Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A....
-
Upload
jocelin-bennett -
Category
Documents
-
view
214 -
download
1
Transcript of Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A....
![Page 1: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/1.jpg)
Magneto-Optical Study of High Purity Nb for SRF Application
A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier
ASC, NHMFL, FSU,Tallahassee, USA
SSTIN-2010, Jefferson Lab, NewPort News, Virginia, September 22-24, 2010
This work was supported by the US DOE under grants DE-FG02-07ER41451, FNAL PO 570362, and the Florida State
![Page 2: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/2.jpg)
3D Parametric Surface
1
2
3D Parametric Surface
1
2
MOTIVATION• The recent studies showed that superconducting cavity
performance is very sensitive to quality of Nb surface.
• The penetration of small numbers of flux lines into the cavity surface during RF operation is leading to breakdown of the superconducting state and causing Q-drop or quench.
• Q-drop can be triggered by early flux penetration in hotsports leading to thermal breakdown on the cavity surface (1 and 2). (Model by A. Gurevich).
1
4
7
10
13
16
19
22
25
28
31
34
S1 S
3 S5 S
7 S9
S1
1
S1
3
S1
5
0
0 .1
0 .2
0 .3
0 .4
0 .5
0 .6
0 .7
T ( K )
A z im u t hB o t t o m I r is
T o p Ir i s
E q u a t o r
Q 0 = 2 .8 1 0 9
B p = 1 1 0 m T
1
2
1
4
7
10
13
16
19
22
25
28
31
34
S1 S
3 S5 S
7 S9
S1
1
S1
3
S1
5
0
0 .1
0 .2
0 .3
0 .4
0 .5
0 .6
0 .7
T ( K )
A z im u t hB o t t o m I r is
T o p Ir i s
E q u a t o r
Q 0 = 2 .8 1 0 9
B p = 1 1 0 m T
1
2
• Local study of flux penetration is important
![Page 3: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/3.jpg)
MOTIVATION
Magnetization and Magneto-Optical Imaging (MOI) techniques can detect local magnetic flux penetrate in Nb
![Page 4: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/4.jpg)
EXPERIMENTALTECHNIQUE :
1. MAGNETO-OPTICAL2. VSM3. SEM4. ZYGO LIGHT MICROSCOPY by Z. H. Sung(See:www.zygo.com/?/products/nv6000)
![Page 5: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/5.jpg)
Protective layer
F=V Bz 2d
dBa,z GGG
YIG: Bi
Polarized light
M
Ba,x
PRINCIPILE OF MAGNETO-OPTICAL TECHNIQUE MAGNETO-OPTICAL INDICATOR ON BASE OF GARNET
FILM DOPED BY Bi DETECTS MAGNETIC FIELD
Reflective layerNb
![Page 6: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/6.jpg)
M
AP
H
H
H=0
THE FARADAY ROTATION IN A FERRIMAGNETIC Bi-DOPED IRON GARNET INDICATOR FILMS WITH IN-PLANE
MAGNETIZATION
LIGHT POLARIZATION
![Page 7: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/7.jpg)
MAGNETO-OPTICAL CONTRAST PICKS UP ON PLASTIC REFRIGIRATE CARD:
DISTRIBUTION OF STRAY FIELD AROUND MAGNETIC STRIPS
![Page 8: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/8.jpg)
5.25 inch disc 3.5 inch disc Audio tape
MO IMAGES OF MAGNETIC FIELD IN AUDIO TAPE AND COMPUTER DISCETS
500m 100m
![Page 9: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/9.jpg)
(AAA)
American Automobile
Association Card
Library Vendor
Card
Visa Credit
Card
500m
MO IMAGES OF MAGNETIC CODES IN DIFFERENT PLASTIC CARDS
![Page 10: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/10.jpg)
MAGNETO-OPTICAL IMAGE OF MAGNETIC SECURITY CODE IN US $100
![Page 11: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/11.jpg)
He
CRYOSTAT
TV
cryostat
MAGNETO-OPTICAL IMAGING SETUP FOR SUPERCONDUCTING RESEARCH: electromagnetic
system creates magnetic field in two direction: X and Z
Polarized Optical Microscope
Hext
ZHext
X
LHe
![Page 12: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/12.jpg)
MAGNETO-OPTICAL SETUP ON THE BASE OF A POLARIZING MICROSCOPE IN REFLECTIVE MODE
![Page 13: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/13.jpg)
Hz=(1/1-Nz) x Hext
Hext
Z
X
GEOMETRY OF MAGNETO-OPTICAL EXPERIMENT ON Nb SAMPLES FOR CAVITY APPLICATION IN
PERPENDICULAR-Z AND PARALLEL-X (IN-PLANE) FIELDS
Demagnetization factor Nz
NbNbNb
MO indicator
MO indicator with in-plane magnetization detects the normal component of magnetic flux
![Page 14: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/14.jpg)
MAGNETIC FLUX DISTRIBUTION IN RECTANGULAR SAMPLE: EFFECT OF SAMPLE SHAPE WITH DEMAGNETIZATION
FACTOR Nz>0.
