Radiation Tolerant Sensors for Solid State Tracking Detectorsseminar/extern/moll29Jan07.pdf ·...
Transcript of Radiation Tolerant Sensors for Solid State Tracking Detectorsseminar/extern/moll29Jan07.pdf ·...
EPFL – LPHE, Lausanne, January 29, 2007
Radiation Tolerant Sensors for Solid State Tracking Detectors
- CERN-RD50 project –http://www.cern.ch/rd50http://www.cern.ch/rd50
Michael MollMichael MollCERN CERN -- Geneva Geneva -- SwitzerlandSwitzerland
Michael Moll – Lausanne, 29. January 2007 -2-
RD50 Outline
• Introduction: LHC and LHC experiment
• Motivation to develop radiation harder detectors
• Introduction to the RD50 collaboration
• Part I: Radiation Damage in Silicon Detectors (A very brief review)• Microscopic defects (changes in bulk material)• Macroscopic damage (changes in detector properties)
• Part II: RD50 - Approaches to obtain radiation hard sensors• Material Engineering• Device Engineering
• Summary and preliminary conclusion
Michael Moll – Lausanne, 29. January 2007 -3-
RD50 LHC - Large Hadron ColliderStart : 2007
• Installation inexisting LEP tunnel
• 27 Km ring
• 1232 dipoles B=8.3T
• ≈ 4000 MCHF(machine+experiments)
• pp √s = 14 TeVLdesign = 1034 cm-2 s-1
• Heavy ions (e.g. Pb-Pb at √s ~ 1000 TeV)
p p
LHC experiments located at 4 interaction points
Michael Moll – Lausanne, 29. January 2007 -4-
RD50 LHC Experiments
CMS
+ LHCf
Michael Moll – Lausanne, 29. January 2007 -5-
RD50 LHC Experiments
CMS
LHCf
Michael Moll – Lausanne, 29. January 2007 -6-
RD50 LHC example: CMS inner tracker
5.4 m
2.4
m
Inner Tracker Outer Barrel (TOB)Inner Barrel
(TIB) End Cap (TEC)Inner Disks
(TID)
CMS – “Currently the Most Silicon”• Micro Strip:• ~ 214 m2 of silicon strip sensors, 11.4 million strips• Pixel:• Inner 3 layers: silicon pixels (~ 1m2) • 66 million pixels (100x150µm)• Precision: σ(rφ) ~ σ(z) ~ 15µm• Most challenging operating environments (LHC)
CMS
Pixel
93 cm
30 cm
Pixel Detector
Total weight 12500 t
Diameter 15m
Length 21.6m
Magnetic field 4 T
Michael Moll – Lausanne, 29. January 2007 -7-
RD50 Status December 2006• LHC Silicon Trackers close to or under commissioning
• CMS Tracker (12/2006)(foreseen: June 2007 into the pit)
• ATLAS Silicon Tracker (08/2006)August 2006 – installed in ATLAS
CMS Tracker Outer Barrel
Michael Moll – Lausanne, 29. January 2007 -8-
RD50 Motivation for R&D on Radiation Tolerant Detectors: Super - LHC
• LHC upgradeLHC (2007), L = 1034cm-2s-1
φ(r=4cm) ~ 3·1015cm-2
Super-LHC (2015 ?), L = 1035cm-2s-1
φ(r=4cm) ~ 1.6·1016cm-2
• LHC (Replacement of components)e.g. - LHCb Velo detectors (~2010)
- ATLAS Pixel B-layer (~2012)
• Linear collider experiments (generic R&D)Deep understanding of radiation damage will be fruitful for linear collider experiments where high doses of e, γ will play a significant role.
5 years
2500 fb-1
10 years
500 fb-1
× 5
0 10 20 30 40 50 60r [cm]
1013
51014
51015
51016
Φeq
[cm
-2] total fluence Φeqtotal fluence Φeq
neutrons Φeq
pions Φeq
other charged
SUPER - LHC (5 years, 2500 fb-1)
hadrons ΦeqATLAS SCT - barrelATLAS Pixel
Pixel (?) Ministrip (?)Macropixel (?)
(microstrip detectors)
[M.Moll, simplified, scaled from ATLAS TDR]
Michael Moll – Lausanne, 29. January 2007 -9-
RD50 The CERN RD50 Collaborationhttp://www.cern.ch/rd50
• Collaboration formed in November 2001• Experiment approved as RD50 by CERN in June 2002• Main objective:
• Presently 264 members from 52 institutes
Development of ultra-radiation hard semiconductor detectors for the luminosity upgrade of the LHC to 1035 cm-2s-1 (“Super-LHC”).
Challenges: - Radiation hardness up to 1016 cm-2 required- Fast signal collection (Going from 25ns to 10 ns bunch crossing ?)- Low mass (reducing multiple scattering close to interaction point)- Cost effectiveness (big surfaces have to be covered with detectors!)
