8/12/2009 1 AE 587
Metal Casting Processes
AE 587: Automotive Manufacturing Processes
By
Dr. E. Orady
8/12/2009 2 AE 587
Lecture Topics
Introduction Sand casting Design of mold elements Solidification of casting Fluidity Casting processes; expendable and permanent
casting processes Melting practice and Furnaces Factors affecting casting cost Casting quality Design Considerations for Casting
8/12/2009 3 AE 587
Casting Processes
• DEFINITION:– The casting process is defined as the process of
melting (heating to a proper temperature above the freezing point) of a material (mostly metals) and treating it to have a proper composition, then pouring the molten material into a cavity or mold which holds it in the proper shape during solidification.
– The product of this process a casting.
8/12/2009 4 AE 587
Selection of casting processes over other manufacturing processes
Casting Processes are selected for the following reasons:
» to produce complex shapes with internal cavities or hollow sections.
» to produce very large parts weighing up to 30 tons.» to utilize work piece materials that are difficult to process by
some other means.» Some casting processes are net shape; others are near net
shape» economical to use» Some casting methods are suited to mass production
8/12/2009 5 AE 587
Disadvantages of Casting
Different disadvantages for different casting processes: » Limitations on mechanical properties» Poor dimensional accuracy and surface
finish for some processes; e.g., sand casting
» Safety hazards to workers due to hot molten metals
» Environmental problems
8/12/2009 6 AE 587
TYPICAL EXAMPLES OF CASTING PRODUCTS
• Frames and housings of machines
• Structural parts
• Machine components
• Engine blocks
• Crank shafts
• Pistons
• Pipes
• Valves
• Rail road equipment, etc.
Some Cast Components in a Typical AutomobileSource Kalpakjian
8/12/2009 7 AE 587
Categories of Casting Processes
Expendable Mold Casting processes» Mold is used one time» Molds made of sand or
Plaster or similar materials
» typical:– Sand mold– Shell mold– Expended
Polystyrene– Plaster– Investment– etc.
Permanent Mold casting processes» Mold is used over and
over to produce many castings
» Mold made of metal » Typical:
– Slush– Low pressure– Die casting– Centrifugal
8/12/2009 8 AE 587
Automotive Casting Processes
Following are the commonly used casting processes in automotive applications:
Sand Casting Die casting Lost Wax casting Lost Foam casting Cosworth Casting Squeeze casting
8/12/2009 9 AE 587
BASIC OPERATIONS INVOLVED IN CASTING
1. MOLDING
a) single-use molds: for small production such as sand casting, and
b) permanent molds: for large production such as die casting.
2. MELTING PROCESSES
3. POURING TECHNIQUES
4. SOLIDIFICATION PROCESS
5. SHAKEOUT AND REMOVAL OF THE PRODUCT
6. CLEANING, FINISHING AND INSPECTION
8/12/2009 10 AE 587
Mold Features
Mold Terminology: Cavity Well Gating System
» Sprue or Downsprue
» Runner
» Gates Riser Parting Line Flask/Cope/Drag
FIGURE 5.10 Schematic illustration of a typical sand mold showing various features.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 11 AE 587
Sand Casting
Most widely used casting process, accounting for a significant majority of total tonnage cast
Nearly all alloys can be sand casted, including metals with high melting temperatures, such as steel, nickel, and titanium
Castings range in size from small to very large Production quantities from one to millions
8/12/2009 12 AE 587
Figure 11.1 A large sand casting weighing over 680 kg (1500 lb) for an air compressor frame (photo courtesy of Elkhart Foundry).
Source: M. Groover, 2nd Ed.
Example of a Sand Cast
8/12/2009 13 AE 587
Sand Casting Molds
Sand casting mold» Sand +bonding material+
Water» Sand +bonding material
Types » Green sand mold» Dry sand mold» Core sand molds» Loam molds» Shell molds» Cement bond molds
Pattern + Core = Product
A Typical Sand Mold Source: DeGarmo/Black/Kohser
8/12/2009 14 AE 587
Characteristics of a Sand Mold
Strong enough to hold the metal Resist erosive action of rapidly flowing metal during
pouring Generates a minimum amount of gas when filled with
molten metal Allows gases generated to pass through Refractory enough to withstand high temperature and
strip away cleanly from the casting after cooling Core must collapse enough to permit the casting to
contract after solidification
8/12/2009 15 AE 587
Properties of Molding Sand
Refractoriness» The ability of sand to withstand high temperature» It is provided by the basic nature of sand
» Common sand: Silica (SiO2), Zircon, or Olivine Cohesiveness
» The ability to retain a given shape when packed into a mold» Adding bonding materials such as: Bentonite, kaolinite, or illite
Permeability» The ability to permit gases to escape through it» Function of size and shape of sand particles, clay and moisture contents
Collapsibility» The ability to permit the metal to shrink after it solidifies and to free the
casting from surrounding mold» Obtained by adding cereals, cellulose or other organic materials that burn
out when they contact hot metal.
8/12/2009 16 AE 587
Types of Molding Sand
Natural sand» Sand + natural bond clay» Used as received
Loam sand» Sand + 50% clay
(natural)» Used for large castings
Synthetic sand
» Washed sand + Binder (Bentonite) + Water
» Advantages over natural sand
– Uniform grain size
– Higher refractoriness
– Moldability with less moisture
– Require less binder
– Easier to control properties
– Less storage space
8/12/2009 17 AE 587
PATTERNS
The pattern is a duplicate of the part to be cast, modified to meet the requirements of the casting process, metal being cast, and molding technique.
The pattern dimensions are the same as the final product plus a set of allowances which include :
» shrinkage allowance; for the contraction of the metal after it solidifies and cools.
» machining allowance; needed when the final product has surfaces to be machined after the casting process.
» draft allowance; a slope on the walls of the pattern to allow easy withdrew of the pattern from the mold.
» Other allowances such as distortion allowance
8/12/2009 18 AE 587
PATTERNS
Pattern materials» Wood; for small quantity
» Metal; for larger quantity
» Hard Plastics; used with organically bonded sand to avoid sand stick to pattern skin
» Wax; for investment casting
» Polystyrene; used with full mold-process
Selection of pattern material is function of:» number of castings
» size and shape of the casting
» desired dimensional precision
» molding process
8/12/2009 19 AE 587
Types of Patterns
Figure 11.3 Types of patterns used in sand casting:
(a) solid pattern
(b) split pattern
(c) match‑plate pattern
(d) cope and drag pattern
8/12/2009 20 AE 587
CORE
A core is made when the final product has an internal cavity or hollow. The core usually has the shape of the cavity plus allowances and a support, called a core print, to hold the core in the mold. The core(in sand casting) is made from a special sand mix which is collapsible under the shrinkage stress of the casting to avoid causing cracks on the casing.
