KIRAN AG – 701
ACRYLIC RESIN COATED FIBERGLASS SLEEVING
UL recognized component under UL File No. # E491961, Acrylic Coated Fiberglass Braided Sleeving are
precisely engineered sleeving with high Dielectric Strength capabilities. The product available in different grades
with varying Dielectric Strength upto 7000 Volts as per applications, consisting an inner wall layer made out of
Fiberglass Yarn that is Braided and Coated with Acrylic Resin. KIRAN Acrylic - F sleeving is recommended as a
universal coated sleeving for all thermal requirements from -30°C through 155°C. The sleeving is compatible with
most insulating varnishes and is capable of short-thermo operation above its thermal classification.
These Sleevings in nature are extremely flexible and very easy to use. They are used in electric equipments such as
Generators, Transformers, Electric Motors, Lightening, Home Appliances, Circuits and Control of various
instruments, Breaker Panels, Switches and Welding Equipments.
FEATURES :
Highly craze resistant. Withstands severe bending with no loss of dielectric properties.
Coating film will not flow upon application of heat.
Extremely tough and flexible. Able to withstand assembly handling, cut-through and mechanical stress.
Resistant to most acids and most organic solvents.
UNIQUE PROPERTIES :
Superior Electrical Properties.
Excellent Low Temperature Flexibility.
Chemical Resistance.
Extreme Abrasion Resistance.
Oil Resistance.
Longer Shelf Life.
TYPICAL APPLICATION :
Two & Four Wheeler Wiring Harness.
Alternator Core Winding.
Oil Filled Transformers Lead Wire Protection.
Relays, Radio Circuits.
Motor and Generator Lead Wire Protection.
www.kiranudyog.com
Parameters Details
Thermal Class “F” Class
Thermal Temp. -30° C to +155° C
Inner Diameter 0.5mm to 40.0mm
Color Available in different colors on request
Grade
&
Dielectric Strength
A - 7000 Volts
B – 4000 Volts
C – 2500 Volts
C1 – 1500 Volts
Length Continuous or Customized cut lengths
available on request.
MANUFACTURING STANDARD
PRODUCT COMPLIANCE
KIRAN AG – 701
IV. TECHNICAL CHARACTERISTICS :
SL. No. Property Test Result
1. Heat Resistance Bending after heating IEC 60684 part
2 Clause 13,
48hrs at +155°C
No Cracking or detachment of coating shall
be visible and the original colors shall be
clearly recognized.
1.a UL 1441 – 60days at +190°C Dielectric Strength after ageing : average
break down voltage 5000Volts
2. Flammability Flame Propagation :
IEC 60684 part 2 Clause 26
Method A
Vertical with Mandrel
Self Extinguish (within 60 Sec.)
2.a UL 1441 Vertical with Mandrel Passes
3. Cold Resistance Bending at Low temperature
IEC 60684 part 2 clause 14 at -70°C
No Cracking or detachment of coating shall
be visible
3.a UL 1441 -1Hr at -10°C No Cracking
4. Chemical Resistance Simulation of real operating
conditions
Compatible with most insulating varnishes.
5. Insulation
Resistance
At room Temp. as per IEC 60684 Min. 103 MΩ
V. DIMENSIONS as per IEC 60684 :
Part No. Nominal Bore
(AWG)
Nominal Bore
(mm)
Bore Tolerance
(mm)
Minimum Wall
Thickness (mm)
Standard
Packing (Mtrs)
1 AG701 AWG # 18 1 ± 0.20 0.25 100
2 AG701 AWG # 12 2 ± 0.20 0.25 100
3 AG701 AWG # 09 3 ± 0.40 0.35 100
4 AG701 AWG # 06 4 ± 0.40 0.5 100
5 AG701 AWG # 04 5 ± 0.50 0.5 100
6 AG701 AWG # 03 6 ± 0.50 0.5 100
7 AG701 AWG # 01 7 ± 0.50 0.5 100
8 AG701 AWG # 00 8 ± 0.50 0.5 100
9 AG701 AWG # 1/0 9 ± 0.50 0.5 100
10 AG701 AWG # 2/0 10 ± 0.50 0.65 100
12 AG701 AWG # 3/0 12 ± 0.50 0.65 50
14 AG701 AWG # 250 14 ± 0.50 0.65 50
16 AG701 AWG # 300 16 ± 1.00 0.65 50
18 AG701 AWG # 400 18 ± 1.00 0.65 50
20 AG701 AWG # 500 20 ± 1.00 0.65 50
22 AG701 AWG # 600 22 ± 1.00 0.65 25
25 AG701 AWG # 750 25 ± 1.00 0.65 25
** Other diameters supplied upon request.
www.kiranudyog.com
KIRAN KFC/KFH 001/NMG 601 IEEMA UL File No. # E318161
FIBERGLASS CORD-KFC 001
Fiberglass braided Cords are intended for high-temperature applications up to 550ºC. The Cord consists of fiberglass
yarn core with a fiberglass braided jacket to form an exact diameter for controlled compression seals. Larger diameters
have a "Braid-Over-Braid" or “Yarn- Filled -Braid” jacket for durability and precise gasket dimensions.
Cords are available in many sizes and manufactured to fit Customer Specifications for Roundness and Softness.
