4 Asme Sec Ix Wps Pqr Slide 36 to 70
Transcript of 4 Asme Sec Ix Wps Pqr Slide 36 to 70
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 1/35
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
36
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 2/35
A Weld: a localized coalescence of metals or
nonmetals roduced either b heatin the
materials to the welding temperature, with
or without the application of pressure, or
by the appl cat on o pressure alone andwith or without the use of filler material.
A Joint: A junction of members or the edge of
members which are to be ointed or havebeen joined
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 3/35
tee joint (T): a joint between two members located
approximately at right angles to each other
butt joint: a joint between two members aligned
.
approx ma e y n e same p ane.
approximately at right angles to each other
in the form of an L.
lap joint: a joint between two overlapping
members in arallel lanes.
Lap joint:
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 4/35
Butt joints:
T joints:
La oints:
Closed
corner
Open
corner
Corner joints:
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 5/35
Butt welds:
Fillet welds:
S ot/Seam welds:
Plug/Slot welds:
Edge welds:
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 6/35
Single bevel
Single J
Single U
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 7/35
Double bevel
Double J
Double U
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 8/35
A fillet welded butt joint
A compound welded butt joint
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 9/35
A butt welded T joint
A compound welded T joint
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 10/35
backing: a material placed at the root of a weld joint
for the purpose of supporting molten weldme a so as o ac a e comp e e o n
penetration. The material may or may not
. .
nonmetallic, which is used to contain or
shape molten weld metal. See also backing.
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 11/35
Groove angle
oo spac ng.
T
Backing
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
46
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 12/35
QW – 253
WELDING VARIABLES PROCEDURE SPECIFICATIONS (WPS)-
Paragraph Brief of Variables Essential
Supplementary
Essential Nonessential
.1 ∅ Groove design ×
QW-402Joints
.4 − Backing ×
.10 ∅ Root spacing ×
.11 ± Retainers ×
Legend:
+ Addition > Increase/greater than ↑ Uphill ← Forehand ∅ Change
- Deletion < Decrease/less than ↓ Downhill → Backhand
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
47
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 13/35
QW-402.1 A change in the type of groove (Vee-
groove, U-groove, single-bevel, double-bevel, etc.).QW-402.4 The deletion of the backing in single-
welded groove welds. Double-welded groove welds are
cons ere we ng w t ac ng.QW-402.10 A change in the specified root spacing.
QW-402.11 The addition or deletion of nonmetallic
retainers or nonfusing metal retainers.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
48
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 14/35
Question: If a WPS states that the GTAW process
shall be used on root and second ass of o en root ormetal backed groove joints and the SMAW process
shall be used on the remainder of the roove oint is
it necessary to state that the SMAW portion of theWPS must be erformed with backin i.e. the
GTAW process)?
ep y: o.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
49
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 15/35
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
50
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 16/35
Base metal: the metal or allo that is welded brazed or
cut.
Pass: a single progression of a welding or surfacing
operation along a joint, weld deposit, or
substrate. The result of a pass is a weld bead
or layer.
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 17/35
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
52
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 18/35
QW – 253
WELDING VARIABLES PROCEDURE SPECIFICATIONS (WPS)Shield Metal-Arc SMAW
Paragraph Brief of Variables Essential
Supplementary
Essential Nonessential
.5 ∅ Group Number
QW-403
Base
Metals
.6 T Limit impact
.7 T/t Limits > 8 in. (200 mm) ×
.8 ∅ T Qualified
.9 t Pass > ½ in. 13 mm
.11 ∅ P-No. qualified
.13 ∅ P-No. 5/9/10 ×
Le end:
+ Addition > Increase/greater than ↑ Uphill ← Forehand ∅ Change
- Deletion < Decrease/less than ↓ Downhill → Backhand
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
53
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 19/35
QW-403.11 Base metals specified in the WPS shall be
qualified by a procedure qualification test which wasmade using base metals in accordance with QW-424.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
54
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 20/35
QW-424.1 Base metals are assigned P-Number in
table QW/QB-422; metals that do not appear in tableQW/QB- 422 are considered to be unassigned metals
except as otherwise defined for base metals having the
.