Core Box
Core made by gluing the two halves
Two Core HalvesSource:DeGarmo/Black/Kohser
8/12/2009 21 AE 587
Core in Mold
Figure 11.4 (a) Core held in place in the mold cavity by chaplets, (b) possible chaplet design, (c) casting with internal cavity.
Source: M. L. Groover, 2nd Ed.
8/12/2009 22 AE 587
Core Materials
Green sand Dry sand [ sand plus binder packed
in wood or metal core box] Packed sand [ made by mixing sand
with a vegetable oil or synthetic oil as binder, and water with cereal or clay to develop green strength. This process is called core-oil process. The mix is cured using hot force air at 400 to 500oF.]
CO2 sand [sand + sodium silicate (water glass)]
Shell sand [sand plus liquid thermosetting and catalyst is blown into a core box heated to around 450oF.]
Dry-sand cores for V-8 engine block
Engine Block Casting
Source: DeGarmo/ Black/ Kohser
8/12/2009 23 AE 587
CORE
Characteristics » sufficient hardness and strength (after baking or hardening)
to withstand handling and forces of the molten metal» sufficient strength before hardening to permit handling» adequate permeability» collapsibility to permit shrinkage of the casting as it cools,
thereby prevent cracking and allow easy shakeout.» adequate refractoriness» smooth surface» minimum generation of gases when heated during pour
8/12/2009 24 AE 587
Mold Preparation
Manual Use of jolting machines Squeezing machines Combined jolting and squeezing Automatic mold-making machines
» Match-plate machines» Vertically parted flaskless molding machine
8/12/2009 25 AE 587
Manual Preparation of Sand Mold
Source: Kalpakjian
8/12/2009 26 AE 587
POURING (GATING) SYSTEM
Pouring system should be designed to ensure smooth flow "laminar flow" and fill the mold at the shortest possible time before metal solidify. A typical pouring system is shown in the Figure. It consists of the following:
1. POURING BASIN
2. SPRUE :It should be designed to ensure smooth flow and avoid aspiration
3. WELL
4. RUNNERS
5. GATESPouring SystemSource: Ghosh/Mallik
ht
8/12/2009 27 AE 587
POURING (GATING) SYSTEM
POURING TIME:
The pouring time is defined as the time needed to fill or inject the molten metal into the mold. The pouring time can be estimated by applying the fluid flow laws; namely, the equation of continuity and Bernoulli's Equation
The flow velocity at any point in the pouring system (sprue , gates, and runners) is controlled by the continuity equation:
Q = A1 v1 = A2 v2 ... etc. where Q = volumetric flow rate, in.3/sec (cm3/s), A = cross sectional area,in.2 (cm2) and v= flow velocity in./sec (cm/s).
The flow velocity at the bottom of the sprue (see figure) is determined by applying Bernoulli's Equation. The velocity is
v3 = sqrt( 2. g. ht) where: g = gravitational acceleration; g=386 in./sec2 (981 cm/s2), and h3 = the height of the sprue, in. (cm)
8/12/2009 28 AE 587
POURING (GATING) SYSTEM
Pouring time VERTICAL (TOP) POURING
SYSTEM, See Figure
tf = V/ A3 v3
where V= volume of the casting including riser, in.3 (cm3) A3 = gating area in2 (cm2),
and tf= pouring time in sec. BOTTOM GATING
See Figure
where Am = the mold projection area. ( You have to do some integration to calculate the time in
bottom gating)
mttm
f hhhgA
At (
2
2
3
8/12/2009 29 AE 587
Flow Characteristics
Two type of flow:» Laminar flow» Turbulent
Governing factor is Reynolds number, Re
Where: v is the velocity of the liquid, D is the diameter of the channel, and and are the density and viscosity, respectively of the fluid.
Re < 2000 laminar flow2000<Re < 20,000 is a mixture of laminar and turbulent flowRe>20,000 represent severe turbulent flow. Proper flow and design of gating system is needed to prevent
mold erosion and introduction of dross and slag inside the mold cavity
vD
Re
8/12/2009 30 AE 587
POURING (GATING) SYSTEM
Sprue Design» Tapered sprue is used to
maintain constant liquid flow through it and avoid aspiration.
» Therefore, the following relation should be satisfied
Q = A2 v2 = A3 v3
Hence,
A2/A3 = sqrt(h3/h2)
Runner and Gates Design» The ratio between:
A3:Ar:Ag = 1: 4 :4
i.e. the runner area (Ar)
Ar = 4xA3
And the total gating area(Ag) Ag = Ar = 4xA3
h2
h3
8/12/2009 31 AE 587
Example 1
A mold has a top gating system with a downspure of length = 175 mm. The cross-sectional area at the bottom of the sprue is 400 mm2. The sprue leads into a horizontal runner that feeds the mold cavity, whose volume = 0.001 m3. Determine (a) the velocity of the molten metal flowing through the base of the downsprue, (b) the volume rate of flow, and (c) the time required to fill up the cavity.
8/12/2009 32 AE 587
Example 2
The volume rate of flow of molten metal into the downsprue from the pouring cup is 50 in.3/sec. The length of the sprue is 8.00 in. and the cross-sectional area at the top where the pouring cup leads into the downsprue is 1.0 in.2. Determine what the area should be at the bottom of the sprue in order to avoid aspiration of the liquid metal.
8/12/2009 33 AE 587
Solidification of Metals
Solidification is the transformation of molten metal back into solid state
Solidification of pure metals is different from that of alloys.
Proper solidification is the second step of producing a high quality casting.
8/12/2009 34 AE 587
Pure Metal Solidification
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
FIGURE 5.1 (a) Temperature as a function of time for the solidification of pure metals. Note that freezing takes place at a constant temperature. (b) Density as a function of time.
8/12/2009 35 AE 587
Pure Metal Solidification
Solidification is the growth of favorably oriented nuclei in the direction of heat extraction» Randomly oriented small grains form near the
mold walls » Columnar grains form towards the center of the
mold » shrink cavities (pipe) forms due to low supply of
fresh liquid
8/12/2009 36 AE 587
Solidification of Eutectic Alloys
Solidification occurs at a constant temperature (like pure metal).
Eutectic cells form inside the grains The properties of the cast part are affected by:
» Cooling rate» Nucleation agents» Alloy modifications
8/12/2009 37 AE 587
Solid Solution Solidification
Solidification takes place over a freezing range. Grains grow in the direction of heat extraction. Initially solidified material has lower alloying element
concentration. Solidification proceeds by dendritic form. Dendritics arms can break off and re-melt. At high cooling rate, the formed grains are smaller
and the strength is improved. Dendrites result in microporosity.