These Cords are suitable for all types of sealing applications where High Temperatures upto 550ºC are needed.
Cords are the best choice for new or alternative gaskets for boilers, fireproof safe applications, flanges, furnaces, gas
fireplaces, glass manufacturing, ovens, pipe wraps, thermal insulation.
1. Thermal Class : “E” Glass
2. Thermal Temperature : +550° C
3. Outer Diameter : 1.0mm to 40mm
4. Color : White
5. Length : 25, 50, 100, 500 Meters and As per Customer Request
6. Type : Glass Filled Type and Braided Type
7. Features :a. Free of environmentally contaminating and hazardous chemicals.
b. Extremely flexible.
c. Able to withstand assembly handling, cut-through and mechanical stress.
8. Unique Properties :
i..Extremely Soft and Flexible
ii. Good Mechanical Protection.
iii. Oil Resistant.
iv. Very High Tensile Strength
9. Typical Application :
i. Motor and Generator Core Binding
ii. Transformer Core Binding
iii. Traction Motor Core Binding (Railways)
iv. Wind Generators Core Binding.
www.kiranudyog.com
FIBERGLASS FLAT HOSE- KFH 001
Fiberglass Braids are made from high temperature fiberglass yarn with low thermal conductivity. The rope and braid
are designed as gasket or seal for various industrial applications.
1. Thermal Class : “E” Glass
2. Thermal Temperature : +550° C
3. Inner Diameter : 1.0mm to 40mm
4. Color : White
5. Length : 25, 50 and 100 Meters
6. Type : Braided Type
7. Features : a. Free of environmentally contaminating and hazardous chemicals.
b. Extremely flexible.
c. Able to withstand assembly handling, cut-through and mechanical stress.
8. Unique Properties :
i. Very Flexible.
ii. Good Mechanical Protection.
iii. Oil Resistance.
iv. Extreme Soft Material.
9. Typical Application :
i. Wind Generator Core Cover.
www.kiranudyog.com
KIRAN NMG 601
NYLON MONOFILAMENT EXPANDABLE SLEEVING
NYLON Monofilament Expandable Sleeving is commonly used in the automotive industry to protect wires and hoses
from excessive Wear. Vibration and Abrasion can tear automotive hoses to pieces, but Nylon can increase hose life up
to 300%. This lengthened lifespan is recognized in terms of reduced maintenance and downtime leading to greater
customer satisfaction.
NYLON Monofilament Expandable Sleeving is braided from 0.012" Nylon 6-6 polyamide monofilament. The tight
braid construction fully covers and provides excellent surface abrasion resistance for assemblies exposed to excessive
wear. The smooth Nylon fibers and tight construction also reduces abrasion damage caused by hoses and harnesses
rubbing against the inside wall of the sleeving.
1. Thermal Class : “F” Class
2. Thermal Temperature : -70° C to +150° C
3. Inner Diameter : 1 mm to 40 mm
4. Color : Black, Grey
6. Length : Continuous or customized cut length on request
7. Type : Nylon 6.6
8. Expandability :1:2
9. Features :a. Adaptable & Suitable for all weather conditions.
b. Open weave construction allows expansion above or below original diameter.
10. Unique Properties:
i. Lightweight and flexible for ultimate protection.
ii. Sleeving expands up to 200% to fit over most connectors.
iii. Resists automotive fluids to keep engines safe.
iv. Cut & abrasion resistant to protect hoses from excessive wear.
v. UV resistant for outdoor usage.
11. Typical Application:
i. Aerospace
ii. Automobile Industry
iii. Computer Cable Management
iv. Satellite, Robotics
v. Audio Visual, Home Entertainment Wiring Protection
KIRAN KFT 001/002
FIBERGLASS NON ADHESVIE TAPE-KFT 001
Fiberglass Tapes are narrow woven fabric made of Non-alkali E-glass fibers with a strong selvage edge. This prevents
fraying and unraveling of fabric at the edges. The narrow widths eliminate the cutting of wider fiberglass fabrics down
to size and increases accuracy and productivity. The tightly woven tapes offer more uniformity and are highly drapable.
1. Thermal Class : “E” Glass
2. Thermal Temperature : +550° C
3. Width : 1/4 Inch to 6 Inch
4. Thickness : As per Customer Request
4. Color : White
5. Length : 50, 100, 500 Meters or as per Customer Request
6. Type : Plain Weave and Twill Weave upon Customer Request
7. Features : a. Free of environmentally contaminating and hazardous chemicals.
b. Able to withstand assembly handling, cut-through and mechanical stress.
8. Unique Properties :
i. High Dimensional Stability.
ii. High Tensile Strength
iii. Oil Resistant.
iv. Extreme Soft Material.
v. Excellent Flexibility and Reinforcing Quality.
9. Typical Application :
i. Motor and Generator Core Binding
ii. Transformer Core Binding
iii. Traction Motor Core Binding
iv. Wind Generators Core Binding
v. Used in Boilers, Furnaces and Ovens for sealing.
MANUFACTURING STANDARD COMPLIANCES
www.kiranudyog.com
QUALITY CERTIFICATIONS PRODUCT COMPLIANCES
POLYESTER NON ADHESIVE TAPES- KFT002
Polyester Non Adhesive Tapes are manufactured from Polyester yarn. These Polyester woven tapes will not burn or
smoulder and retain as much as 25% of its tensile strength at 1550 C.
