Corning® Gorilla® Glass 3 with Native Damage Resistance™ is an alkali-aluminosilicate thin sheet glass that is better able to survive the real-world events that most commonly cause glass failure. With its new core composition, this glass enables improved damage resistance and toughness by helping to prevent the deep chips and scratches that cause glass to break. Product Information Benefits • Glass designed with improved native damage resistance, - Enhances retained strength after use - High resistance to scratch and sharp contact damage - Superior surface quality Applications • Ideal protective cover for electronic displays in: - Smartphones - Laptop and tablet computer screens - Mobile devices • Touchscreen devices • Optical components • High strength glass articles Dimensions Available thicknesses 0.4 mm - 2.0 mm Viscosity Softening Point (10 7.6 poises) 900 ˚C Annealing Point (10 13.2 poises) 628 ˚C Strain Point (10 14.7 poises) 574 ˚C Properties Density 2.39 g/cm 3 Young’s Modulus 69.3 GPa Poisson’s Ratio 0.22 Shear Modulus 28.5 GPa Vickers Hardness (200 g load) Un-strengthened 534 kgf/mm 2 Strengthened 649 kgf/mm 2 Fracture Toughness 0.66 MPa m 0.5 Coefficient of Expansion 75.8 x 10 -7 /˚C (0 ˚C - 300 ˚C) Chemical Strengthening Compressive stress ≥ 950 MPa @ 40 μm DOL Depth of Layer ≥ 50 μm Corning® Gorilla® Glass 3 with NDR™ / Product Information Sheet / E_050613 Optical Refractive Index (590 nm) Core glass* 1.50 Compression layer 1.51 Photo-elastic constant 31.9 nm/cm/MPa Chemical Durability Durability is measured via weight loss per surface area after immersion in the solvents shown below. Values are highly dependent upon actual testing conditions. Data reported is for Corning’s Gorilla Glass 3 with NDR™. Reagent HCl - 5% NH4F:HF - 10% HF - 10% NaOH - 5% Time 24 hrs 20 min 20 min 6 hrs Temperature (C°) 95 20 20 95 Weight Loss (mg/cm 2 ) 0.6 2.1 12.3 1.9 Electrical Frequency (MHz) 54 163 272 381 490 599 912 1499 1977 2466 2986 Dielectric Constant 7.59 7.48 7.44 7.42 7.38 7.37 7.30 7.26 7.23 7.20 7.19 Loss Tangent 0.022 0.022 0.021 0.022 0.021 0.022 0.023 0.023 0.023 0.024 0.025 0 10 20 30 40 50 60 70 80 90 100 250 500 750 1000 1250 1500 1750 2000 2250 2500 % Transmission Wavelength (nm) Wavelength [nm] Transmiance [%] 380 > 91.5 560 > 92.2 840 > 92.3 1200 > 92.4 1750 > 92.6 2000 > 92.6 Terminated coaxial line similar to that outlined in NIST Technical Notes 1520 and 1355-R. * Core index is used for FSM-based measurements since it is unaffected by ion-exchange conditions.
Transcript of Product Information Optical - Corning Inc. · 1 1.2 1.4 0 2 4 6 8 10 12 14 16 Normalized...
Corning® Gorilla® Glass 3 with Native Damage Resistance™ is an alkali-aluminosilicate thin sheet glass that is better able to survive the real-world events that most commonly cause glass failure. With its new core composition, this glass enables improved damage resistance and toughness by helping to prevent the deep chips and scratches that cause glass to break.