8/12/2009 38 AE 587
Alloy SolidificationAlloy Solidification
Figure Source: M.P. Groover
8/12/2009 39 AE 587
Alloy Solidification
FIGURE 5.6 Schematic illustration of alloy solidification and temperature distribution in the solidifying metal. Note the formation of dendrites in the semi-solid (mushy) zone.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
Pouring Temperature
SuperheatStart of SolidificationEnd of SolidificationSolid Cooling
8/12/2009 40 AE 587
Cast Structures
FIGURE 5.5 Schematic illustration of three cast structures of metals solidified in a square mold: (a) pure metals, with preferred texture at the cool mold wall. Note in the middle of the figure that only favorable oriented grains grow away from the mold surface; (b) solid-solution alloys; and (c) structure obtained by heterogeneous nucleation of grains.
Columnar grains oriented towards the center of the moldSmall, randomly oriented grains
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 41 AE 587
Dendritic SolidificationDendritic Solidification
Ref: Porter, et al., Phase Transformations In Metals & Alloys, Van Nostrand Reinhold, UK, 1981
8/12/2009 42 AE 587
Solidification Patterns for Gray Cast Iron
FIGURE 5.7 (a) Solidification pattern for gray cast iron in a 180-mm (7-in) square casting. Note that after 11 min of cooling, dendrites reach each other, but the casting is still mushy throughout. It takes about two hours for this casting to solidify completely. (b) Solidification of carbon steels in sand and chill (metal) molds. Note the difference in solidification pattern as the carbon contents increase, Source: After H. F. Bishop and W.S. Pellini.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 43 AE 587
Cast Structures
FIGURE 5.9 Schematic illustration of cast structures in (a) plane front, single phase, and (b) plane front, two phase. Source: After D. Apelian.
FIGURE 5.8 Schematic illustration of three basic types of cast structures: (a) columnar dendritic; (b) equiaxed dendritic; and (c) equiaxed nondendritic. Source: After D. Apelian.
8/12/2009 44 AE 587
Effects of Solidification RateEffects of Solidification Rate
Faster solidification results in:» Smaller microstructural features» Smaller & more uniformly dispersed porosity and
intermetallics» Reduced grain size» Improved mechanical properties (strength, fatigue,
& ductility)
Faster solidification will not affect the morphology of inclusions
8/12/2009 45 AE 587
Temperature Distribution
FIGURE 5.11 Temperature distribution at the mold wall and liquid-metal interface during solidification of metals in casting.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 46 AE 587
Solidification Example
FIGURE 5.12 Solidified skin on a steel casting; the remaining molten metal is poured out at the times indicated in the figure. Hollow ornamental and decorative objects are made by a process called slush casting, which is based on this principle. Source: After H.F. Taylor, J. Wulff, and M.C. Flemings.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 47 AE 587
Shrinkage
Stages» Liquid contraction during
cooling prior to solidification
» Solidification shrinkage: Contraction during the phase change from liquid to solid
» Thermal contraction of the solidified casting during cooling to room temperature.
Solidification StagesSource: Groover
8/12/2009 48 AE 587
Shrinkage and Contraction DataShrinkage and Contraction Data
Volumetric Contraction
Metal
Solidification Shrinkage, %
Solid Thermal Contraction, %
Aluminum 7.0 5.6
Al Alloys 7.0 5.0
Gray cast iron 1.8 3.0
Gray cast iron, high C 0 3.0
Low C cast steel 3.0 7.2
Copper 4.5 7.5
Bronze 5.5 6.0
8/12/2009 49 AE 587
HEAT EXTRACTION AND SOLIDIFICATION TIME
The solidification time (TST) of a mold can be estimated using Chvorinov's law:
TST = Cm(V/A)n
where TST = Total solidification time in minutes
n = is an exponent has a value between 1.5 to 2.0
V= casting volume in in.3 (cm3)
A= surface area of the casting in.2 (cm2).
Cm= the mold constant which depends on:
• metal characteristics ( density, specific heat, and heat fusion)
• the properties of the mold material( density, thermal conductivity, and specific heat)
• amount of superheat
» Cm can be determined experimentally for each mold and metal combination.
8/12/2009 50 AE 587
Riser design
The minimum size of a riser can be determined from Chvorinov's rule; the time of solidification of the riser (TSTr) should be at least 25% longer than that for the casting (TSTc):
TSTr = 1.25 TSTc
Taking n =2
(V/A)2 r = 1.25 (V/A)2
c Calculation of the riser geometry requires that V/A be maximum, and The size of the riser should be greater than the shrinkage volume of the
casting.
Vr > Shrinkage volume of the casting
8/12/2009 51 AE 587
TYPES OF RISERS
1. Top Riser:
» Characteristics:– sits on top of the casting– short feed distance
required– occupies less space in
the flask,
2. Side Riser:
» Characteristics:– located adjacent to the
mold cavity in the horizontal direction.
– longer feeding distance– occupies some of the
flask space.
Basic types of risersSource: DeGarmo/Black/ Kohser
8/12/2009 52 AE 587
Riser location and feeding Distance
Risers must solidify after casting
The riser should be placed so that it is continuously feed the casting and directional solidification is maintained
Riser should be placed on the thermal center of the casting
The feeding distance should be less than or equal the following recommendations.
Max. distance between risers
Placement of risers and chill blocksSource: Ghosh and Mallik
8/12/2009 53 AE 587
Riser Aids
Purpose» Promoting directional solidification» Reducing number and size of risers
Methods» External chills» Internal chills» Reducing the cooling rate of risers
– Use open risers– Use insulating sleeves around the rise– Surround the sides and top of riser with exothermic
materials that supply added heat to the riser.
8/12/2009 54 AE 587Figure 10.9
ChillsChills
Heat sinks that promote directional solidification Internal or External
8/12/2009 55 AE 587
Chills
FIGURE 5.35 Various types of (a) internal and (b) external chills (dark areas at corners), used in castings to eliminate porosity caused by shrinkage. Chills are placed in regions where there is a larger volume of metal, as shown in (c).
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 56 AE 587
Example 3
A cylindrical riser is to be designed for a sand mold. The length of the cylinder is to be 1.25 times its diameter. The casting is a square plate, each side = 10 in., and thickness = 1.25 in. If the metal is cast iron and Cm = 16.0 min./in2 in Chvorinov’s rule, determine the dimensions of the riser so that it will take 30% longer for the riser to solidify.
8/12/2009 57 AE 587
Fluidity
Fluidity is defined as the ability of a molten metal to flow and fill the mold.
Fluidity measurement:» Length of a spiral
shape cast (Figure a)» Plate mold length
(Figure b)» Length of a fill under
vacuum
Methods of measuring fluiditySource: El-Wakil
8/12/2009 58 AE 587
Factors Affecting Fluidity
Mold Design» Component dimensions, sprue, runners, riser affect fluidity to
varying degree Mold Materials and its characteristics
» The higher the thermal conductivity and the rougher the surface the lower the fluidity.