They exhibit a high strength-to-weight ratio while maintaining excellent flexibility.
1. Thermal Class : “F” Glass
2. Thermal Temperature : 155° C
3. Width : 1/4 Inch to 4 Inches
4. Thickness : As per Customer Request
4. Color : White
5. Length : 50, 100, 500 Meters or as per Customer Request
6. Features : a. Free of environmentally contaminating and hazardous chemicals.
b. Able to withstand assembly handling, cut-through and mechanical stress.
7. Unique Properties :
i. High Dimensional Stability.
ii. High Tensile Strength
iii. Oil Resistance.
iv. Excellent Flexibility and Reinforcing Quality.
8. Typical Application :
i. Motor and Generator Core Binding
ii. Traction Motor Core Binding
iii. Transformer Core Binding
iv. Wind Generators Core Binding
v. Used in Boilers, Furnaces and Ovens for sealing.
www.kiranudyog.com
QUALITY CERTIFICATIONS MANUFACTURING STANDARD COMPLIANCES
KIRAN PVG – 301
POLYURETHANE COATED FIBERGLASS SLEEVING
Fiberglass sleeving impregnated with Polyurethane varnish is used where reliable heat resistance & dielectric
strength is required. The product available in different grades with varying Dielectric Strength upto 4000 Volts as
per applications, consisting an inner wall layer made out of Fiberglass Yarn that is Braided and Coated with
Polyurethane. KIRAN PVG - 301 F Class sleeving is recommended as a universal coated sleeving for all thermal
requirements of Class 155°C. The sleeving is compatible with most insulating varnishes and is capable of short-
thermo operation above its thermal classification.
They are used in electric equipments such as Generators, Transformers, Electric Motors, Lightening, Home
Appliances, Circuits and Control of various instruments.
FEATURES :
Free of environmentally hazardous and contaminating chemicals, completely different from
conventional polyurethane coating.
Tough, highly flexible, reliable with smooth finish.
Excellent compatibility with Class F impregnating resins and varnishes.
Solvent free.
UNIQUE PROPERTIES :
Incombustible in Nature.
Good Compatibility with Class F Impregnation Varnish.
Excellent Resistance to Ageing.
Oil Resistance.
TYPICAL APPLICATION :
Two & Four Wheeler Wiring Harness.
Alternator Core winding.
Oil Filled Transformers Lead Wire Protection.
Relays, Radio Circuits.
Class “F” Motor and Generator Lead Wire Protection.
www.kiranudyog.com
Parameters Details
Thermal Class “F” Class
Thermal Temp. 0° C to +155° C
Inner Diameter 1.0mm to 40.0mm
Color Natural, Black
Grade
&
Dielectric Strength
A - 4000 Volts
B – 3000 Volts
C – 2500 Volts
Length Continuous or Customized cut lengths
available on request.
MANUFACTURING STANDARD
PRODUCT COMPLIANCE
KIRAN PVG – 301
IV. TECHNICAL CHARACTERISTICS :
SL. No. Property Test Result
1. Heat Resistance Bending after heating IEC 60684 part
2 Clause 13.
No Cracking or detachment of coating shall
be visible and the original colors shall be
clearly recognized.
2. Flammability Flame Propagation :
IEC 60684 part 2 Clause 26
Method A
Horizontal with Mandrel
Passes horizontal flame test.
3. Cold Resistance Bending at Low temperature
IEC 60684 part 2 clause 14
No Cracking or detachment of coating shall
be visible
4. Chemical Resistance Simulation of real operating
conditions.
Compatible with most insulating varnishes.
5. Flexibility Passes. There are neither cracks to be
observed on the surface of the sleeving, nor
does the varnish film come off.
6. Insulation
Resistance
At room Temp. as per IEC 60684 Min. 103 MΩ
V. DIMENSIONS as per IEC 60684 :
Part No. Nominal Bore
(AWG)
Nominal Bore
(mm)
Bore Tolerance
(mm)
Minimum Wall
Thickness (mm)
Standard
Packing (Mtrs)
