Mineral additivesFriday 09.10.2015
Fahim Al-Neshawy & Esko Sistonen
Mineral additivesPozzolanic materials are:
• Siliceous or siliceous-aluminous materials,
• Little or no cementitious value,
• In finely divided form and in the presence of moisture,
Chemically react with calcium hydroxide liberated on hydration, atordinary temperature, to form compounds, possessing cementitious properties.
They are also known as POZZOLANIC materials.
Why Mineral additives?
Improves many qualities of concrete, such as:
• Lower the heat of hydration and thermal shrinkage;
• Increase the water tightness;
• Reduce the alkali-aggregate reaction;
• Improve resistance to attack by sulphate soils and sea water;
• Improve extensibility;
• Lower susceptibility to dissolution and leaching;
• Improve workability;
• Lower costs.
Types of mineral additives
Natural Pozzolans
• Clay and Shales
• Opalinc Cherts
• Diatomaceous Earth
• Volcanic Tuffs and Pumicites.
Artificial Pozzolans
• Fly ash
• Blast Furnace Slag
• Silica Fume
• Rice Husk ash
• Metakaoline
Fly Ash
Coal-fired electrical generating station
Production of fly ash, o Coal is first pulverized in grinding mills before being
blown with air into the burning zone of the boiler. o In this zone the coal combusts producing heat with
tempertures reaching approximately 1500°C o At this temperature the non-combustible inorganic
minerals (such as quartz, calcite, gypsum, pyrite, feldspar and clay minerals) melt in the furnace and fuse together as tiny molten droplets.
o These droplets are carried from the combustion chamber of a furnace by exhaust or flue gases.
o Once free of the burning zone, the droplets cool to form spherical glassy particles called fly ash
o The fly ash is collected from the exhaust gases by mechanical and electrostatic precipitators.
Fly ash
Fly ash is finely divided residue resulting from thecombustion of powdered coal and transported by the fluegases and collected by;
• Electrostatic
• Precipitator
Fly ash is the most widely used
pozzolanic material all over the world.
Types of fly ash
Class F
• Fly ash normally produced by burning anthracite or bituminous coal, usually has less than 5% CaO.
• Class F fly ash has pozzolanic properties only.
Class C
• Fly ash normally produced by burning lignite or sub-bituminous coal.
• Some class C fly ash may have CaO content in excess of 10%.
• In addition to pozzolanicproperties, class C fly ash also possesses cementitious properties.
9
Fly ash
Amount used
Results - effects• Reduction of water demand for desired
slump. With the reduction of unit watercontent, bleeding and drying shrinkage willalso be reduced.
fly ash is not highly reactive, the heat ofhydration can be reduced throughreplacement of part of the cement with flyash.
• Up to 35% by mass of cement & minimumshall not be less than 15%.
Fly ash
Effects of Fly Ash on Hardened Concrete
• contributes to the strength of concrete due to itspozzolanic reactivity.
• continued pozzolanic reactivity concrete developsgreater strength at later age not at initial stage.
• contributes to making the texture of concretedense, resulting in decrease of water permeabilityand gas permeability.
Fly ash
Used at
• Many high-rise buildings
• Industrial structures
• Water front structures
• Concrete roads
• Roller compacted concrete dams.
In India, fly ash was used for the first time in the constructionof Rihand Irrigation Project, Uttar Pradesh in 1962, replacingcement up to about 15 per cent
12
Silica fume
Silica fume
Silica fumeSilica fume is a product resulting from reduction of high purity quartz with coal in an electric arc furnace in the manufacture of silicon or ferrosilicon alloy.
Silica fumeMicro silica is initially produced as an ultrafine undensified powder
• At least 85% SiO2 content
• Mean particle size between 0.1 and 0.2 micron
• Minimum specific surface area is 15,000 m2/kg
• Spherical particle shape
Silica fumeMicro silica is available in the following forms:
• Undensified forms with bulk density of 200–300 kg/m3
• Densified forms with bulk density of 500–600 kg/m3
• Micro-pelletised forms with bulk density of 600–800 kg/m3
• Slurry forms with density 1400 kg/m3
• Admixtures and Construction Chemicals.
• Slurry is produced by mixing undensified micro silica powder and water in
equal proportions by weight. Slurry is the easiest and most practical way to
introduce micro silica into the concrete mix.
• Surface area 15–20 m2/g.
• Standard grade slurry pH value 4.7, specific gravity 1.3 to 1.4, dry content
of micro silica 48 to 52%.
Silica fume
Silica fume
Effect on fresh concrete
• The increase in water demand of concrete containing microsilica will be about 1% for every 1% of cement substituted.
• lead to lower slump but more cohesive mix.
• make the fresh concrete sticky in nature and hard to handle.
• large reduction in bleeding and concrete with microsilica could be handled and transported without segregation.
