COLD WEATHERING CONCRETE
INDEX
SR.NO. CONTENTSPAGE
NO.
1 INTRODUCTION 2
2EFFECTS OF COLD WEATHER ON CONCRETE
3
3METHODS OF COLD WEATHER CONCRETING
8
4PRECAUTIONS IN COLD WEATHER CONCRETING
13
5 COLD WEATHER CONSTRUCTION 16
6 CONCLUSION 26
7 REFERENCES 27
-- 1 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
Abstract
Cold weather inhibits construction productivity in the northern tier of theUnited States. Over the years the U.S. Army Engineer Research and DevelopmentCenter’s Cold Regions Research and Engineering Laboratory (CRREL) hasdeveloped formulations for cold-weather concrete that facilitate economicalplacement of concrete at mix temperatures well below freezing. Like many othertechnological advances, the commercialization of this technology has effectively beenblocked by a lack of standards. CRREL is working with several State Transportation Departments to develop a near-term cold-weather concreting capability using off-theshelftechnology. Paralleling this effort, the Civil Engineering Research Foundation isspearheading an initiative to develop an acceptance standard for low-temperatureadmixtures. The world of cold-weather concreting promises to become a bit friendlierwithin the next few years and beyond.
-- 2 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
1. INTRODUCTION
COLD WEATHER CONCRETING:-
Cold weather is defined as a period when the average daily temperature
falls below 40°F [4°C] for more than three successive days. These conditions
warrant special precautions when placing, finishing, curing and protecting
concrete against the effects of cold weather. Since weather conditions can change
rapidly in the winter months, good concrete practices and proper planning are
critical.
The normal procedure adopted for concreting in fair weather will not be
valid for concreting when the temperature is low or below the freezing point. In
India, such areas are fairly small when compared to fair weather regions. The
production of concrete in cold weather introduces special and peculiar problems,
such as delay in setting and hardening, damage to concrete in plastic condition
when exposed to below freezing point owing to the formation of ice lenses.
Therefore, it is essential to maintain the temperature of the concrete positively
above o0C, possibly at much higher temperature.
-- 3 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
2. EFFECTS OF COLD WEATHER ON CONCRETE
(a) Delay in setting and hardening : Rate of hydration depends
upon the temperature. If temperature is low, concrete takes a long time to set and
a longer time to harden i.e., for the development of strength. The delay in setting
time makes concrete vulnerable to frost attack and other disturbances. Delay in
hardening period does not facilitate removal of formwork in a short period. Also
the rate of progress of work will be very slow, all of which affects economy.
(b) Freezing of concrete at early age : When the temperature
goes below freezing point, the free water contained in the plastic concrete freezes.
Freezing of water, not only prevents the hydration of cement but also makes the
concrete expand. This expansion causes disruption of concrete due to which
irrepairable loss of strength and quality takes places.
(c) Freezing and Thawing : It is likely that due to varied behavior
of climatic conditions in the cold weather regions, the fresh concrete or hardened
concrete gets subjected to freezing and thawing cycles. The durability of concrete
gets greatly impaired due to this alternate freezing and thawing. Freezing and
thawing may also exert fatigue in the concrete.
-- 4 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
In dealing with the aspect of cold weather concreting, the following
conditions may be discussed.
a) Low temperature, but above o0C, at the time of concreting and later during
hardening period.
b) Low temperature at the time of concreting but below o0C, during hardening
period.
c) Temperature below o0C at the time of concreting and during hardening
period.
d) Hardened concrete subject to alternate freezing and thawing.
It is necessary to deal with the above four conditions to understand the
behavior of concrete clearly and to take appropriate steps to offset the harmful
effects of such conditions for the successful placing of concrete.
A) Low Temperature but above o 0 C:-
If the temperature is only low but always above the freezing point, it only
retards the rate of development of strength as shown in the maturity equations
stated earlier. There is no other bad effect on the fresh concrete or hardening
concrete. As a matter of fact, the ultimate strength of the concrete cured at 9 0C
has been found to be a higher order than that of the concrete cure at higher
temperature. This may be due to the surperiority of gel structure on account of
slow growth. No other precautions are necessary except recognition of the fact of
delayed strength for stripping the formwork or for putting the concrete into
service.
