POLY BALL VALVEItem Operating FeatureDesigned/Tested Valves meet ASTM D 2513 requirements and ISO 9001.Materials PE4710/PE100 Black SDR 11 rated @ 100 PSI for gas & 200 PSI for waterTemperature From –20˚ F to 140˚ F (-20° C to 60° C)Bore Full PortPipe Connection Butt FusionValve Boxes IntegriFuse valves are supported by all the leading valve box manufacturers
Hydrostatic Strength TestTEMP: 74° F TEMP 100° F TEMP: 176° F1000 Hours 1000 Hours 170 Hours265 PSI 214 PSI 136 PSI
Physical Properties Metric English Comments
Density .959 g/cm3 0.0346 lb/in Black: ASTM D4883
Environmental Stress CrackResistance >= 5000 hour >= 5000 hour Condition C; ASTM D1693
Carbon Black Loading 2.30% 2.30% ASTM D1603
8.00 g/10 min 8.00 g/10 min
Melt Flow @Load 21.6 kg, @Load 47.6 lb, ASTM D1238Temperature 190 °C Temperature 374 °F
Mechanical Properties Metric English Comments
PENT >= 10000 hour >= 10000 hour Notched Tensile; ASTM F1473
Hardness, Shore D 66.0 66.0 ASTM D2240
Tensile Strength at Break 37.9 MPa 5500 PSI 2 in/min; ASTM D638
Tensile Strength Yield 24.99 MPa 3625 PSI 2 in/min; ASTM D638
Elongation at Break >= 600% >= 600% 2 in/min; ASTM D638
Flexural Modulus 1.03 GPa 150 KSI 2% Secant-Method; ASTM D790
Izod Impact, Notched 4.81 J/cm 9.00 ft-lb/in ASTM D256
Hydrostatic Design Basis6.89 MPa 1000 PSI At 60 °C; ASTM D2837
11.0 MPa 1600 PSI Room Temp; ASTM D2837
Thermal Properties Metric English Comments
Vicat Softening Point 126 °C 259 °F ASTM D1525
Brittleness Temperature = -118 °C <= -180 °F ASTM D746
Decomposition Temperature >= 220 °C >= 428 °F Thermal Stability; ASTM D2513
Descriptive Properties Metric English Comments
Cell Classification 445574C ASTM D3350
Process Injection Molding
Poly Ball Valve SpecificationsIntegriFuse fittings are manufactured from 0% recycled materials with black high density bimodal polyethylene copolymer designed for use in, but not limited to, potable water, golf courses, natural gas, industrial, landfill, oil & gas, and mining applications.
Valves meet NSF/ANSI 61, AWWA C901/906, ASTM-D2513, ASTM D3261 and ASME16.40 requirements
Manufactured for quality and longevity utilizing:• Polyethylene body
• Nitrile (HNBR) or EPDM seats
• Polypropylene ball and Op Nut
• Stainless steel stems
• ¼ turn 2” operating nut
• All valves are Full Port
• Available in ¾” to 4” SDR 11
• NSF/ANSI 61, AWWA C901/906 & ASME 16.40 approved
Integrity Fusion Products, Inc.270 Parkade Court, Peachtree City, GA 30269
P: 1 888 770 6330 or 770 632 7530 | F: 770 632 7540 | E: [email protected]
Authorized DistributorLinc Energy Systemswww.LincEnergySystems.com
IntegriFuse Poly Ball ValvesIntegriFuse Poly Ball Valves are offered in sizes from ¾” to 4”. Our full port black valves are approved for both gas and water applications. All valves are equipped with a 1/4 turn 2" square operating nut.
1
2
3
4
5
9
8
6
7
–IPS Sizes–SDR 11¾” to 4’’
Certified to NSF / ANSI 61,AWWA C901 / 906
RequirementsMost commonly used in
potable water applications
–IPS Sizes–SDR 11¾” to 4’’
Nitrile(NBR)
EPDM
Meets ASME 16.40Requirements
Most commonly used inGas, Industrial, Landfill, Golf Courses,
and other non-potablewater applications
Poly Ball Valves with 2” Operating Nut - IPS - SDR 11
Nominal Size Port SDR D MinW/T L H C I E CV Weight¾" IPS Full 11 1.050" .095 11.50" 5.12" 3.70" 1.06" 3.62" 32 1.1 lbs.
1" IPS Full 11 1.315" .119 11.50" 5.12" 3.70" 1.06" 3.62" 50 1.1 lbs.