1 PVG301 AWG # 18 1 ± 0.30 0.25 100
2 PVG301 AWG # 12 2 ± 0.40 0.25 100
3 PVG301 AWG # 09 3 ± 0.50 0.35 100
4 PVG301 AWG # 06 4 ± 0.50 0.5 100
5 PVG301 AWG # 04 5 ± 0.50 0.5 100
6 PVG301 AWG # 03 6 ± 0.50 0.5 100
7 PVG301 AWG # 01 7 ± 0.50 0.5 100
8 PVG301 AWG # 00 8 ± 0.60 0.5 100
9 PVG301 AWG # 1/0 9 ± 0.60 0.5 100
10 PVG301 AWG # 2/0 10 ± 0.60 0.65 100
12 PVG301 AWG # 3/0 12 ± 0.60 0.65 50
14 PVG301 AWG # 250 14 ± 1.00 0.65 50
16 PVG301 AWG # 300 16 ± 1.00 0.65 50
18 PVG301 AWG # 400 18 ± 1.00 0.65 50
20 PVG301 AWG # 500 20 ± 1.00 0.65 50
22 PVG301 AWG # 600 22 ± 1.00 0.65 25
25 PVG301 AWG # 750 25 ± 1.00 0.65 25
** Other diameters supplied upon request.
www.kiranudyog.com
KIRAN VG – 501
POLYVINYL CHLORIDE COATED FIBERGLASS SLEEVING
Fiberglass sleeving impregnated with Polyvinyl chloride varnish is used where reliable heat resistance & dielectric
strength is required. The product available in different grades with varying Dielectric Strength upto 3000 Volts as
per applications, consisting an inner wall layer made out of Fiberglass Yarn that is Braided and Coated with
Polyvinyl. KIRAN VG - 501 B Class sleeving is recommended as a universal coated sleeving for all thermal
requirements of Class 130°C. The sleeving is compatible with most insulating varnishes and is capable of short-
thermo operation above its thermal classification.
They are used in electric equipments such as Generators, Transformers, Electric Motors, Lightening, Home
Appliances, Circuits and Control of various instruments.
FEATURES :
Free of environmentally hazardous and contaminating chemicals, completely different from
conventional polyurethane coating.
Extremely flexible and smooth finish.
UNIQUE PROPERTIES :
Very Flexible.
Good Mechanical Protection.
Extreme Soft Material.
Excellent Resistance to Ageing.
Oil Resistance.
TYPICAL APPLICATION :
Wiring Harness.
TV Sets.
Domestic Home Appliances.
Relays, Radio Circuits.
Mechanical Protection for “B” Class Electrical Machinery.
www.kiranudyog.com
Parameters Details
Thermal Class “B” Class
Thermal Temp. -20° C to +130° C
Inner Diameter 1.0mm to 40.0mm
Color Black, Yellow
Grade
&
Dielectric Strength
A - 3000 Volts
B – 3000 Volts
Length Continuous or Customized cut lengths
available on request.
STANDARD SPECIFICATION
KIRAN VG – 501
IV. TECHNICAL CHARACTERISTICS :
SL. No. Property Test Result
1. Heat Resistance Bending before and after Heating as
per BS 2848:1973.
No Cracking or detachment of coating shall
be visible and the original colors shall be
clearly recognized.
2. Rate of Burning Flame Propagation :
As per BS 2848 : 1973 Passes.
3. Chemical Resistance Simulation of real operating
conditions.
Compatible with most insulating varnishes.
4. Flexibility Passes. There are neither cracks to be
observed on the surface of the sleeving, nor
does the varnish film come off.
5. Insulation
Resistance
At room Temp. as per BS 2848:1973 Min. 104 MΩ
V. DIMENSIONS as per BS 2848 :
Part No. Nominal Bore
(AWG)
Nominal Bore
(mm)
Bore Tolerance
(mm)
Minimum Wall
Thickness (mm)
Standard
Packing (Mtrs)
1 VG501 AWG # 18 1 ± 0.15 0.35 100
2 VG501 AWG # 12 2 ± 0.15 0.45 100
3 VG501 AWG # 09 3 ± 0.15 0.45 100
4 VG501 AWG # 06 4 ± 0.15 0.45 100
5 VG501 AWG # 04 5 ± 0.15 0.45 100
6 VG501 AWG # 03 6 ± 0.15 0.45 100
7 VG501 AWG # 01 7 ± 0.15 0.5 100
8 VG501 AWG # 00 8 ± 0.15 0.5 100
9 VG501 AWG # 1/0 9 ± 0.15 0.5 100
10 VG501 AWG # 2/0 10 ± 0.15 0.5 100
12 VG501 AWG # 3/0 12 ± 0.30 0.7 50
14 VG501 AWG # 250 14 ± 0.30 0.7 50
16 VG501 AWG # 300 16 ± 0.30 0.7 50
18 VG501 AWG # 400 18 ± 0.30 0.7 50
20 VG501 AWG # 500 20 ± 0.50 0.7 50
22 VG501 AWG # 600 22 ± 0.50 0.7 25
25 VG501 AWG # 750 25 ± 0.50 0.7 25
** Other diameters supplied upon request.
www.kiranudyog.com
KIRAN SRG – 001 (Fire)
FIRE RETARDENT SILICON COATED FIBERGLASS SLEEVING Fire retardant Fiberglass sleeving is coated with Silicon are flexible, Fire Sleeving is designed to protect hoses,
wires and cables from the hazards of intense heat and occasional direct flame. KIRAN SRG – 001 Fire Sleeving
protects continuously to 500°F (260°C) and will withstand a molten splash at 2200°F (1200°C). Made of braided
high quality fiberglass yarns in a flexible substrate, it is then coated with a high-grade, fully-cured silicone rubber.
Resistant to hydraulic fluids, lubricating oils, and fuels, fire sleeve insulates against energy loss in piping and
hosing, protects employees from burns and provides flame and molten splash resistant protection for wires, hoses,
and cables. Both Aerospace and Industrial fire sleeves are coated with the same proprietary silicone rubber
compound for increased durability and enhanced heat & flame protection.