• to plastic shrinkage cracking and, therefore, sheet or mat curing should be considered.
• produces more heat of hydration at the initial stage of hydration.
• the total generation of heat will be less than that of reference concrete.
Silica fume : Effect on hardened concrete
Silica fume : Effect on hardened concrete
Silica fume
• Conserve cement
• Produce ultra high strength concrete of the order of 70 to 120 Mpa.
• Increase early strength of fly concrete.
• Control alkali-aggregate reaction.
• Reduce sulfate attack & chloride associated corrosion.
Used for
Blast furnace slag
• Blast furnace slag is obtained by quenching molten iron slag (a by- product of iron and steel-making) from a blast furnace in water or steam, to produce a glassy, granular product that is then dried and ground into a fine powder.
• Temperature in the molten iron slag reaches 1400 oC
• Annual production is about 0.6 million ton in Finland
Blast furnace slag
Blast furnace slag
Cooling methods
• Slow cooling of slag melts results in an unreactive
crystalline material consisting of an assemblage of Ca-Al-
Mg silicates
• to obtain a good slag reactivity or hydraulicity, the slag
melt needs to be rapidly cooled or quenched below 800 °C
in order to prevent the crystallization of merwinite and
melilite
• pelletized slag (swelling by a smaller water amount)
• granulated slag (swelling in large water amount)
Granulated slag• swelling is produced by water sprays• final cooling in large water pool• granulated particles are lifted from the pool • fast cooling prevents the crystallization and the particles
possess a glassy outer surfacePelletized slag
• molten slag is poured on a plate• water sprays cause swelling in the slag• revolving cylinder brakes the slag into particles • water is sprayed into the pellet heap to prevent the
particles from sintering togetherPelletized slag - vs - granulated slag
• pelletized has larger grains• pelletized is more porous• pelletized is lighter and dryer• pelletized is more crystalline and easier to grind
Blast furnace slag
• Blast-furnace slag is a nonmetallicproduct consisting essentially ofsilicates and aluminates of calciumand other bases.
• The molten slag is rapidly chilled byquenching in water to form a glassysand like granulated material.
• The granulated material whenfurther ground to less than 45micron will have specific surface ofabout 400 to 600 m2/ kg (Blaine).
Blast furnace slag
Blast furnace slag
Blast furnace slag
Blast furnace slag
Blast furnace slag
Blast furnace slag
Blast furnace slag
Blast furnace slag
Blast furnace slag
Blast furnace slag
Effects on fresh concrete
• Reduces the unit water content necessary to obtain the same slump.
• Water used for mixing is not immediately lost, as the surface hydration of slag is slightly slower than that of cement.
• Reduction of bleeding.
Effects on hardened concrete
• Reduced heat of hydration
• Refinement of pore structures
• Reduced permeabilities to the external agencies
• Increased resistance to chemical attack.
Reduction in unit water contain
Rice husk ash
Rice husk ash
Rice husk ash is obtained by
• Burning rice husk in a controlled manner without causing environmental pollution.
• Material of future as mineral additives.
Rice husk ash
Amount used
• 10% by weight of cement.
• It greatly enhances the workability and impermeability of concrete.
Contains
• Amorphous silica (90% SiO2) in very high proportion when burnt in controlled manner.
• 5% carbon.
• 2% K2O.
Rice husk Ash
Effects
• Reduces susceptible to acid attack and improves resistance to chloride penetration.
• Reduces large pores and porosity resulting very low permeability.
• Reduces the free lime present in the cement paste.
• Decreases the permeability of the system.
• Improves overall resistance to CO2 attack.
• Enhances resistance to corrosion of steel in concrete.
• Reducing micro cracking and improving freeze-thaw resistance.
• Improves capillary suction and accelerated chloride diffusivity.
Metakaolin
Metakaolin
• Highly reactive metakaolin is made by water processing to remove unreactive impurities to make100% reactive pozzolan.
• Such a product, white or cream in colour, purified, thermally activated is called High Reactive Metakaolin (HRM).
Metakaolin
Effects of Metakaolin
• High reactive metakaolinshows high pozzolanic reactivity and reduction in Ca(OH)2 even as early as one day.
• The cement paste undergoes distinct densification.
• Densification includes an increase in strength and decrease in permeability.
Use of Metakaolin
• The high reactive metakaolin is having the potential to compete with silica fume.
References• Silica Fume User’s Manual:
http://www.silicafume.org/pdf/silicafume-users-manual.pdf
• Fly Ash, Slag, Silica Fume, and Natural Pozzolans: http://www.ce.memphis.edu/1101/notes/concrete/PCA_manual/Chap03.pdf
• Optimizing the Use of Fly Ash in Concrete: http://www.cement.org/docs/default-source/fc_concrete_technology/is548-optimizing-the-use-of-fly-ash-concrete.pdf