1 ¼" IPS Full 11 1.660" .151 11.50" 5.12" 3.70" 1.06" 3.62" 79 1.1 lbs.
1 ½" IPS Full 11 1.900" .173 11.81" 5.51" 3.78" 1.26" 3.15" 104 1.7 lbs.
2" IPS Full 11 2.375" .216 19.53" 9.65" 7.01" 1.77" 6.69" 164 4.6 lbs.
3" IPS Full 11 3.500" .318 21.18" 11.81" 8.50" 2.52" 6.69" 375 8.8 lbs.
4" IPS Full 11 4.500" .409 24.02" 14.92" 10.39" 3.58" 6.69" 591 18.7 lbs.
Poly Ball Valves - Features
No. Component Material Features1 Body Polyethylene PE3408/PE4710/PE100
2 End Polyethylene PE3408/PE4710/PE100
3 Ball Polypropylene Excellent Strength & Thermal Resistance
4 Retainer Polypropylene Positive seal under any condition. Retains seat under high differential pressure
5 Ball Seat Nitrile (NBR) or EPDM Reliable sealing from –20˚ F to 140˚ F
6 Stem Stainless Steel Excellent durability & strength
7 Stem Seal Nitrile (NBR) or EPDM Redundant sealing with multiple O-rings
8 Weather Seal Nitrile (NBR) or EPDM Protects from ground water and dirt
9 Operating Nut Polypropylene 1/4 turn 2 inch (50mm) squareFull Port
Full Port
POLY BALL VALVEItem Operating FeatureDesigned/Tested Valves meet ASTM D 2513 requirements and ISO 9001.Materials PE4710/PE100 Black SDR 11 rated @ 100 PSI for gas & 200 PSI for waterTemperature From –20˚ F to 140˚ F (-20° C to 60° C)Bore Full PortPipe Connection Butt FusionValve Boxes IntegriFuse valves are supported by all the leading valve box manufacturers
Hydrostatic Strength TestTEMP: 74° F TEMP 100° F TEMP: 176° F1000 Hours 1000 Hours 170 Hours265 PSI 214 PSI 136 PSI
Physical Properties Metric English Comments
Density .959 g/cm3 0.0346 lb/in Black: ASTM D4883
Environmental Stress Crack Resistance >= 5000 hour >= 5000 hour Condition C; ASTM D1693
Carbon Black Loading 2.30% 2.30% ASTM D1603
8.00 g/10 min 8.00 g/10 min
Melt Flow @Load 21.6 kg, @Load 47.6 lb, ASTM D1238 Temperature 190 °C Temperature 374 °F
Mechanical Properties Metric English Comments
PENT >= 10000 hour >= 10000 hour Notched Tensile; ASTM F1473
Hardness, Shore D 66.0 66.0 ASTM D2240
Tensile Strength at Break 37.9 MPa 5500 PSI 2 in/min; ASTM D638
Tensile Strength Yield 24.99 MPa 3625 PSI 2 in/min; ASTM D638
Elongation at Break >= 600% >= 600% 2 in/min; ASTM D638
Flexural Modulus 1.03 GPa 150 KSI 2% Secant-Method; ASTM D790
Izod Impact, Notched 4.81 J/cm 9.00 ft-lb/in ASTM D256
Hydrostatic Design Basis 6.89 MPa 1000 PSI At 60 °C; ASTM D2837
11.0 MPa 1600 PSI Room Temp; ASTM D2837
Thermal Properties Metric English Comments
Vicat Softening Point 126 °C 259 °F ASTM D1525
Brittleness Temperature = -118 °C <= -180 °F ASTM D746
Decomposition Temperature >= 220 °C >= 428 °F Thermal Stability; ASTM D2513
Descriptive Properties Metric English Comments
Cell Classification 445574C ASTM D3350
Process Injection Molding
Poly Ball Valve SpecificationsIntegriFuse fittings are manufactured from 0% recycled materials with black high density bimodal polyethylene copolymer designed for use in, but not limited to, potable water, golf courses, natural gas, industrial, landfill, oil & gas, and mining applications.
Valves meet NSF/ANSI 61, AWWA C901/906, ASTM-D2513, ASTM D3261 and ASME16.40 requirements
Manufactured for quality and longevity utilizing:• Polyethylene body
• Nitrile (HNBR) or EPDM seats
• Polypropylene ball and Op Nut
• Stainless steel stems
• ¼ turn 2” operating nut
• All valves are Full Port
• Available in ¾” to 4” SDR 11
• NSF/ANSI 61, AWWA C901/906 & ASME 16.40 approved