Chameleon-Inspired Mechanochromic Photonic Films...
Transcript of Chameleon-Inspired Mechanochromic Photonic Films...
Subscriber access provided by University of Sydney Library
ACS Nano is published by the American Chemical Society. 1155 Sixteenth StreetN.W., Washington, DC 20036Published by American Chemical Society. Copyright © American Chemical Society.However, no copyright claim is made to original U.S. Government works, or worksproduced by employees of any Commonwealth realm Crown government in the courseof their duties.
Article
Chameleon-Inspired Mechanochromic Photonic FilmsComposed of Nonclose-Packed Colloidal Arrays
Gun Ho Lee, Tae Min Choi, Bomi Kim, Sang Hoon Han, Jung Min Lee, and Shin-Hyun KimACS Nano, Just Accepted Manuscript • DOI: 10.1021/acsnano.7b05885 • Publication Date (Web): 02 Nov 2017
Downloaded from http://pubs.acs.org on November 3, 2017
Just Accepted
“Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are postedonline prior to technical editing, formatting for publication and author proofing. The American ChemicalSociety provides “Just Accepted” as a free service to the research community to expedite thedissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscriptsappear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have beenfully peer reviewed, but should not be considered the official version of record. They are accessible to allreaders and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offeredto authors. Therefore, the “Just Accepted” Web site may not include all articles that will be publishedin the journal. After a manuscript is technically edited and formatted, it will be removed from the “JustAccepted” Web site and published as an ASAP article. Note that technical editing may introduce minorchanges to the manuscript text and/or graphics which could affect content, and all legal disclaimersand ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errorsor consequences arising from the use of information contained in these “Just Accepted” manuscripts.
1
Chameleon-Inspired Mechanochromic Photonic
Films Composed of Nonclose-Packed Colloidal
Arrays
Gun Ho Lee†, Tae Min Choi
†, Bomi Kim
†, Sang Hoon Han
†, Jung Min Lee
‡, and Shin-Hyun
Kim*,†
†Department of Chemical and Biomolecular Engineering (BK21+ Program), Korea Advanced
Institute of Science and Technology (KAIST), Daejeon 34141, Republic of Korea
‡The 4th R&D Institute, Agency for Defense Development, Daejeon 34060, Republic of Korea
Page 1 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
2
ABSTRACT
Chameleon uses a nonclose-packed array of guanine nanocrystals in iridophores to develop and
tune skin colors in full visible range. Inspired from the biological process uncovered in panther
chameleons, we design photonic films containing a nonclose-packed face-centered cubic (fcc)
array of silica particles embedded in an elastomer. The nonclose-packed array is formed by
interparticle repulsion exerted by solvation layers on the particle surface, which is rapidly
captured in the elastomer by photo-curing of the dispersion medium. The artificial skin exhibits
the structural color that shifts from red to blue under stretching or compression. The separation
between inelastic particles enables the tuning without experiencing significant rearrangement of
particles, providing elastic deformation and reversible color change, as chameleons do. The
simple fabrication procedure consists of film casting and UV irradiation, potentially enabling the
continuous high-throughput production. The mechanochromic property of the photonic films
enables the visualization of deformation or stress with colors, which is potentially beneficial for
various applications, including mechanical sensors, sound-vision transformers, and color display.
KEYWORDS: Chameleons, Colloidal crystals, Nonclose-packed arrays, Structural colors,
Mechanochromism
Page 2 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
3
Several species of chameleons have a distinguished talent to rapidly tune their colors between
a cryptic (camouflage) state and a highly-visible excited state during male-male combats and
courtship.1-3
Recent analysis combining microscopy, photometric videography, and photonic
bandgap modeling has revealed that panther chameleons change colors primarily through the
active tuning of a lattice of guanine nanocrystals within iridophore cells.3 Theses specialized
dermal cells constitute therefore tunable photonic crystals. Photonic crystals are periodic
nanostructures in the length scale of half the wavelength, which develops colors through the
reflection of selected wavelength of the visible light.4-6
As the period of photonic crystals
dictates the wavelength of reflection, the color can be tuned by adjusting the period with
mechanical strain. Colloidal crystals have been used to provide strain-induced color change, or
mechanochromism, for various applications. For example, strain or pressure can be measured in
a colorimetric manner with mechanochromic films;7-9
fingerprint can be readily recognized by
analyzing color pattern.9 In addition, lasing from fluorescent molecules in the photonic crystals
can be modulated by strain-induced adjustment of stop band position.10
Through a local
modulation of elastic modulus, the color pattern can be encrypted; the hidden pattern is disclosed
when the films are subjected to extensional stress.11,12
To render colloidal crystals mechanochromic, various combinations of materials and processes
have been exploited. For example, interstices of close-packed colloidal crystals, or opal
structures, are filled with elastomers;13-15
although the composites show strain-induced color
shift, strain and color shift are highly limited because the extension entails significant
rearrangement of close-packed colloids. Swelling of the elastomeric matrix with organic solvents
slightly increases the allowable strain.16,17
Inverse opals composed of close-packed air cavities
embedded in elastomers have negligible resistance against deformation of cavities, thereby
Page 3 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
4
providing a full-color change.18
However, delicate procedures of fabrication and low mechanical
stability of inverse opal structures restrict practical uses; small extensional strain is only allowed.