-- 5 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
B) Low Temperature at the time of Concreting but Below
o 0 C after Concreting:-
The first condition has been discussed in the above para. But after
concreting, if the temperature falls below o0C, it is again necessary to view the
conditions under the following two categories :
a. Temperature falling below o0C when the concrete is still green.
b. Temperature prevailing below o0C after the concrete is sufficiently
hardened.
Many times it may so happen that the concrete will have been mixed and
placed when the ambient temperature is above freezing point. But before the
concrete has attained sufficient strength, the temperature of the air and also
temperature within the concrete may fall below freezing point, in which case the
free water still available in the concrete to freeze and form ice lenses in
microscopic scale. These ice lenses formed in the capillary cavities may cause
capillary suction of water from the ground, if the ground is saturated, and become
bigger to disrupt the mass which disturbs the compaction of concrete. Ice
formations may also appears as ice needles in the contact surfaces between
aggregates and cement paste. After thawing these ice needles will melt forming
cavities. Therefore, it can be concluded that freezing of freshly laid concrete
seriously impair the structural integrity of concrete and results in considerable
loss of strength.
In extreme cases, it make the concrete an absolutely useless friable mass.
On the other hand if the concrete is sufficiently hardened when freezing
takes place, there will not be much harm to the structural integrity of the concrete.
If the concrete has sufficiently hardened, the water that has been mixed for
-- 6 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
making concrete will have been lost either being used up in hydration process or
lost by evaporation. Due to the formation of cement gels, the capillary cavities
also will have been very much reduced, with the results that there exists very little
of free water in the body of concrete to freeze. Therefore, firstly the magnitude of
volume change due to the formation of microscopic ice lens is much less.
Secondly, the concrete at this stage is strong enough to resist whatever osmotic
pressure resulting from the freezing. Therefore, there is no immediate danger to
the concrete.
C) Temperature Blow o 0 C at the time of Concreting and
During Hardening Period:-
Concrete precautions are absolutely necessary for concreting when the
temperature is below o0C, so that the fresh concrete. Does not get frozen. The
consequences of freezing of fresh concrete. And the effect of sub-zero
temperature on the hardened but not fully matured concrete has been explained in
the para. Precautions to be taken and methods for carrying out concreting
operations will be explained later.
D) Hardened Concrete subjected to Alternate Freezing and
Thawing:-
Concrete pavements constructed at high altitude is normally subjected to
alternate freezing and thawing. The interval of cycles may be between season to
season or between day and night or even a couple of times in a day. It has been
-- 7 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
found that the durability of hardened Concrete is reduced to 1/3 to 1/7 when it is
subjected to alternate freezing and thawing depending on the quality of concrete.
It is to be noted that concrete is a previous material. Degree of porosity is
depending upon the Gel/space ratio. A concrete member is likely to get saturated
due to the absorption of moisture from surface or from bed. The free water that
has filled the capillary cavities of concrete will get frozen with the fall of
temperature. Subsequently when the temperature goes above o0C, the ice lens
melts. Due to this alternate freezing and thawing, concrete is subjected to distress
and surface scaling.
Concreting Methods at Sub-zero Temperature:-
It is clear that fresh concrete should not be subjected to freezing condition
till such time it attains a certain amount of strength. This time interval is known
as ‘Pre-hardening Period’. The recommended pre-hardening period as
recommended by IS 7861 (Part-2) 1979 is given in the following table.
Table - Time taken by Different Grades of Concrete
Specified minimum
strength at 28 days
for ordinary
Portland cement
MPa
Requisite Pre-hardening period
At any concrete
temperature above
freezing in units of
maturity 0C hr
At stated concrete temperature in
hours.
200C 100C 50C
M 20 1050 35 53 70
M 25 780 26 39 52
M 30 660 22 33 44
M 40 480 16 24 32
-- 8 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
3. METHODS OF COLD WEATHER CONCRETING
The precautions to be taken and methods adopted for concreting in sub-
zero temperature is listed below :
(a) Utilization of the heat developed by the hydration of cement and practical
methods of insulation.
(b) Selection of suitable type of cement.
