8/22/2019 o Xyt Nhom Nong Chay
1/10
White Fused Alumina (Refractory grade)
White Fused Alumina(WFA or WA)is made from chemicalAl2O
3by Higgns furnace or Tilting furnace at
high temperature.It is very important raw material for advanced refractories and abrasives.Its properties
are as following.
Low sodium I Middle sodium II
Fraction(mm)
0-1 1-2 3-5(mm)
Fine(mesh)
0-180 0-325
Fraction(mm)
0-1 1-2 3-5(mm)
Fine(mesh)
0-180 0-325
Type
PropertiesGuarantee
Value
Typical valueGuarantee
Value
Typical value Guarantee Value Typical value Guarantee Value Typical value
Al2O3 99 99.48 98.5 99.23 99 99.14 98.5 99.12
SiO2 0.2 0.15 0.3 0.22 0.4 0.12 0.4 0.19
Fe2O3 0.1 0.08 0.25 0.08 0.2 0.04 0.25 0.08
Chemical
Composition (%)
Na2O 0.15 0.12 0.25 0.18 0.4 0.35 0.5 0.23
Principal crystalline phase -Al2O3
Crystal system Hexagon
Colour white
True density (g/cm3) 3.92
Packing density (g/cm3) 1.75-1.95
Mohs hardness 9
Linear expansion (1/C) 8.310-4
Size(mm) 8-5 5-3 3-1 1-0
Fine(mesh) -80,-180,-240,-320 etc
Micropowder(um) 3-5 5-10
Test standard GB/T3044-89
Packaging 25kg/bag 1000kg/big bag
Usage Refractories
-
8/22/2019 o Xyt Nhom Nong Chay
2/10
White Fused Alumina (Abrasive grade)
WA for Abrasives Composition of the Grain Size Standard(ISO8486:1996,EPA42,GB1984,IS R6001-1998,ANSI B74.12-1992,GB/T2481.1-1998)
Best Coarse Coarse Normal part Mixed part Fine part
Grain
size 100%pass these mesh NO. Not pass mesh NO Weight%short Not pass Weight%M ore than Not pass mesh NO Weight%Mo re than
More than 3% pass
these mash NO.
F4 5/16 31/2 20 4 40 4 5 70 6
F5 0.265 4 20 5 40 5 6 70 7
F6 31/2 5 20 6 40 6 7 70 8
F7 4 6 20 7 40 7 8 70 10
F8 5 7 20 8 45 8 10 70 12
F10 6 8 20 10 45 10 12 70 14
F12 7 10 20 12 45 12 14 70 16
F14 8 12 20 14 45 14 16 70 18
F16 10 14 20 16 45 16 18 70 20
F20 12 16 20 18 45 18 20 70 25
F22 14 18 20 20 45 20 25 70 30
F24 16 20 25 25 45 25 30 65 35
F30 18 25 25 30 45 30 35 65 40
F36 20 30 25 35 45 35 40 65 45
F40 25 35 30 40 40 40 45 65 50
F46 30 40 30 45 40 45 50 65 60
F54 35 45 30 50 40 50 60 65 70
F60 40 50 30 60 40 60 70 65 80
F70 45 60 25 70 40 70 80 65 100
F80 50 70 25 80 40 80 100 65 120
F90 60 80 20 100 40 100 120 65 140
F100 70 100 20 120 40 120 140 65 200
F120 80 120 20 140 40 140 170 65 230
F150 100 140 15 200 40 200 230 65 325
F180 120 170 15 200 230 40 200 230 270 65
F220 140 200 15 230 270 40 230 270 325 65
F240 170 200 5 230 270 8 230 270 325 38
(1)The mark for same grain size is mentioned differently,such as:ANSIB and are:#60;ISO.FEPA.GB are :F60
(2)JIS R6001and ANSI B74.12 have no the mark of F22 and F40
(3)Only ANSI B74.12 have 240#,others have no 240#
-
8/22/2019 o Xyt Nhom Nong Chay
3/10
High Alumina Corundum
Properties:
Fusing typeType
Properties SWA-A SWA-B
Al2O3 98 98.5
TiO2 1 0.8
Chemical
Composition
(%) C 0.15 0.12
Bulk density(g/cm3) 3.80 3.85
Apparent porosity (%) 3.5 3.0
Dust rate (%) 1 0.80
Test standard KTB01013-2004
Packaging 25kg/bag
-
8/22/2019 o Xyt Nhom Nong Chay
4/10
Calcium Aluminate Clinker
Calcium Aluminate Clinker is made from Calcium,Aluminium and little quantity other raw material,mixed in proper
proportion,and fused.The composition of the main phase:C12A7,C3A,C2S etc.