Alternatively, colloids composed of an inelastic core and elastic shell are crystallized and fused
by melt-flow technique to form highly stable, flexible composite structures;19-22
this approach
enables the continuous production of the composite films or fibers by roll-to-roll or extrusion
process.23, 24
Although the composites can display a color shift in the full visible by stretching,
the deformation is not purely elastic and leaves a residual strain as interparticle separation is
insufficient.19, 21
Furthermore, colloids are crystallized only near the surfaces, achieving a limited
photonic performance.19
Nonclose-packed array of colloids can provide a large deformation of the elastic matrix and
therefore enables a full-color change in the absence of colloidal rearrangement. To achieve the
large interparticle separation, charged colloids have been spontaneously crystallized in an
aqueous medium through electrostatic repulsion, which are immobilized by a hydrogel.25-27
Although the nonclose-packed arrays embedded in water-swollen gels provide mechanochromic
property, the low mechanical stability of gels against stretching and vaporization of water in the
air environment only allows a short-term use in restricted conditions. Thus, a simple and scalable
method to create nonclose-packed arrays in liquid-free elastic matrix remains an important yet
unmet need for highly stretchable, durable photonic films with reversible full-color tunability.
In this work, we design mechanochromic elastomers containing a nonclose-packed array of
silica particles by mimicking the iridophore structure of chameleons.3 Silica particles are
dispersed in a carefully selected rubber precursor to induce interparticle repulsion through the
formation of solvation layer on the surface of particles. The repulsive potential leads to
spontaneous crystallization of silica particles above threshold volume fraction and the regular
Page 4 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
5
array is captured by rapid photo-polymerization of the precursor in a liquid-free rubber matrix.
The elastic composites exhibit a pronounced reflection color which blue-shifts in full visible
range as the film is stretched up to a strain of 70%. During the stretching, silica particles remain
untouched by following the positions of the elongated lattice. The negligible rearrangement of
particles renders the photonic composites fully reversible in a color shift along the strain,
implying that the deformation is elastic and no residual strain remains. The elastic composites
also show color change with compression. The compression with stamps causes blue-shift of
color on relief regions and red-shift on engraved regions, developing multicolor patterns. This
approach based on photocurable colloidal dispersion is potentially applicable for roll-to-roll or
jetting processes to continuously produce mechanochromic films or fibers for versatile uses.
RESULTS AND DISCUSSION
Nonclose-packed array embedded in elastomeric matrix
In dermal iridophores of chameleons, particles of rigid guanine nanocrystals are embedded in a
matrix of elastic cytoplasm to form nonclose-packed crystals.3 As the cytoplasm undergoes rapid
volume change, a lattice parameter is altered in the range of 240 - 480 nm, while maintaining the
lattice structure, thereby leading to a drastic color shift in full visible range (Figure 1a). We
mimic the iridophore structure by embedding a nonclose-packed array of rigid silica particles in
an elastomeric matrix (Figure 1b). To compose the structures, silica particles are dispersed in a
rubber precursor of poly(ethylene glycol) phenyl ether acrylate (PEGPEA). The dispersion is
highly stable against agglomeration and sedimentation even at volume fraction higher than 40%
at least for several months. The high stability is attributed to repulsive interparticle potential
exerted by solvation layers formed on the particle surface. The acrylate groups of PEGPEA are
Page 5 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
6
strongly bound on the surface of silica particles through the hydrogen bonds with silanol groups,
forming a dense solvation layer.28,29
Therefore, silica particles repel each other due to the
disjoining pressure when particles are brought close. The interparticle repulsion facilitates the
formation of a regular array of silica particles. The composite films, produced by
photopolymerization of the dispersion, show pronounced reflection colors (Figure 1c); the film is
prepared by infiltrating the dispersion into a gap between two slides glasses by a capillary force
and irradiating with ultraviolet (UV) (Figure S1 of Supporting Information). At the same time,
the films are translucent (Figure 1d). The films are composed of a nonclose-packed array of
silica particles embedded in the matrix of polymerized PEGPEA (pPEGPEA) (Figure 1e). The
ordered array develops the color and the low contrast of refractive index between silica (np =
1.45) and pPEGPEA (nm = 1.502) leads to negligible scattering out of stop band, rendering the
films translucent. These optical properties are further confirmed with reflectance and
transmittance spectra which show a narrow peak and dip respectively at the same wavelength of
stop band (Figure S2). The transmittance is as high as 80% out of stop band and the sum of
reflectance and transmittance is close to 95% even for short wavelength, indicating negligible
scattering in entire visible range. The photonic film exhibits blue-shift of reflection color as
stretched (Movie S1 of Supporting Information). The red film at normal reflection turns to green
and blue for the strains of 0.20 and 0.47 respectively (Figure 1f). With a backlight, the film
shows complementary color as light at stop band is blocked, while light out of stop band is
transmitted (Figure 1g). Therefore, the red film at reflection appears cyan at transmission which
is the result of color mixing of green and blue. The cyan color turns to magenta and yellow at the
transmission as stretched; magenta is originated from the color mixing of red and blue and
yellow is of red and green, respectively.