MOI of magnetic flux distribution in uniform square
Nb sample
1 mm
Maximum field enhancement at the center of each side.
(“roof pattern” or “pillow”)
![Page 15: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/15.jpg)
MSC
ZERO FIELD COOLED (ZFC) IN PERPENDICULAR FIELD: MO images in uniform rectangular and circle Nb samples
1 mm
Calculated current streamlines
MO images
(“roof pattern” or “pillow”)
![Page 16: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/16.jpg)
SC
FIELD COOLED (FC) IN PERPENDICULAR FIELD: MO images trapped magnetic flux in uniform rectangular and circle Nb
samples
Calculated current streamlines
MO images(“roof pattern”
![Page 17: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/17.jpg)
SAMPLES
Thomas Jefferson Lab National Accelerator Facility (JLAB):• Nb samples were cut from 1.8 mm thick large slice from the extremely large grain ingot fabricated by CBMM - Brazil for Jlab: GBs were randomly oriented • In case of cavities some planes of GBs could be parallel to direction of RF magnetic field
Fermi National Accelerator Laboratory (FNAL): • Nb pure polycrystalline samples taken through a typical cavity optimization process and cut from regular and weld regions• Samples with artificial grooves and deformed samples• Samples with PIT in weld seam
![Page 18: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/18.jpg)
JLAB samples with big grains were cut from extremely large-
grain ingotSamples rectangular and circle shapes were cut from large
grain 1.8 mm thick material fabricated by CBMM-Brazil
Disc shape sample- to avoid flux penetration due to sample shape
Bi-crystal and Tri-crystal samples
Plane of GBs were perpendicular and random oriented to face of sample: some plane of GBs in cavity wall parallel to RF field
![Page 19: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/19.jpg)
Tri-crystalTri-crystal
Tri-crystal
Tri-crystal
Bi-crystalGB (#1)
Normal to Surface
Bi-crystalGB (#1)
Normal to SurfaceBi-crystalGB (#2)
Angle to Surface
Bi-crystalGB (#2)
Angle to Surface
Nb slice was cut from ingot with big grains. Sample shapes: rectangular and circle (disc) with big variety of GBs
Tri-crystalTri-crystal
Thickness of sheet is 1.88 mm
GB #2GB #1
RF field in-plane
![Page 20: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/20.jpg)
Overlap top and bottom surfaces of Nb sheet with traces of GBs, Sample #9
Bottom face
Top face
GB #1 and GB #2 form triple-point. Plane of of GB #1 twisted in the vicinity of the triple point: Orientation of RF field in cavity may be parallel the plane of any GBs. Samples were taken from different part of GB#1 and GB#2 and in triple-point
#9
![Page 21: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/21.jpg)
Perpendicular and random angle orientation GBs in bi- and tri-crystals samples rectangular and round shapes
GB #2 has angle about 30-35 degree to wide face of sample
bi-crystal
GB#1 perpendicular to wide face of sample
bi-crystal
![Page 22: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/22.jpg)
MO imaging sample on different surface: when GB - 330 angle and after 900 rotation - GB perpendicular to surface
GB trace on top face of sample
No GB trace on side face
GB trace on bottom face of sample
This face has been imaged by MO, when sample was turned by 900
H
MO indicator
2.78mm
2.17
mm1.89mm
![Page 23: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/23.jpg)
H=80 mT T=5.4K
H=100 mT
Bi-crystal #6 with the 330 angle GB #2 to surface, no remarkable flux penetration along GB
1 mm
Optical, GB#2, angle to surface 330
![Page 24: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/24.jpg)
MO Image and current distribution in sample with perpendicular plane , ZFC, T=5.5K. 170GB #1 admits magnetic flux and shows
obstacle to current flow: distortion of current stream lines
1 mm
GB #1
T=5.5K H=80 mT
17.80 GB17.80 GB 17.80 GB
Current streamline : GB is obstacle to
current flow Jb=0.5Jc
![Page 25: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/25.jpg)
Misorientation angle between two grains ≈17.8o Orientation Imaging Microscopy (OIM): from D. Abraimov
17.80 GBMisorientation profile
![Page 26: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/26.jpg)
Nb JLAN #3A bicrystal, Jc in grain and across GB
T, K
5 6 7 8 9 10
Jc,
kA/c
m2
0
10
20
30
40
50
60
Jc, Grain Jc, GB
Critical current vs T : bulk Jc and Jb across 17.80 GB (from MO measurement)
Ratio Jgb/Jb
T, K
5 6 7 8 9 10
R=
Jgb
/Jb
0.25
0.30
0.35
0.40
0.45
0.50
0.55
0.60
Nb 17.80 GB T=5.5 K Jb ~ 0.5Jc
YBCO 50 GB T=7 K Jb ~ 0.5JcA.A. Polyanskii, at el, Phys. Rev. B, 53, 8687, (1996).