(c) Economical heating of materials of concrete.
(d) Admixtures of anti-freezing materials.
(e) Electrical heating of concrete mass.
(f) Use of air-entraining agents.
An enormous quantity of heat is generated in the hydration of cement. If
this heat is preserved within the body of the concrete for a duration equal to the
prehardening period, it can do the useful job of offsetting the harmful effect of
low temperature. To conserve the heat, in concrete. In case of very low
temperature, it is very necessary that the insulation of concrete be so efficient as
to keep the surface temperature of concrete higher than o0C during pre-hardening
period.
Certain type of cement, hydrates fast, in turn gives out much larger quantity
of heat and develops early strength. The pre-hardening period for such a cement
will be about 40 to 50% of the normal Portland cement. Such cement contains
higher percentage of tricalcium silicate (C3S) and comparatively lower percentage
of dicalcium silicate (C2S). Rapid hardening cement is one such cement that can
be used. Extra rapid hardening cement. High Alumina Cement or mixture of
-- 9 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
ordinary Portland cement and high alumina cement in certain proportions can also
be used for this purpose. All the above will only reduce the time for which the
concrete is vulnerable to frost attack.
Preheating of the materials of concrete is one of the methods very
commonly employed in sub-zero temperature concreting. Heating of water is the
easiest to be adopted. If the ambient temperature is not very low, heating of water
alone will be sufficient, if the aggregates and cement are not in frozen condition.
In case of very low temperature or if it is estimated that a good amount of heat is
lost in transportation and placing, the heating of mixing water alone may prove to
be inadequate to maintain the required temperature in concrete. In such cases,
aggregate is also heated either by closed steam coils under the stock piles or by
injecting live steam into the stock piles or by hot air blowers. Fine aggregate can
also be heated on hot plates. Overheating of aggregates should be avoided.
Cement should never be heated.
To maintain the prehardening temperature, electrical heating of the entire
mass of concrete may be adopted where plenty of cheap power is available. Only
alternating current should be used for this purpose. Electricity is conducted
through mats or reinforcing bars. Sometimes special electrodes are carefully
positioned in such a way that uniform heat is generated. In order to protect the
workers, only low current should be used. The heating has to be designed very
carefully including the voltage, the type and location of the electrodes as well as
heating for each element. Evaporation of the mixing water has to be restricted by
covering the entire surface with vapour tight memberane.
-- 10 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
Inspite of these precautions it is found that the strength of electrically
heated concrete is about 20% less than normally cured concrete because of water
loss and temperature stresses caused by the cooling of the heated concrete.
Electrical heating is justified only in very cold climatic conditions where cheap
power is available, but it has the disadvantage of high cost of installation, power
consumption and loss of strength. In Sweden, Russia and Japan electrical curing
is being used quite extensively for protecting concrete from frost.
One of the widely adopted practices in winter concreting is the use of
accelerating admixtures which incidentally works as antifreeze also. The most
commonly employed material is calcium chloride. There are divergent views
about the quantity of calcium chloride to be admixed for optium results. Many
specifications do not permit the use of more than 3% CaCl2 by weight of cement
for fear of flash set and loss of long term strength. However, there are other
reports that the CaCl2 can be used in much higher quantity where the temperature
is very low, without any fear of retrogression of strength or corrosion of
reinforcement. But the use of CaCl2 may cause some increase in volume
change, greater tendency for alkali aggregate reaction and lower resistance to
sulphate attack.
All existing methods of winter concreting namely thermos, steam heating,
electric heating or their combined application are based on maintaining positive
temperatures during the early age of concrete, till such a time it develops
minimum strength at which freezing has no detrimental effect. The addition of
NaCl and CaCl2 makes it possible to regulate the freezing point of water in
-- 11 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
concrete and help to promote the continued hydration. CaCl2 forms high hydro-
complexes particularly with C3A, to make it active for accelerating the hydration.
As the temperature goes down, the rate of chemical reaction becomes much
slower. If NaCl alone is added, almost the same condition as stated above will
result except that it exhibits a better plasticising properties. But is is found that if
a combination of CaCl2 and NaCl is used, the concrete will show quicker
hardening property, a much higher frost resistance property and also better
placeability characteristics.