Amount of Superheat» Fluidity increases with the increase of superheat. Increase of
superheat lowers viscosity and delays solidification. Mold temperature
» Fluidity increase with increasing mold temperature Type of solidification
» Columnar is helpful» Dendritic slows down flow
Rate of pouring» Fluidity decreases with the decrease of the pouring rate.
8/12/2009 59 AE 587
Shell Molding: Casting process in which the mold is a thin
shell of sand held together by thermosetting resin binder
» teps
A heated match plate is placedon the box containing sand with resin binder
Invert the box so that the sand resin fall on the hot plate and form a shell
Reposition the box to clear awayuncured sand. The mold and shell are then placed in a furnace for several minutes to complete curing.
Strip shell molds from the pattern
Assemble two halves andplace support with sand or metal shot in a box.The mold now is ready for pouring.
Source: DeGarmo/Black/Kohser
8/12/2009 60 AE 587
Shell Molding
Advantages
» Provides better surface finish than ordinary sand casting (100 in or 2.5 m)
» Better dimensional accuracy, Tolerance of 0.003 to 0.005 (0.08 to 0.13 mm) are quite common.
» Economical; less labor, no further machining, etc.
» Good collapsibility of the mold help in avoiding tearing and cracking of the casting.
» The process can be completely mechanized
Disadvantages
» More expensive metal pattern, thus it can not be justified for low volume production.
» Not suitable for large size products above 25 lb.
Two halves of a shell mold pattern
Shell Mold
Final Product
8/12/2009 61 AE 587
Expanded Polystyrene Process
Uses a mold of sand packed around a polystyrene foam pattern which vaporizes when molten metal is poured into mold
Other names: lost‑foam process, lost pattern process, evaporative‑foam process, and full‑mold process
Polystyrene foam pattern includes sprue, risers, gating system, and internal cores (if needed)
Mold does not have to be opened into cope and drag sections
8/12/2009 62 AE 587
Expanded Polystyrene Process(Lost Foam Casting)
(1) Polystyrene patternis made and assembled
(2) The pattern is dipped in refractory slurry or sprayed byrefractory compound
(3) The pattern is placed in a metal box and supported by sand
(4) The sand is compactedby vibration
(5) The molten metal is thenpoured in the polystyrenepattern.
(6) Casting is removed andsand reclaimed
8/12/2009 63 AE 587
Expanded Polystyrene Process (Lost Foam Casting)
8/12/2009 64 AE 587
Expanded Polystyrene Process (Lost Foam Casting)
Advantages» Patterns need not to be removed from the mold;
– speed up the process of mold making, – no draft or parting lines are needed,– cores and risers build in the pattern
» Precision and surface finish are sufficiently good, then many machining and finishing operations could be eliminated.
» High metal utilization» Sand can be recycled» There is no limitations on the shape and size of product. » Most metal can be cast
Limitations» Pattern cost can be high for small quantities» Patterns are easily damaged or distorted because of their low
strength
8/12/2009 65 AE 587
Expanded Polystyrene Process
Applications:» Mass production of castings for automobile engines
» Automated and integrated manufacturing systems are used to 1. Mold the polystyrene foam patterns and then
2. Feed them to the downstream casting operation
8/12/2009 66 AE 587
Investment Casting (Lost Wax Process)
A pattern made of wax is coated with a refractory material to make mold, after which wax is melted away prior to pouring molten metal
"Investment" comes from a less familiar definition of "invest" - "to cover completely," which refers to coating of refractory material around wax pattern
It is a precision casting process - capable of producing castings of high accuracy and intricate detail
8/12/2009 67 AE 587
Investment Casting (Lost Wax)
Steps:(1) Wax patterns are produced in a mold (a, and b)(2) patterns are attached to a sprue to form a tree (c)(3) The tree is then coated with a thin layer of refractory material (d).(4) The full mold (f) is formed by covering it with sufficient material to make it rigid (e).(5) the mold is then placed in an oven to melt away the wax (g)(6) The hot pattern is then placed on a container and molten metal is poured.(7) The mold is the broken away to separate casting.
Source: Kalpakjian
8/12/2009 68 AE 587
Investment Casting (Lost-Wax)
Advantages» Can be used to produce casting
of high accuracy and intricate detail.
» Close dimensional control; tolerances of +/- 0.003 in. are possible
» Good surface finish» Wax can be recovered and
used» A net shape process,
machining is not required Limitations
» Costly patterns and molds» Labor costs can be high» Limited size (less than 10 lb.)
8/12/2009 69 AE 587
Permanent Mold Casting Processes
Method
» Molds are made of steel or fine-grain cast iron
» Mold halves or sections are hinged so that they can open or close accurately.
» Molds are preheated at the beginning of the run to maintain uniform temperature.
» Cavity surfaces are to be coated with thin layer of refractory materials
» Cores can be used with permanent molds to form interior surfaces
8/12/2009 70 AE 587
Permanent Mold Casting Processes
Mold preheated and coatedCores are inserted and mold closed
Pour molten metal into the mold Open mold and eject product
Finished ProductSource: Groover
8/12/2009 71 AE 587
Permanent Mold Casting Processes
Advantages» Good surface finish» Accurate dimensions (within 0.01 in.)» Solidification can be controlled using
proper chill design» Faster cooling rate produces stronger
material than with sand casting.» Multiple cavities can often be included
in a single mold
8/12/2009 72 AE 587
Permanent Mold Casting Processes
Disadvantages» Limited to low melting point metals
– Common metals include alloys of aluminum, magnesium, copper, lead, tin, and zinc; irons and steel can also be cast in graphite molds.
» High initial cost» Shape, size and part complexity are limitations » Low yield rate, less than 60%» Mold life is very limited; the actual mold life varies with:
– Alloy being cast– Mold material– Pouring temperature– Mold temperature– Mold configurations
8/12/2009 73 AE 587
Applications of Permanent Mold Casting
Due to high mold cost, process is best suited to high volume production and can be automated accordingly
Typical parts: automotive pistons, pump bodies, and certain castings for aircraft and missiles
Metals commonly cast: aluminum, magnesium, copper‑base alloys, and cast iron
8/12/2009 74 AE 587
Permanent Mold Casting :Die Casting
Metal is injected in the mold at high pressure (1000 to 50,000 psi) Pressure is maintained during solidification Combination of metal mold and pressure, fine sections and
excellent details can be achieved. Special zinc-, copper and aluminum-based alloys can be produced
with excellent properties Dies are made from hardened hot-worked steel. Dies tend to be
expensive. Dies can be designed for simple products, multiple product, or
complex products. Dies usually have water cooling passages, cores, ejectors. Dies often cost in excess of $5000 to $10,000 Die life is limited by wear, and thermal fatigue. Die casting process is limited to mass production
8/12/2009 75 AE 587
Hot-Chamber Die Casting
Metal is melted in a container, and a piston injects liquid metal under high pressure into the die
High production rates - 500 parts per hour not uncommon
Applications limited to low melting‑point metals that do not chemically attack plunger and other mechanical components
Casting metals: zinc, tin, lead, and magnesium
8/12/2009 76 AE 587
Hot Chamber Die Casting Machine
Components of a hot-chamber die-castingmachineSource:DeGarmo/Black/Kohser
Close chamber and let metal flow in chamber
Plunger then forces metal into die, andmaintains the pressure during part solidification
After part solidification, plunger withdrawnand die opened, and the part is then ejected using ejectors
Finished product
Source: Groover
8/12/2009 77 AE 587
Cold‑Chamber Die Casting Machine
Molten metal is poured into unheated chamber from external melting container, and a piston injects metal under high pressure into die cavity
High production but not usually as fast as hot‑chamber machines because of pouring step
Casting metals: aluminum, brass, and magnesium alloys
Advantages of hot‑chamber process favor its use on low melting‑point alloys (zinc, tin, lead)
8/12/2009 78 AE 587
Cold-Chamber Die Casting Machines
Configuration of cold chamber die-casting machine
Close die and withdraw ram, then pour molten metal in the chamber Activate ram to force metal in the die
and maintain pressure until part solidify
Once part solidify, withdraw ram and activate ejection system to eject casting.
