BROAD CLASSIFICATION
Ai) MICRO CRACKSii) MACRO CRACKSBi) STRUCTURAL CRACKSii) NON-STRUCTURAL CRACKSCi) STABLE CRACKSii) UNSTABLE CRACKSDi) HARMFUL CRACKSii) HARMLESS CRACKS
-
ORIGIN OF CRACKS
CRACKS MIGHT DEVELOP DUE TO -
1.STRUCTURAL DEFICIENCY RESULTING FROM DESIGN DEFICIENCY OR CONSTRUCTION DEFICIENCY.
2.DETERIORATION OF CONCRETE OR CORROSION OF REBARS DUE TO POOR CONSTRUCTION OR INAPPROPRIATE SELECTION OF CONSTITUENT MATERIALS.
3.TEMPERATURE AND SHRINKAGE EFFECTS.
-
4.OVERLOADING OF MEMBERS
5. SETTLEMENT OF SUPPORTS.
6. NATURAL HAZARDS; ETC.
ORIGIN OF CRACKS (Contd)
-
CHARACTERSTICS
Occurs when there is flexural st. deficiency Occurs in maximum moment region Maximum width at bottom face Converges towards top Occurs either singly or in group
REPURCUSSIONS
Affects structural soundness Needs to be attended to as early as possible
-
CHARACTERSTICS
Occurs when there is flexural st. deficiency Occurs in maximum moment region Maximum width at top face Converges towards bottom Occurs either singly or in group
REPURCUSSIONS
Affects structural soundness Needs to be attended to as early as possible
-
CHARACTERSTICS
Occurs when there is shear st. deficiency Occurs in maximum shear region Maximum width at mid-depth Converges towards top/bottom Occurs either singly or in group
REPURCUSSIONS
Affects structural soundness Needs to be attended to as early as possible
-
CHARACTERSTICS
Occurs when there is torsional st. deficiency Uniform width throughout Occurs in the form of a spiral Occurs singly
REPURCUSSIONS
Affects structural soundness Needs to be attended to immediately
-
CHARACTERSTICS
Occurs when there is bond deficiency Occurs directly over internal rebars Uniform width Occurs at deficient locations
REPURCUSSIONS
Affects structural soundness Rebar corrosion triggered Needs to be attended to as early as possible
-
CHARACTERSTICS
Bulging of cross section significant Occurs when loaded beyond capacity Several cracks appear in bulged region
REPURCUSSIONS
Structurally dangerous situation Needs to be attended immediately
-
CHARACTERSTICS
Occurs in tension members when capacity is exceeded Uniform width throughout and parallel to each other Occurs over the whole length
REPURCUSSIONS
Affects structural soundness Needs to be attended to as early as possible
-
PLAN
-
DIRECTION OF CONCRETING
-
LIMITATION OF CRACK WIDTHSDEPENDING ON THE EXPOSURE CONDITIONS LIMITATIONS ON CRACK WIDTH ARE IMPOSED.
1. FOR MEMBERS IN WATER STORAGE UNITS, SEWAGE TREATMENT PLANTS, STRUCTURES IN CHEMICALLY HAZARDOUS ATMOSPHERE, ETC.CRACKS ARE NOT PERMITTED IN R.C. MEMBERS.
2. IN SEVERE ATMOSPHERES UPTO 0.1MM CRACK WIDTH PERMITTED.
3. IN MILD AND MODERATE ATMOSPHERE UPTO 0.2mm CRACK WIDTH PERMITTED.
-
Measuring Magnifier - Proceq
-
CRACKSCOPE - GERMANN INSTRUMENTS
-
DIGITAL CRACK GUAGE - ELE
-
LOMARO MICROSCOPE- ELE