1.Low melting point,Low Melt dreg viscidity,high mobility,short time become dreg.
2.High Dreg and material sulphur,good desulphurization,dephosphorization,deoxidation,It can absorb the impurity.
3.Widely used in the process of LF,SKF,VHP,it can increase the life-span of the ladle.
Calcium Aluminate clinker for steel-making
Fusing TypeType
Properties
KTS-5 KTS-6
TiO2 3-5 3-5
Al2O3 38-42 36-41
Fe2O3 -1.5 -1.5
CaO 48-52 49-54
MgO 1.5 1.5
Chemical
Composition
(%)
TiO2 2.5 2.5
Test starcdard KTB01013-2004
Packaging 25kg/bag or based on buyers requirement
Usage Metallurgy
-
8/22/2019 o Xyt Nhom Nong Chay
5/10
Fused Spinel
The Fused Spinel produced by us has high bulk density and good color.It is strong to resist corroding and anti-detonation is better.it dopts high
pure MgO and Chemical Al2O3 to smelt by EAF.Apply to the proof of EAF and basic oxygen furnace.steel ladle,intermediate zone of cement
otary kiln,etc.
AM-66 AM-70 AM-85 AM-90Type
IndexGuarantee value Typical value Guarantee value Typical value
Guarantee
valueTypical value
Guarantee
value
Typical
value
Al2O3 63-68 66.5 71-76 74.12 82-87 83.76 88-92 88.12
MgO 30-35 32.2 22-27 24.66 12-17 15.57 8-12 11.24
CaO 0.8 0.52 0.65 0.39 0.5 0.16 0.4 0.14
SiO2 0.6 0.36 0.4 0.29 0.4 0.19 0.25 0.16
Chemical
Composition
(%)
Fe2O3 0.5 0.30 0.4 0.19 0.4 0.13 0.4 0.14
True Density (g/cm3) 3.30 3.36 3.20 3.26 3.20 3.39 3.30 3.40
Grain size (mm) 8-5 5-3 3-1 1-0
Fine(mesh) -180 -220 -240 -320
Test standard KTB01002-2003
Packaging 25kg/bag 1000kg/bag
Usage Refractories
-
8/22/2019 o Xyt Nhom Nong Chay
6/10
Fused Mullite
Type
Index
Guarantee value Typical value
Al2O3 70-77 75.30
SiO2 22-29 24.08
Fe2O3 0.1 0.05
R2O 0.35 0.18
Chemical
Composition
(%)
RO 0.3 0.28
Mullite phase 3Al2O3 2SiO2(%) 95
Glass phase (%) 5
Linear expansion coefficient (1/C) -6.010-6
Volume (g/cm3)
density 3.0
Refractoriness( C ) 1840
Grain size (mm) 5-3 3-1 1-0
Color White or Grey
Test standard KTB01006-2003
Packaging25kg/plastic bag 1000kg/plastic bag At buyer's
option
-
8/22/2019 o Xyt Nhom Nong Chay
7/10
Fused Zirconia mullite
Type
Properties
Guarantee valueTypical
value
Al2O3 44-47 45.8
ZrO2 35-39 36.5Chemical C omposition
(% )
SiO 2 15.5 - 19.5 17.1
3A l2O32SiO2 Phase(%) 50 - 55
Indined ZrSiO4 Phase (%) 30 - 33
Corundum Phase (%) 5.0
Crystal Phases
Glass Phase (%) 5.0
Bulk density (g/cm3)
3.6
Apparen t poros ity (% ) 3.0
Grain size (mm) 5-33-11-00.59-0.210.21-0
Test standard KTB01006-2003 GB/T4984-85
Pack aging 25kg/plastic bag
Usage Steel-making
-
8/22/2019 o Xyt Nhom Nong Chay
8/10
Alumina Bubble
Index
Properties
Guarantee value Typical value
Chemical composition (%) Al2O3 98.5 98.8
Packing density (g/cm3) 0.5-1.0 0.74
Damaged rate(%) 15 12
Refractoriness(C) 1800
Particle size 5-0.2mm
Test standard GB/T3044-89
Packaging 20kg/plastic bag(Dampproof)
Usage Insulating
-
8/22/2019 o Xyt Nhom Nong Chay
9/10
Reactive a-Al2O
3Micropowder
Series KT of reactive a-Al2O
3micropowder were the "8.5" key tasy task project of the state.Its praise at the state level was adopted in 1994
and its level reached the advanced one of the state.The products are characterized by great activity,micro grain size and complete phase
transformation etc.and are the necessary raw materials for fine ceramics and castable refractories in high quality.