RD50: Development of Radiation Hard Semiconductor Devices for High Luminosity Colliders
Belarus (Minsk), Belgium (Louvain), Canada (Montreal), Czech Republic (Prague (3x)), Finland (Helsinki, Lappeenranta), Germany (Berlin, Dortmund, Erfurt, Freiburg, Hamburg, Karlsruhe),
Israel (Tel Aviv), Italy (Bari, Bologna, Florence, Padova, Perugia, Pisa, Trento, Turin), Lithuania (Vilnius), The Netherlands (Amsterdam), Norway (Oslo (2x)), Poland (Warsaw (2x)), Romania (Bucharest (2x)), Russia
(Moscow), St.Petersburg), Slovenia (Ljubljana), Spain (Barcelona, Valencia), Switzerland (CERN, PSI), Ukraine (Kiev), United Kingdom (Diamond, Exeter, Glasgow, Lancaster, Liverpool, Sheffield),
USA (Fermilab, Purdue University, Rochester University, SCIPP Santa Cruz, Syracuse University, BNL, University of New Mexico)
Michael Moll – Lausanne, 29. January 2007 -10-
RD50 Outline
• Motivation to develop radiation harder detectors
• Introduction to the RD50 collaboration
•Part I: Radiation Damage in Silicon Detectors (A very brief review)
• Microscopic defects (changes in bulk material)• Macroscopic damage (changes in detector properties)
• Part II: RD50 - Approaches to obtain radiation hard sensors• Material Engineering• Device Engineering
• Summary and preliminary conclusion
Michael Moll – Lausanne, 29. January 2007 -11-
RD50 Radiation Damage – Microscopic Effects
particle
SiSVacancy
+ Interstitial
point defects (V-O, C-O, .. )
point defects and clusters of defects
EK>25 eV
EK > 5 keV
V
I
I
I
V
V
♦ Spatial distribution of vacancies created by a 50 keV Si-ion in silicon.(typical recoil energy for 1 MeV neutrons)
van Lint 1980
M.Huhtinen 2001
Michael Moll – Lausanne, 29. January 2007 -12-
RD50 Radiation Damage – Microscopic Effects
particle
SiSVacancy
+ Interstitial
point defects (V-O, C-O, .. )
point defects and clusters of defects
EK>25 eV
EK > 5 keV
V
I
•Neutrons (elastic scattering)• En > 185 eV for displacement• En > 35 keV for cluster
•60Co-gammas•Compton Electronswith max. Eγ ≈1 MeV(no cluster production)
•Electrons•Ee > 255 keV for displacement•Ee > 8 MeV for cluster
Only point defects point defects & clusters Mainly clusters
10 MeV protons 24 GeV/c protons 1 MeV neutronsSimulation:
Initial distribution of vacancies in (1µm)3
after 1014 particles/cm2
[Mika Huhtinen NIMA 491(2002) 194]
Michael Moll – Lausanne, 29. January 2007 -13-
RD50 Primary Damage and secondary defect formation
• Two basic defectsI - Silicon Interstitial V - Vacancy
• Primary defect generationI, I2 higher order I (?)
⇒ I -CLUSTER (?)V, V2, higher order V (?)
⇒ V -CLUSTER (?)
• Secondary defect generation
Main impurities in silicon: Carbon (Cs)Oxygen (Oi)
I+Cs → Ci ⇒ Ci+Cs → CiCSCi+Oi → CiOiCi+Ps → CiPS
V+V → V2 V+V2 → V3 V+Oi → VOi ⇒ V+VOi → V2OiV+Ps → VPs
I+V2 → V I+VOi → Oi .......................
I
I
V
V
Damage?! (“V2O-model”)
Damage?!
Michael Moll – Lausanne, 29. January 2007 -14-
RD50 Example of defect spectroscopyExample of defect spectroscopy-- neutron irradiated neutron irradiated --
50 100 150 200 250Temperature [ K ]
-0.6
-0.4
-0.2
0
0.2
0.4
0.6
0.8
DLT
S-sig
nal (
b 1) [
pF]
60 min 60 min170 days170 days
CiCs(-/0)CiCs(-/0)
VOi(-/0)VOi(-/0)
VV(--/-)VV(--/-)
Ci(-/0)Ci(-/0)
CiOi(+/0)CiOi(+/0)
H(220K)H(220K)
Ci(+/0)Ci(+/0)
E(40K)E(40K)E(45K)E(45K)
E(35K)E(35K)
? + VV(-/0) + ?? + VV(-/0) + ? Introduction RatesNt/Φeq:
Ci :1.55 cm-1
CiCs : CiOi :0.40 cm-1 1.10 cm-1
Introduction rates of main defects ≈ 1 cm-1
Introduction rate of negative space charge ≈ 0.05 cm-1
example : Φeq = 1×1014 cm-2
defects ≈ 1×1014 cm-3
space charge ≈ 5×1012cm-3
Deep Level Transient Spectroscopy
Michael Moll – Lausanne, 29. January 2007 -15-
RD50 Impact of Defects on Detector properties
ShockleyShockley--ReadRead--Hall statistics Hall statistics (standard theory)(standard theory)
Trapping (e and h)⇒ CCE
shallow defects do not contribute at room
temperature due to fast detrapping
charged defects ⇒ Neff , Vdep
e.g. donors in upper and acceptors in lower half of band
gap
generation⇒ leakage current
Levels close to midgap
most effective
enhanced generation⇒ leakage current
⇒ space charge
InterInter--center chargecenter chargetransfer model transfer model
(inside clusters only)(inside clusters only)
Impact on detector properties can be calculated if all defect paImpact on detector properties can be calculated if all defect parameters are known:rameters are known:σσn,pn,p : cross sections : cross sections ∆∆E : ionization energy E : ionization energy NNtt : concentration: concentration
Michael Moll – Lausanne, 29. January 2007 -16-
RD50 Reverse biased abrupt pReverse biased abrupt p++--n junctionn junction
depleted zone
neutral bulk(no electric field)
Poisson’s equationPositive space charge, Neff =[P](ionized Phosphorus atoms)
Electrical Electrical charge densitycharge density
Electrical Electrical field strengthfield strength
Electron Electron potential energypotential energy
( ) effNqxdxd
⋅=−0
02
2
εεφ
2
0
0 dNqV effdep ⋅⋅=εε
effective space charge density
depletion voltage
Full charge collection only for VB>Vdep !
particle (mip)
+V <VB dep +V >VB dep
Michael Moll – Lausanne, 29. January 2007 -17-
RD50 Macroscopic Effects – I. Depletion Voltage
Change of Depletion Voltage Vdep (Neff)…. with particle fluence:
before inversion
after inversion
n+ p+ n+
• “Type inversion”: Neff changes from positive to negative (Space Charge Sign Inversion)
10-1 100 101 102 103
Φeq [ 1012 cm-2 ]
1
510
50100
5001000
5000
Ude
p [V
] (d
= 3
00µm
)
10-1
100
101
102
103
| Nef
f | [
1011
cm
-3 ]
≈ 600 V
1014cm-2
type inversion
n-type "p-type"
[M.Moll: Data: R. Wunstorf, PhD thesis 1992, Uni Hamburg]
• Short term: “Beneficial annealing”• Long term: “Reverse annealing”
- time constant depends on temperature:~ 500 years (-10°C)~ 500 days ( 20°C)~ 21 hours ( 60°C)
- Consequence: Detectors must be cooledeven when the experiment is not running!