Braided (Industrial / Aerospace grade) fire sleeve utilizes a braided interior fiberglass sleeve to provide the highest
level of protection in critical areas potentially exposed to intense fire conditions (ex. an oil line inside of an engine
compartment). In addition to being applicable for use in Aerospace applications by meeting requirements, braided
fire sleeve is also commonly used in Automotive, Maritime, Locomotive, Heavy Equipment and Petrochemical
industries
I. FEATURES :
Excellent High temperature, flexibility with outstanding flame retardant properties.
Resistant to acids, alkalis, organic solvents and aliphatic hydrocarbons.
II. UNIQUE PROPERTIES :
Superior Electrical Properties.
Good Expandability and Flexibility.
Chemical Resistance.
Extreme Abrasion Resistance.
Oil Resistance.
Self Extinguishable.
III. TYPICAL APPLICATION :
Transportation (Aerospace, Auto, Locomotive, Heavy Equipment) Metals, Iron & Steel Hose Fabrication Oil & Gas OEM
www.kiranudyog.com
Parameters Details
Thermal Class “H” Class
Thermal Temperature 500°F (260°C)
Sizes 10.0mm to 50mm
Color Black and Red Oxide
Grade
&
Dielectric Strength
Min,. 12000 Volts
Length Continuous or Customized cut lengths
available on request.
STANDARD SPECIFICATION
PRODUCT COMPLIANCE
KIRAN SRG – 001 (Fire)
IV. TECHNICAL CHARACTERISTICS :
SL. No. Property Test Result
1. Heat Resistance Bending after heating IEC 60684 part
2 Clause 13,
48hrs at +180°C
No Cracking or detachment of coating shall
be visible and the original colors shall be
clearly recognized.
1.a UL 1441 – 60days at +190°C Dielectric Strength after ageing : average
break down voltage 5000Volts
2. Flammability Flame Propagation :
IEC 60684 part 2 Clause 26
Method A
Vertical with Mandrel
Self Extinguish (within 60 Sec).
2.a UL 1441 Vertical with Mandrel Passes
3. Cold Resistance Bending at Low temperature
IEC 60684 part 2 clause 14 at -70°C
No Cracking or detachment of coating shall
be visible
3.a UL 1441 -1Hr at -10°C No Cracking
4. Chemical Resistance Simulation of real operating
conditions
Compatible with most insulating varnishes.
5. Insulation
Resistance
At room Temp. as per IEC 60684 Min. 105 MΩ
After damp Test as per IEC 60684 Min. 104 MΩ
V. DIMENSIONS as per IEC 60684 :
Part No. Nominal Bore
(AWG)
Nominal Bore
(mm)
Bore Tolerance
(mm)
Minimum Wall
Thickness (mm)
Standard
Packing (Mtrs)
10 SRG001 AWG # 2/0 10 ± 0.50 0.65 30
12 SRG001 AWG # 3/0 12 ± 0.50 0.65 30
14 SRG001 AWG # 250 14 ± 1.00 0.65 30
16 SRG001 AWG # 300 16 ± 1.00 0.65 30
18 SRG001 AWG # 400 18 ± 1.00 0.65 30
20 SRG001 AWG # 500 20 ± 1.00 0.65 30
22 SRG001 AWG # 600 22 ± 1.00 0.65 30
25 SRG001 AWG # 750 25 ± 1.00 0.65 30
** Other diameters supplied upon request.
www.kiranudyog.com
KIRAN SRG – 001
HIGH TEMPERATURE SILICON ELASTOMER COATED
FIBERGLASS SLEEVING UL recognized GRADE “A” component under UL File No. # E324343 (UZFT2) and Grade-B UL FILE
NO.E491961,Silicon Elastomer Coated Fiberglass Sleeving are flexible, confirming to wired and connections,
keeping its elasticity in a range between-60ºC to +220º C. It can also with stand up to +250 º C for a short while.
KIRAN SRG - 001 sleeving is a high temperature Silicon Rubber Elastomer that is pressure bonded to a heat
stabilized fiberglass braid. Its outstanding flexibility allows to withstand severe push-back, even in lower
dielectric grades. KIRAN SRG - 001 sleeving is the ideal insulation where sharp bends are encountered or the
ability to expand over irregular shaped parts is required. The electrical strength stays higher even after folding and
bending. The sleeving have excellent abrasion resistance, flame retardant and are physically tough. It can with
stand high difference in temperatures and being moisture resistant, prevents humidity to enhance the life of the
generator / motor.
I. FEATURES :
Excellent low temperature flexibility with outstanding flame retardant properties.
Resistant to acids, alkalis, organic solvents and aliphatic hydrocarbons.
II. UNIQUE PROPERTIES :
Superior Electrical Properties.
Good Expandability and Flexibility.
Chemical Resistance.
Extreme Abrasion Resistance.
Oil Resistance.
Self Extinguishable.
III. TYPICAL APPLICATION :
Two & Four Wheeler Wiring Harness.
Alternator Core winding.
Transformers Lead Wire Protection.
Wind Generators.
Motor and Generator Lead Wire Protection.
Parameters Details
Thermal Class “H” Class
Thermal Temperature -60° C to +180° C
Sizes 0.50mm to 40.0mm
Color Available in different colors on request
Grade
&
Dielectric Strength
A -- Above 7000 Volts
B – 4000 Volts
C – 2500 Volts
C1 – 1500 Volts
C2 – Less than 1500 Volts
Length Continuous or Customized cut lengths
available on request.
