Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special...
Transcript of Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special...
![Page 1: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/1.jpg)
Lessons Learned From Nitrogen Doping at JLab
Ari D. Palczewski, SRF Scientist Jefferson Lab, USA
9/14/2015
Exploration of Surface Resistance with Varied Interstitial Atom Diffusion on Niobium Cavity Surfaces
MOBA07
![Page 2: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/2.jpg)
What to remember/what I learned 1) It now seem clear, Nitrogen doping i.e. getting nitrogen into
cavity at 800C is the easy part. 2) Controlling the test environments: magnetic field, cooling rate,
and test hardware is the hard part. Environmental monitoring instrumentation is your friend.
3) Q vs Eacc is not enough, Q vs Eacc vs T in a controlled
environment with “surface resistance decomposition” is a must (all data that follows is 1.3GHz @ 2.0K unless noted).
4) What is the nitrogen doing? Where is it going?
![Page 3: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/3.jpg)
Cavity tests to date – 2.0K
9 cell mini production and re-doping second run
![Page 4: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/4.jpg)
Cavity tests to date – 2.0K
Single cell systematic doping
![Page 5: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/5.jpg)
Cavity tests to date – 2.0K
Single cell large grain incremental EP – Dhakal et al, IPAC 2015 WEPWI009
![Page 6: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/6.jpg)
Cavity tests to date – 2.0K
Large grain vs fine grain –systematic removal
![Page 7: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/7.jpg)
Furnace doping - absorption rate
See Report for JLab High Q0 R&D for LCLS-II - FY14,JLab tech note JLAB-TN-15-008
![Page 8: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/8.jpg)
Test environment – accidental uniform cooling D8
![Page 9: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/9.jpg)
Test environment – accidental uniform cooling D8
Temperature sensors
![Page 10: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/10.jpg)
Test environment – accidental uniform cooling D8
Temperature sensors
![Page 11: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/11.jpg)
Test environment - magnetic field drift
Report for JLab High Q0 R&D for LCLS-II - FY14 JLab tech note JLAB-TN-15-008
![Page 12: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/12.jpg)
Test environment - magnetic field drift
Report for JLab High Q0 R&D for LCLS-II - FY14 JLab tech note JLAB-TN-15-008
![Page 13: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/13.jpg)
Surface decomposition is essential - Qo vs. Eacc vs. T
All single cell cavities, all with now know good doping, all should easily have Q0 > 3.5e10 @ 16MV/m
![Page 14: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/14.jpg)
Surface decomposition is essential - Qo vs. Eacc vs. T
All single cell cavities, all with now know good doping, all should easily have Q0 > 3.5e10 @ 16MV/m
Uniform cooling, 7 mGauss field and BCP pitted cavity
![Page 15: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/15.jpg)
Surface decomposition is essential - Qo vs. Eacc vs. T
All single cell cavities, all with now know good doping, all should easily have Q0 > 3.5e10 @ 16MV/m
Uniform cooling, 5 mGauss field
![Page 16: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/16.jpg)
Surface decomposition is essential - Qo vs. Eacc vs. T
All single cell cavities, all with now know good doping, all should easily have Q0 > 3.5e10 @ 16MV/m
Stratified cooling 2 mGauss field
![Page 17: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/17.jpg)
Surface decomposition is essential - Qo vs. Eacc vs. T
All single cell cavities, all with now know good doping, all should easily have Q0 > 3.5e10 @ 16MV/m
Uniform cooling, 5 mGuass field Stratified cooling 2 mGuass field
1.5K
2.1K
![Page 18: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/18.jpg)
Surface decomposition is essential - Qo vs. Eacc vs. T
All single cell cavities, all with now know good doping, all should easily have Q0 > 3.5e10 @ 16MV/m
Uniform cooling, 7 mGuass field and BCP pitted cavity Uniform cooling, 5 mGuass field Stratified cooling 2 mGuass field
Mostly environmental
Mostly doping
,
![Page 19: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/19.jpg)
G2 – Large grain incremental EP
Bas
elin
e
N2A
30 +
EP1
0
+ E
P5
+ 9
0C 1
6hr
+ E
P5
+ 1
20C
16h
r
+ E
P10
+ 1
20C
16h
r
+ E
P5
+ 1
20C
16h
r
Courtesy of R.L. Geng IPAC 2015 WEPWI013 for Q vs Eacc
![Page 20: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/20.jpg)
Quench analysis on 9 cell cavities
Palczewski et al. – IPAC2015 WEPWI019 QUENCH STUDIES OF SIX HIGH TEMPERATURE NITROGEN DOPED 9 CELL CAVITIES FOR USE IN THE LCLS-II BASELINE PROTOTYPE CRYOMODULE AT JEFFERSON LABORATORY
N20A30 +EP 16μm Average quench field – 16.8MV/m N2A6 + EP 5 μm Average quench field – 23MV/m lower Q0 @ 16MV/m With lower N2?
![Page 21: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/21.jpg)
LCLS-II prototype results before and after HV welding
Average Q0 is lower after HV welding by ~10% or 1.25nΩ
Current data suggest environmental effects are the major cause of Q0 degradation after HV welding. Palczewski et al. – this conference MOPB040 today
![Page 22: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/22.jpg)
Systematic doping vs. EP (FG and LG)
![Page 23: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/23.jpg)
Systematic doping vs. EP (FG and LG)
Palczewski et al. – this conference MOPB039 today
Fitting results remove environmental effects
![Page 24: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/24.jpg)
Sample analysis High resolution – from previous slide
H. Tian et al. – this conference MOPB107 today
The near surface N concentration of Nb sample
with 20 minutes exposure of N2 (20N) was
measured by SIMS with incremental EP.
After 20 µm removal by EP, the concentration
of N keeps constant , but decreases by 60%
after 40 µm.
![Page 25: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/25.jpg)
Pashupati Dhakal et. al ASC’14 1LOr1B-05
Effectiveness of doping vs niobium RRR
No significant signature of doping @ 2.0K on low RRR FG cavities These are 1.5Ghz @ 2.0K
![Page 26: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/26.jpg)
Questions?
Contributing Data C. E. Reece Pashupati Dhakal Grigory Eremeev Hui Tian R.-L. Geng
Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell studies and all 9 cell work
Making nitrogen doping work is not that easy but can be done – off to the cryomodules.
![Page 27: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/27.jpg)
Questions?
Contributing Data C. E. Reece Pashupati Dhakal Grigory Eremeev Hui Tian R.-L. Geng
Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell studies and all 9 cell work
Making nitrogen doping work is not that easy but can be done – off to the cryomodules.
History can come back to bite you
![Page 28: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/28.jpg)
Backup
![Page 29: Lessons Learned From Nitrogen Doping at JLabGrigory Eremeev Hui Tian R.-L. Geng Funding Special thanks to LCLS-II, especially for taking chance on Nitrogen doping -Initial single cell](https://reader036.fdocuments.us/reader036/viewer/2022071517/613ae9d2f8f21c0c8268b53c/html5/thumbnails/29.jpg)
Furnace doping - redoping
Re-doping with external chemistry changes total absorption rate