limestone shall be blended with clinker during manufacture of rapid-hardening sulphoaluminate cement. The rapid-hardening cement product is hydraulicity binding material. It has high early strength. The code no is R-SAC and with four grades. Properties 1) High early strength and high strength properties Its compressive strength can reach 35-50Mpa within 1 day, 50-70Mpa after 3 days, and it also can grows continually with the increasing of curing age. 2) High froze-resistance property: If used at the temperature as low as 0-10℃,which early strength is 5-6 times than that of OPC; if used in 0-20℃ with little admixture, its strength in 3-7d can reach 70-80% of designed strength, with very little strength loss after 300 times of froze-thaw circle. 3) High impermeability: Because of its dense structure, the impermeability of the concrete is 2-3 times than that of OPC in same grade. 4)Anti-carbonation property: It has good anti-carbonation property, and low dry-shrinkage. 5) Corrosion-resistance: Rapid-hardening cement has good corrosion-resistance quality, especially much better in seawater corrosion resistance than that of high anti-sulphate Portland cement, with more than 1 corrosion-resistance coefficient. Data Specific surface area(m 2 /kg): ≥350 Setting time(min): Initial setting time: ≥25 Final setting time: ≤180 (Remark: the setting time can be adjusted according to the customer’s demand.)
-
Upload
jack-young -
Category
Documents
-
view
76 -
download
3
Transcript of Rapid set CSA cement
Rapid Hardening Cement (Grade 42.5) Introduction
General characteristics
The product obtained by grinding cement clinker obtained by roasting suitable raw material,
consisting essentially of anhydrous calcium sulphoaluminate and dicalcium silicate. Suitable
gypsum and 0-10% limestone shall be blended with clinker during manufacture of rapid-hardening
sulphoaluminate cement. The rapid-hardening cement product is hydraulicity binding material. It
has high early strength. The code no is R-SAC and with four grades.
Properties
1) High early strength and high strength properties
Its compressive strength can reach 35-50Mpa within 1 day, 50-70Mpa after 3 days, and it also can
grows continually with the increasing of curing age.
2) High froze-resistance property:
If used at the temperature as low as 0-10℃,which early strength is 5-6 times than that of OPC; if
used in 0-20℃ with little admixture, its strength in 3-7d can reach 70-80% of designed strength,
with very little strength loss after 300 times of froze-thaw circle.
3) High impermeability:
Because of its dense structure, the impermeability of the concrete is 2-3 times than that of OPC in
same grade.
4)Anti-carbonation property:
It has good anti-carbonation property, and low dry-shrinkage.
5) Corrosion-resistance:
Rapid-hardening cement has good corrosion-resistance quality, especially much better in
seawater corrosion resistance than that of high anti-sulphate Portland cement, with more than 1
corrosion-resistance coefficient.
Data
Specific surface area(m2/kg): ≥350
Setting time(min): Initial setting time: ≥25 Final setting time: ≤180
(Remark: the setting time can be adjusted according to the customer’s demand.)
Strength data in different ages:
Grade Compressive Strength (Mpa) Bending Strength (Mpa)
1 day 3 days 28 days 1 day 3 days 28 days
42.5 33.0 42.5 45.0 6.0 6.5 7.0
52.5 42.0 52.5 55.0 6.5 7.5 7.5
62.5 50.0 62.5 65.0 7.0 7.5 8.0
72.5 56.0 72.5 75.0 7.5 8.0 8.5
Application Areas
1. Construction in winter.
2. Urgent repairs and rapid construction.
3. Spraying anchor and supporting engineering.
4. Water conservancy facilities and offshore projects.
5. Bridge and road construction.
6. Cement products and prefabricated components.
7. Industrial and civil engineering,etc.
Storage
Bulk and weave package with membrane, 40kg per bag, conservation in cool and dry place,
prevent wet.
Note: Edit by Jack Young, 2015-05-12,as references only. For more informations, please contact:
cell phone no.: +0086 158 1032 6158 or mail box: [email protected]
online: [email protected] (MSN) yangjian1886 (Skype)
![Mechanical performance of sulfo-based rapid hardening ... · alternative fuels in the cement kiln [3]. As about 60% of the CO2 emission in Portland cement production come from the](https://static.fdocuments.us/doc/165x107/5e2c165b611432794a7286ff/mechanical-performance-of-sulfo-based-rapid-hardening-alternative-fuels-in-the.jpg)