Page 6 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
7
Threshold volume fraction for crystallization
The interparticle repulsion is effective only when solvation layers of neighboring particles are
overlapped. Therefore, there exists a threshold volume fraction of particles, ϕth, for the formation
of the ordered array (Figure 2a). At volume fractions lower than the threshold (ϕ < ϕth), no
overlap among the solvation layers and a disordered array of particles are expected. At the
threshold (ϕ = ϕth), the average interparticle separation is comparable to double the thickness of
solvation layer and particles spontaneously form a regular array with a long-range order. The
interparticle separation will be reduced, while maintaining the long-range order, above the
threshold (ϕ > ϕth). To estimate the thickness of solvation layer and the threshold volume fraction
responsible for the long-range ordering, composite films are prepared from dispersions of silica
particles with various volume fractions in the range of ϕ = 0.1 - 0.4; silica particles with a
diameter of d = 150 nm are used for all volume fractions. The film at ϕ = 0.1 shows no
pronounced color. The film at ϕ = 0.2 shows green colors, which blue-shifts along with ϕ for ϕ ≥
0.20 (Figure 2b). The volume-fraction dependence of color change is further confirmed with
reflectance spectra (Figure 2c). The spectrum peak blue shifts along with ϕ for ϕ ≥ 0.20, whereas
no peak at ϕ = 0.1. The peak positions for ϕ ≥ 0.26 are in a good agreement with the stop band
position, λmax, expected from Bragg’s diffraction from (111) planes of nonclose-packed face-
centered cubic (fcc) lattice (Figure 2d):
���� = 2������ = � �√���
�� ��
���� � ��, (1)
where d111 is the distance between two neighboring (111) planes and neff is an effective refractive
index.30
To determine the value of neff, we use Maxwell-Garnett average of refractive indices of
silica particles and pPEGPEA matrix:
Page 7 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
8
��� = ��� + �� �1 − ��. (2)
The coincidence between the peak positions of spectra and λmax from eq 1 indicates that silica
particles form nonclose-packed fcc structure whose (111) planes are aligned along with film
surfaces. The peaks for ϕ ≥ 0.26 have a self-consistent value of a full width at half maximum
normalized by the stop band, ∆λ/λmax, as approximately 0.04 (Figure 2d), indicating an
insignificant difference in ordering. By contrast, the peak for ϕ = 0.20 has the value of ∆λ/λmax as
large as 0.081, implying colloidal array less ordered. In addition, the peak is located at 543 nm
which is smaller than λmax of 565 nm from eq 1. This indicates that the colloidal array does not
fully occupy the whole volume of the film; the value of d111 estimated from the peak position by
assuming a perfect fcc crystal is 182 nm, whereas the value of d111 is 189 nm according to eq 1
which assumes nonclose-packed crystals that occupy the whole volume. When we assume that
all the silica particles in the film constitute the crystal, the film is composed of 89% crystal
region and 11% particle-free region. The interparticle separation in the crystal region is 73 nm,
from which the thickness of solvation layer, t, is estimated as 36.5 nm and ϕth is estimated as
0.225 for silica particles with d = 150 nm.
The value of ϕth varies with the diameter of silica particles. The thickness of solvation layer, t, is
expected to be independent of particle diameter, d. Therefore, the surface-to-surface separation at
the threshold volume fraction for large particles is same to that of small particles. Therefore,
larger particles occupy more volume and result in larger threshold volume fraction than smaller
ones. The values of ϕth are estimated as 0.222 for d = 148 nm, 0.248 for d = 166 nm, 0.260 for d
= 175 nm, 0.285 for d = 195 nm and 0.309 for d = 216 nm (see Figure S3 and related paragraph
in the Supporting Information for the detailed calculation). We prepare photonic films with
various stop band positions with silica particles with different diameters while maintaining ϕ =
Page 8 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
9
0.33 which is larger than ϕth for all particles (Figure S4). Therefore, a colloidal array with a long-
range order fully occupy the films and reflectance peak positions are in a good agreement with
eq 1.
Mechanical and surface properties of photonic films
The particle-free matrix polymer of pPEGPEA is highly elastic and shows constant Young’s
modulus of 0.23 MPa for the entire range of strain below the fracture at 0.91. The composite
photonic film has Young’s modulus of 0.46 MPa for the strain smaller than 0.47, which increases
to 1.03 MPa for the strain below the fracture at 0.75 (Figure S5). The modulus at low strain is
only 2 times larger than that of particle-free pPEGPEA because rigid silica particles are
embedded without a contact. As strain increases, the silica particles are brought closer, leading to
the increase of modulus. Strain at the fracture slightly decreases as the film contains the inelastic
fillers. The low elastic modulus, as well as finite surface energy, renders the photonic film
adhesive. Therefore, the film sticks to itself or other materials to reduce surface energy, making
it difficult to handle. To prevent the self-adhesion, the surfaces of the photonic film are modified
by reactive ion etching (RIE) with SF6. The RIE treatment fluorinates the surfaces and therefore
reduce surface energy. We confirm the reduction of the surface energy from contact angles of
water; the angle is 67° for the pristine films and 138° for the fluorinated ones (Figure S6). The
fluorinated films are almost free from self-adhesion (Movie S2). The RIE treatment alters only
the surface property of the films while retaining the colloidal crystals in the thickness, providing
the color and reflectance spectrum same to the pristine (Figure S6). The non-sticky property is
maintained for several days.