Average Particle Diameter
(um)True Density (g/cm
3) Chemical composition (%)Index
Properties Guarantee valueTypical
value
Guarantee
value
Typical
value
Guarantee
value
Typical
value
B1L-4D 3.0 6.92 3.95 3.97 Al2O399.0 99.47
B2L-06D 1.2 0.68 3.93 3.96 SiO20.2 0.12Low soda
B1L-40 3-5 3.81 3.95 3.96 Na2O0.1 0.05
B2M-20D 1.5-2.5 2.06 3.93 3.94 Al2O399.0 99.43
B1M-3D 2.5-4 3.2 3.96 3.97 SiO20.2 0.15
B2M-SF1 1-2 1.35 3.93 3.95 Na2O0.3 0.21
B3M-20D 1.5-2.5 2.36 3.93 3.95 Na2O0.3 0.21
B3M-12D 1-1.5 1.29 3.93 3.94 SiO20.2 0.08
Middle soda
B3M-4D 3-5 3.33 3.93 3.95 Fe2O30.3 0.13
Test standard GB/T3044-89 GB3604-83 Na2O0.3 0.20
Packaging 25kg/bag
-
8/22/2019 o Xyt Nhom Nong Chay
10/10
Fused Pure Calcium Aluminate Cement
Choosing the lime stone carefully as raw materials with the alumina,SmeLt and make and fetch the grog
through the electric arc furnace(EAF),and then rubed and made the finished product thinly,Fine early
intensity,the broad scope of application,steady coagulation time,make it become the first-selected brand
Castable Refractory producer both at home and abroad.
Brands
Properties
AL-65 AL-70 AL-75 AL-80
Al2O3 63.5-66.5 68.5-71.5 73.5-76.5 78.5-81.0
CaO 32.5-34.0 26.5-30.5 24.0-26.0 17.0-20.0
SiO2 0.5
Chemical Composition
(%)
Fe2O3
0.5
Specific Surface Area (cm2/g)5000 5000 5500 7000
Initial setting (min) 40 45 30 15Setting time
Final setting (h) 6 6 6 6
Bending Strength 6.0 5.0 4.5 4.0Strength Cured for 24h
(MPa)Compressive
Strength45.0 40.0 40 35
Refractoriness(C) 1560 1560 1790 1790
Test standard KTB01013-2004
Packaging 25kg/bag
Usage Monolithic additives
High Alumina Cement CA-50H
Items Unit Index
Al2O3 % 53.00
CaO % 33.00
SiO2 % 6.0
Fe2O3 % 2.50
Chemical
Composition
TiO 3 % 3.5
Specific surface area cm2/g 4000
Initial setting time min 90
Final setting time h 6
1(day) MPa 8.0Bending strength
3(day) MPa 10.0
1(day) MPa 70.0Crushing strength
3(day) MPa 80.0
Refractoriness C 1400
Test standard KTB01013-2004
Packaging 25kg/bag
Usage Refractories