![Page 1: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/1.jpg)
ESI-p1
Electronic Supplementary Information for
Controlled Overgrowth of Pd on Au Nanorods
Hao Jing and Hui Wang*
Department of Chemistry and Biochemistry, University of South Carolina,
631 Sumter Street, Columbia, South Carolina 29208, United States
* To whom correspondence should be addressed.
Email: [email protected]; Phone: 1-803-777-2203; Fax: 1-803-777-9521.
Electronic Supplementary Material (ESI) for CrystEngComm.This journal is © The Royal Society of Chemistry 2014
![Page 2: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/2.jpg)
ESI-p2
BB
AA
Figure S1. (A) TEM and (B) SEM images of cylindrical Au nanorods.
![Page 3: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/3.jpg)
ESI-p3
(002)
(022)(020)
Au (002)
Pd (002)Pd (022)
A
Au (020)
B
Figure S2. TEM images (left panels) and SAED patterns (right panels) of (A) an individual Au@Pd
core-shell nanorod with a polycrystalline Pd shell formed in CTAC and (B) an individual Au@Pd core-
shell nanocuboid with a conformal single-crystalline Pd shell formed in CTAB.
![Page 4: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/4.jpg)
ESI-p4
5 min 15 min 30 min
1 h 2 h 12 h
Figure S3. TEM images of Au@Pd core-shell nanorods obtained at 5 min, 15 min, 30 min, 1 h, 2 h and
12 h during the Pd overgrowth on Au nanorods in the presence of CTAC at 30 °C. The molar ratio of
AA to H2PdCl4 was 1.0. All the TEM images share the same scale bar in panel A.
![Page 5: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/5.jpg)
ESI-p5
30 min 1 h 2 h
4 h 8 h 12 h
Figure S4. TEM images of Au@Pd core-shell nanocuboids obtained at 30 min, 1 h, 2 h, 4 h, 8 h and 12
h during the Pd overgrowth on Au nanorods in the presence of CTAB at 30 °C. The molar ratio of AA
to H2PdCl4 was 1.0. All the TEM images share the same scale bar in panel A.
![Page 6: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/6.jpg)
ESI-p6
A
B
Figure S5. EDS spectra of Au@Pd core-shell nanostructures obtained through Pd overgrowth in CTAC
at 30 oC (A) in the absence of Ag+ and (B) in the presence of Ag+. The molar ratio of AA to H2PdCl4
was 0.5.
![Page 7: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/7.jpg)
ESI-p7
A
B
Figure S6. EDS spectra of Au@Pd core-shell nanostructures obtained through Pd overgrowth in CTAB
at 30 oC (A) in the absence of Ag+ and (B) in the presence of Ag+. The molar ratio of AA to H2PdCl4
was 0.5.
![Page 8: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/8.jpg)
ESI-p8
AA
BB
Figure S7. TEM images of Au@Ag core-shell nanorods obtained after Ag UPD in (A) CTAC and (B)
CTAB for 9 hours.
![Page 9: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/9.jpg)
ESI-p9
A
B
C
Figure S8. EDS spectra of (A) Au nanorods and Au@Ag core-shell nanorods after Ag UPD in (B)
CTAC and (C) CTAB for 9 hours.
![Page 10: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/10.jpg)
ESI-p10
400 600 800 1000
Ext
inct
ion
/ ar
b.u
.
Wavelength / nm
Ag UPD in CTAB Ag UPD in CTAC Au NRs
Figure S9. Optical extinction spectra of colloidal Au nanorods and Au@Ag core-shell nanorods
obtained after Ag UPD in CTAC and CTAB for 9 hours.
![Page 11: Controlled Overgrowth of Pd on Au Nanorods · ESI-p1 Electronic Supplementary Information for Controlled Overgrowth of Pd on Au Nanorods Hao Jing and Hui Wang* Department of Chemistry](https://reader034.fdocuments.us/reader034/viewer/2022050314/5f7701cb3029dd13b37375a3/html5/thumbnails/11.jpg)
ESI-p11
AA
BB
Figure S10. TEM images of Au@Pd core-shell nanostructures synthesized with the addition of 400 μL
of 1 mM Ag+, 300 µL of 10 mM H2PdCl4, and 30 µL of 50 mM AA into the solution of Au@Ag core-
shell nanorods (pre-formed through Ag UPD on Au nanorods) in (A) CTAC and (B) CTAB.