Page 9 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
10
High reversibility of mechanochromism
The elastic photonic films instantly change the color as they are stretched. The stretching reduces
the thickness of the film, thereby causing the reduction of d111. The color is therefore dictated by
strain along the lateral direction, εx. The photonic film composed of d = 195 nm at ϕ = 0.33
shows red reflection color and stop band at 618 nm in the absence of strain. As εx increases to
69%, the color and stop band continuously shifts from red to blue, covering almost entire visible
range (Figure 3a and 3b). Compared with swollen opals, inverse opals, or mechanochromic
gels,18-22
the photonic films allow significantly high extensional strain (~ 70%) as the composite
structure is composed of nonclose-packed silica particles embedded in a solvent-free elastomeric
matrix with high stability against extension. The maximum strains of swollen opals and
mechanochromic organic gels are limited to approximately 20% and 22%;16, 31
inverse opals and
mechanochromic hydrogel only allow compressive strain.18
The color shift induced by the
extensional strain is also highly reversible (Figure 3c) as a result of elastic deformation. Because
particles do not rearrange during the deformation, no residual strain is observed when the film is
free from stress even after applying the maximum strain of 70%, thereby fully recovering the
original color and stop band wavelength (Movie S3). Although photonic films prepared by a
melt-flow technique using colloids with an inelastic core and elastic shell allow the large
extensional strain, insufficient particle separation leads to plastic deformation and therefore,
results in a residual strain for color tuning in a full visible range.19, 21
The high reversibility is
conserved for at least 3 days of stretching with εx = 0.4 in the temperature range between -20℃
and 70℃ (Figure S7). Moreover, the photonic films maintain resonant wavelength and
reflectivity during a long-term storage at room temperature, as shown in Figure S8. This
indicates that the photocurable dispersions and photonic films contain a negligibly small amount
Page 10 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
11
of volatile solvent. The elastic deformation and corresponding color shift across the entire visible
range are the results of sufficient separation between two neighboring silica particles; crystals
with small separation undergo plastic deformation for large εx.19, 21
The average separation
between two nearest particles is 60 nm for the film composed of d = 195 nm at ϕ = 0.33.
We model the structural change of colloidal array from blue-shift of the stop band. The stop
band wavelength, λmax(εx), blue shifts as much as εz λmax (εx = 0) as a film is stretched:
�������� = 2�����1 − � ��� = 2�����1 − !����� , (3)
where ν is Poisson’s ratio. The responses of εz and ν for εx are estimated from reflectance peak
positions using eq 3. The lattice structure of deformed composite film can be constructed from
values of εx and εz, where εy is set to εz because the pPEGPEA matrix is isotropic (insets of
Figure 3d). The centers of particles follow the deformation of the matrix, which does not cause a
contact between two particles for given ranges of εx, εy, and εz. The interparticle separation at
strain-free state is sufficient to avoid rearrangement of particles during the stretching, thereby
enabling the elastic extension without a residual strain. We confirm no rearrangement of silica
particles embedded in the stretched photonic film from cross-sectional SEM image (Figure S9).
As expected from the lattice model, the silica particles follow the position of elongated lattice
without additional rearrangement. The stop band steeply shifts at small strain and the slope is
lowered as the strain increases (left y-axis of Figure 3d). The value of ν calculated from the slope
for εx ≤ 0.077 is 0.45, which is slightly smaller than 0.5 (value for rubbers); that is, the
deformation of the composite film is governed by elastic pPEGPEA matrix for small strain as
inelastic silica particles are separated. As the strain increases, the value of ν for the small interval
of εx decreases (y-axis of Figure 3d); the value of ν for 0.61 ≤ εx ≤ 0.69 is 0.23. For the large
Page 11 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
12
stain, inelastic particles are brought close, partially losing the property of elastic matrix. That is,
the volume is not conserved as silica particles resist the matrix deformation during the stretching.
During the blue shift of stop band, reflectivity at the stop band is reduced. Because silica
particles are embedded in the elastic matrix, particles maintain the regular array during the
stretching. Nevertheless, silica particles in two neighboring (111) planes are partially
interpenetrated to each other, reducing refractive index contrast between a slice containing (111)
plane at the middle and an intermediate slice. The effective refractive indices of two slices are
estimated using eq 2 based on model structures (Figure S10a). The volume fraction of matrix
increases as the matrix is expanded by the strain for the slice containing (111) plane, whereas the
volume fraction of silica particles increases as silica particles invade from (111) planes for the
intermediate slice (Figure S10b). Therefore, the index contrast decreases as strain increases. As
the strength of Bragg reflection linearly varies with the index contrast for a fixed number of
alternating layers, the reflectivity is also expected to vary in the same manner.32
It is clearly
shown that the tendency of the contrast reduction is comparable to that of reflectance reduction
(Figure 3e), implying that the reflectance reduction is caused by the contrast reduction.