…. with time (annealing):
NC
NC0
gC Φeq
NYNA
1 10 100 1000 10000annealing time at 60oC [min]
0
2
4
6
8
10
∆ N
eff [
1011
cm-3
]
[M.Moll, PhD thesis 1999, Uni Hamburg]
p+
Michael Moll – Lausanne, 29. January 2007 -18-
RD50 Radiation Damage – II. Leakage Current
1011 1012 1013 1014 1015
Φeq [cm-2]10-6
10-5
10-4
10-3
10-2
10-1
∆I /
V
[A/c
m3 ]
n-type FZ - 7 to 25 KΩcmn-type FZ - 7 KΩcmn-type FZ - 4 KΩcmn-type FZ - 3 KΩcm
n-type FZ - 780 Ωcmn-type FZ - 410 Ωcmn-type FZ - 130 Ωcmn-type FZ - 110 Ωcmn-type CZ - 140 Ωcm
p-type EPI - 2 and 4 KΩcm
p-type EPI - 380 Ωcm
[M.Moll PhD Thesis][M.Moll PhD Thesis]
• Damage parameter α (slope in figure)
Leakage currentper unit volume
and particle fluence
• α is constant over several orders of fluenceand independent of impurity concentration in Si
can be used for fluence measurement
eqVI
Φ⋅∆
=α
80 min 60°C
Change of Leakage Current (after hadron irradiation)…. with particle fluence:
• Leakage current decreasing in time (depending on temperature)
• Strong temperature dependence
Consequence:Cool detectors during operation!Example: I(-10°C) ~1/16 I(20°C)
1 10 100 1000 10000annealing time at 60oC [minutes]
0
1
2
3
4
5
6
α(t)
[10-1
7 A/c
m]
1
2
3
4
5
6
oxygen enriched silicon [O] = 2.1017 cm-3
parameterisation for standard silicon [M.Moll PhD Thesis]
80 min 60°C
…. with time (annealing):
⎟⎠⎞
⎜⎝⎛−∝ Tk
EIB
g2exp
Michael Moll – Lausanne, 29. January 2007 -19-
RD50 Radiation Damage – III. CCE (Trapping)
Deterioration of Charge Collection Efficiency (CCE) by trapping
Trapping is characterized by an effective trapping time τeff for electrons and holes:
⎟⎟⎠
⎞⎜⎜⎝
⎛⋅−= tQtQ
heeffhehe
,,0,
1exp)(τ defects
heeff
N∝,
1τwhere
0 2.1014 4.1014 6.1014 8.1014 1015
particle fluence - Φeq [cm-2]
0
0.1
0.2
0.3
0.4
0.5
Inve
rse
trapp
ing
time
1/τ
[ns-1
]
data for electronsdata for electronsdata for holesdata for holes
24 GeV/c proton irradiation24 GeV/c proton irradiation
[M.Moll; Data: O.Krasel, PhD thesis 2004, Uni Dortmund][M.Moll; Data: O.Krasel, PhD thesis 2004, Uni Dortmund]
Increase of inverse trapping time (1/τ) with fluence ….. and change with time (annealing):
5 101 5 102 5 103
annealing time at 60oC [min]
0.1
0.15
0.2
0.25
Inve
rse
trapp
ing
time
1/τ
[ns-1
]
data for holesdata for holesdata for electronsdata for electrons
24 GeV/c proton irradiation24 GeV/c proton irradiationΦeq = 4.5.1014 cm-2 Φeq = 4.5.1014 cm-2
[M.Moll; Data: O.Krasel, PhD thesis 2004, Uni Dortmund][M.Moll; Data: O.Krasel, PhD thesis 2004, Uni Dortmund]
Michael Moll – Lausanne, 29. January 2007 -20-
RD50 Summary: Radiation Damage in Silicon Sensors
Two general types of radiation damage to the detector materials:
• Bulk (Crystal) damage due to Non Ionizing Energy Loss (NIEL)- displacement damage, built up of crystal defects –
I. Change of effective doping concentration (higher depletion voltage, under- depletion)
II. Increase of leakage current (increase of shot noise, thermal runaway)
III. Increase of charge carrier trapping (loss of charge)
• Surface damage due to Ionizing Energy Loss (IEL)- accumulation of positive in the oxide (SiO2) and the Si/SiO2 interface –
affects: interstrip capacitance (noise factor), breakdown behavior, …
Impact on detector performance and Charge Collection Efficiency(depending on detector type and geometry and readout electronics!)
Signal/noise ratio is the quantity to watch ⇒ Sensors can fail from radiation damage !
Same for all tested Silicon
materials!
Influenced by impuritiesin Si – Defect Engineeringis possible!
Can be optimized!
Michael Moll – Lausanne, 29. January 2007 -21-
RD50 Outline
• Motivation to develop radiation harder detectors
• Introduction to the RD50 collaboration
• Part I: Radiation Damage in Silicon Detectors (A very brief review)• Microscopic defects (changes in bulk material)• Macroscopic damage (changes in detector properties)
• Part II: RD50 - Approaches to obtain radiation hard sensors• Material Engineering• Device Engineering
• Summary and preliminary conclusion
Michael Moll – Lausanne, 29. January 2007 -22-
RD50 Approaches of RD50 to develop radiation harder tracking detectors
• Defect Engineering of Silicon• Understanding radiation damage
• Macroscopic effects and Microscopic defects• Simulation of defect properties and defect kinetics• Irradiation with different particles at different energies
• Oxygen rich silicon• DOFZ, Cz, MCZ, EPI
• Oxygen dimer enriched silicon• Hydrogen enriched silicon• Pre-irradiated silicon• Influence of processing technology
• New Materials• Silicon Carbide (SiC), Gallium Nitride (GaN)• Diamond: CERN RD42 Collaboration
• Device Engineering (New Detector Designs)• p-type silicon detectors (n-in-p)• Thin detectors• 3D and Semi 3D detectors• Cost effective detectors• Simulation of highly irradiated detectors
Scientific strategies:
I. Material engineering
II. Device engineering
III. Variation of detectoroperational conditions
CERN-RD39“Cryogenic Tracking Detectors”
Michael Moll – Lausanne, 29. January 2007 -23-
RD50 Defect Engineering of Silicon
• Influence the defect kinetics by incorporation of impurities or defects
• Best example: Oxygen
Initial idea: Incorporate Oxygen to getter radiation-induced vacancies⇒ prevent formation of Di-vacancy (V2) related deep acceptor levels
Observation: Higher oxygen content ⇒ less negative space charge(less charged acceptors)
• One possible mechanism: V2O is a deep acceptor
O VO (not harmful at room temperature)V
VO V2O (negative space charge) V2O(?)