STANDARD SPECIFICATION
PRODUCT COMPLIANCE
www.kiranudyog.com
KIRAN SRG – 001
IV. TECHNICAL CHARACTERISTICS :
SL. No. Property Test Result
1. Heat Resistance Bending after heating IEC 60684 part
2 Clause 13,
48hrs at +180°C
No Cracking or detachment of coating shall
be visible and the original colors shall be
clearly recognized.
1.a UL 1441 – 60days at +190°C Dielectric Strength after ageing : average
break down voltage 5000Volts
2. Flammability Flame Propagation :
IEC 60684 part 2 Clause 26
Method A
Vertical with Mandrel
Self Extinguish (within 60 Sec).
2.a UL 1441 Vertical with Mandrel Passes
3. Cold Resistance Bending at Low temperature
IEC 60684 part 2 clause 14 at -70°C
No Cracking or detachment of coating shall
be visible
3.a UL 1441 -1Hr at -10°C No Cracking
4. Chemical Resistance Simulation of real operating
conditions
Compatible with most insulating varnishes.
5. Insulation
Resistance
At room Temp. as per IEC 60684 Min. 105 MΩ
After damp Test as per IEC 60684 Min. 104 MΩ
V. DIMENSIONS as per IEC 60684 :
Part No. Nominal Bore
(AWG)
Nominal Bore
(mm)
Bore Tolerance
(mm)
Minimum Wall
Thickness (mm)
Standard
Packing (Mtrs)
0.5 SRG001 AWG # 24 0.5 ± 0.20 0.25 100
1 SRG001 AWG # 18 1 ± 0.20 0.25 100
2 SRG001 AWG # 12 2 ± 0.40 0.25 100
3 SRG001 AWG # 09 3 ± 0.40 0.35 100
4 SRG001 AWG # 06 4 ± 0.50 0.5 100
5 SRG001 AWG # 04 5 ± 0.50 0.5 100
6 SRG001 AWG # 03 6 ± 0.50 0.5 100
7 SRG001 AWG # 01 7 ± 0.50 0.5 100
8 SRG001 AWG # 00 8 ± 0.50 0.5 100
9 SRG001 AWG # 1/0 9 ± 0.50 0.5 100
10 SRG001 AWG # 2/0 10 ± 0.50 0.65 100
12 SRG001 AWG # 3/0 12 ± 0.50 0.65 50
14 SRG001 AWG # 250 14 ± 1.00 0.65 50
16 SRG001 AWG # 300 16 ± 1.00 0.65 50
18 SRG001 AWG # 400 18 ± 1.00 0.65 50
20 SRG001 AWG # 500 20 ± 1.00 0.65 50
22 SRG001 AWG # 600 22 ± 1.00 0.65 25
25 SRG001 AWG # 750 25 ± 1.00 0.65 25
** Other diameters supplied upon request.
www.kiranudyog.com
KIRAN SRG – 002
SILICON RESIN COATED FIBERGLASS SLEEVING
IEEMA UL recognized component under UL File No. # E318161, Silicon Resin Coated Fiberglass Sleeving are
flexible, confirming to wires and connections, keeping its elasticity in a range between -60°C to +180°C. It can
also with stand up to +220°C for a short while.
KIRAN SRG - 002 is the ideal insulation where sharp bends are encountered or the ability to expand over irregular
shaped parts is required. It is typically used as a protective covering for automotive wiring harnesses and ABS
brake wiring also used for aerospace and aircraft wiring leads as well as for heat generating appliances such as
coffee pots, hair dryers, toasters, etc. KIRAN SRG 002 can also be used for covering leads on extrusion plastic
molding, die casting machinery and presses.
I. FEATURES :
Good abrasion and radiation resistance.
Aero space and Atomic energy applications.
II. UNIQUE PROPERTIES :
Superior Electrical Properties.
Good Expandability and Flexibility.
Chemical Resistance.
Extreme Abrasion Resistance.
Oil Resistance.
Self Extinguishable.
III. TYPICAL APPLICATION :
Two & Four Wheeler Wiring Harness.
Alternator Core Winding.
Transformers Lead Wire Protection.
Carbon Brush Wiring Protection.
Motor and Generator Lead Wire Protection.
www.kiranudyog.com
Parameters Details
Thermal Class “H” Class
Thermal Temperature -60° C to +180° C
Sizes 0.50mm to 40.0mm
Color Available in different colors on request
Grade
&
Dielectric Strength
A -- Above 7000 Volts
B – 4000 Volts
C – 2500 Volts
C1 – 1500 Volts
C2 – Less than 1500 Volts
Length Continuous or Customized cut lengths
available on request.
STANDARD SPECIFICATION
PRODUCT COMPLIANCE
KIRAN SRG – 002 IV. TECHNICAL CHARACTERISTICS :
SL. No. Property Test Result
1. Heat Resistance Bending after heating IEC 60684 part
2 Clause 13,
48hrs at +180°C
No Cracking or detachment of coating shall
be visible and the original colors shall be
clearly recognized.
2. Flammability Flame Propagation :
IEC 60684 part 2 Clause 26
Method A
Vertical with Mandrel
Self Extinguish (within 60 Sec).