Source: Groover
8/12/2009 79 AE 587
Die Casting Machine
Source: Introduction to Manufacturing Processes By John Schey, McGraw Hill, 2000.
8/12/2009 80 AE 587
Hot Chamber vs. Cold ChamberHot Chamber vs. Cold Chamber
Advantages Short cycle time Better thermal control of
the process Loading a new charge
of molten metal is done automatically
The molten metal exposure to the atmosphere is reduced
Disadvantages Alloy limitations Lower injection
pressures and speed than cold chamber
Higher maintenance costs
8/12/2009 81 AE 587
Advantages
Allows for casting of wider range of alloys
Higher injection pressure and speed
Lower tooling maintenance cost
Disadvantages Slower cycle times than hot
chamber process Less control of metal
temperature The charge cools prior to
injection. Molten metal exposed to
atmosphere
Cold Chamber vs. Hot ChamberCold Chamber vs. Hot Chamber
8/12/2009 82 AE 587
Die Casting
Advantages» High production rate» Economical for mass production» Extremely smooth surface (40 to 100 in.) » Excellent dimensional accuracy (Typically tolerances are 0.005 in. for the
first inch and 0.002 in. for each additional inch)» Can produce thin sections up to 0.03 in.» Rapid cooling provides fine grain size and high strength.
Limitations» High initial cost» Limited to high-fluidity nonferrous metals» Part size is limited (1 oz up to 15 lb.)» Porosity may be a problem» Some scrap in sprue, runners and flash
8/12/2009 83 AE 587
Multi-slide Dies
Is a variation of hot-chamber die casting
Use 4 perpendicular slides in the tool
» enables complex castings to be produced.
» In some cases, up to 6 slides can be added
This process is used primarily for casting small zinc components and is being used for casting magnesium parts
PC controllers are used to control the position of the slides
Up to 75 cycles per minute can be achieved
8/12/2009 84 AE 587
Permanent Mold Casting Low Pressure Die casting
8/12/2009 85 AE 587
The process is capable of producing high quality castings
Commonly cast materials Al alloys, Mg alloys, and other low melting point alloys
Sand cores can be used in the manufacture of parts with complex shapes.
Aluminum castings from 2 - 150kg can be cast, but the most common casting weight is around 10kg
High volume production is needed to justify the cost of the dies.
Permanent Mold Casting Low Pressure Die casting
8/12/2009 86 AE 587
Squeeze-Casting
FIGURE 5.28 Sequence of operations in the squeeze-casting process. This process combines the advantages of casting and forging.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 87 AE 587
Permanent Mold Casting Squeeze Casting (Melt Forging)
A variation of cold chamber pressure die casting. Results in highly refined grain structure. Used in making pistons for diesel engines. Is performed by:
» Pouring a pre-measured amount of molten metal into the die.
» Allowing the metal to cool below liquidus.» Closing the die.
8/12/2009 88 AE 587
Sample of Squeeze Cast Parts
Source: http://www.entirecoupling.com/Product.htm
8/12/2009 89 AE 587
Permanent Mold Casting :Vacuum Casting
The principle is the same as low-pressure die casting. The pressure inside the die is decreased by a vacuum pump and the difference of pressure forces the liquid metal to enter the die. This transfer is less turbulent than by other casting techniques so that gas inclusions can be very limited. As a consequence, this new technique is specially aimed to components which can subsequently be heat-treated.
This is an alternative to investment casting, shell mold casting, and green-sand casting
Suitable for thin-walled (0.75 mm; 0.03 in.) complex shaped with uniform properties
Can be automated.
8/12/2009 90 AE 587
Vacuum-Casting Process
FIGURE 5.19 Schematic illustration of the vacuum-casting process. Note that the mold has a bottom gate. (a) before and (b) after immersion of the mold into the molten metal. Source: After R. Blackburn.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 91 AE 587
Casting Processes Comparison
TABLE 5.8 Casting Processes, and their Advantages and Limitations.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 92 AE 587
Properties of Die-Casting Alloys
TABLE 5.6 Properties and typical applications of common die-casting alloys.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 93 AE 587
Additional Steps After Solidification
Trimming Removing the core Surface cleaning Inspection Repair, if required Heat treatment
8/12/2009 94 AE 587
Trimming
Removal of sprues, runners, risers, parting‑line flash, fins, chaplets, and any other excess metal from the cast part
For brittle casting alloys and when cross sections are relatively small, appendages can be broken off
Otherwise, hammering, shearing, hack‑sawing, band‑sawing, abrasive wheel cutting, or various torch cutting methods are used
8/12/2009 95 AE 587
Removing the Core
If cores have been used, they must be removed Most cores are bonded, and they often fall out of
casting as the binder deteriorates In some cases, they are removed by shaking casting,
either manually or mechanically In rare cases, cores are removed by chemically
dissolving bonding agent Solid cores must be hammered or pressed out
8/12/2009 96 AE 587
Surface Cleaning
Removal of sand from casting surface and otherwise enhancing appearance of surface
Cleaning methods: tumbling, air‑blasting with coarse sand grit or metal shot, wire brushing, buffing, and chemical pickling
Surface cleaning is most important for sand casting» In many permanent mold processes, this step can be
avoided Defects are possible in casting, and inspection is
needed to detect their presence
8/12/2009 97 AE 587
Heat Treatment
Castings are often heat treated to enhance properties Reasons for heat treating a casting:
» For subsequent processing operations such as machining
» To bring out the desired properties for the application of the part in service
8/12/2009 98 AE 587
Economics of Casting
FIGURE 5.39 Economic comparison of making a part by two different casting processes. Note that because of the high cost of equipment, die casting is economical mainly for large production runs. Source: The North American Die Casting Association.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 99 AE 587
Casting Cost Considerations
Reduced direct assembly costs
Reduced inventory
Reduced floor space
Reduced production flow, control, and inspection operations
8/12/2009 100 AE 587
Factors Influencing Casting Costs
Casting Design» Size, weight, and complexity of the casting are
most important parameters Alloy Selection
» Alloying elements can be expensive (i.e. Ag)» Some alloys are more difficult to melt and pour» Higher temperatures may be needed to produce
desired fluidity» Protective environments may be needed
8/12/2009 101 AE 587
Quality » How well casting meets customer’s requirements» How “repeatable” is the process.» Quality is measured by:
– Chemical and mechanical properties– “defect-free” casting– Accuracy & consistency of dimensions
» Premium quality requirements will lead to cost increase
» Producing substandard part quality leads to cost increase
Factors Influencing Casting Costs
8/12/2009 102 AE 587
Cost of patterns/dies Cost of Tooling Production Quantity Cost of Machining Cost of Heat treatment Other Costs
Factors Influencing Casting Costs
8/12/2009 103 AE 587
Example: Cylinder Head» Scrapped after casting: $50» Scrapped after final machining: $120» Scrapped after component assembly: $500» Replacement engine: $4000