Ec
EV
VO
V2 in clusters
Michael Moll – Lausanne, 29. January 2007 -24-
RD50 Spectacular Improvement of γ-irradiation tolerance
• No type inversion for oxygen enriched silicon!• Slight increase of positive space charge
(due to Thermal Donor generation?)
[E.Fretwurst et al. 1st RD50 Workshop] See also:- Z.Li et al. [NIMA461(2001)126]- Z.Li et al. [1st RD50 Workshop]
0 200 400 600 800 1000dose [Mrad]
0
50
100
150
200
250
Vde
p [V
]
0
10
20
30
40
Nef
f [10
11 c
m-3
]
CA: <111> STFZ CA: <111> STFZ CB: <111> DOFZ 24 hCB: <111> DOFZ 24 hCC: <111>DOFZ 48 hCC: <111>DOFZ 48 hCD: <111> DOFZ 72 hCD: <111> DOFZ 72 hCE: <100> STFZCE: <100> STFZCF: <100> DOFZ 24hCF: <100> DOFZ 24hCG: <100> DOFZ 48hCG: <100> DOFZ 48hCH: <100> DOFZ 72hCH: <100> DOFZ 72h
(a)(a)
Depletion Voltage
0 200 400 600 800 1000dose [Mrad]
0
500
1000
1500
I rev [
nA]
CA: <111> STFZCA: <111> STFZCB: <111> DOFZ 24hCB: <111> DOFZ 24hCC: <111> DOFZ 48hCC: <111> DOFZ 48hCD: <111> DOFZ 78hCD: <111> DOFZ 78h
(b)(b)
CE: <100> STFZ CE: <100> STFZ CF: <100> DOFZ 24hCF: <100> DOFZ 24hCG: <100> DOFZ 48hCG: <100> DOFZ 48hCH: <100> DOFZ 72hCH: <100> DOFZ 72h
(b)
• Leakage increase not linear and depending on oxygen concentration
Leakage Current
Michael Moll – Lausanne, 29. January 2007 -25-
RD50 Characterization of microscopic defects- γ and proton irradiated silicon detectors -
• 2003: Major breakthrough on γ-irradiated samples• For the first time macroscopic changes of the depletion voltage and leakage current
can be explained by electrical properties of measured defects !
• since 2004: Big steps in understanding the improved radiation tolerance ofoxygen enriched and epitaxial silicon after proton irradiation
[APL, 82, 2169, March 2003]
Almost independent of oxygen content:• Donor removal•“Cluster damage” ⇒ negative charge
Influenced by initial oxygen content:• I–defect: deep acceptor level at EC-0.54eV
(good candidate for the V2O defect)⇒ negative charge
Influenced by initial oxygen dimer content (?):• BD-defect: bistable shallow thermal donor
(formed via oxygen dimers O2i)⇒ positive charge
Levels responsible for depletion voltage changes after proton irradiation:
ΒD-defect I-defect
[I.Pintilie, RESMDD, Oct.2004]
Michael Moll – Lausanne, 29. January 2007 -26-
RD50 Oxygen enriched silicon – DOFZ- proton irradiation -
• DOFZ (Diffusion Oxygenated Float Zone Silicon) 1982 First oxygen diffusion tests on FZ [Brotherton et al. J.Appl.Phys.,Vol.53, No.8.,5720]
1995 First tests on detector grade silicon [Z.Li et al. IEEE TNS Vol.42,No.4,219]
1999 Introduced to the HEP community by RD48 (ROSE)
0 1 2 3 4 5Φ24 GeV/c proton [1014 cm-2]
0
2
4
6
8
10
|Nef
f| [1
012cm
-3]
100
200
300
400
500
600
Vde
p [V
] (30
0 µm
)
Carbon-enriched (P503)Standard (P51)
O-diffusion 24 hours (P52)O-diffusion 48 hours (P54)O-diffusion 72 hours (P56)
Carbonated
Standard
Oxygenated
[RD48-NIMA 465(2001) 60]
http://cern.ch/rd48
ROSERD48
First tests in 1999 show clear advantage of oxygenation
Later systematic tests reveal strong variations with no clear dependence
on oxygen content
0 2 4 6 8 10Φ 24G eV /c pro ton [1014 cm -2]
0123456789
10
|Nef
f| [1
012cm
-3]
100
200
300
400
500
600
700
Vde
p [V
] (30
0 µm
)15 K Ω cm <111> - oxygenated
15 K Ω cm <111> - standard
[M .M oll - N IM A 511 (2003) 97]
However, only non-oxygenated diodes show a “bad” behavior.
Michael Moll – Lausanne, 29. January 2007 -27-
RD50 Silicon Growth Processes
Single crystal silicon
Poly silicon
RF Heating coil
Float Zone Growth
• Czochralski Silicon (CZ)• Floating Zone Silicon (FZ)
Czochralski Growth
• Basically all silicon detectors made out of high resistivety FZ silicon
• Epitaxial Silicon (EPI)
• The growth method used by the IC industry.