![Page 27: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/27.jpg)
MAGNETIC FLUX BEHAVIOR AROUND 3o, 5o, and 10o GRAIN BOUNDARIES in YBCO bi-crystals T = 7 K, H ~ 40 mT, H||c
10o GB
Jb/Jc =0.95
A.A. Polyanskii, at el, Phys. Rev. B, 53, 8687, (1996).
5o GB3o GB
Jb=0.95Jc Jb=0.5Jc Jb=0.065Jc
![Page 28: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/28.jpg)
#9 H=28 mT
#11 H=32 mT #13 H=40 mT
After 900 rotation GB is perpendicular to surface. GB is a weak link in ZFC and FC. T=6K
#23 H=0 FC T=6K
#7 H=24 mT #8 H=26 mT
1 mm
GB#2
GB#2
GB#2
![Page 29: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/29.jpg)
GB perpendicular to surface: Top and bottom surfaces of Nb sample after electro-polishing (EP) has different roughness
Top surface. After Mechanical polishing + Electropolishing
Bottom surface. After diamond saw + Electropolishing
GB is not visible GB hardly
visible
TOP BOTTOM
![Page 30: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/30.jpg)
MO image of top and bottom surfaces of Nb sample after (EP): good flux penetration on both surfaces
ZFC H=60 mT T=6.5KCurrent streamline on top side: GB is obstacle to current flow
TOP BOTTOM
Nb sample with GB perpendicular to surface.
![Page 31: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/31.jpg)
ROUND JLAB SAMPLE, with random oriented GBs in triple-point
Bottom face
Top face
![Page 32: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/32.jpg)
#81 H=80 mT, ZFC T=5.5K
Tri-crystal #9 fully processed: 5 steps, top face, no preferential flux penetration along GBs, but flux penetrates faster in some additional local places ??
GB #2
GB #1
GB #2
GB #1
GB #2
Optical, top face. Shape is not perfectly round.
1 mm
![Page 33: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/33.jpg)
JLAB #11 with GB #2 with angle 30-350 , ZFC T=5.6K. No flux penetration along GB #2. Flux penetrates in some additional places much faster. What is a reason??
#33 H=86 mTSurface, bottom face
GB #2
1 mm
![Page 34: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/34.jpg)
Tri-crystal #12, fully processed: 5 steps, top face, no preferential flux penetration due to GBs. Asymmetric flux penetration
GBs
Optical, top surface #15 ZFC H=72 mT
![Page 35: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/35.jpg)
Optical, Surface of tri-crystal 3D MODEL of GBs on the base GB traces on top and bottom. Random orientation (Peter Lee)
1 mm
Nb tri-crystal JLAB #4: GBs with random orientation, thickness is 1.88 mm
![Page 36: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/36.jpg)
1 mm
T=5.5 K H=120 mT Remn T=7 K H=0 after H=24 mT
Visible traces of GB
Nb tri-crystal JLAB #4: no penetration at to GB with random orientation, no evidence of weak link, but traces of GBs are visible
![Page 37: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/37.jpg)
1. GBs can accept magnetic flux in case when plane of GB is parallel to external magnetic field2. Some additional flux penetration has been found on surface of many fully processed samples.