Factors Influencing Casting Costs
8/12/2009 104 AE 587
Process Selection Procedure
1. Identify process characteristics using product design requirements
2. Identify feasible processes (use constraints). Eliminate unfeasible ones
3. Rank feasible processes using desirable criteria (cost, lead time, No. of units, etc.)
4. Identify any additional characteristics of feasible processes
5. Select process of choice
8/12/2009 105 AE 587
Process-Material Relationship
Manufacturing Process Compatible Material(s)
Sand casting F, NF
Die casting F, NF
Investment casting F, NF
Low pressure casting NF
Hot chamber die casting NF
Lost Foam casting F, NF
Cosworth casting NF
F = Ferrous, NF = Non-Ferrous
8/12/2009 106 AE 587
Process-Product Relationship
Manufacturing Process Min Thicknessmm
Sand casting ~5
Die casting ~1
Investment casting 2-3
Low pressure casting 3-5
Lost Foam casting 2-3
8/12/2009 107 AE 587
Other process-product relationships include Shape Capability Surface finish Dimensional tolerances Cost Etc.
Process-Product Relationship
8/12/2009 108 AE 587
Casting Applications
TABLE 5.3 Typical applications for castings and casting characteristics.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 109 AE 587
Metals for Casting
Most commercial castings are made of alloys rather than pure metals » Alloys are generally easier to cast, and properties of
product are better Casting alloys can be classified as:
» Ferrous
» Nonferrous
8/12/2009 110 AE 587
Ferrous Casting Alloys: Cast Iron
Most important of all casting alloys Tonnage of cast iron castings is several times that of
all other metals combined Several types: (1) gray cast iron, (2) nodular iron, (3)
white cast iron, (4) malleable iron, and (5) alloy cast irons
Typical pouring temperatures 1400C (2500F), depending on composition
8/12/2009 111 AE 587
Properties & Applications of Cast Iron
TABLE 5.4 Properties and typical applications of cast irons.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 112 AE 587
Cast Irons
Gray cast iron : » 2.5% to 4% C and 1% to 3% Si» Has graphite flakes
Ductile Iron:» Has similar C and Si content as gray cast iron but with
graphite spheroids White cast iron
» 2% to 3.3% C and 0.7% to 2% Si» Produced by rapid cooling thus has cementite rather than
flakes Malleable iron
» Heat treated white cast iron to get carbon out of cementite to form graphite
8/12/2009 113 AE 587
Microstructure for Cast Irons
FIGURE 5.14 Microstructure for cast irons. (a) ferritic gray iron with graphite flakes; (b) ferritic nodular iron, (ductile iron) with graphite in nodular form; and (c) ferritic malleable iron. This cast iron solidified as white cast iron, with the carbon present as cementite (Fe3C), and was heat treated to graphitize the carbon.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 114 AE 587
Ferrous Casting Alloys: Steel
The mechanical properties of steel make it an attractive engineering material
The capability to create complex geometries makes casting an attractive shaping process
Difficulties when casting steel:» Pouring temperature of steel is higher than for most
other casting metals 1650C (3000F)
» At such temperatures, steel readily oxidizes, so molten metal must be isolated from air
» Molten steel has relatively poor fluidity
8/12/2009 115 AE 587
Nonferrous Casting Alloys: Aluminum
Generally considered to be very castable Pouring temperatures low due to low melting
temperature of aluminum » Tm = 660C (1220F)
Properties: » Light weight
» Range of strength properties by heat treatment
» Easy to machine
8/12/2009 116 AE 587
Nonferrous Casting Alloys: Copper Alloys
Includes bronze, brass, and aluminum bronze Properties:
» Corrosion resistance
» Attractive appearance
» Good bearing qualities Limitation: high cost of copper Applications: pipe fittings, marine propeller blades,
pump components, ornamental jewelry
8/12/2009 117 AE 587
Nonferrous Alloys
TABLE 5.5 Typical properties of nonferrous casting alloys.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 118 AE 587
Aluminum Casting
Aluminum is cast using» Sand casting.» Permanent Mold (gravity feed) casting.» Cold chamber pressure die casting.» Cosworth casting.» Low pressure die casting.
Steel dies are used in die casting of Al
8/12/2009 119 AE 587
Advantages of Al Alloys for Casting
Low melting temperature. Negligible solubility of all gases (except hydrogen) in
molten Al. Good surface finish of the cast product. Good fluidity. Better creep properties than wrought Al alloys.
8/12/2009 120 AE 587
Hydrogen Solubility in Aluminum
FIGURE 5.36 Solubility of hydrogen in aluminum. Note the sharp decrease in solubility as the molten metal begins to solidify.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 121 AE 587
Problem with Al Castings
Variability in mechanical properties. Shrinkage in the amount of (3.5%- 8.5%). Mechanical properties are inferior to wrought Al
products.
8/12/2009 122 AE 587
Advantages of Mg Die Casting
High fluidity in most alloys Lower volumetric specific heat than Al and Zn Low density Low solubility of Fe in liquid Mg Good machineability.