• Difficult to producevery high resistivity
• Chemical-Vapor Deposition (CVD) of Si• up to 150 µm thick layers produced• growth rate about 1µm/min
Michael Moll – Lausanne, 29. January 2007 -28-
RD50 Oxygen concentration in FZ, CZ and EPI
0 10 20 30 40 50 60 70 80 90 100Depth [µm]
51016
51017
51018
5
O-c
once
ntra
tion
[1/c
m3 ]
SIMS 25 µm SIMS 25 µm
25 m
u25
mu
SIMS 50 µmSIMS 50 µm
50 m
u50
mu
SIMS 75 µmSIMS 75 µm
75 m
u75
mu
simulation 25 µmsimulation 25 µmsimulation 50 µmsimulation 50 µmsimulation 75µmsimulation 75µm
DOFZ and CZ silicon Epitaxial silicon
• EPI: Oi and O2i (?) diffusion from substrateinto epi-layer during production
• EPI: in-homogeneous oxygen distribution
[G.Lindström et al.,10th European Symposium on Semiconductor Detectors, 12-16 June 2005]
• DOFZ: inhomogeneous oxygen distribution• DOFZ: oxygen content increasing with time
at high temperature
EPIlayer CZ substrate
0 50 100 150 200 250depth [µm]
51016
51017
51018
O-c
once
ntra
tion
[cm
-3]
51016
51017
51018
5
DOFZ 72h/1150oCDOFZ 48h/1150oCDOFZ 24h/1150oC
Data: G.Lindstroem et al.
[M.Moll]
• CZ: high Oi (oxygen) and O2i (oxygen dimer)concentration (homogeneous)
• CZ: formation of Thermal Donors possible !
0 50 100 150 200 250depth [µm]
51016
51017
51018
O-c
once
ntra
tion
[cm
-3]
51016
51017
51018
5
Cz as grown
DOFZ 72h/1150oCDOFZ 48h/1150oCDOFZ 24h/1150oC
Data: G.Lindstroem et al.
[M.Moll]
Michael Moll – Lausanne, 29. January 2007 -29-
RD50 Silicon Materials under Investigation by RD50
Material Symbol ρ (Ωcm) [Oi] (cm-3)
Standard FZ (n- and p-type) FZ 1–7×10 3 < 5×1016
Diffusion oxygenated FZ (n- and p-type) DOFZ 1–7×10 3 ~ 1–2×1017
Magnetic Czochralski Si, Okmetic, Finland(n- and p-type)
MCz ~ 1×10 3 ~ 5×1017
Diffusion oxygenated Epitaxial layers on CZ EPI–DO 50 – 100 ~ 7×1017
Czochralski Si, Sumitomo, Japan (n-type) Cz ~ 1×10 3 ~ 8-9×1017
Epitaxial layers on Cz-substrates, ITME, Poland(n- and p-type, 25, 50, 75, 150 µm thick)
EPI 50 – 400 < 1×1017
• DOFZ silicon - Enriched with oxygen on wafer level, inhomogeneous distribution of oxygen
• CZ/MCZ silicon - high Oi (oxygen) and O2i (oxygen dimer) concentration (homogeneous)- formation of shallow Thermal Donors possible
• Epi silicon - high Oi , O2i content due to out-diffusion from the CZ substrate (inhomogeneous)- thin layers: high doping possible (low starting resistivity)
• Epi-Do silicon - as EPI, however additional Oi diffused reaching homogeneous Oi content
standardfor
particledetectors
used for LHC Pixel
detectors
“new”material
Michael Moll – Lausanne, 29. January 2007 -30-
RD50 Standard FZ, DOFZ, Cz and MCz Silicon
24 GeV/c proton irradiation
• Standard FZ silicon• type inversion at ~ 2×1013 p/cm2
• strong Neff increase at high fluence
• Oxygenated FZ (DOFZ)• type inversion at ~ 2×1013 p/cm2
• reduced Neff increase at high fluence
• CZ silicon and MCZ siliconno type inversion in the overall fluence range (verified by TCT measurements) (verified for CZ silicon by TCT measurements, preliminary result for MCZ silicon)⇒ donor generation overcompensates acceptor generation in high fluence range
• Common to all materials (after hadron irradiation):reverse current increaseincrease of trapping (electrons and holes) within ~ 20%
0 2 4 6 8 10proton fluence [1014 cm-2]
0
200
400
600
800
Vde
p (30
0µm
) [V
]0
2
4
6
8
10
12
|Nef
f| [1
012 c
m-3
]
FZ <111>FZ <111>DOFZ <111> (72 h 11500C)DOFZ <111> (72 h 11500C)MCZ <100>MCZ <100> CZ <100> (TD killed) CZ <100> (TD killed)
Michael Moll – Lausanne, 29. January 2007 -31-
RD50• Epitaxial silicon
• Layer thickness: 25, 50, 75 µm (resistivity: ~ 50 Ωcm); 150 µm (resistivity: ~ 400 Ωcm)• Oxygen: [O] ≈ 9×1016cm-3; Oxygen dimers (detected via IO2-defect formation)
EPI Devices – Irradiation experiments
• Only little change in depletion voltage
• No type inversion up to ~ 1016 p/cm2 and ~ 1016 n/cm2
high electric field will stay at front electrode!reverse annealing will decreases depletion voltage!
• Explanation: introduction of shallow donors is biggerthan generation of deep acceptors
G.Lindström et al.,10th European Symposium on Semiconductor Detectors, 12-16 June 2005G.Kramberger et al., Hamburg RD50 Workshop, August 2006
0 2.1015 4.1015 6.1015 8.1015 1016
Φeq [cm-2]
0
1014
2.1014
Nef
f(t0)
[cm
-3]
25 µm, 80 oC25 µm, 80 oC50 µm, 80 oC50 µm, 80 oC75 µm, 80 oC75 µm, 80 oC
23 GeV protons23 GeV protons
≈320V (75µm)
≈105V (25µm)
≈230V (50µm)
• CCE (Sr90 source, 25ns shaping):6400 e (150 µm; 2x1015 n/cm-2)3300 e (75µm; 8x1015 n/cm-2)2300 e (50µm; 8x1015 n/cm-2)
0 20 40 60 80 100Φeq [1014 cm-2]
0
2000
4000
6000
8000
10000
12000
Sign
al [e
]
150 µm - neutron irradiated 75 µm - proton irradiated 75 µm - neutron irradiated 50 µm - neutron irradiated 50 µm - proton irradiated
[M.Moll]
[Data: G.Kramberger et al., Hamburg RD50 Workshop, August 2006]
Michael Moll – Lausanne, 29. January 2007 -32-
RD50 Advantage of non-inverting materialp-in-n detectors (schematic figures!)