Till recently concrete technologists were of the view that durability of
concrete is dependant upon the compressive strength only. But with the
innovation of air-entrained concrete, the opinion got reversed. It is now known
that weaker concrete with air-entrainment is more durable under freezing
condition than that of strong concrete without air-entrainment. In general the
entrainment of air will increase durability to the extent of about 3 to 7 times of
that of ordinary concrete.
Modification of pore structure caused by air-entrainment is believed to be
responsible for the marked improvement in resistance to frost attack. It is
assumed that the concrete member is wet and quick freezing occurs. The surface
is immediately sealed due to the freezing of water at the surface and when
freezing continues ice crystals are formed inside the voids. Since the volume of
ice is 10% more than that of water, only 90% of water in the voids will turn into
ice. The excess of water is forced out through the capillary channels into the
adjoining lower air-voids, and the pressure is relieved. If sufficient water free
-- 12 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
voids are available, pressure build up will not occur and the eventual disruption of
the concrete will not take place.
The reduction in water cement ratio that might be permitted by the use of
air entrainment in concrete may also account for the greater resistance to freezing
and thawing action.
From the above discussion, it can be seen that the use of air-entraining
admixtures in concrete is positively useful in increasing the durability of concrete
in very cold regions.
-- 13 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
4. PRECAUTIONS IN COLD WEATHER
CONCRETING
To summerise, the following general precautions may be observed in cold
weather concreting:
(a) Preparation for concreting in cold weather may be completed well in
advance of severe conditions. Wind breakers shall be erected to shield the
mixing and batching plants; tarpaulins, plastic sheets and other covering
and insulting materials may be made available at the site and the steam
generating plant or other necessary equipments may be installed and
checked for correct functioning.
(b) The concrete shall be delivered to the point of placing at not less than 5 0C.
It is necessary to place the concrete quickly and cover the top of the
concrete with an insulating material
(c) Before any concrete is placed, all ice, snow and frost shall be completely
removed and the temperature be raised as close to the temperature of fresh
concrete to be placed thereon, as practicable. No concrete shall be placed
on a frozen subgrade or on that contains frozen materials. Where concrete
is to be placed over permanently frozen ground, subgrade materials may
be thawed deep enough to ensure that it will not freeze back up to the
concrete or it may be covered with a sufficient depth of dry granular
material.
(d) During cold weather, all concrete surfaces shall be covered as soon as the
concrete has been placed in order to preserve the heat and to help prevent
freezing. Clean straw bankets about 50 mm thick, sacks, tarpaulins,
expanded polystyrene, plastic sheets and waterproof paper can all be used
-- 14 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
in conjunction with air gap as an insulation. If possible insulating material
shall be placed against any formwork before concreting and the same can
be used as protection after the formwork has been stripped.
(e) Heated enclosures are commonly used for protecting concrete when air
temperatures are near or below freezing. Enclosures may be heated by
steam, steam pipes and other types of heaters. Enclosures may be made of
wood, canvas, fibre insulation board, plywood etc.
(f) During placement of unformed concrete, tarpaulins or other readily
moveable coverings supported on frame work shall follow closely the
placing of concrete, so that only a small area of finished slab is exposed to
outside air at any time. Such tarpaulins shall be used so that hot air can be
circulated freely on the slab. Layers of insulating materials placed directly
on the concrete are also effective in protecting the concrete.
(g) During periods of freezing or near-freezing conditions, water curing is not
necessary as the loss of moisture from the concrete by evaporation will be
greatly reduced in cold air conditions.
(h) For concrete cast in insulating formwork, it is only necessary to cover the
member completely In order to retain sufficient water for the hydration of
cement. On removal of the formwork and insulation, the member shall
immediately be covered with plastic sheet or tarpaulins, properly lapped
and made air-tight. On no account should such concrete, just released
from insulated formwork, be saturated with cold water. When protective
measures are to be discontinued, the surface temperature of the concrete
shall be gradually adjusted to the air temperature.
