Mechanistic Understanding of Crack Initiation in Carburised 316H Stainless Steel Subjected to Cyclic Loading Andrew James PhD Researcher 2015-2019 Solid Mechanics Research Group
-
Upload
solid-mechanics-group-university-of-bristol -
Category
Engineering
-
view
14 -
download
3
Transcript of Andrew James summary slides 2017
![Page 1: Andrew James summary slides 2017](https://reader035.fdocuments.us/reader035/viewer/2022062522/58e580101a28abbf5d8b5849/html5/thumbnails/1.jpg)
Mechanistic Understanding of Crack Initiation in Carburised 316H Stainless SteelSubjected to Cyclic Loading
Andrew JamesPhD Researcher 2015-2019
Solid Mechanics Research Group
![Page 2: Andrew James summary slides 2017](https://reader035.fdocuments.us/reader035/viewer/2022062522/58e580101a28abbf5d8b5849/html5/thumbnails/2.jpg)
2D X-ray diffraction onsmall scale tensile samples
Phase-specific strain evolution
hkl-specific strain evolution
Above: Strain evolution measured in oxide.
Below: Bulk hkl information measured to inform mechanistic models
Above: Sample tested under monotonic loading Below: Loading rig used in experiment
![Page 3: Andrew James summary slides 2017](https://reader035.fdocuments.us/reader035/viewer/2022062522/58e580101a28abbf5d8b5849/html5/thumbnails/3.jpg)
Identification and classificationof small cracks Left: Magnified view of
ductile failure region
Right: One of the main surface cracks showing brittle failure in oxideAbove: Surface cracking
observed post test under SEM