Fully depleted detector(non – irradiated):
Michael Moll – Lausanne, 29. January 2007 -33-
RD50
inverted to “p-type”, under-depleted:
• Charge spread – degraded resolution
• Charge loss – reduced CCE
Advantage of non-inverting materialp-in-n detectors (schematic figures!)
Fully depleted detector(non – irradiated):
heavy irradiation
inverted
non-inverted, under-depleted:
•Limited loss in CCE
•Less degradation with under-depletion
non inverted
Be careful, this is a very schematic explanation, reality is more complex !
Michael Moll – Lausanne, 29. January 2007 -34-
RD50 Epitaxial silicon - Annealing• 50 µm thick silicon detectors:
- Epitaxial silicon (50Ωcm on CZ substrate, ITME & CiS) - Thin FZ silicon (4KΩcm, MPI Munich, wafer bonding technique)
100 101 102 103 104 105
annealing time [min]
0
50
100
150
Vfd
[V]
EPI (ITME), 9.6.1014 p/cm2EPI (ITME), 9.6.1014 p/cm2
FZ (MPI), 1.7.1015 p/cm2FZ (MPI), 1.7.1015 p/cm2
Ta=80oCTa=80oC
[E.Fretwurst et al., Hamburg][E.Fretwurst et al., Hamburg]
0 20 40 60 80 100proton fluence [1014 cm-2]
0
50
100
150
200
250
Vde
p [V
]
0.20.40.60.81.01.21.4
|Nef
f| [1
014 c
m-3
]
EPI (ITME), 50µmEPI (ITME), 50µmFZ (MPI), 50µmFZ (MPI), 50µm
Ta=80oCTa=80oCta=8 minta=8 min
[E.Fretwurst et al.,RESMDD - October 2004]
• Thin FZ silicon: Type inverted, increase of depletion voltage with time• Epitaxial silicon: No type inversion, decrease of depletion voltage with time
⇒ No need for low temperature during maintenance of SLHC detectors!
Michael Moll – Lausanne, 29. January 2007 -35-
RD50 New Materials: Epitaxial SiC“A material between Silicon and Diamond”
Property Diamond GaN 4H SiC Si Eg [eV] 5.5 3.39 3.3 1.12 Ebreakdown [V/cm] 107 4·106 2.2·106 3·105 µe [cm2/Vs] 1800 1000 800 1450 µh [cm2/Vs] 1200 30 115 450 vsat [cm/s] 2.2·107 - 2·107 0.8·107 Z 6 31/7 14/6 14 εr 5.7 9.6 9.7 11.9 e-h energy [eV] 13 8.9 7.6-8.4 3.6 Density [g/cm3] 3.515 6.15 3.22 2.33 Displacem. [eV] 43 ≥15 25 13-20
• Wide bandgap (3.3eV) ⇒ lower leakage current
than silicon
• Signal:Diamond 36 e/µmSiC 51 e/µmSi 89 e/µm
⇒ more charge than diamond
• Higher displacement threshold than silicon
⇒ radiation harder than silicon (?)
R&D on diamond detectors:RD42 – Collaboration
http://cern.ch/rd42/
Michael Moll – Lausanne, 29. January 2007 -36-
RD50 SiC: CCE after neutron irradiation
• CCE before irradiation• 100 % with α particles and MIPS
• CCE after irradiation (example)• material produced by CREE• 55 µm thick layer• neutron irradiated samples• tested with β particles
• Conclusion:• SiC is less radiation tolerant than
expected
• Consequence:• RD50 will stop working on this topic
0.1 1E14 1E15 1E160
1000
2000
3000
Before irradiation
Col
lect
ed C
harg
e ( e
- )Fluence ((1MeV) n/cm2)
@ 950 V
[F.Moscatelli, Bologna, December 2006]
Michael Moll – Lausanne, 29. January 2007 -37-
RD50 Outline
• Motivation to develop radiation harder detectors
• Introduction to the RD50 collaboration
• Part I: Radiation Damage in Silicon Detectors (A very brief review)• Microscopic defects (changes in bulk material)• Macroscopic damage (changes in detector properties)
• Part II: RD50 - Approaches to obtain radiation hard sensors• Material Engineering• Device Engineering
• Summary and preliminary conclusion
Michael Moll – Lausanne, 29. January 2007 -38-
RD50 Device engineeringp-in-n versus n-in-p detectors
p-type silicon after high fluences:n-type silicon after high fluences:
p-on-n silicon, under-depleted:
• Charge spread – degraded resolution
• Charge loss – reduced CCE
p+on-n
n-on-p silicon, under-depleted:
•Limited loss in CCE
•Less degradation with under-depletion
•Collect electrons (fast)
n+on-p
Be careful, this is a very schematic explanation,reality is more complex !
Michael Moll – Lausanne, 29. January 2007 -39-
RD50 n-in-p microstrip detectors
n-in-p: - no type inversion, high electric field stays on structured side- collection of electrons
0 2 4 6 8 10fluence [1015cm-2]
0
5
10
15
20
25
CCE
(103 e
lect
rons
)
24 GeV/c p irradiation24 GeV/c p irradiation
[M.Moll][M.Moll]
[Data: G.Casse et al., NIMA535(2004) 362][Data: G.Casse et al., NIMA535(2004) 362]
• n-in-p microstrip detectors (280µm) on p-type FZ silicon• Detectors read-out with 40MHz
CCE ~ 6500 e (30%)after 7.5 1015 p cm-2
at 900V
0 100 200 300 400 500time at 80oC[min]
0 500 1000 1500 2000 2500time [days at 20oC]
02468
101214161820
CCE
(103 e
lect
rons
) 800 V800 V
1.1 x 1015cm-2 1.1 x 1015cm-2 500 V500 V
3.5 x 1015cm-2 (500 V)3.5 x 1015cm-2 (500 V)
7.5 x 1015cm-2 (700 V)7.5 x 1015cm-2 (700 V)
M.MollM.Moll[Data: G.Casse et al., to be published in NIMA][Data: G.Casse et al., to be published in NIMA]
• no reverse annealing visible in the CCE measurement !e.g. for 7.5 × 1015 p/cm2 increase of Vdep from
Vdep~ 2800V to Vdep > 12000V is expected !