Color change by compression
The elastic photonic films show a color shift in a response to compressive stress. When the film
is compressed by stamps, the film under the relief region is contracted, thereby causing a blue-
shift of color (Figure 4a). At the same time, the film under engraved regions is expanded as the
volume of the composite is roughly conserved, thereby causing red-shift.33
To confirm the color
shift, the elastic photonic film that exhibits red reflection color is compressed with a stamp
composed of relieves of small ‘K’s that form a large ‘K’. The single-colored film turns dual-
colored pattern by the compression (Figure 4b). Reflectance spectrum is also changed from a
Page 12 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
13
sharp peak at 610 nm to a broad peak (Figure 4c). The broadening is caused by simultaneous
blue- and red-shifts of color on the relief and engraved regions, respectively. The shifts are
further confirmed by reflectance spectra taken at local areas; spectrum at small ‘K’ has a sharp
peak at 591 nm, whereas that at background has a sharp peak at 619 nm. The photonic film can
develop dual-colored patterns in a high resolution. For example, a stamp of line pattern
composed of 100-µm-width relieves and 100-µm-width engraves produces alternate green and
red lines with comparable dimensions under compression (Figure 4d). A stamp containing a
square array of 50-µm-diameter circular pillars develops green dot array on red surrounding
(Figure 4e). The development of the dual-colored patterns is reversible (Movie S4).
CONCLUSION
In summary, we mimic the photonic structure of dermal iridophores of panther chameleons by
embedding a nonclose-packed array of silica particles in an elastic polymer matrix.3 The
sufficient separation between particles enables the reversible color-shift in the full visible range
in the absence of significant particle rearrangement under extensional stress as the iridophores
do. Only the remaining problem is the reduction of reflectivity during the stretching process. As
we proved with a lattice model, the optical loss is caused by the reduction of refractive-index
contrast. The problem is potentially overcome by swelling the photonic structure with
nonvolatile organic solvent. As the swelling increases the interparticle separation, a larger blue-
shift of structural color can be achieved with a small reduction in the index contrast. The
mechanochromic materials can visualize strain with colors. This deformation-vision
transformation is useful for various colorimetric measurements. For example, surface topologies
of materials, such as fingerprints, can be mapped with color by compressing the films with them
(Figure 4). In addition, the real-time deformation of skins can be visualized by attaching the
Page 13 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
14
photonic film on the surfaces (Figure S11 and Movie S5); elastic modulus of films,
approximately 1 MPa, is comparable to that of skin, thereby minimizing mechanical mismatch
between two layers during the deformation.34
The mechanochromic films have a great potential
as active color reflectors for large-scale wallpaper or signboard displays in the combination with
site-addressable pneumatic compressors.35, 36
In addition, the photonic films with low elastic
modulus are potentially able to convert acoustic waves into colors, transforming sound into
visual senses.37
The mechanochromic films are simply prepared by casting of colloidal
dispersion and subsequent UV exposure without any tedious processes. This process is
compatible with continuous roll-to-roll or slot coating production with high throughput.
Moreover, the format of materials can be further modified into granules, fibers, and any 3D
architectures by employing microfluidic or 3D printing techniques, extending the applicable area
of mechanochromic materials.38
EXPERIMENTAL METHODS
Preparation of photocurable colloidal dispersions. Monodisperse silica particles are
synthesized by two steps: Seed particles are synthesized by two-phase method,39
which are then
grown to silica particles with target diameter by Stöber method.40
The suspension is fully dried in
a convection oven at 70°C for 12 h after washing with ethanol and weight of the silica powder is
measured. The dried powders are redispersed in ethanol, which is then mixed with PEGPEA
(Mw 324, Sigma-Aldrich) containing 1 w/w% photoinitiator of 2-hydroxy-2-methyl-1-phenyl-1-
propaneone (Darocur 1173, Ciba Chemical), where the amount of PEGPEA is determined from
the weight of silica powder to have a target volume fraction of silica particles in ethanol-free
basis; densities of silica particles and PEGPEA are approximated as 2.0 and 1.127 g mL-1
,
respectively. Ethanol is vaporized in a convection oven at 70°C for 12 h to prepare silica-in-
Page 14 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
15
PEGPEA dispersion; the protocol to prepare concentrated dispersions has been reported in
literature.41
Fabrication of mechanchromic photonic films. The photocurable dispersion is spontaneously
infiltrated by capillary force into a gap between two glass slides separated by 50 µm-thick
spacers of polyimide tape (Kapton). The dispersion is irradiated by UV light (Inno-cure 100N,
Lichtzen) with an intensity of 2 W cm-2
for 20 s. The polymerized composite film is released
from the glass slides. To render the film to have low surface energy, both surfaces of the film are
treated by reactive ion etching (VSRIE-400A, Vacuum Science Inc.) with sulfur hexafluoride gas
(SF6) for 30 s with a power of 150 W and a flow rate of 100 sccm.
Characterization. Images of photonic films are taken by an optical microscope in reflection
mode (Eclipse L150, Nikon) and reflectance spectra are measured using a fiber-coupled
spectrometer (USB 4000, Ocean Optics Inc.) equipped in the microscopy; ×10 lens with
numerical aperture of 0.30 is used for spectrum measurement and a field stop is used to measure
spectra from local areas in some experiments. The transmission spectra are measured using a
spectrometer (SP-2300i/PIXIS: 400B_eXcelon, Princeton Instruments) equipped in an inverted
microscope (Eclipse Ti, Nikon). Cross-sections of the films are observed using scanning electron
microscopy (S-4800, Hitachi) after coating with osmium tetraoxide. Stress-strain curves are
measured using a microforce testing system (8848, Instron Corporation). Contact angles of water
drops on the films are measured using a goniometer (DSA 10-Mk2, KRUSS).
ASSOCIATED CONTENT
Supporting Information.
This material is available free of charge via the Internet at http://pubs.acs.org.