8/12/2009 123 AE 587
Post-Casting Operations for Mg
Trimming Heat treating Machining Surface treatment Forming Joining
8/12/2009 124 AE 587
Characteristics of Zinc Die Castings
Fast cooling rate, thus fine grains
Castings solidify from mold walls to center creating fine grains with low porosity in walls, and larger more porous grains in the core
Wall
Core
http://www.dezign.org/zinc
8/12/2009 125 AE 587
Mold made of steel or graphite
U-shaped riser is often used with gravity die casting
Thicker gates are also used with gravity die casting
Characteristics of Zinc Die Castings
http://www.dezign.org/zinc
8/12/2009 126 AE 587
Characteristics of Casting
TABLE 5.2 General characteristics of casting processes.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 127 AE 587
Furnaces for Casting Processes
Furnaces most commonly used in foundries:» Cupolas
» Direct fuel‑fired furnaces
» Crucible furnaces
» Electric‑arc furnaces
» Induction furnaces
8/12/2009 128 AE 587
Cupolas
Vertical cylindrical furnace equipped with tapping spout near base
Used only for cast irons» Although other furnaces are
also used, the largest tonnage of cast iron is melted in cupolas
The "charge," consisting of iron, coke, flux, and possible alloying elements, is loaded through a charging door located less than halfway up height of cupola
Cupola furnace used in melting cast ironSource: Groover
8/12/2009 129 AE 587
Direct Fuel‑Fired Furnaces
Small open‑hearth in which charge is heated by natural gas fuel burners located on side of furnace
Furnace roof assists heating action by reflecting flame down against charge
At bottom of hearth is a tap hole to release molten metal
Generally used for nonferrous metals such as copper‑base alloys and aluminum
8/12/2009 130 AE 587
Crucible Furnaces
Metal is melted without direct contact with burning fuel mixture
Sometimes called indirect fuel‑fired furnaces Container (crucible) is made of refractory material or
high‑temperature steel alloy Used for nonferrous metals such as bronze, brass,
and alloys of zinc and aluminum
Three types used in foundries: (a) lift‑out type, (b) stationary, (c) tilting
8/12/2009 131 AE 587
Crucible Furnaces
Figure 11.19 Three types of crucible furnaces: (a) lift‑out crucible, (b) stationary pot, from which molten metal must be ladled, and (c) tilting-pot furnace.
Source: Groover
8/12/2009 132 AE 587
Electric‑Arc Furnaces
Charge is melted by heat generated from an electric arc
High power consumption, but electric‑arc furnaces can be designed for high melting capacity
Used primarily for melting steel
Figure 6.9 Electric arc furnace
for steelmakingSource: Groover
8/12/2009 133 AE 587
Induction Furnaces
Uses alternating current passing through a coil to develop magnetic field in metal
Induced current causes rapid heating and melting
Electromagnetic force field also causes mixing action in liquid metal
Since metal does not contact heating elements, environment can be closely controlled to produce molten metals of high quality and purity
Melting steel, cast iron, and aluminum alloys are common applications in foundry work
Figure 11.20 Induction furnaceSource: Groover
8/12/2009 134 AE 587
Ladles
Moving molten metal from melting furnace to mold is sometimes done using crucibles
More often, transfer is accomplished by ladles
Figure 11.21 Two common types of ladles: (a) crane ladle, and (b) two‑man ladle. Source: Groover
8/12/2009 135 AE 587
Casting Quality
There are numerous opportunities for things to go wrong in a casting operation, resulting in quality defects in the product
The defects can be classified as follows:» General defects common to all casting processes
» Defects related to sand casting process
8/12/2009 136 AE 587
A casting that has solidified before completely filling mold cavity
Figure 11.22 Some common defects in castings: (a) misrun
General Defects: Misrun
Source: Groover
8/12/2009 137 AE 587
Two portions of metal flow together but there is a lack of fusion due to premature freezing
Figure 11.22 Some common defects in castings: (b) cold shut
General Defects: Cold Shut
Source: Groover
8/12/2009 138 AE 587
Depression in surface or internal void caused by solidification shrinkage that restricts amount of molten metal available in last region to freeze
Figure 11.22 Some common defects in castings: (d) shrinkage cavity
General Defects: Shrinkage Cavity
Source: Groover
8/12/2009 139 AE 587
Casting DefectCasting Defect
Micro Defects Gas Porosity Microshrinkage Porosity or
microporosity Inclusions
Inclusions
Courtesy of Dr. J. Boileau
8/12/2009 140 AE 587
Elimination of Porosity in Castings
FIGURE 5.37 (a) Suggested design modifications to avoid defects in castings. Note that sharp corners are avoided to reduce stress concentrations; (b, c, d) examples of designs showing the importance of maintaining uniform cross-sections in castings to avoid hot spots and shrinkage cavities.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 141 AE 587
Balloon‑shaped gas cavity caused by release of mold gases during pouring
Figure 11.23 Common defects in sand castings: (a) sand blow
Sand Casting Defects: Sand Blow
Source: Groover
8/12/2009 142 AE 587
Formation of many small gas cavities at or slightly below surface of casting
Figure 11.23 Common defects in sand castings: (b) pin holes
Sand Casting Defects: Pin Holes
Source: Groover
8/12/2009 143 AE 587
When fluidity of liquid metal is high, it may penetrate into sand mold or core, causing casting surface to consist of a mixture of sand grains and metal
Figure 11.23 Common defects in sand castings: (e) penetration
Sand Casting Defects: Penetration
Source: Groover
8/12/2009 144 AE 587
A step in cast product at parting line caused by sidewise relative displacement of cope and drag
Figure 11.23 Common defects in sand castings: (f) mold shift
Sand Casting Defects: Mold Shift
Source: Groover
8/12/2009 145 AE 587
Foundry Inspection Methods
Visual inspection to detect obvious defects such as misruns, cold shuts, and severe surface flaws
Dimensional measurements to insure that tolerances have been met
Metallurgical, chemical, physical, and other tests concerned with quality of cast metal
8/12/2009 146 AE 587
Design Considerations for Casting
8/12/2009 147 AE 587
Design for Casting
FIGURE 5.38 Suggested design modifications to avoid defects in castings. Source: Courtesy of The North American Die Casting Association.
Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian • Schmid© 2008, Pearson EducationISBN No. 0-13-227271-7
8/12/2009 148 AE 587
Product Design Considerations
Corners on the casting:» Sharp corners and angles should be avoided, since
they are sources of stress concentrations and may cause hot tearing and cracks
» Generous fillets should be designed on inside corners and sharp edges should be blended
8/12/2009 149 AE 587
Product Design Considerations
Draft Guidelines:» In expendable mold casting, draft facilitates removal of
pattern from mold – Draft = 1 for sand casting
» In permanent mold casting, purpose is to aid in removal of the part from the mold
– Draft = 2 to 3 for permanent mold processes
» Similar tapers should be allowed if solid cores are used
8/12/2009 150 AE 587
Core Elimination
Minor changes in part design can reduce need for coring
Figure 11.25 Design change to eliminate the need for using a core: (a) original design, and (b) redesign.