Michael Moll – Lausanne, 29. January 2007 -40-
RD50 3D detector - concepts Introduced by: S.I. Parker et al., NIMA 395 (1997) 328
• “3D” electrodes: - narrow columns along detector thickness,- diameter: 10µm, distance: 50 - 100µm
• Lateral depletion:- lower depletion voltage needed- thicker detectors possible- fast signal- radiation hard
n-columns p-columnswafer surface
n-type substrate
p+
------
++++
++++
--
--
++
300
µm
n+
p+
50 µm
------
++ ++++++
----
++
3D PLANARp+
Michael Moll – Lausanne, 29. January 2007 -41-
RD50 3D detector - concepts
• “3D” electrodes: - narrow columns along detector thickness,- diameter: 10µm, distance: 50 - 100µm
• Lateral depletion:- lower depletion voltage needed- thicker detectors possible- fast signal- radiation hard
n-columns p-columns wafer surface
n-type substrate
• Simplified 3D architecture • n+ columns in p-type substrate, p+ backplane• operation similar to standard 3D detector
• Simplified process • hole etching and doping only done once• no wafer bonding technology needed
• Simulations performed• Fabrication:
• IRST(Italy), CNM Barcelona
[C. Piemonte et al., NIM A541 (2005) 441]
hole
hole metal strip
C.Piemonte et al., STD06, September 2006
Hole depth 120-150µmHole diameter ~10µm
• First CCE tests under way
Michael Moll – Lausanne, 29. January 2007 -42-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
• In the following: Comparison of collected charge as published in literature
• Be careful: Values obtained partly under different conditions• irradiation• temperature of measurement• electronics used (shaping time, noise)• type of device – strip detectors or pad detectors
⇒ This comparison gives only an indication of which material/technology could be used, to be more specific, the exact application should be looked at!
• Remember: The obtained signal has still to be compared to the noise
• Acknowledgements:
• Recent data collections: Mara Bruzzi (Hiroschima conference 2006)
Cinzia Da Via (Vertex conference 2006)
Michael Moll – Lausanne, 29. January 2007 -43-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
0
1000
2000
3000
4000sig
nal [
elec
trons
]
SiC, n-type, 55 µm, (RT, 2.5µs) [Moscatelli et al. 2006]
[M.Moll 2007]
4H-SiC layer, 55µm, pad detector24 GeV/c protonsSr-90 source, 2.5 µs shaping, room temperature mean values presented
sample:irradiation:
measurement:analysis:
Michael Moll – Lausanne, 29. January 2007 -44-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
0
1000
2000
3000
4000
5000
6000sig
nal [
elec
trons
]
pCVD-Diamond, 500µm, (RT, µs) [RD42 2002]SiC, n-type, 55 µm, (RT, 2.5µs) [Moscatelli et al. 2006]
[M.Moll 2007]
polycrystal, 500µm thick, strip24 GeV/c protonstestbeam, µs shapingmost probable values
sample:irradiation:
measurement:analysis:
Michael Moll – Lausanne, 29. January 2007 -45-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
01000200030004000500060007000
signa
l [el
ectro
ns]
pCVD-Diamond, 500µm, (RT, µs) [RD42 2005]pCVD-Diamond, 500µm, (RT, µs) [RD42 2002]SiC, n-type, 55 µm, (RT, 2.5µs) [Moscatelli et al. 2006]
[M.Moll 2007]
polycrystal, 500µm thick, strip24 GeV/c protonstestbeam, µs shapingmost probable values
sample:irradiation:
measurement:analysis:
Michael Moll – Lausanne, 29. January 2007 -46-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
0
2000
4000
6000
8000
10000sig
nal [
elec
trons
]
pCVD-Diamond, 500µm, (RT, µs) [RD42 2006]pCVD-Diamond, 500µm, (RT, µs) [RD42 2005]pCVD-Diamond, 500µm, (RT, µs) [RD42 2002]SiC, n-type, 55 µm, (RT, 2.5µs) [Moscatelli et al. 2006]
[M.Moll 2007]
polycrystal, 500µm thick, strip24 GeV/c protonstestbeam, µs shapingmost probable values
sample:irradiation:
measurement:analysis:
Diamond quality increasing [2000-2006]
Michael Moll – Lausanne, 29. January 2007 -47-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
0
2000
4000
6000
8000
10000sig
nal [
elec
trons
]
pCVD-Diamond, 500µm, (RT, µs) [RD42 2002-2006] (scaled)SiC, n-type, 55 µm, (RT, 2.5µs) [Moscatelli et al. 2006]
[M.Moll 2007]
polycrystal, 500µm thick, strip24 GeV/c protonstestbeam, µs shapingmost probable values
sample:irradiation:
measurement:analysis:
Michael Moll – Lausanne, 29. January 2007 -48-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
0
2000
4000
6000
8000
10000
12000sig
nal [
elec
trons
] pCVD-Diamond, 500µm, (RT, µs), strip, [RD42 2002-2006] (scaled)n-epi Si, 150 µm, (-30oC, 25ns), pad [Kramberger 2006]n-epi Si, 75 µm, (-30oC, 25ns), pad [Kramberger 2006]SiC, n-type, 55 µm, (RT, 2.5µs), pad [Moscatelli et al. 2006]
[M.Moll 2007]
Michael Moll – Lausanne, 29. January 2007 -49-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
0
5000
10000
15000
20000
25000sig
nal [
elec
trons
]
p-FZ Si, 280 µm, (-30oC, 25ns), strip [Casse 2004]p-MCZ Si, 300 µm, (-30oC, µs), pad [Bruzzi 2006]n-epi Si, 150 µm, (-30oC, 25ns), pad [Kramberger 2006]n-epi Si, 75 µm, (-30oC, 25ns), pad [Kramberger 2006]pCVD-Diamond, 500µm, (RT, µs), strip, [RD42 2002-2006] (scaled)SiC, n-type, 55 µm, (RT, 2.5µs), pad [Moscatelli et al. 2006]