-- 15 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
(i) Low pressure wet steam provides the best means of both heating the
enclosures and for moist curing the concrete. Early curing with liquid
membrane forming compounds may be followed on concrete surface with
heated enclosures. It is better to cure first with steam curing during the
initial period of protection and then apply a curing compound after the
protection is removed and the air temperature is above freezing.
(j) Forms shall not be released until the concrete has achieved a strength of at
least twice the stress to which the concrete may be subjected at the time of
removal of formwork. In the normal circumstances where ambient
temperature does not fall below 150C and where OPC cement is used and
adequate curing is done.
(k) In cold weather protection offered by formworks other than of steel, is
often of greater importance. With suitable insulations, the forms,
including those of steel, in many cases will provide adequate protection
without supplementary heating. Therefore, it is often advantageous not to
remove forms until the end of a minimum period of protection or even
later.
(l) During cold weather, inspection personnel should keep a record of the date,
time outside air temperature, temperature of concrete at the time of placing
and general weather (calm, windy, clear, cloudy, etc.). The record should
also include the temperature at several points within the enclosure and on
the concrete surface, corners and edges in sufficient number to show the
highest and lowest temperatures of the concrete.
-- 16 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
5. COLD-WEATHER CONSTRUCTION
Concrete construction at temperatures <30°F normally requires additional
equipment and protective material. At temperatures >30°F, emplace concrete
using standard equipment and methods. Use the following techniques when
constructing pavement during cold weather:
1. Prepare, treat, and protect the subgrade.
2. Produce and deliver concrete at temperatures that will compensate for heat
loss during placement so that the concrete will harden at a normal or
accelerated rate.
3. Place and finish the slab with minimal heat loss from the concrete.
4. Protect the slab to maintain satisfactory hardening temperatures.
Preparation:-
Except in unusually protracted cold spells, freezing can be prevented by
covering the grade with straw. Before freezing temperatures occur, cover the area
with 12 to 24 inches of straw. The thickness required depends on the expected
temperature. Dry straw has better insulating properties than wet straw, so cover
the straw with tarpaulins or waterproof paper if necessary.
Uncover the subgrade during form setting and fine grading, and recover it
with straw to protect it until concrete placement. If the finished subgrade becomes
soft and muddy, remove free water and mud. Add sand, screening, gravel,
cinders, or unfrozen earth (tamped or rolled) to produce a firm grade and bring
the subgrade to the proper elevation. Heating the added material further protects
-- 17 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
the subgrade from freezing, and the heat can be retained by covering the subgrade
with straw until concrete placement.
Treatment:-
Thaw the surface layer of frozen subgrade by burning straw on it, using
torches or steam or, where permitted, covering the subgrade with hot sand,
screening, or cinders. Burning straw covered with sand removes frost >8 inches
deep. Spread the straw loosely on the subgrade, about 4 feet deep (50 to 70
pounds per square yard). Flax straw is preferred, but any dry straw can be used;
loose straw is better than baled straw. Spread sand on top of the straw at the rate
of about 4 cubic yards per 100 square yards (100 to 150 pounds per square yard)
of subgrade. Use pit-run sand, blow sand, or any other inexpensive sand that is
available. The sand ordinarily weighs the straw down to about half of its original
depth. Ignite the straw at the edges. It will smolder for hours under the sand,
holding in heat to thaw the subgrade. Cover the thawed subgrade with fresh straw
to hold the heat and prevent refreezing. There will be a layer of granular material
on the subgrade. It can be left in place or, if necessary, removed during fine
grading or before concrete placement. When the frost to be removed is only about
2 inches deep, reduce the thickness of the straw to about 3 feet (30 to 50 pounds
per square yard) and apply sand at the rate of about 3 cubic yards per 100 square
yards (50 to 100 pounds per square yard) of subgrade.
Surface layers of frozen subgrade can be thawed with surface heaters, such
as those used for patching and resurfacing asphalt pavements. A layer of hot sand
or screening can remove frost from subgrade that is frozen to a shallow depth. If
the grade permits, the layer of material can be left in place to provide insulation
-- 18 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
between the concrete and frost that may be left in the subgrade. The amount of
heated material required depends on the depth of the frost. A 1-inch layer of
heated material may be sufficient when the frost has slightly penetrated the
subgrade; however, greater frost depths may require a 3- or 4-inch layer of
material. A large volume of material is needed for very thick frost, and this
method of thawing is not practical unless suitable material is locally available at a
low cost.