Source: Groover
8/12/2009 151 AE 587
Product Design Considerations
Dimensional Tolerances and Surface Finish:» Significant differences in dimensional accuracies
and finishes can be achieved in castings, depending on process:
– Poor dimensional accuracies and finish for sand casting
– Good dimensional accuracies and finish for die casting and investment casting
8/12/2009 152 AE 587
Product Design Considerations
Machining Allowances:» Almost all sand castings must be machined to achieve
the required dimensions and part features
» Additional material, called the machining allowance, is left on the casting in those surfaces where machining is necessary
» Typical machining allowances for sand castings are around 1.5 and 3 mm (1/16 and 1/4 in)
8/12/2009 153 AE 587
Shrinkage behavior of Various Alloys
The defects caused by shrinkage vary with the type of alloy. This can be explained with the adjoining figure 1. All alloys exhibit a large shrinkage volume.
» (a) Directionally solidifying alloys cause large shrinkage voids.
» (b) An eutectic type alloy causes shrinkage depression.
» (c) An Equiaxed solidifying alloy produces shrinkage in the form of small voids and dispersed shrinkage. Showcasing
various shrinkage defectsfor different alloys.
8/12/2009 154 AE 587
Solidification and Shrinkage
The figures above showcase various solidifications and their respective shrinkages. The shrinkage associated with each type of alloy changes with the riser and plate design. Consider the Fig 2(a) in this the alloy is a directionally solidifying type and by adding a taper to the plate the shrinkage has been forced from plate to the riser. In the case of eutectic alloy shown in Fig 2(b) there is shrinkage associated in the form of a depression in the riser. While in equiaxed alloy as shown in Fig 2(c), no change in the plate taper results in less shrinkage. In this case sections must be frozen at the same rate if possible.
Figure 2a: DirectionallySolidifying Alloy.
Figure 2b: Eutectic Alloy. Figure 2c: Equiaxed Alloy.
8/12/2009 155 AE 587
Design Strategies to Counteract Shrinkage
Provision of a riser near the heavier section in a casting results in reduction of shrinkage.
Proper design of casting whereby lighter section follows a heavier section resulting in less shrinkage.
Proper design of casting helps in the reduction of shrinkage defects.
Source: Schrader & Elshennawy
8/12/2009 156 AE 587
Design Strategies to Counteract Shrinkage
Replacing sharp corners and angles with fillets (Fig.4) results in less defects associated with shrinkage along with a reduction in stresses caused due to thermal stress concentrations.
Providing fillets and taper helps in Reduction of thermal stresses near joints.
Source: Schrader & Elshennawy
8/12/2009 157 AE 587
Strategies to Avoid Defects During Cooling
Mechanical stresses are induced in a casting on cooling. The solidification process in metals always proceeds from the mold face to the center of the casting.
Sharp corners and angles cause higher stresses and hence rounding of corners is suggested in the Figure Rounding of corners necessary for
reduction in stresses.
Source: Schrader & Elshennawy
8/12/2009 158 AE 587
Strategies to Avoid Defects during Cooling
The design engineer must take into consideration the cooling curves for various junction designs. The best casting design would entail bringing the minimum number of sections and also by avoiding acute angles along with large fillets.
Cooling curves can be consulted in designing junctions in castings.
Source: Schrader & Elshennawy
8/12/2009 159 AE 587
Slag and Dross Formation
Slag/Dross – These are synonyms meaning “refuse from melting of metals”. Although slag is usually referred with higher melting point metals and dross with lower melting point metals.
Various metals have varying tendencies for the formation of slag/dross. This makes it critical in choosing the right alloy for the casting. Not necessarily choosing the alloy which causes less slag/dross but by choosing the alloy keeping in mind the application.
8/12/2009 160 AE 587
Pouring Temperature
Pouring temperature becomes a critical parameter in casting design due to the extremely high temperatures associated with molten metal.
The designer must hence take into consideration problems associated with thermal degradation of the mold and formation of hot spots.
8/12/2009 161 AE 587
Metal Alloys and Their Approximate Pouring Temperatures
Table 2 courtesy “Tool and Manufacturing Engineers Handbook” provides the design engineer with approximate pouring temperatures which would result in the least amount of thermal abuse.
The pouring temperatures would also be affected with the type of mold material, eg: Only titanium alloys are poured in graphite molds.
Table 2: Table gives recommended approximate poring temperatures.
8/12/2009 162 AE 587
Section Thicknesses
Due to variable cooling rates sections designed should be as uniform in thickness as possible. Non uniform sections would cause defects in the casting due to the variable cooling rates. Chills can be provided to counteract this phenomenon
Uniform thickness of section for the lugs is recommended.
Source: Schrader & Elshennawy
8/12/2009 163 AE 587
Correct proportioning of inner wall dimensions
Cooling rates of inner portions are much slower compared to outer surfaces. This makes it necessary to avoid as far as possible sharp angles and corners.
A good rule of thumb is to reduce the inner sections to 9/10th the thickness of the outer walls.
Reduction of the inner section to 9/10th of outer walls.
Source: Schrader & Elshennawy
8/12/2009 164 AE 587
Correct proportioning of inner wall dimensions
For economy purposes the radius of the inner cylinder should be bigger than the wall thickness. As in in the Figure since the inner radius is much smaller it is advisable to cast it as a solid and to then drill the required hole.
Inner cylinder should be bigger than the casting wall thickness.
Source: Schrader & Elshennawy
8/12/2009 165 AE 587
Rib Design Principles
Since ribs are designed to increase stiffness and for weight reduction. So if the ribs are designed with less depth or are widely spaced they become redundant.
Thickness of the ribs should be 80% of casting thickness and the ribs should be rounded at the edges and filleted correctly.
Figures show the Do’s and Don’t’s of Rib design in castings.
Source: Schrader & Elshennawy
8/12/2009 166 AE 587
Rib Design
Design of complex ribbing should be avoided where necessary due to simplification in casting process on the whole.
If the casting wall itself can provide the necessary stiffness then omission of ribs is recommended.
Complex Rib design should be avoided if possible.
Source: Schrader & Elshennawy
8/12/2009 167 AE 587
Bosses, Lugs and Pads
Since bosses and pads increase the metal thickness this entail results in hot spots in the casting requiring the presence of chills etc. Hence it is recommended to not use these elements where possible.
Best design practices for bosses and pads.
Source: Schrader & Elshennawy
8/12/2009 168 AE 587
Bosses, Lugs and Pads
As is the case with junction design the design of bosses should be such that they seamlessly mate with the casting with the help of proper tapers and allowances as in the Figure.
Table 3 gives an approximate reference guide for the heights of bosses.
Table 3: Guide to designing bosses.
Recommended design for bosses and pads.
Source: Schrader & Elshennawy
8/12/2009 169 AE 587
Redundancies
By providing a recess in the above casting. Cost becomes a factor due to the need for a core. This can be reduced if the casting can be done solid without the recess. So the design engineer must work closely in minimizing the complexities involved in the casting.
A projection increases the cost of making a casting
Source: Schrader & Elshennawy