Fundamentals of Concrete
![Page 2: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/2.jpg)
Fundamentals of Concrete
Concrete Components
Cement Water Fine Aggregate Coarse Aggregate
![Page 3: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/3.jpg)
Fundamentals of Concrete
Range in Proportions
![Page 4: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/4.jpg)
Fundamentals of Concrete
Advantages of Reducing Water Content:
Increased strength Lower permeability Increased resistance to
weathering Better bond between concrete and
reinforcement Reduced drying shrinkage and
cracking Less volume change from wetting
and drying
![Page 5: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/5.jpg)
Fundamentals of Concrete
— that property of freshly mixed concrete that determines its working characteristics ie. the ease with which it can be mixed, placed, compacted and finished.
Workability
![Page 6: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/6.jpg)
Fundamentals of Concrete
Cross Section of Hardened ConcreteConcrete made with siliceous rounded gravel
Concrete made with crushed limestone
![Page 7: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/7.jpg)
Fundamentals of Concrete
Workability
![Page 8: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/8.jpg)
Fundamentals of Concrete
Factors Affecting Workability
Method and duration of transportation
Quantity and characteristics of cementing materials
Concrete consistency (slump) Agg. grading, shape & surface
texture % entrained air Water content Concrete & ambient air temperature Admixtures
![Page 9: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/9.jpg)
Fundamentals of Concrete
Effect of Casting Temperature on Slump
![Page 10: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/10.jpg)
Fundamentals of Concrete
Bleeding and Settlement
![Page 11: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/11.jpg)
Fundamentals of Concrete
Consolidation
![Page 12: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/12.jpg)
Fundamentals of Concrete
Effect of Voids in Concrete on Modulus of Elasticity, Compressive Strength, and Flexural Strength.
![Page 13: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/13.jpg)
Fundamentals of Concrete
Hydration─ is the chemical reaction between the cement and water in which new compounds with strength producing properties are formed.
Heat of Hydration─ is the heat given off during the chemical reaction as the cement hydrates.
![Page 14: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/14.jpg)
Fundamentals of Concrete
Setting Times at Different Temperatures
![Page 15: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/15.jpg)
Fundamentals of Concrete
Curing─ maintenance of a satisfactory moisture
content and temperature in concrete for a suitable period of time immediately following placing & finishing so that the desired properties may develop.
Time Temperature Moisture
![Page 16: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/16.jpg)
Fundamentals of Concrete
Effect of Curing on Strength Development
![Page 17: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/17.jpg)
Fundamentals of Concrete
Effect of Casting and Curing Temperature on Strength Development
![Page 18: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/18.jpg)
Fundamentals of Concrete
Concrete Strength Gain Versus Time for Concrete Exposed to Outdoor Conditions
![Page 19: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/19.jpg)
Fundamentals of Concrete
Rel. Humidity of 150 x 300-mm Cylinders Moist Cured for 7 days
![Page 20: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/20.jpg)
Fundamentals of Concrete
Drying Shrinkage and Mass Loss of 150 x 300-mm Cylinders Moist Cured for 7 days
![Page 21: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/21.jpg)
Fundamentals of Concrete
Compressive Strength
— is defined as the measured maximum resistance of a concrete or mortar specimen to an axial load, usually expressed in MPa at an age of 28-days.
Most general use concrete
20 to 40 MPa
High-strength concrete by definition
70 MPa or greater
![Page 22: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/22.jpg)
Fundamentals of Concrete
Compressive Strength Test Specimen SizesCSA A23.1-00
Mortar — 50 mm cubes
Concrete — 100 x 200 mm cylinders*
*(generally 150 x 300 mm in USA)
![Page 23: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/23.jpg)
Fundamentals of Concrete
Strength Development of Concretes in Percent of 28-Day Strength
![Page 24: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/24.jpg)
Fundamentals of Concrete
Ratios — W/CM and W/C
Water-cementing materials ratio (w/cm)
— ratio of mass of water to mass of cementing materials in a concrete mix expressed as a decimal. The water is exclusive to that absorbed by the agg.
Water-cement ratio (w/c) — ratio of mass of water to mass
of cement in a concrete mix expressed as a decimal.
![Page 25: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/25.jpg)
Fundamentals of Concrete
Typical Relationships of Strength to W/C-Ratio
![Page 26: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/26.jpg)
Fundamentals of Concrete
Testing of Compressive Strength
![Page 27: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/27.jpg)
Fundamentals of Concrete
Approximations of Concrete Strengths
Compressive strength ( ƒc′ )7-day — 75% of 28-day56 and 90-day — 10% - 15% > 28-day
Flexural Strength ( Modulus of Rupture)normal density — 8% - 12% of ƒc′
Tensile Strength direct tensile — 8% -12% of ƒc′splitting tensile — 8% -14% of ƒc′
![Page 28: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/28.jpg)
Fundamentals of Concrete
Observed Average Density of Fresh Concrete
MaximuMaximumm
size of size of aggregataggregat
e,e,mmmm
AirAir,,%%
WateWater,r,
kg/mkg/m33
CemeCement,nt,
kg/mkg/m33
Density, kg/mDensity, kg/m33
Relative density of Relative density of aggregateaggregate
2.52.555
2.62.600
2.62.655
2.72.700
2.72.755
1919 6.06.0 168168 336336 21921944
22222277
22522599
22922911
23223233
37.537.5 4.54.5 145145 291291 22522599
22922911
23323399
23723711
24024033
7575 3.53.5 121121 242242 23023077
23523555
23823877
24324355
24624677
![Page 29: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/29.jpg)
Fundamentals of Concrete
E and DensityApproximate Values Modulus of Elasticity ( E )
normal concrete — 14,000 to 41,000 MPa
Densitynormal concrete — 2200 to 2400 kg/m3
reinforced concrete — 2400 kg/m3
low density insulating concrete — 240 kg/m3
high density concrete — 6000 kg/m3
(radiation shielding, counterweights)
![Page 30: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/30.jpg)
Fundamentals of Concrete
Watertightness / Permeability
Watertightness— the ability of concrete to hold back or retain water without visible leakage.