[M.Moll 2007]
Michael Moll – Lausanne, 29. January 2007 -50-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
0
5000
10000
15000
20000
25000sig
nal [
elec
trons
]
3D FZ Si, 235 µm, (laser injection, scaled!), pad [Da Via 2006]p-FZ Si, 280 µm, (-30oC, 25ns), strip [Casse 2004]p-MCZ Si, 300 µm, (-30oC, µs), pad [Bruzzi 2006]n-epi Si, 150 µm, (-30oC, 25ns), pad [Kramberger 2006]n-epi Si, 75 µm, (-30oC, 25ns), pad [Kramberger 2006]pCVD-Diamond, 500µm, (RT, µs), strip, [RD42 2002-2006] (scaled)SiC, n-type, 55 µm, (RT, 2.5µs), pad [Moscatelli et al. 2006]
[M.Moll 2007]
Michael Moll – Lausanne, 29. January 2007 -51-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
0 20 40 60 80 100 120Φeq [1014 cm-2]
0
5000
10000
15000
20000
25000sig
nal [
elec
trons
]
3D FZ Si, 235 µm, (laser injection, scaled!), pad [Da Via 2006]p-FZ Si, 280 µm, (-30oC, 25ns), strip [Casse 2004]p-MCZ Si, 300 µm, (-30oC, µs), pad [Bruzzi 2006]n-epi Si, 150 µm, (-30oC, 25ns), pad [Kramberger 2006]n-epi Si, 75 µm, (-30oC, 25ns), pad [Kramberger 2006]sCVD-Diamond, 770µm, (RT, µs), [RD42 2006] (preliminary data, scaled)pCVD-Diamond, 500µm, (RT, µs), strip, [RD42 2002-2006] (scaled)SiC, n-type, 55 µm, (RT, 2.5µs), pad [Moscatelli et al. 2006]
[M.Moll 2007]
Michael Moll – Lausanne, 29. January 2007 -52-
RD50 Signal Charge / Threshold• Do not forget: The signal has still to be compared to the noise (the threshold)
Michael Moll – Lausanne, 29. January 2007 -53-
RD50 Summary – Radiation Damage
• Radiation Damage in Silicon Detectors• Change of Depletion Voltage (type inversion, reverse annealing, …)
(can be influenced by defect engineering!)• Increase of Leakage Current (same for all silicon materials)• Increase of Charge Trapping (same for all silicon materials)
Signal to Noise ratio is quantity to watch (material + geometry + electronics)
• Microscopic defects• Good understanding of damage after γ-irradiation (point defects)• Damage after hadron damage still to be better understood (cluster defects)
• CERN-RD50 collaboration working on:• Material Engineering (Silicon: DOFZ, CZ, EPI, other impurities,. ) (Diamond)• Device Engineering (3D and thin detectors, n-in-p, n-in-n, …)
⇒ To obtain ultra radiation hard sensors a combination of material and device engineering approaches depending on radiation environment, application and available readout electronics will be best solution
Michael Moll – Lausanne, 29. January 2007 -54-
RD50 Summary – Detectors for SLHC• At fluences up to 1015cm-2 (Outer layers of SLHC detector) the change of the depletion
voltage and the large area to be covered by detectors are major problems.
• CZ silicon detectors could be a cost-effective radiation hard solution no type inversion (to be confirmed), use cost effective p-in-n technology
• oxygenated p-type silicon microstrip detectors show very encouraging results:CCE ≈ 6500 e; Φeq
= 4×1015 cm-2, 300µm
• At the fluence of 1016cm-2 (Innermost layers of SLHC detector) the active thickness of any silicon material is significantly reduced due to trapping.
The two most promising options besides regular replacement of sensors are: Thin/EPI detectors : drawback: radiation hard electronics for low signals needed
(e.g. 2300e at Φeq 8x1015cm-2, 50µm EPI)
3D detectors : looks very promising,drawback: technology has to be optimized
• SiC and GaN have been characterized and abandoned by RD50.
Further information: http://cern.ch/rd50/
Michael Moll – Lausanne, 29. January 2007 -55-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices
1014 1015 10160
5000
10000
15000
20000
25000
# el
ectro
ns
1 MeV n fluence [cm-2]
stripspixels
p FZ Si 280µm; 25ns; -30°C [1] p-MCz Si 300µm;0.2-2.5µs; -30°C [2] n EPI Si 75µm; 25ns; -30°C [3] n EPI Si 150µm; 25ns; -30°C [3] sCVD Diam 770µm; 25ns; +20°C [4] pCVD Diam 300µm; 25ns; +20°C [4] n EPI SiC 55µm; 2.5µs; +20°C [5] 3D FZ Si 235µm [6]
[1] G. Casse et al. NIM A (2004)[2] M. Bruzzi et al. STD06, September 2006[3] G. Kramberger, RD50 Work. Prague 06[4] W: Adam et al. NIM A (2006)[5] F. Moscatelli RD50 Work.CERN 2005[6] C. Da Vià, "Hiroshima" STD06
(charge induced by laser)
Line to guide the eye for planar devices
160V
M. Bruzzi, Presented at STD6 Hiroshima Conference,Carmel, CA, September 2006
• Thick (300µm) p-type planar detectors can operate in partial depletion, collected charge higher than 12000e up to 2x1015cm-2.
• Most charge at highest fluences collected with 3D detectors• Silicon comparable or even better than diamond in terms of collected charge
(BUT: higher leakage current – cooling needed!)
Michael Moll – Lausanne, 29. January 2007 -56-
RD50 Comparison of measured collected charge on different radiation-hard materials and devices