Principles and Applications of X-Ray Microanalysis
Introduction:
The quantitative characterization of X-rays emanating from the specimen forms the basisof X-ray microanalysis. The use of fine and intense electron probe facilitates analysis
with high spatial resolution (at the nm level). Consequently it is possible to study
localized variation in chemical composition. The mechanism of X-ray and Augerelectron production, as already explained, consist of the excitation, relaxation and
emission stages and is schematically illustrated in Fig. 6.1.
Fig. 6.1: Mechanism of X-ray and Auger electron production
The intensity of the X-rays produced varies considerably. The nomenclature for principal
X-ray lines and the values for relative intensities of these lines (K, K, L etc.) areshown in Fig.6.2 and Table 6.1 respectively.
Fig. 6.2: Nomenclature for principal X-ray lines
The emission process
Excitation
Relaxation
Emission
L M
N shell
L shellM shell
K shellK
K
K L
LM
91
-
8/11/2019 4.VI Chapter.pdf
2/18
Table 6.1: Relative intensities of various X-ray lines
K1= 100
K2= 50
K1= 15.30
K2= 1-10K3= 6-15
L1= 100
L2= 50
L1= 50
L2= 20L3= 1-6
L4= 3-5L1 = 1-10
L3 = 0.5-2
M1-2 = 100M= 60
K X-rays are normally used for the study of elements with Z ~ 30, say upto Cu while for
the heavier elements L and M rays are used. L-radiation for the elements with Z
-
8/11/2019 4.VI Chapter.pdf
3/18
Fig. 6.4: Electron Excitation of Continuum (Background) Intensity
X-Ray Detectors:
X-rays are characterized by the use of Energy dispersive (EDS) and wave lengthdispersive (WDS) systems. The principle of the energy dispersive detector is illustrated in
Fig. 6.5. The detector uses a lithium-drifted silicon crystal, Si(Li) with surface area in the
range 5 to 200 mm2
and kept at liquid nitrogen temperature and under high vacuum. X-
rays enter through a thin beryllium (0.7m thick) window and create electron-hole pars,the number depending on the energy of the X-rays. The x-ray spectrometer converts the
x-ray photon into an electrical pulse with specific characteristics of amplitude and width.
A multi-channel analyzer measures the pulse and increments a corresponding "energy
slot" in a monitor display. The location of the slot is proportional to the energy of the x-ray photon entering the detector. The display is a histogram of the x-ray energy received
by the detector, with individual "peaks," the heights of which are proportional to the
amount of a particular element in the specimen being analyzed.
There is a trend towards a newer EDS detector, called the Silicon Drift Detector (SDD).The SDD consists of a high-resistivity silicon chip where electrons are driven to a small
collecting anode. The advantage lies in the extremely low capacitance of this anode,thereby utilizing shorter processing times and allowing very high throughput. Benefits of
the SDD include 1) High count rates and processing 2) Better resolution than traditional
SiLi detectors at high count rates 3) Lower dead time (time spent on processing x-ray
event) 4) Faster analytical capabilities and more precise X-ray maps or particle datacollected in seconds and 5) Ability to be stored and operate at relatively high
temperatures, eliminating the need for liquid nitrogen cooling. Since the capacitance of
the SDD chip is independent of the active area of the detector, much larger SDD chips
93
-
8/11/2019 4.VI Chapter.pdf
4/18
can be utilized (40mm sq. or more). This allows for even higher count rate collection.
Further benefits of large area chips include 1) Minimizing SEM beam current allowingfor optimization of imaging under analytical conditions 2) Reduced sample damage and
3) Smaller beam interaction and improved spatial resolution for high speed maps.
In recent years a different type of EDS detector, based upon a microcalorimeter, hasbecome commercially available. This new model allegedly has the simultaneousdetection capabilities of EDS as well as the high spectral resolution of WDS. The EDS
microcalorimeter relies highly on two components: an absorber, and a thermistor. The
former absorbs X-rays emitted from the sample and converts this energy into heat; thelatter measures the subsequent change in temperature due to the influx of heat (in
essence, a thermometer). The EDS microcalorimeter has suffered from a number of
drawbacks; including low count rates, poor collection efficiencies and small detectorareas. The count rate is hampered by its reliance on the tiime constant of the calorimeters
electrical circuit. The collection efficiency is a function of the absorber material and
remains to be optimized. The detector area must be small in order to keep the heat
capacity as small as possible and maximize thermal sensitivity (resolution). Innovativeengineering solutions are necessary for further improvement of spectroscopic
microanalysis.