Permeability— amount of water migration through concrete when the water is under pressure or the ability of concrete to resist penetration by water or other substances (liquids, gas, ions, etc.)
![Page 31: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/31.jpg)
Fundamentals of Concrete
Relationship between Hydraulic Permeability, W/C-Ratio, and Initial Curing
![Page 32: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/32.jpg)
Fundamentals of Concrete
Effect of W/C-Ratio and Curing Duration on Permeability of Mortar
![Page 33: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/33.jpg)
Fundamentals of Concrete
Effect of W/C-Ratio and Air Content on the Total Charge at the End of the Rapid Chloride Permeability Test
![Page 34: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/34.jpg)
Fundamentals of Concrete
Effect of Compressive Strength and Aggregate Type on the Abrasion Resistance of Concrete
![Page 35: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/35.jpg)
Fundamentals of Concrete
Effect of Hard Steel Troweling and Surface Treatments on the Abrasion Resistance of Concrete (ASTM C 779)
![Page 36: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/36.jpg)
Fundamentals of Concrete
Measuring Abrasion Resistance of Concrete
![Page 37: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/37.jpg)
Fundamentals of Concrete
Specimens subjected to 150 Cycles of Freezing and Thawing
Non-air-entrained High water-cement ratio
Air-entrained Low water-cement ratio
![Page 38: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/38.jpg)
Fundamentals of Concrete
Type 10 cement
Relationship Between Freeze-Thaw Resistance, W/C- Ratio, and Different Concretes and Curing Conditions (1)
![Page 39: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/39.jpg)
Fundamentals of Concrete
Type 10 cement
Relationship Between Freeze-Thaw Resistance, W/C- Ratio, and Different Concretes and Curing Conditions (2)
![Page 40: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/40.jpg)
Fundamentals of Concrete
Alkali- Aggregate Reactivity ( AAR ) — is a reaction between the active
mineral constituents of some aggregates and the sodium and potassium alkali hydroxides and calcium hydroxide in the concrete.
Alkali-Silica Reaction ( ASR ) Alkali-Carbonate Reaction ( ACR )
Refer CSA A23.1-00 Appendix B — Alkali-Aggregate Reaction
![Page 41: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/41.jpg)
Fundamentals of Concrete
Alkali-Silica Reactivity ( ASR )
Control ASR with: SCM’s Blended cement
Limit concrete alkali content
Test for effectiveness
![Page 42: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/42.jpg)
Fundamentals of Concrete
Effect of Fly Ash on Alkali-Aggregate Reactivity
![Page 43: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/43.jpg)
Fundamentals of Concrete
Corroded Steel Due to Carbonation
![Page 44: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/44.jpg)
Fundamentals of Concrete
Methods to Reduce Corrosion of Embedded Steel by Chlorides Use low w/cm ratio concrete
Moist cure Reduce permeability with SCM’s Increase concrete cover Corrosion inhibitors Epoxy-coated reinforcing steel Concrete overlays Surface treatments Cathodic protection
![Page 45: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/45.jpg)
Fundamentals of Concrete
Reducing Corrosion by Chlorides Using Epoxy-Coated Rebars
![Page 46: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/46.jpg)
Fundamentals of Concrete
Sulphate Attack
Use low w/cm (ie. 0.4)
Use sulphate resistant cement
![Page 47: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/47.jpg)
Fundamentals of Concrete
Concrete Beams After Seven Years of Exposure to Sulphate-Rich Wet Soil
![Page 48: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/48.jpg)
Fundamentals of Concrete
Average 16-yr Ratings of Concrete Beams in Sulphate Soils
![Page 49: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/49.jpg)
Fundamentals of Concrete
Concrete Exposed to Seawater
![Page 50: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/50.jpg)
Fundamentals of Concrete
Secondary Ettringite Deposits in Void
![Page 51: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/51.jpg)
Fundamentals of Concrete
Heat Induced Delayed Expansion
![Page 52: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/52.jpg)
Fundamentals of Concrete
Videos 1/2
Concrete Fundamentals
![Page 53: Fundamentals of Concrete (1)](https://reader037.fdocuments.us/reader037/viewer/2022110106/577cc7a71a28aba711a19178/html5/thumbnails/53.jpg)
Fundamentals of Concrete
Videos 2/2
Concrete Durability Freeze-Thaw