Fatigue of Materials
![Page 2: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/2.jpg)
FatigueDefinition: Damage accumulated through the application of repeated stress cycles
Variable amplitude loadings cause different levels of fatigue
Fatigue is cumulative through the life of an engineering element
![Page 3: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/3.jpg)
Factors Affecting Fatigue LifeLoading Conditions Type of stress Stress amplitude, mean value
Condition of Specimen/Structural Member Stress concentrations Surface finish
Material Thermal history (e.g. grain size in metals)
Environmental conditions Temperature Corrosion effects
![Page 4: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/4.jpg)
Loading Characteristics
![Page 5: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/5.jpg)
Effect of Mean Stresses
am=0
am>0
ult
Mean Stresses reduce the stress range
No mean stress
![Page 6: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/6.jpg)
Stress Amplitude vs. MeanGoodman Relationship: lower the mean stresses, the greater the allowable stress amplitude for the same life.
1u
m
f
a
a
m
f
u
![Page 7: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/7.jpg)
Example: Goodman Diagram
If f=u/2, m=u/2, What is the max and min that can be applied?
a
m
u/2f
u
u/4f
u/2m
min= u/4 max= 3u/4
![Page 8: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/8.jpg)
Stress vs. Number of Cycles
S-N Diagram
Lower mean stress
![Page 9: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/9.jpg)
Miner’s RuleDamage from variable loadings is related to the life consumed by number of cycles at each particular STRESS RANGE. The summation of life consumed at each stress range must be less than 1 to avoid failure.
where:
ni = number of repetitions applied at i
Nfi = number of repetitions to cause failure at a stress range, i
(ni < Nfi)
ni/Nfi 1
![Page 10: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/10.jpg)
Example problem - Miner’s Rule
Ni/Nfi = 900/10,000 + 50/500
= 0.09 + 0.10
= 0.19 0.19 < 1.0 OK Used 19% of fatigue life,81% remains
Stress Range,
i (ksi)
No. Applied Cycles, Ni
No. Cycles to Failure,Nfi
3 900 10,000
5 50 500
Log N
5
500
3
10,000
![Page 11: Fatigue of Materials. Fatigue Definition: Damage accumulated through the application of repeated stress cycles Variable amplitude loadings cause different.](https://reader036.fdocuments.us/reader036/viewer/2022082711/56649f2c5503460f94c47075/html5/thumbnails/11.jpg)
Fatigue tests
2. Tension- Compression
Loading Patterns:1. Reverse stresses, + to -2. Alternate zero to some maximum3. Alternate above some base value
V
M
1. Beam Fatigue
M 2c
max = Mc/I
3. Others