Fig. 6.5: Principle of the Energy Dispersive Detector
The following are the characteristics of the energy dispersive spectrometer:
Simple, nearly operator independent Large solid angle (0.05-0.3 sr)
Virtually specimen position independent
No moving parts
Parallel detection
Quantification by standardless or standards methods
Poor energy resolution (~130 eV). Superconducting systems (~20 eV)
Poor peak/background ratio (100:1)
94
-
8/11/2019 4.VI Chapter.pdf
5/18
Detection efficiency depends upon x-ray energy
The principle of the wavelength detector is illustrated in Fig. 6.6. It operates using
Fig. 6.6: Principle of Wave Length Dispersion Spectrometer
diffraction principles (Braggs law). X-rays emitted by the sample being analyzed arecollimated by parallel copper blades (called collimator or Soller slits), and irradiate a
known single crystal at a precise angle. The single crystal diffracts the photons (Braggs
law) which are collected by a detector, usually a scintillation counter or a proprtional
counter. The single crystal, the specimen, and the detector are mounted precisely on a
goniometer with the distance from the source of x-rays (the specimen) and the crystalequal to the distance from the crystal to the detector. It is usually operated under vacuum
to reduce the absorption of soft radiation (low-energy photons) by the air and thusincrease the sensitivity for the detection and quantitation of light elements (between
boron and oxygen). Modern systems contain a small number of crystals of known but
differing properties, with automated changing of the crystal depending on the energybeing analysed, enabling elements from the entire periodic table (excepting the very light
elements) to be analyzed.
Details of analysing crsytals used in WDs are given in Table 6.2. It is posible to analysefor elements in the range B to U using a variety of crytals with different interplanar
spacings. The following are the characteristics of the wavelength system:
Excellent energy resolution (~5 eV)
High peak/background ratios (1000:1)
Good detection efficiency for all x-rays
High counting rates
Good light elements capabilities
95
-
8/11/2019 4.VI Chapter.pdf
6/18
Complex mechanical devices, operator intensive
Specimen height dependent focus
Moving components in the AEM
Limited solid angle (
-
8/11/2019 4.VI Chapter.pdf
7/18
Probe current 10-11
-10-9
A 10-9
10-6
A
Running costs ~ 500 l liquid nitrogen peryear for cooling the crystal
Argon/methane gas for gasflow proportional counter
Typical output, cps 5000-10000 50,000
Time to collect full spectrum 1 min 30 min.
Artefacts Escape and sum peaks Higher order lines
Field of usefulness Good for quick, readily
interpreted qualitative
analysis
Very good for precise
quantitative analysis and line
scans
The advantages of the EDS are simultaneous collection of entire spectrum from the
sample and hence less time for analysis, ease of fitting to the main instrument. The
disadvantages are the limited resolution and hence overlap of some peaks, e.g. Fe, Cr, Ni
Kand Kand difficulty of detection of light elements due to absorption in the berylliumwindow and outer layers of the detecting crystal. It is possible to analyse the light
elements by replacing the beryllium window with an ultrathin plastic window or an openhole (windowless detector). The nominal FWHM values in modern Si(Li) detectors is ~80 to eV for O K(0.52keV) and 140-160 eV for Mn (~140 to 160 eV). The WDS has
excellent energy resolution and capability to analyse light elements. These facts are
illustrated in Figs. 6.7 by a comparison of the WDS and EDS spectra on a glass sample.
Fig. 6.7: Comparison of EDS and WDS spectra of a glass sample.
The minimum detection limit for the two systems is specified in terms of minimum mass
fraction (MMF) with typical values of 0.001 for EDS and 0.0001 for WDS.
97
-
8/11/2019 4.VI Chapter.pdf
8/18
The two systems can be mounted on a number of electron optical systems to provide
information on chemical composition; the details including typical applications are givenin Table 6.4.