MO conclusion on Jlab samples with big grains
![Page 38: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/38.jpg)
SAMPLES FROM FNAL FNAL samples-square shape 3.75 x 3.75 x 1.5 mm were cut from
the same 2.8 mm thick sheet (RRR~ 450) but in two different places:
• Samples from fine-grained Nb sheet (regular), where grain sizes were small ~ 50 m,
• Samples from weld region, where grain sizes were big > 1 mm
• Both types of samples taken through a typical cavity optimization process:
• The processing sequence includes 5 steps:
• (1) cold work produced by the sample machining process, followed by degreasing,
• (2) ~100 m BCP etch,
• (3) HT 5 hours at 750°C in a vacuum < 10-6 Torr,
• (4) ~20 m BCP etch
• (5) bake 50 hours at 120°C in a vacuum < 10-6 Torr
![Page 39: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/39.jpg)
SOME EXAMPLE: OPTICAL IMAGES OF Nb samples cut feom REGULAR AND WELD regions
1 mm
Machine marks (like grooves), large grains and steps at GBs are well visible
REGULAR AREA: small grain size
WELDED AREA: large grain size
![Page 40: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/40.jpg)
VSM Magnetization of Regular and Weld samples taken through a typical cavity optimization process: 5 steps. Magnetization hysteresis is significantly reduced after step 4, the large reduction Hc2 and the small increase in the first field of flux penetration
Regular: small grains Weld: big grains
![Page 41: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/41.jpg)
MOI of Regular samples with small grains taken through a typical cavity optimization process: 5 steps
1 mm
80 мТ 80 мТ 34 мТ 48 мТ40 мТ
60 мТ 60 мТ 30 мТ 40 мТ34 мТ
Optical
ZFC Then H applied
ZFC Then H applied
FC in 110 mT, then H=0 applied
2. 100 µm etch1. CW, degrease 3. HT 5 hr/7500C 5. Bake 50 hr/1200C4. 20 µm etch
![Page 42: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/42.jpg)
MOI of Weld samples with big grains taken through a typical cavity optimization process: 5 steps
1 mm
Optical
ZFC Then H applied
ZFC Then H applied
FC in 110 mT then H=0 H applied
80 мТ 80 мТ 40 мТ 48 мТ40 мТ
60 мТ 48 мТ 36 мТ 31 мТ31 мТ
2. 100 µm etch1. CW, degrease 3. HT 5 hr/7500C 5. Bake 50 hr/1200C4. 20 µm etch
![Page 43: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/43.jpg)
We have observed unusual central flux penetration in weld sample after HT and 20
min BCP (second etching), step 3, 4
Details of flux penetration
![Page 44: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/44.jpg)
32 mT T=5.6KHx
Hz
Details of a flux nucleation on surface weld sample in perpendicular field: demagnetization factor of sample Nz 0
Optical, machinery marks (grooves) and large grains are well visible
Enhancement of magnetic flux at surface defect
1 mm
![Page 45: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/45.jpg)
#28 H=54 mT
ZFC T=5.6 K
Details of a flux nucleation on surface W2-5 in perpendicular field: Expansion of central flux penetration vs H
1 mm
#27 H=52 mT
![Page 46: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/46.jpg)
#30 ZFC H=56 mT
Details of a flux nucleation on surface W2-5 in perpendicular field: Farther expansion of central flux penetration in weld sample ZFC T=5.6 K
X, m
0 1000 2000 3000 4000
Inte
nci
ty (
a.u
.)
500
1000
1500
2000
2500
3000
3500
4000
1 mm
Flux profile taken across sample
![Page 47: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/47.jpg)
T=5.6K 48 mT
Surface profile taken along marked line (ZYGO microscope). Max step height is about 10 m
Form of penetrated flux correlates with surface shape
Surface weld sample and profile: “dome” shape. Good correlation with MO central flux penetration.
1 mm
![Page 48: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/48.jpg)
• MO STUDY IN IN-PLANE FIELD.
• OPTICAL STUDY THE SURFACE OF WELD SAMPLE BY USING ZYGO LIGHT MICROSCOPE (See:www.zygo.com/?/products/nv6000) (by SUNG).
Topological defects on surface weld sample
![Page 49: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/49.jpg)
H in-plain =60 mT
H
H
MO contrast in in-plane field on topological defects, when field changes direction. MO contrasts are different on different defects: double and monochrome.
Machinery marks have double MO contrast (black and white)
Steps at GBs have only monochrome contrast
1 mm
H
![Page 50: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/50.jpg)
1
32
4
5
In-plane field 60 mT, T=5.7KX, m
0 1000 2000 3000 4000
Inte
nsity
(a.
u.)