3. Cold Resistance Bending at Low temperature
IEC 60684 part 2 clause 14 at -70°C
No Cracking or detachment of coating shall
be visible
4. Chemical Resistance Simulation of real operating
conditions
Compatible with most insulating varnishes.
5. Insulation
Resistance
At room Temp. as per IEC 60684 Min. 105 MΩ
After damp Test as per IEC 60684 Min. 104 MΩ
V. DIMENSIONS as per IEC 60684 :
Part No. Nominal Bore
(AWG)
Nominal Bore
(mm)
Bore Tolerance
(mm)
Minimum Wall
Thickness (mm)
Standard
Packing (Mtrs)
0.5 SRG001 AWG # 24 0.5 ± 0.20 0.25 100
1 SRG001 AWG # 18 1 ± 0.20 0.25 100
2 SRG001 AWG # 12 2 ± 0.40 0.25 100
3 SRG001 AWG # 09 3 ± 0.40 0.35 100
4 SRG001 AWG # 06 4 ± 0.50 0.5 100
5 SRG001 AWG # 04 5 ± 0.50 0.5 100
6 SRG001 AWG # 03 6 ± 0.50 0.5 100
7 SRG001 AWG # 01 7 ± 0.50 0.5 100
8 SRG001 AWG # 00 8 ± 0.50 0.5 100
9 SRG001 AWG # 1/0 9 ± 0.50 0.5 100
10 SRG001 AWG # 2/0 10 ± 0.50 0.65 100
12 SRG001 AWG # 3/0 12 ± 0.50 0.65 50
14 SRG001 AWG # 250 14 ± 1.00 0.65 50
16 SRG001 AWG # 300 16 ± 1.00 0.65 50
18 SRG001 AWG # 400 18 ± 1.00 0.65 50
20 SRG001 AWG # 500 20 ± 1.00 0.65 50
22 SRG001 AWG # 600 22 ± 1.00 0.65 25
25 SRG001 AWG # 750 25 ± 1.00 0.65 25
** Other diameters supplied upon request.
www.kiranudyog.com
KIRAN VPI – 155
VPI ACRYLIC COATED FIBERGLASS SLEEVING
UL recognized component under UL File No. # E491961, Acrylic Coated Fiberglass Braided Sleeving are
precisely engineered sleeving are flexible with an outer layer of E glass Fiberglass braid. The outer fiberglass braid
is lightly treated with acrylic resin to prevent fray, improve abrasion resistance and allow coating by the VPI resin.
KIRAN VPI - 155 is used for applications which require VPI processes and higher temperatures. It can be used for
high voltage transformers as well as for aerospace and aircraft wiring leads. VPI-155 sleeving allows for expansion
to fit over difficult joints and terminals.
FEATURES :
KIRAN VPI - 155 with an over braided glass jacket.
Lightly treated with acrylic resin to prevent end fray and improve abrasion resistance.
Resistant to most acids and most organic solvents.
UNIQUE PROPERTIES :
Superior Electrical Properties.
Excellent Low Temperature Flexibility.
Chemical Resistance.
Extreme Abrasion Resistance.
Oil Resistance.
Longer Shelf Life.
TYPICAL APPLICATION :
Aero Space and Aircraft Wiring.
Wind Turbines, Solar Panels and Alternator Core Winding.
High Voltage Transformers.
Heat Generating Appliances.
VPI Application.
www.kiranudyog.com
Parameters Details
Thermal Class “F” Class
Thermal Temp. -30° C to +155° C
Inner Diameter 2mm to 20.0mm
Color Available in different colors on request
Grade
&
Dielectric Strength
A - 7000 Volts
B – 4000 Volts
Length Continuous or Customized cut lengths
available on request.
MANUFACTURING STANDARD
PRODUCT COMPLIANCE
KIRAN VPI – 155
IV. TECHNICAL CHARACTERISTICS :
SL. No. Property Test Result
1. Heat Resistance Bending after heating IEC 60684 part
2 Clause 13,
48hrs at +155°C
No Cracking or detachment of coating shall
be visible and the original colors shall be
clearly recognized.
1.a UL 1441 – 60days at +190°C Dielectric Strength after ageing : average
break down voltage 5000Volts
2. Flammability Flame Propagation :
IEC 60684 part 2 Clause 26
Method A
Vertical with Mandrel
Self Extinguish (within 60 Sec.)
2.a UL 1441 Vertical with Mandrel Passes
3. Cold Resistance Bending at Low temperature
IEC 60684 part 2 clause 14 at -70°C
No Cracking or detachment of coating shall
be visible
3.a UL 1441 -1Hr at -10°C No Cracking
4. Chemical Resistance Simulation of real operating
conditions
Compatible with most insulating varnishes.