Table 6.4: Instrumentation for X-ray analysis and typical applications
Gun characteristics
The intensity of X-rays depends on the electron energy and probe current while the
spatial resolution for analysis is influenced by the probe size. The relationship between
probe current and probe size is shown in Fig. 6.8. At small probe size values (1 nm) the
FEG is superior to the other two gun sources. For all nanoanalytical work, the FEG ispreferred; note that at large probe size values (1 m) the W filament gun is good enough.It would be useful at this stage to review the characteristics of different types of guns
(although this aspect has already been discussed in II Chapter). The information is
tabulated for various gun sources (Table 6.5).
Quantitative Analysis:
Quantitative analysis involves the measurement of characteristic X-ray intensities fromthe specimen (I) and a standard (Is) (which may be a pure element or a compound)
C = CsI/Is
.where C and Cs are the concentrations of the element in the sample and the standard
respectively
The equation does not take into account a number of phenomena occurring in the sample
before and after the excitation of the X-rays. For this purpose, it is necessary to apply the
98
-
8/11/2019 4.VI Chapter.pdf
9/18
-
8/11/2019 4.VI Chapter.pdf
10/18
ray photon has energy exceeding the critical excitation energy. Backscattered electrons
are ineffective in exciting X-rays and therefore contribute to the atomic number effect
(Note that increases with Z). Methods of applying these corrections are well
documented in the literature.
The measured intensity of X-rays of a particular species (say K) from the specimendepends on a number of factors, , the ionization cross section, , the radiative partition
function, , the fluorescent yield and a number of constants. The details are given in Fig.
6.19.
Fig. 6.9: Expression for X-ray intensity as a function of properties of the sample
Absorption of X-rays depends on the well known absorption equation,
It= Ioexp(-/)t
where Itand Io are the transmitted and original intensities, (-/) is the mass absorptioncoefficient, is the density and t the thickness. The absorption characteristics of X-rays
in some samples are schematically illustrated in Fig. 6. 10. It is clear that soft X-rays (N,O in the figure) are heavily absorbed even in samples with thickness of ~ 100 nm; the
effect will be more intense when we consider bulk samples where X-rays are generated
from a region of a few m size.
100
-
8/11/2019 4.VI Chapter.pdf
11/18
Fig. 6.10: Absorption of X-rays in various samples
Broadening of the electron probe even can in the thin samples used in transmission
electron microscopy can contribute to errors in analysis This is illustrated in Fig.6.11; the
results of theoretical calculations based on single elastic scattering shown in Table 6.6that beam broadening depends on thickness and atomic number.
Fig. 6.11: Electron beam spread in bulk and thin specimens
101
-
8/11/2019 4.VI Chapter.pdf
12/18
Table 6.6: Theoretical calculation of beam broadening
Complications in analysis:
omplications in analysis arise from a number of effects:
1. X-ray emission characteristic of support grids, goniometer stage, pole pieces,
2. s from the specimen other the one defined by the incident
3. intensities associated with thin specimens
This is illustrated in Fig. 6.12. The extent to which stray sources contribute to the X-ray
Fig. 6.12: Complications in analysis
C
anticontamination device and any other material in the vicinity of the specimen
SYSTEM PEAKS
Peaks due to X-rayelectron beam
Abnormal peak
4. Extra Si peak from detector, sum and escape peaks
spectrum can be evaluated by carrying out a hole count, where the electron probe is
focused on a hole in the sample and X-ray spectrum collected (fig. 6.13).
102
-
8/11/2019 4.VI Chapter.pdf
13/18
Fig. 6.13: Spectral artifacts in AEM: uncollimated radiation : The hole count
Applications:
Fig. 6.13: Illustration of hole count the Ni K peak in the hole is significant
pplications
he ability to carry out high spatial resolution chemical analysis opens up enormous
1. Identification of phasesnear defects such as GB (e.g. precipitate-free zones,
3.
ome examples are given below:
-ray spectra from fired bullets (forming part of a forensic study) are shown in Fig 6.14.