Page 15 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
16
Reflectance and transmittance spectra of photonic films; color tunability with particle
diameter; stress-strain curve and elastic modulus of photonic film; influence of surface
modification; reversibility, thermal, long-term stability tests; a lattice model; cross-
sectional SEM image of stretched film; film on the skin (PDF).
Color change by stretching; non-sticky, fluorinated film; reversible change of color and
spectrum; dual-color patterns formed by compression of photonic film with stamps; color
change of photonic film on the skin by folding and unfolding elbow (AVI).
AUTHOR INFORMATION
Corresponding Author
*E-mail: [email protected].
Author Contributions
G.H.L. carried out all experiment; G.H.L. and T.M.C. analyzed the data; B.K. S.H.H. and J.M.L.
helped the characterization; S.-H.K. designed and supervised the research.
ACKNOWLEDGMENT
This work was supported by the Agency for Defense Development of Korea (17-113-706-011)
REFERENCES
(1) Stuart-Fox, D.; Whiting, M. J.; Moussalli, A. Camouflage and Colour Change: Antipredator
Responses to Bird and Snake Predators Across Multiple Populations in a Dwarf Chameleon.
Biol. J. Linn. Soc. 2006, 88, 437–446.
(2) Weiss, S. L. Reproductive Signals of Female Lizards: Pattern of Trait Expression and Male
Response. Ethology 2002, 108, 793–813.
Page 16 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
17
(3) Teyssier, J.; Saenko, S. V.; Van Der Marel, D.; Milinkovitch, M. C. Photonic Crystals Cause
Active Colour Change in Chameleons. Nat. Commun. 2015, 6, 6368.
(4) Kim, S.-H.; Lee, S. Y.; Yang, S.-M.; Yi, G.-R. Self-Assembled Colloidal Structures for
Photonics. NPG Asia Mater. 2011, 3, 25–33.
(5) Lee, H. S.; Shim, T. S.; Hwang, H.; Yang, S.-M.; Kim, S.-H. Colloidal Photonic Crystals
toward Structural Color Palettes for Security Materials. Chem. Mater. 2013, 25, 2684–2690.
(6) Arsenault, A. C.; Puzzo, D. P.; Manners, I; Ozin, G. A. Photonic-Crystal Full-Colour
Displays. Nat. Photonics 2007, 1, 468–472.
(7) Wang, X. Q.; Wang, C. F.; Zhou, Z. F.; Chen, S. Robust Mechanochromic Elastic One
Dimensional Photonic Hydrogels for Touch Sensing and Flexible Displays. Adv. Opt. Mater.
2014, 2, 652–662.
(8) Jia, X.; Wang, J.; Wang, K.; Zhu, J. Highly Sensitive Mechanochromic Photonic Hydrogels
with Fast Reversibility and Mechanical Stability. Langmuir 2015, 31, 8732–8737.
(9) Hong, R.; Shi, Y.; Wang, X.-Q.; Peng, L.; Wu, X.; Cheng, H.; Chen, S. Highly Sensitive
Mechanochromic Photonic Gel towards Fast-Responsive Fingerprinting. RSC Adv. 2017, 7,
33258–33262.
(10) Lawrence, J. R.; Ying, Y.; Jiang, P.; Foulger, S. H. Dynamic Tuning of Organic Lasers with
Colloidal Crystals. Adv. Mater. 2006, 18, 300–303.
(11) Ye, S.; Fu, Q.; Ge, J. Invisible Photonic Prints Shown by Deformation. Adv. Funct. Mater.
2014, 24, 6430–6438.
(12) Ding, T.; Cao, G.; Schäfer, C. G.; Zhao, Q.; Gallei, M.; Smoukov, S. K.; Baumberg, J. J.
Revealing Invisible Photonic Inscriptions: Images from Strain. ACS Appl. Mater. Interfaces
2015, 7, 13497–13502.
Page 17 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
18
(13) Fudouzi, H.; Sawada, T. Tuning Stop Band of Soft Opal Film by Deformation for Strain
Sensing Applications. Proc. SPIE 2006, 6369, 63690D–1.
(14) Sun, X.; Zhang, J.; Lu, X.; Fang, X.; Peng, H. Mechanochromic Photonic-Crystal Fibers
Based on Continuous Sheets of Aligned Carbon Nanotubes. Angew. Chem. Int. Ed. 2015, 54,
3630–3634.
(15) Zhang, J.; He, S.; Guan, G.; Lu, X.; Sun, X.; Peng, H. The Continuous Fabrication of
Mechanochromic Fibers. J. Mater. Chem. C 2016, 4, 2127–2133.
(16) Fudouzi, H.; Sawada, T. Photonic Rubber Sheets with Tunable Color by Elastic
Deformation. Langmuir 2006, 22, 1365–1368.
(17) Ito, T.; Katsura, C.; Sugimoto, H.; Nakanishi, E.; Inomata, K. Strain-Responsive Structural
Colored Elastomers by Fixing Colloidal Crystal Assembly. Langmuir 2013, 29, 13951–13957.
(18) Arsenault, A. C.; Clark, T. J.; Freymann, G. V.; Cademartiri, L.; Sapienza, R.; Bertolotti, J.;
Verkis, E.; Wong, S.; Kitaev, V.; Manners, I.; Wang, R. Z.; John, S.; Wiersma, D.; Ozin, G. A.
