FILLER METAL SELECTOR GUIDE STRENGTH REQUIREMENTS ASTM TENSILE YIELD NO. DESCRIPTION GRADES (ksi) (ksi) 6 A204 Boiler & Pressure Vessel (.5% Mo) A 65-85 37 min Plates > 1-1/2” Normalized B 70-90 40 min C 75-95 43 min A209 C-Mo Boiler Tubes (1/2”- 5” Dia.) T1, T1a, & T1b 55, 53, & 60 min 30, 28, & 32 min A210 Carbon Steel Boiler Tubes (1/2”- 5” Dia.) A-1 60 min 37 min C 70 min 40 min A211 Spiral Welded Pipe (Discontinued in 1993) See A570 A213 Boiler Tubes (1/8” - 5” Dia.) T2 (.75% Cr, .5% Mo) 60 min 30 min T11 (1.25% Cr, .5% Mo) 60 min 30 min T12 (1% Cr, .5% Mo) 60 min 30 min T17 (1% Cr) 60 min 30 min T21 (3% Cr, 1% Mo) 60 min 30 min T22 (2.25% Cr, 1% Mo) 60 min 30 min A214 Heat-Exchanger Tubes (3” Max. Dia.) A216 Carbon Steel Castings - High Temp. WCA 60-85 30 min WCB 70-95 36 min WCC 70-95 40 min A217 Steel Castings, High Temp. WC1 (.5% Mo) 65-90 35 min WC4(.75%Cr,.5%Mo, .9%Ni) 70-95 40 min WC5(.75%Cr,1%Mo, .8% Ni) 70-95 40 min WC6 (1.25% Cr, .5% Mo) 70-95 40 min WC9 (2.5% Cr, 1% Mo) 70-95 40 min WC11 (1.25% Cr, .5% Mo) 80-105 50 min A225 Pressure Vessel, Mn-V- .5% Ni C (> 2” Normalized) 105-135 70 min D (Normalized) 80-105 60 min A226 High-Pressure Service (5” Max. Dia.) 47 min 26 min (Discontinued in 1997) A234 Wrought Welding Fittings for Moderate & Elevated WPB 60-85 35 min Temperatures WPC 70-95 40 min WP1 (.5% Mo) 55-80 30 min WP11, Class 1(1.25% Cr,.5% Mo) 60-85 30 min WP11, Class 2(1.25%Cr,.5%Mo) 70-95 40 min WP11, Class 3 (1.25%Cr,.5%Mo) 75-100 45 min WP12, Class 1 (1%Cr,.5% Mo) 60-85 30 min WP12, Class 2 (1%Cr,.5% Mo) 70-95 40 min WP22, Class 1(2.25% Cr,1% Mo) 60-85 30 min WP22, Class 3 (2.25% Cr,1% Mo) 75-100 45 min A242 High Strength, Low Alloy Structural-Cu Shapes-Group 1 & 2, (Plates 3/4” & less) 70 min 50 min (.2% Cu min.) Groups listed are for Structural Shapes-Group 3, (Plates Over 3/4 to 1-1/2”) 67 min 46 min Shapes. For Plates & Bars, Tensile requirements Shapes-Group 4 & 5, (Plates Over 1-1/2 to 4’) 63 min 42 min are based on thickness. A250 C-Mo Tubes (1/2” - 5” Dia.) T1 (.5% Mo) 55 min 30 min T1a (.5% Mo) 60 min 32 min T1b (.5% Mo) 53 min 28 min T2 (.75% Cr, .5% Mo) 60 min 30 min T11 (1.25% Cr, .5% Mo) 60 min 30 min T12 (1% Cr, .5% Mo) 60 min 30 min T22 (2.25% Cr, 1% Mo) 60 min 30 min A252 Steel Pipe Piles 1 50 min 30 min 2 60 min 35 min 3 66 min 45 min A266 Pressure Vessel Forgings 1 60-85 30 min 2 & 4 70-95 36 min 3 75-100 37.5 min

description

Weld Consumables

Transcript of C150ext

Page 1: C150ext

FILLER METAL SELECTOR GUIDE

STRENGTH REQUIREMENTS

ASTM TENSILE YIELD

NO. DESCRIPTION GRADES (ksi) (ksi)

6

A204 Boiler & Pressure Vessel (.5% Mo) A 65-85 37 min

Plates > 1-1/2” Normalized B 70-90 40 min

C 75-95 43 min

A209 C-Mo Boiler Tubes (1/2”- 5” Dia.) T1, T1a, & T1b 55, 53, & 60 min 30, 28, & 32 min

A210 Carbon Steel Boiler Tubes (1/2”- 5” Dia.) A-1 60 min 37 min

C 70 min 40 min

A211 Spiral Welded Pipe (Discontinued in 1993) See A570

A213 Boiler Tubes (1/8” - 5” Dia.) T2 (.75% Cr, .5% Mo) 60 min 30 min

T11 (1.25% Cr, .5% Mo) 60 min 30 min

T12 (1% Cr, .5% Mo) 60 min 30 min

T17 (1% Cr) 60 min 30 min

T21 (3% Cr, 1% Mo) 60 min 30 min

T22 (2.25% Cr, 1% Mo) 60 min 30 min

A214 Heat-Exchanger Tubes (3” Max. Dia.)