Sand can be heated to about 400°F in a sand-dryer unit similar to that used
by a portable or stationary asphalt plant. The unit will produce enough heated
sand to cover the subgrade ahead of one concrete paving mixer. Do not place
concrete on the sand immediately. Spread the heated sand and cover it with straw
the day before concrete is to be placed, allowing the subgrade to thaw. The
temperature of the subgrade should not exceed 90°F when the concrete is placed.
It is unnecessary to remove frost to its full depth from subgrade that does
not have appreciable volume change under frost action, provided there is a layer
of frost-free material insulating the concrete from the frozen subgrade soil. This is
particularly applicable where granular subbases are being used. The required
thickness of the unfrozen, insulating layer depends on the depth of the frost that
underlies it. Use the methods discussed in FM 5-428 to determine the required
thickness.
Effect of Temperature:-
The rate that concrete hardens and gains strength is retarded by low
temperatures and accelerated by high temperatures. Near the freezing point, the
-- 19 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
rate is very slow; and at temperatures below freezing, there is almost no increase
in strength. Concrete that has been kept at a low temperature will later gain
strength rapidly when more favorable conditions are provided. Ensure that the
concrete's temperature is high enough for it to harden, and keep the concrete at a
suitable temperature until it has gained ample strength. It may be necessary to
heat concrete ingredients and protect the concrete against low temperatures.
Heating Materials:-
If the aggregate is above 50°F, it is only necessary to heat the mixing
water. Do not heat the mixing water above 175°F because there is danger of flash
setting. If the aggregate is below 47°F, heat the aggregate and the mixing water to
bring the concrete's temperature to 70°F. Add heated mixing water to the
aggregate to distribute the heat before adding the cement; never place heated
mixing water directly in cement.
Aggregates are more difficult to heat than water, and special equipment is
required to heat them in the quantity needed. It is usually possible to produce
concrete of the required temperature by heating only the sand; but if the CA
contains frozen lumps, it must also be heated.
Using steam is a practicable method of heating aggregate. Closed steam
coils are preferable to open jets due to the moisture-control problem in the
aggregate. However, closed steam coils require larger storage piles or bins than
those needed when live steam is used because the transfer of heat is slower. Live
steam can be fed into the base of stockpiles that have been covered with
tarpaulins. Further increases in temperature can be attained by discharging steam
-- 20 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
through the aggregates in the bins above the weighing hoppers. Best results are
obtained when the bins are full and the batches are loaded out at a uniform rate.
When using live steam, it is better to use steam under considerable pressure
because low pressure is more likely to result in the accumulation of condensed
moisture. Variable moisture content in the aggregate can cause undesirable
variations in concrete consistency, so watch it carefully.
Oil-burning heaters can be used to heat concrete by injecting a hot flame
into the mixer drum. In mild weather and on small jobs, they can be the sole
means for heating concrete. Other heating methods are required in cold weather
and on large jobs because oil-burning heaters will only produce a boost in
temperature.
Heating Requirements:-
Determine the amount of heating necessary to bring the mix to the
specified temperature. Assuming that no ice is present in the water or the
aggregate, use Figure and the following formula to determine the amount of heat
required. Increase temperatures until the concrete temperature is at the desired
point.
where—
X = weighted average temperature of aggregates and cement
-- 21 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
T = temperature of heated gravel, sand, or cement
W = weight of gravel, sand, or cement
g = gravel
s = sand
c = cement
Figure. Mixing Temperatures Versus Component Temperature
-- 22 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
Solution: Heat the aggregate >32°F (preferably 35°F) to avoid contact freezing
between the aggregate and the water. Heat the water to 137°F(from Figure).
Heating Equipment:-
Operate heating equipment several hours before paving starts. A sand dryer
should be started early so that an ample supply of heated sand is available when
the mixer starts. Make provisions for heating or store aggregates in insulated bins
overnight and during shutdowns to keep them from freezing. If steam heating is
used, discharge live steam constantly into the covered stockpile throughout the
entire 24 hours to ensure an adequate supply of aggregate at the required
temperature.