From Colour Fingerprinting to The Control of Photoluminescence in Elastic Photonic Crystals.
Nat. Mater. 2006, 5, 179–184.
(19) Viel, B.; Ruhl, T.; Hellmann, G. P. Reversible Deformation of Opal Elastomers. Chem.
Mater. 2007, 19, 5673–5679.
(20) Schäfer, C. G.; Gallei, M.; Zahn, J. T.; Engelhardt, J.; Hellmann, G. P.; Rehahn, M.
Reversible Light-, Thermo-, and Mechano-Responsive Elastomeric Polymer Opal Films. Chem.
Mater. 2013, 25, 2309–2318.
(21) Schäfer, C. G.; Viel, B.; Hellmann, G. P.; Rehahn, M.; Gallei, M. Thermo-cross-Linked
Elastomeric Opal Films. ACS Appl. Mater. Interfaces 2013, 5, 10623–10632.
Page 18 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
19
(22) Scheid, D.; Lederle, C.; Vowinkel, S.; Schäfer, C. G.; Stühn, B.; Gallei, M. Redox-and
Mechano-Chromic Response of Metallopolymer-Based Elastomeric Colloidal Crystal Films. J.
Mater. Chem. C 2014, 2, 2583–2590.
(23) Zhao, Q.; Finlayson, C. E.; Snoswell, D. R. E.; Haines, A.; Schäfer, C. G.; Spahn, P.;
Hellmann, G. P.; Petukhov, A. V.; Herrmann, L.; Burdet, P. et al. Large-Scale Ordering of
Nanoparticles Using Viscoelastic Shear Processing. Nat. Commun. 2016, 7, 11661.
(24) Finlayson, C. E.; Goddard, C.; Papachristodoulou, E.; Snoswell, D. R. E.; Kontogeorgos,
A.; Spahn, P.; Hellmann, G. P.; Hess, O.; Baumberg, J. J. Ordering in Stretch-Tunable Polymeric
Opal Fibers. Opt. Express 2011, 19, 3144–3154.
(25) Asher, S. A.; Holtz, J.; Liu, L.; Wu, Z. Self-Assembly Motif for Creating Submicron
Periodic Materials. Polymerized Crystalline Colloidal Arrays. J. Am. Chem. Soc. 1994, 116,
4997–4998.
(26) Foulger, S. H.; Jiang, P.; Lattam, A. C.; Smith, D. W.; Ballato, J. Mechanochromic
Response of Poly (Ethylene Glycol) Methacrylate Hydrogel Encapsulated Crystalline Colloidal
Arrays. Langmuir 2001, 17, 6023–6026.
(27) Iwayama, Y.; Yamanaka, J.; Takiguchi, Y.; Takasaka, M.; Ito, K.; Shinohara, T.; Sawada,
T.; Yonese, M.; Optically Tunable Gelled Photonic Crystal Covering Almost the Entire Visible
Light Wavelength Region. Langmuir 2003, 19, 977–980.
(28) Raghavan, S. R.; Walls, H.; Khan, S. A. Rheology of Silica Dispersions in Organic Liquids:
New Evidence for Solvation Forces Dictated by Hydrogen Bonding. Langmuir 2000, 16, 7920–
7930.
Page 19 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
20
(29) Krisanangkura, P.; Packard, A. M.; Burgher, J.; Blum, F. D. Bound Fractions of
Methacrylate Polymers Adsorbed on Silica Using FTIR. J. Polym. Sci. B. Polym. Phys. 2010, 48,
1911–1918.
(30) Kim, S.-H.; Park, H. S.; Choi, J. H.; Shim, J. W.; Yang, S.-M. Integration of Colloidal
Photonic Crystals toward Miniaturized Spectrometers. Adv. Mater. 2010, 22, 946-950.
(31) Yang, D.; Ye, S.; Ge, J. From Metastable Colloidal Crystalline Arrays to Fast Responsive
Mechanochromic Photonic Gels: An Organic Gel for Deformation-Based Display Panels. Adv.
Funct. Mater. 2014, 24, 3197–3205.
(32) Chris E. Finlayson, Haines, A. I.; Snoswell, D. R. E.; Kontogeorgos, A.; Vignolini, S.;
Baumberg, J. J.; Spahn, P.; Hellmann, P. Interplay of Index Contrast with Periodicity in Polymer
Photonic Crystals. Appl. Phys. Lett. 2011, 99, 261913.
(33) Yang, D.; Ye, S.; Ge, J. Old Relief Printing Applied to The Current Preparation of
Multicolor and High Resolution Colloidal Photonic Crystal Patterns. Chem. Commun. 2015, 51,
16972–16975.
(34) Yu, B.; Kang, S.-Y.; Akthakul, A.; Ramadurai, N.; Pilkenton, M.; Patel, A.; Nashat, A.;
Anderson, D. G.; Sakamoto, F. H.; Gilchrest, B. A.; Anderson, R. R.; Langer, R. An Elastic
Second Skin. Nat. Mater. 2016, 15, 911–918.
(35) Unger, M. A.; Chou, H. P.; Thorsen, T.; Scherer, A.; Quake, S. R. Monolithic
Microfabricated Valves and Pumps by Multilayer Soft Lithography. Science 2000, 288, 113–
116.