A216 Carbon Steel Castings - High Temp. WCA 60-85 30 min

WCB 70-95 36 min

WCC 70-95 40 min

A217 Steel Castings, High Temp. WC1 (.5% Mo) 65-90 35 min

WC4(.75%Cr,.5%Mo, .9%Ni) 70-95 40 min

WC5(.75%Cr,1%Mo, .8% Ni) 70-95 40 min

WC6 (1.25% Cr, .5% Mo) 70-95 40 min

WC9 (2.5% Cr, 1% Mo) 70-95 40 min

WC11 (1.25% Cr, .5% Mo) 80-105 50 min

A225 Pressure Vessel, Mn-V- .5% Ni C (> 2” Normalized) 105-135 70 min

D (Normalized) 80-105 60 min

A226 High-Pressure Service (5” Max. Dia.) 47 min 26 min

(Discontinued in 1997)

A234 Wrought Welding Fittings for Moderate & Elevated WPB 60-85 35 min

Temperatures

WPC 70-95 40 min

WP1 (.5% Mo) 55-80 30 min

WP11, Class 1(1.25% Cr,.5% Mo) 60-85 30 min

WP11, Class 2(1.25%Cr,.5%Mo) 70-95 40 min

WP11, Class 3 (1.25%Cr,.5%Mo) 75-100 45 min

WP12, Class 1 (1%Cr,.5% Mo) 60-85 30 min

WP12, Class 2 (1%Cr,.5% Mo) 70-95 40 min

WP22, Class 1(2.25% Cr,1% Mo) 60-85 30 min

WP22, Class 3 (2.25% Cr,1% Mo) 75-100 45 min

A242 High Strength, Low Alloy Structural-Cu Shapes-Group 1 & 2, (Plates 3/4” & less) 70 min 50 min

(.2% Cu min.) Groups listed are for Structural Shapes-Group 3, (Plates Over 3/4 to 1-1/2”) 67 min 46 min

Shapes. For Plates & Bars, Tensile requirements Shapes-Group 4 & 5, (Plates Over 1-1/2 to 4’) 63 min 42 min

are based on thickness.

A250 C-Mo Tubes (1/2” - 5” Dia.) T1 (.5% Mo) 55 min 30 min

T1a (.5% Mo) 60 min 32 min

T1b (.5% Mo) 53 min 28 min

T2 (.75% Cr, .5% Mo) 60 min 30 min

T11 (1.25% Cr, .5% Mo) 60 min 30 min

T12 (1% Cr, .5% Mo) 60 min 30 min

T22 (2.25% Cr, 1% Mo) 60 min 30 min

A252 Steel Pipe Piles 1 50 min 30 min

2 60 min 35 min

3 66 min 45 min

A266 Pressure Vessel Forgings 1 60-85 30 min

2 & 4 70-95 36 min

3 75-100 37.5 min

Page 2: C150ext

FILLER METAL SELECTOR GUIDE

SMAW SAW GMAW** FCAW-S FCAW-G**

7

(34) LA90

(34) LA90

(34) LA90

SA-85, LH-78 MR, Excalibur 7018-A1 LA90, (16) (21) (23)

(2), (4) (16) (21) (23)

SA-85, LH-78 MR, Excalibur 7018-A1 (16) (21) (23)

LH-90 MR, Jet-LH 8018-B2 MR LA90

LH-90 MR, Jet-LH 8018-B2 MR

LH-90 MR, Jet-LH 8018-B2 MR

LH-90 MR, Jet-LH 8018-B2 MR

Jet-LH 9018-B3 MR

Excalibur 7018, 7018-1, (16)

LH-78 MR

(1) (10), (11) LA75, LA90 (18) (23)

(1) (10), (11) LA75, LA90 (18) (23)

(1) (10), (11) LA75, LA90 (18) (23)

LH-90 MR, Jet-LH 8018-B2 MR (10), (11) LA90

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

Jet-LH 9018-B3 MR MIL800-H, 880M, 882/LA93

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

LH-110M MR (12) MC1100

LH-8018-C3 MR, Excalibur 8018-C3 MR 860, 960/LA75 LA75 (24)

Excalibur 7018, 7018-1, (16) (21) (23)

LH-78 MR, (4)

Excalibur 7018, (10), (11) (16) (18) (23)

LH-78 MR, (4)

Excalibur 7018, 7018-1, (10), (11) (16) (18) (23)

LH-78 MR, (4)

SA-85, Excalibur 7018-A1 (34) LA90

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

LH-90 MR, Jet-LH 8018-B2 MR MIL800-H, 880M, 882/LA92, (26)

Jet-LH 9018-B3 MR MIL800-H, 880M, 882/LA92, (26)

Jet-LH 9018-B3 MR MIL800-H, 880M, 882/LA93

(1), (6) (10), (11), (15) (29) NR-203Ni1% (25)

(1), (6) (10), (11), (15) (29) NR-203Ni1% (25)

(1), (6) (10), (11), (15) (29) NR-203Ni1% (25)

SA-85, Excalibur 7018-A1 LA90 (23)

SA-85, Excalibur 7018-A1 LA90 (23)

SA-85, Excalibur 7018-A1 LA90 (23)

LH-90 MR, Jet-LH 8018-B2 MR

LH-90 MR, Jet-LH 8018-B2 MR

LH-90 MR, Jet-LH 8018-B2 MR

Jet-LH 9018-B3 MR

Excalibur 7018, 7018-1, (10), (11), (32) (16) (17) (23)

LH-78 MR, (4)

Excalibur 7018, 7018-1, (10), (11), (32) (16) (17) (23)

LH-78 MR, (4)

Excalibur 7018, 7018-1, (10), (11), (32) (16) (17) (23)

LH-78 MR, (4)

(1) (10). (11) (16) (18) (23)

(1) (10), (11) (16) (18) (23)

LH-8018-C3 MR, Excalibur 8018-C3 MR (10), (11) (16) (18) (24)