40
60
80
100
120
140
160
180
200
220
1
32
4
52 3
Enhancement of normal component Hz on steps at GBs, well visible on profile by Zygo microscope
1 mm
H in H in
![Page 51: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/51.jpg)
MECHANICAL POLISHING AND BCP ON WELD SAMPLE
Mechanical polishing with 0.05 m Alumina Suspension
BCP condition
-HF(49%):HNO3(69.5%):H3PO4(85%) = 1:1:2
-Temp; ~13˚C, Time; ~7 min
![Page 52: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/52.jpg)
Before mechanical polishing
After mechanical polishing: traces of GBs are still visible, but machinery marks (grooves) disappeared
Weld sample after mechanical polishing with 0.05 m Alumina Suspension and BCP
After BCP: grains and GBs are well visible, but machinery marks (grooves) disappeared
![Page 53: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/53.jpg)
Zygo light microscope images and surface profiles of weld sample before and after mechanical polishing with 0.05 m Alumina Suspension and BCP
Before mechanical polishing
After mechanical polishing
After BCP
![Page 54: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/54.jpg)
Mechanical polishing BCP
Weld sample after mechanical polishing and BCP
H=60 mT H=60 mTH=60 mT
![Page 55: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/55.jpg)
TOP FACE
Nb O Al Si 41.29 % : 56.73% : 1.62% : 0.36%
SEM on BCP weld sample : BCP produces steps at GBs . As longer BCP as bigger steps
![Page 56: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/56.jpg)
Our study found influence of topological features which are on the surface of fully processed Nb weld sample:
• The second chemical etch (BCP) creates steps at GBs (10-15 m ) and cause the surface to “dome” shape.
• Concentration of magnetic flux much stronger at surface steps than at grooves due to different sizes. The surface steps may be are one of the reasons the hotsport on the cavity surface, where nonuniform thermal breakdown actually happened.
• Sample with demagnetization factor Nz>0 in perpendicular field deforms external magnetic field and creates in-plane components. In-plane components concentrate magnetic flux at GB steps and ignites unusual flux penetration into the center of weld Nb. The “dome” surface contributes the propagation flux toward the edge.
• Mechanical polishing and BCP removed steps and “dome” surface and restored classical flux behavior.
![Page 57: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/57.jpg)
JLAB single crystal with artificial defect (groove) on the surface
Surface, artificial notch
0.5 mm
Depth of notch is not the same on both edges
0.5 mm
![Page 58: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/58.jpg)
Remn H=80 mT T=7KZFC H=40 mT T=7K
Artificial defect (groove) has small impact on flux distribution
![Page 59: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/59.jpg)
no deformation
1 mm35% deformation 46% deformation
MO images of trapped flux in Nb discs deformed by compression at T=6K (samples deformed at Fermi Lab and received from A. Romanenko)
![Page 60: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/60.jpg)
Sample for MO
1 mm
Weld Pit 1
Slice cut from welding area with PIT for MO
Pit in weld seam (Fermi from L. Cooly)
Pit 1 contour map: “moat” around the peaks
![Page 61: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/61.jpg)
1 mm
#20 T=7K ZFC H=40 mT
#27 T=7K ZFC H=100 mT
#28 T=7K H=0 Remn after H=100 mT
MO images in PIT area: obviously more stronger resistivity to flux penetration
Pit 1 in weld seam
Optical, cross-section area with PIT
![Page 62: Magneto-Optical Study of High Purity Nb for SRF Application A.A. Polyanskii, Z.H. Sung, P.J. Lee, A. Gurevich, D.C. Larbalestier ASC, NHMFL, FSU,Tallahassee,](https://reader030.fdocuments.us/reader030/viewer/2022032604/56649e6a5503460f94b67f48/html5/thumbnails/62.jpg)
SUMMARY• MOI is a sensitive tool to check superconducting property of Nb for cavity application
• GBs can admit magnetic flux and depress superconductivity, if magnetic field parallel to plane of GBs
• GBs do not admit magnetic flux in case of random orientation of GB.
• Some additional flux penetration has been found on surface of many fully processed samples. We do not know the reason. It will takes some more study.
• In-plane orientation of magnetic field: detect enhancement of magnetic field on topological defects
• Topological defects stimulate the nucleation of magnetic flux in Nb and may depress superconductivity and Q-drop can be triggered by early flux penetration