(36) Thorsen, T.; Maerkl, S. J.; Quake, S. R. Microfluidic Large-Scale Integration. Science 2002,
98, 580–584.
Page 20 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
21
(37) Fuhrmann, D. A.; Thon, S. M.; Kim, H.; Bouwmeester, D.; Petroff, P. M..; Wixforth, A.;
Krenner, H. J. Dynamic Modulation of Photonic Crystal Nanocavities Using Gigahertz Acoustic
Phonons. Nat. Photonics 2011, 5, 605–609.
(38) Tumbleston, J. R.; Shirvanyants, D.; Ermoshkin, N.; Janusziewicz, R.; Johnson, A. R.;
Kelly, D.; Chen, K.; Pinschmidt, R.; Rolland, J. P.; Ermoshkin, A.; Samulski, E. T.; DeSimone,
J. M. Continuous Liquid Interface Production of 3D Objects. Science 2015, 347, 1349–1352.
(39) Yokoi, T.; Sakamoto, Y.; Terasaki, O.; Kubota, Y.; Okubo, T.; Tatsumi, T. Periodic
Arrangement Of Silica Nanospheres Assisted by Amino Acids. J. Am. Chem. Soc. 2006, 128,
13664–13665.
(40) Hartlen, K. D.; Athanasopoulos, A. P.; Kitaev, V. Facile Preparation of Highly
Monodisperse Small Silica Spheres (15 to > 200 nm) Suitable for Colloidal Templating and
Formation of Ordered Arrays. Langmuir 2008, 24, 1714–1720.
(41) Yang, D.; Ye, S.; Ge, J. Solvent Wrapped Metastable Colloidal Crystals: Highly Mutable
Colloidal Assemblies Sensitive to Weak External Disturbance. J. Am. Chem. Soc. 2013, 135,
18370−18376.
Page 21 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
22
Figure 1. Mechanochromic films containing a nonclose-packed colloidal array. (a)
Chameleon relaxed showing green color (left) and excited showing yellow color (right).
Transmission electron microscope (TEM) images show the change of periodicity in a regular
array of guanine nanocrystals. Reproduced from Teyssier et al. Nature Communications3 by
courtesy of Prof. Michel Milinkovitch. (b) Schematic of mechanochromic photonic films
composed of a nonclose-packed array of silica particles embedded in an elastomeric matrix. (c,
d) Photographs of a photonic film taken at two different conditions: (c) Structurally-colored
when the reflection condition is satisfied and (d) translucent when the condition is unsatisfied.
(e) Scanning electron microscope (SEM) image showing the film cross-section containing a
nonclose-packed array of silica particles. Inset is a fast Fourier transform (FFT) image. (f, g)
Series of photographs of a photonic film with three different strains taken in reflection (f) and
transmission (g).
Page 22 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
23
Figure 2. Threshold volume fraction for crystallization. (a) Cartoons showing the
arrangement of particles in a liquid resin with three different volume fractions: Particles are
randomly distributed at volume fraction below the threshold (ϕ < ϕth), whereas they form
nonclose-packed crystal at volume fraction above the threshold (ϕ > ϕth). (b, c) A set of optical
microscope (OM) images (b) and reflectance spectra (c) of photonic films prepared from
dispersions of silica particles with d = 150 nm at different values of ϕ = 0.1, 0.2, 0.26, 0.33, and
0.4. (d) Volume fraction dependence of a reflectance peak position, λmax (black squares) and a
full width at half maximum, ∆λ, normalized by λmax (red triangles). The black line indicates
Bragg’s equation for staked (111) planes of nonclose-packed fcc structure.
Page 23 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
24
Figure 3. Reversible color change in full visible by extension. (a) A series of OM images and
CIE plot showing a blue-shift of structural color along with extensional strain, ε. The photonic
film is prepared with silica particles with d = 195 nm at ϕ = 0.33. (b) Reflectance spectra of the
film for various strains. (c) Reversible change of λmax during cycles of extension to ε = 40% and
relaxation to ε = 0%. (d) λmax (black squares) and Poisson ratio, ν (red circles) as functions of
extensional strain. Insets correspond to model structures with ε = 0, 21.0, 41.2, and 60.8%. (e)
Extensional-strain dependence of reflectivity at λmax (black squares) and refractive index
contrast, ∆n, between two neighboring slices with equal thickness (red circles) estimated from
model structures: one slice contains (111) plane in the middle and the other contains intermediate
plane. Insets show the pairs of two slices with ε = 0, 21.0, 41.2, and 60.8%.
Page 24 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960
25
Figure 4. Compression of photonic films with stamps. (a) Schematic illustration showing
compression of a photonic film with a patterned stamp. The staked (111) planes are contracted
on relief regions and expanded on engraved regions. (b) Photographs and OM image of a
photonic film before (left panels) and after (right panels) compression with a stamp that contains
small ‘K’s to form a large ‘K’. (c) Reflectance spectra of uncompressed (orange line) and
compressed photonic film (green line). Reflectance spectra locally measured from small ‘K’
(blue line) and background (red line) are included. (d, e) Sets of OM images of a stamp and a
compressed photonic film, where the stamps have parallel lines (d) and a square array of dots (e).
Page 25 of 26
ACS Paragon Plus Environment
ACS Nano
123456789101112131415161718192021222324252627282930313233343536373839404142434445464748495051525354555657585960