P.K. Lin
1
Outline• Introduction• Experiments• Results and Discussion• Conclusion• References
2
Introduction
• Over the past few years, people have proposed numerous physics mechanisms to explain the phenomenon of efficiency droop, such as Auger recombination ,electron leakage , poor hole injection efficiency , polarization effect , and the quantum confined stark effect.
• Up to now, however, the approaches to improve efficiency droop are still mainly to suppress the electron overflow, enhance the hole injection efficiency, and reduce the polarization field.
3
Introduction
• Such as the usage of staggered quantum wells (QWs) ,AlGaN barriers , indium graded last barrier , p-InGaN hole reservoir layer , graded electron blocking layer (EBL) , and AlGaN/GaN superlattice EBL of gradual Al mole fraction.
• In this paper, the idea of InGaN barriers and dip-shaped last barrier is proposed with reduced polarization effect, decreased electron current overflow, and increased hole injection efficiency.
4
Experiments
C-plan Sapphire
2um-undoped GaN Layer
2μm Si-doped N-GaN(n = 5 x1018cm-3)
MQW
20nm Al0.15Ga0.85NEBL (p = 5x1017cm-3)
170nm Mg-doped P-GaN(p = 7x1017cm-3)
N contact
ITO
P contact
LED MQWComposition In0.16Ga0.84N/
GaNPair six-period
Thickness 3nm/10nm
Chip size: 300x300(um2)
5
The structue of the conventional (Original structure)
6
FIG. 1. Schematic view of InGaN LEDs with conventional GaN barrier(original structure), InGaN barriers (structure A), and InGaN barriers anddip-shaped last barrier (structure B).
Fig. 2. (a) Light output power, (b) I –V curves, and (c) IQE for the three LEDs.
7
Results and Discussion
At 200mA Efficiency droopOriginal structure 40.9%
Structure A 27.7%
Structure B 23.5%
Fig. 3. Electrostatic fields and band wavefunctions of the three LEDs at200 mA.
8
Fig. 4. Energy band diagrams of the three LEDs at 200 mA.
9
Fig. 5. (a) Electron concentrations, (b) hole concentrations,and (c) electron current density of the three structures at 200 mA.
10
Fig. 6. Radiative recombination rate inset with spontaneous emission rate of the three structures at 200 mA.
11
• In summary, it is found that the electron leakage is markedly reduced, the hole injection efficiency is greatly enhanced.
• In addition, the electrostatic fields in the MQWs are relieved effectively when the conventional GaN barriers are replaced by InGaN barriers and dip-shaped last InGaN barrier .
• Therefore, the optical and electrical performances of the newly designed LED acquired a significant improvement.
Conclusion
12
• R.M.Lin,S.F.Yu,S.J.Chang, T.H.Chiang,S.P.Chang,andC.H. Chen, “Inserting a p-InGaN layer before the p-AlGaN electron blocking layer suppresses efficiency droop in InGaN-based light-emitting diodes,” Appl. Phys. Lett., vol.101,no.8,pp.081120-1–081120-3,Aug.2012.
• T.Lu,S.Li,C.Liu,K.Zhang,Y.Xu,J.Tong,L.Wu,H.Wang, X.Yang,Y.Yin,G.Xiao,andY.Zhou,“Advantages of GaN basedlight-emitting diodes with a p-InGaN hole reservoir layer,” Appl. Phys. Lett.,vol.100,no.14,pp. 141106-1–141106-3,Apr.2012.
• C.S.Xia,Z.M.Simon Li,W.Lu,Z.H.Zhang,and L.W.Cheng,“Droop improvement in blue InGaN/GaN multiple quantum well light-emitting diodes with indium graded last barrier,”Appl. Phys. Lett.,vol.99,no.23,pp.233501-1–233501-3, Dec. 2011.
References
13
Thanks for your attention!
References
The advanced physical model of semiconductor devices simulation software
The key parameters Set on The radiative 2.0 x 10-11 cm3/s
Internal absorption 2000m-1
Auger cofficients 1.0 x 10-31 cm3/s
SRH recombination lifetime 100ns
Operating temperature 300K
References
My Designed EBL structure of LED
p-GaNn-GaN
p-AlGaN
MQW(GaN/InGaN)Original structure
p-GaNn-GaN
p-AlGaN
MQW(GaN/InGaN)New structure
透過在MQW與 EBL間插入一層 AlGaN superlattice ,做為緩衝 last barrier 與 EBL lattice mismatch 所帶來能帶傾斜的效應 !!進而增加 EBL有效的能障高度…
My Designed EBL structure
p-GaNn-GaN
p-AlGaN
MQW(GaN/InGaN)Original structure
在 last barrier 做一 n參雜,目的在於行程一空乏區內建電場 !透過 PN面空乏區電場來去抵補極化場 !!
n-GaN
New structure
p-GaN
p-type
n-type
極化場方向內建電場方向
My Designed EBL structure
n-GaN
New structure
p-GaN
p-type
n-type
p-type GaN barrier
n-type EBL
p-type EBL
p-GaN