A
Tpossibilities for understanding a number of phenomenon in materials (both organic and
inorganic).
2. Concentration gradientsPFZ), dislocations, coarse precipitate particles; segregation phenomenon
Partition of alloying elements between various phases
S
X
Such studies are important in drawing conclusions about the mode of firing of the pellets.
A metallurgical example from a stainless steel sample containing sigma and chromiumnitride phases and the distribution of the elements Cr, Mo and Fe is illustrated in Figs.
6.15 and 6.16.
103
-
8/11/2019 4.VI Chapter.pdf
14/18
a Pb-Sb pellet fired from Winchester
Fig. 6.14(b): Energy dispersive spectrum from steel pellets fired from Winchester,
is well known that the formation of equilibrium precipitates on grain boundaries during
Fig. 6.14(a) Energy dispersive spectrum from
12 GA
12 GA bird BB
It
the precipitation hardening stages (during quenching of supersaturated solid solution orsubsequent ageing) produces precipitate-free zones (PFZ) near GBs which have an
adverse effect on the resistance to stress corrosion cracking. Examples of analyticalstudies in PFZ in precipitation hardenable aluminium alloys are shown in Figs. 6.17 to
6.19. The width of the PFZ can be measured in the underaged(UA), peakaged(PA) andoveraged (OA) conditions from the microstructures of a 7XXX aluminium alloy
presented in Fig. 6.17. The variation of the elements Zn and Mg in the PFZ and in the
104
-
8/11/2019 4.VI Chapter.pdf
15/18
Fig. 6.15: Composite Decomposition Skin of Sigma Phase and Cr Nitride in 654
SMO Stainless Steel: (left) STEM Image, (right) EDX Mapping Overlap withSignals of Cr (magenta) and Mo (yellow)
Fig. 6.16: Composite Decomposition Skin of Sigma Phase and Cr Nitride in 654
SMO Stainless Steel: (left) STEM Image, (right) EDX Mapping Overlap with
Signals of Fe (green) , Cr (magenta) and Mo (yellow)
surrounding regions can be measured by high resolution X-ray analysis (fig. 6.18). Notethe number of experimental points in the PFZ which ahs a width of < 0.5 m. Themicrostructural and analytical observations can be combined with nanohardness
measurements (fig. 6.19); these studies are useful in understanding the distribution of
alloying elements in various regions during heat treatment.
105
-
8/11/2019 4.VI Chapter.pdf
16/18
Fig. 6.17: PFZ in Al-Zn-Mg alloy aged at 433K in UA, PA and OA conditions
Fig. 6.18: Variation in Zn and Mg concentration across a GB in an Al-Zn-Mg alloy
aged at 433K for 259.2 ks
As the last example we shall consider the X-ray scans on bulk samples in the SEM or
EPMA. As pointed out earlier we can carry out line mapping (variation of a particular
element concentration in one dimension) or area mapping. Such studies are useful inunderstanding a number of metallurgical phenomena (e.g. homogenization of castings).
The X-ray images presented in Fig. 6.20 show how the various elements Si, Mo, Cr and
Co are distributed in the area under observation. A bright region in a given area shows
enrichment of the particular element.
106
-
8/11/2019 4.VI Chapter.pdf
17/18
Fig. 6.19 :Schematic of hardness, solute concentration and precipitate density
variation in Al-Zn-Mg with and without Ag addition
Fig. 6.20
Contamination spots
Contamination spots are formed when high energy electron (typically 200 - 300 keV)probe is focused on the surface of a freshly electropolished thin specimen used for TEM
work. The spots mainly consist of hydrocarbons which diffuse across the surface of the
specimen to the immediate vicinity of electron probe. The amount of contamination is afunction of the time spent at each location. An illustration of this effect is given in Fig.
6.21 for a stainless steel sample observed at 300 kV. The contamination spots tend to
107
-
8/11/2019 4.VI Chapter.pdf
18/18
mask some of the details and therefore need to be cleaned. This is done by reactive gas
plasma processing using argon and oxygen.
UntreatedSpecimen
After 5 minutesof argon
After 5 minutes ofadditional oxygen
Fig. 6.21: Comparison of Results on Electropolished 304 SS