Heat Preservation:-
During the construction of large areas of pavement a comparatively short
distance from the plant, such as an airport, a central mixing plant is advantageous.
The mix can be transported to the subgrade in dump trucks covered with
-- 23 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
tarpaulins. In a short haul from the mixer to the subgrade, heat loss is not great.
With experience, the temperature at the mixer can be adjusted to obtain the
desired temperature of concrete on the subgrade in cold, windy weather. A piece
of sheet metal can also be placed over the mixer drum opening (opposite the
burner) to reduce heat loss.
Placing and Finishing:-
Place and finish the concrete quickly to minimize heat loss. To accelerate
finishing, add the minimal amount of mixing water needed. Keep bleeding to a
minimum by paying special attention to the mix design. For example, increase the
amount of fine material in the sand, make adjustments in the gradation, or use a
different type of aggregate.
When mixing concrete, add calcium chloride to accelerate hardening.
Adding calcium chloride permits quicker finishing and also allows the insulating
layer of straw to be placed on the pavement sooner. Concrete >90°F and
containing calcium chloride hardens too quickly to permit good finishing results.
Finishing can be done in the open if the outside temperature is >15°F and straw,
paper, or a cloth cover is applied quickly. If the temperature is <10°F, especially
with a strong wind, some form of shelter is required. The shelter may be covered
framework that is mounted on wheels and rolled forward as work progresses.
Remember to provide enough room for men to work. Use portable space heaters
if the shelter alone does not sufficiently reduce heat loss. At very low
-- 24 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
temperatures, it may be necessary to heat steel side forms before the concrete is
placed.
Protection After Finishing:-
Ordinary curing specifications, which are aimed at supplying or retaining
sufficient water within the concrete to ensure continuing hydration, can be
disregarded during cold weather. Water evaporates very slowly at low
temperatures, and the covering applied to protect the pavement from cold
sufficiently reduces evaporation and retains plenty of moisture in the concrete.
Apply a layer of dry straw as soon as possible. If the pavement has not
hardened enough to prevent marring from footprints, use light, movable bridges
to apply the protective covering. Dry straw has better insulating properties than
wet straw, so cover it with waterproof paper or canvas to keep it dry. This also
keeps wind from blowing the straw away and exposing portions of the pavement.
In extreme weather conditions, use steam pipes under the covering to provide
additional heat. Hand forks or adapted mechanical equipment can be used to
handle straw. For example, baled and loose straw can be handled with a clamshell
that is equipped with long teeth to convert it into a grappling fork.
The heat of hydration increases the temperature of concrete after it is
covered. This increase in temperature cannot be relied on as a substitute for
heating materials, but it will offset heat loss during finishing. The temperature of
the subgrade rises substantially after the warm concrete is spread. During early
hardening of the concrete, this quick rise in temperature causes an appreciable
volume change in frozen subgrade when it thaws. Protect concrete until it has
-- 25 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
attained a flexural strength of at least 400 psi. The length of time protection is
required depends on the temperatures maintained and the corresponding rate of
hardening. It can range from 72 hours for high-early strength concrete mixtures to
7 to 10 days for normal concrete.
-- 26 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
6. CONCLUSION
In construction of any R.C.C structure the concreting is the most important
part as the concrete provide strength to the structure, it is necessary to do the
proper concreting during construction of any structure.
But in case of the concreting, in cold weather regions, it is very hard to
construct the structure because of the water content present in the concrete freezes
very early due to the decrease in temperature. It is very necessary to do concreting
with great care. The precautions should be taken during the process and the
workers safety should be well maintained. We should know the various method of
concreting in case of cold weathering regions to handle the concrete.
-- 27 -- N.D.M.V.P.S, COE
COLD WEATHERING CONCRETE
7. REFERENCES
1. “CONCRETE TECHNOLOGY , THEORY & PRACTICE” BY
M.S. SHETTY.
2. INFORMATION COLLECTED THROUGH BROWSING
VARIOUS WEB SITES USING PDF SEARCH ENGINE.
-- 28 -- N.D.M.V.P.S, COE