Product InformationBenefits• Glass designed with improved native damage resistance, - Enhances retained strength after use - High resistance to scratch and sharp contact damage - Superior surface quality
Applications • Ideal protective cover for electronic displays in: - Smartphones - Laptop and tablet computer screens - Mobile devices• Touchscreen devices• Optical components• High strength glass articles
DimensionsAvailable thicknesses 0.4 mm - 2.0 mm
ViscositySoftening Point (107.6 poises) 900 ˚CAnnealing Point (1013.2 poises) 628 ˚CStrain Point (1014.7 poises) 574 ˚C
PropertiesDensity 2.39 g/cm3
Young’s Modulus 69.3 GPaPoisson’s Ratio 0.22Shear Modulus 28.5 GPaVickers Hardness (200 g load) Un-strengthened 534 kgf/mm2
Strengthened 649 kgf/mm2
Fracture Toughness 0.66 MPa m0.5
Coefficient of Expansion 75.8 x 10-7/˚C(0 ˚C - 300 ˚C)
Chemical StrengtheningCompressive stress ≥ 950 MPa @ 40 µm DOLDepth of Layer ≥ 50 µm
Corning® Gorilla® Glass 3 with NDR™ / Product Information Sheet / E_050613
OpticalRefractive Index (590 nm) Core glass* 1.50 Compression layer 1.51Photo-elastic constant 31.9 nm/cm/MPa
Chemical DurabilityDurability is measured via weight loss per surface area after immersion in the solvents shown below. Values are highly dependent upon actual testing conditions. Data reported is for Corning’s Gorilla Glass 3 with NDR™.
Reagent
HCl - 5%NH4F:HF - 10%HF - 10%NaOH - 5%
Time
24 hrs20 min20 min
6 hrs
Temperature(C°)
95202095
Weight Loss(mg/cm2)
0.62.1
12.31.9
Electrical Frequency (MHz)
54163272381490599912
1499197724662986
Dielectric Constant
7.597.487.447.427.387.377.307.267.237.207.19
Loss Tangent
0.0220.0220.0210.0220.0210.0220.0230.0230.0230.0240.025
0
10
20
30
40
50
60
70
80
90
100
250 500 750 1000 1250 1500 1750 2000 2250 2500
% Tr
ansm
issi
on
Wavelength (nm)
Wavelength [nm] Transmittance [%] 380 > 91.5 560 > 92.2 840 > 92.3 1200 > 92.4 1750 > 92.6 2000 > 92.6
Terminated coaxial line similar to that outlined in NIST Technical Notes 1520 and 1355-R.
* Core index is used for FSM-based measurements since it is unaffected by ion-exchange conditions.
0
2000
4000
6000
8000
10000
12000
14000
16000
Soda Lime(with IOX)
Gorilla® Glass 2(with IOX)
Gorilla® Glass 3 with NDR™(with IOX)
Criti
cal L
oad
(g)
0
20
40
60
80
100
120
140
0.3 0.5 0.7 0.9 1.1 1.3
Thickness, mm
Load
to fa
ilure
, Kgf
(rin
g-on
-rin
g)
Gorilla® Glass 3 with NDR™ Soda Lime Glass
0
0.2
0.4
0.6
0.8
1
1.2
1.4
0 2 4 6 8 10 12 14 16
Nor
mal
ized
Rin
g-on
-Rin
g Fa
ilure
Load
Scratch Load (N)
mean w/95% CI
Gorilla® Glass 2 Gorilla® Glass with NDR™
Strength, MPa
Failu
re P
roba
bilit
y, %
1.0
5.0
10.0
50.0
90.0
99.0
Gorilla® Glass 3 with NDR™
Soda Lime Glass
Putting Gorilla® Glass 3 with NDR™ to the Test.
It takes more load to initiate radial cracks in the glass.
Devices benefit from greater retained strength.
Corning Gorilla Glass 3 with NDR™ exhibits tighter strength distribution.
Greater damage resistance
Enables the use of thinner cover glass
Enables greater strength
Greater retained strength
Scratches are less visible
For more information:Email: gorillaglass.comWeb: www.corninggorillaglass.com
Corning is a registered trademark of Corning Incorporated. Corning, N.Y. USA© Corning Incorporated 2015_All Rights reserved Rev: F_090315
Gorilla® Glass 3 with NDR™ (7 N)
Gorilla® Glass 2 (4 N)
Competitor Glass (4 N)
Knoop Visual Scratch TestAfter Ion Exchange