5. Insulation
Resistance
At room Temp. as per IEC 60684 Min. 103 MΩ
V. DIMENSIONS as per IEC 60684 :
Part No. Nominal Bore
(AWG)
Nominal Bore
(mm)
Bore Tolerance
(mm)
Minimum Wall
Thickness (mm)
Standard
Packing (Mtrs)
2 AG701 AWG # 12 2 ± 0.20 0.25 100
3 AG701 AWG # 09 3 ± 0.40 0.35 100
4 AG701 AWG # 06 4 ± 0.40 0.5 100
5 AG701 AWG # 04 5 ± 0.50 0.5 100
6 AG701 AWG # 03 6 ± 0.50 0.5 100
7 AG701 AWG # 01 7 ± 0.50 0.5 100
8 AG701 AWG # 00 8 ± 0.50 0.5 100
9 AG701 AWG # 1/0 9 ± 0.50 0.5 100
10 AG701 AWG # 2/0 10 ± 0.50 0.65 100
12 AG701 AWG # 3/0 12 ± 0.50 0.65 50
14 AG701 AWG # 250 14 ± 0.50 0.65 50
16 AG701 AWG # 300 16 ± 1.00 0.65 50
18 AG701 AWG # 400 18 ± 1.00 0.65 50
20 AG701 AWG # 500 20 ± 1.00 0.65 50
** Other diameters supplied upon request.
www.kiranudyog.com
KIRAN KVPI – 200
VPI SILICON COATED FIBERGLASS SLEEVING
UL recognized GRADE “A” component under UL File No. # E324343 (UZFT2) and NEMA TF – 1 Type 5,
Silicon Elastomer Coated Fiberglass Sleeving are flexible with an outer layer of Fiberglass braid. The over braid
bonding process adheres the over braid to the silicon coated substrate and minimizes end fray to improve assembly
performance and eliminate the long term handling effects of operator dermatitis. KIRAN KVPI - 200 sleeving is a
high temperature Silicon Rubber Elastomer that is pressure bonded to a heat stabilized fiberglass braid.
KIRAN VPI – 200 Silicon Sleeving is resistant to most acids, oils, organic solvents and water. It is also compatible
with virtually all Electrical grade varnishes and Impregnation systems suitable for all VPI applications.
I. FEATURES :
This double wall sleeving provides higher abrasion resistance and for vacuum pressure impregnation.
Overlap braid on sleeving being saturated has high resin absorption properties and are highly protective.
II. UNIQUE PROPERTIES :
Superior Electrical Properties.
Good Expandability and Flexibility.
Chemical Resistance.
Extreme Abrasion Resistance.
Oil Resistance.
Self Extinguishable.
III. TYPICAL APPLICATION :
Aero Space and Aircraft Wiring.
Wind Turbines, Solar Panels and Alternator Core Winding.
High Voltage Transformers.
Heat Generating Appliances.
VPI Application.
www.kiranudyog.com
Parameters Details
Thermal Class “H” Class
Thermal Temperature -60° C to +200° C
Sizes 2.0mm to 20.0mm
Braid Color White
Sleeving Color Natural / Black
Grade
&
Dielectric Strength
A -- 7000 Volts
B – 4000 Volts
Length Continuous or Customized cut lengths
available on request.
STANDARD SPECIFICATION
PRODUCT COMPLIANCE
KIRAN KVPI – 200
IV. TECHNICAL CHARACTERISTICS :
SL. No. Property Test Result
1. Heat Resistance Bending after heating IEC 60684 part
2 Clause 13,
48hrs at +180°C
No Cracking or detachment of coating shall
be visible and the original colors shall be
clearly recognized.
1.a UL 1441 – 60days at +190°C Dielectric Strength after ageing : average
break down voltage 5000Volts
2. Flammability Flame Propagation :
IEC 60684 part 2 Clause 26
Method A
Vertical with Mandrel
Self Extinguish (within 60 Sec).
2.a UL 1441 Vertical with Mandrel Passes
3. Cold Resistance Bending at Low temperature
IEC 60684 part 2 clause 14 at -70°C
No Cracking or detachment of coating shall
be visible
3.a UL 1441 -1Hr at -10°C No Cracking
4. Chemical Resistance Simulation of real operating
conditions
Compatible with most insulating varnishes.
5. Insulation
Resistance
At room Temp. as per IEC 60684 Min. 105 MΩ
After damp Test as per IEC 60684 Min. 104 MΩ
V. DIMENSIONS as per IEC 60684 :
Part No. Nominal Bore
(AWG)
Nominal Bore
(mm)
Bore Tolerance
(mm)
Minimum Wall
Thickness (mm)
Standard
Packing (Mtrs)
2 KVPI200 AWG # 12 2 ± 0.40 0.25 100
3 KVPI200 AWG # 09 3 ± 0.40 0.35 100
4 KVPI200 AWG # 06 4 ± 0.50 0.5 100
5 KVPI200 AWG # 04 5 ± 0.50 0.5 100
6 KVPI200 AWG # 03 6 ± 0.50 0.5 100
7 KVPI200 AWG # 01 7 ± 0.50 0.5 100
8 KVPI200 AWG # 00 8 ± 0.50 0.5 100
9 KVPI200 AWG # 1/0 9 ± 0.50 0.5 100
10 KVPI200 AWG # 2/0 10 ± 0.50 0.65 100
12 KVPI200 AWG # 3/0 12 ± 0.50 0.65 50
14 KVPI200 AWG # 250 14 ± 1.00 0.65 50
16 KVPI200 AWG # 300 16 ± 1.00 0.65 50
18 KVPI200 AWG # 400 18 ± 1.00 0.65 50
20 KVPI200 AWG # 500 20 ± 1.00 0.65 50
** Other diameters supplied upon request.
www.kiranudyog.com