identified in the WPS and on the PQR by specification,
t e and rade or b chemical anal sis and mechanical
properties. The minimum tensile strength shall be de-
fined by the organization which specified the unassignedmetal if the tensile strength of that metal is not defined by
the material specification.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
55
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 21/35
ase e a s se or
Procedure Qualification CouponBase Metals Qualified
One metal from a P-Number to any metal from the
same P- Number
Any metals assigned that P-Number
One metal from a P-Number to any metal from any
other P- Number
Any metal assigned the first P- Number to any metal assigned the second P-
Number
One metal from P-No. 3 to any metal from P-No. 3 Any P- No.3 metal to any metal from P- or P- No.3 or 1
ne meta rom - o. to any meta rom - o. ny - o. meta to any meta rom - os. , , or
One metal from P-No. 5A to any metal from P-No. 5A Any P-No. 5A metal to any inew from P-Nos. 5A, 4, 3, or 1
One metal from P-No. 5A to a metal from P-No. 4, or P-
No. 3, or P-No. 1
Any P-No. 5A metal to any metal assigned to P-No. 4, 3, or 1
One metal from P-No. 4 to a metal from P-No. 3 or P- No. 1 Any P- No. 4 metal to any metal assigned to P-No. 3 or 1
Any unassigned metal to the same unassigned metal The unassigned metal to itself
Any unassigned metal to any P- Number metal The unassigned metal to any metal assigned to the same P- Number as thequalified metal
Any unassigned metal to any other unassigned metal The first unassigned metal to the second unassigned metal
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
56
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 22/35
QW/QB-422 FERROUS P-NUMBERS AND S-NUMBERS
Grouping of Base Metals for Qualification
Spec.No.
Type or Grade UNS No.
MinimumSpecified
Tensile, ksiP-
No.Group
No.S-
No.Group
No.P-
No.S-
No.Nominal
CompositionProduct
Form
SA-36 … K02600 58 1 1 … … 101 … C-Mn-Si Plate, bar, & shape
SA-53 Type S, GR. B K03005 60 1 1 … … 101 … C-Mn Smls pipe
SA-105 … K03504 70 1 2 … … 101 … C-Si Flanges & Fitting
SA-106 B K03006 60 1 1 … … 101 … C-Si Smls pipe
SA-516 70 K02700 70 1 2 … … 101 … C-Mn.Si Plate
SA-240 T e 304 S30400 75 8 1 … … 102 … 18Cr-8Ni Plate, sheet, & stri
API 5L B … 60 … … 1 1 … 101 C-Mn Smls. & welded pipe & tubes
and so on
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
57
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 23/35
QW-403.8 A change in base metal thickness beyond
the range qualified in QW-451, except as otherwise permitted by QW-202.4(b).
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
58
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 24/35
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 25/35
QW-403.9 For single-pass or multipass welding in
which any pass is greater than. 1/2 in. (13 mm) thick,an increase in base metal thickness beyond 1.1 times
that of the qualification test coupon.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
60
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 26/35
QW-403.7 For the multipass processes of shielded
metal-are, submerged-arc, gas tungsten-are, and gasmetal-arc, the maximum thickness qualified for 1 1/2 in.
(38 mm) and over thickness T of the test coupon of QW-
. .
QW-451.1. For thicknesses greater than 8 in. (200 mm),
the maximum thicknesses of base metal and
deposited weld metal qualified is 1.33T or l.33t , as
applicable.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
61
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 27/35
QW-403.5 Welding procedure qualifications shall be made using:
(a) The same base metal (including type and grade) to be used in production welding; or
(b) For ferrous material, a base metal listed in the same P-Number and Group Number (seeQW/QB-422) as the base metal to be used in production welding; or
(c) For nonferrous material, a base metal listed in the same P-Number and Group Number(see QW/QB-422) as the base metal to be used in production welding.
For ferrous material in QW/QB-422, a procedure qualification shall be made for each P- Number and Group Number combination of base metals, even though procedure qualification tests
- . 422, a procedure qualification shall be made for each P-Number and Group Number combination
of base metals, even though procedure qualification tests have been made for each of the two base metals welded to itself. If, however the procedure specification for welding the combinationof base metals specifies the same essential variables, including electrode or filler metal, as both
, , ,the procedure specification for welding the combination of base metals is also qualified. Inaddition, when base metals of two different P-Number Group Number combinations are qualified using a single test coupon, that coupon qualifies the welding of those two P-Number Group
Numbers to themselves as well as to each other using the variables qualified.
- by other Sections.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
62
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 28/35
QW-403.6 The minimum base metal thickness quali-
fied is the thickness of the test coupon T or 5/8 in.(16 mm), whichever is less. However, where T is less
than 1/4 in. (6 mm), the minimum thickness qualified
.
qualified with a PWHT above the upper transformation
tem erature or when an austenitic material is solution
annealed after welding.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
63
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 29/35
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 30/35
Question (1): A test coupon is prepared as follows: A
1.75 in. plate is welded to 1.75 in. plate with 1 in. thickweld. Per QW-451.l, is 8 in. the maximum thickness
range of base metal qualified?
Reply (1): Yes, except that further limits or exceptions
may app y as s a e n o es an o - . .
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
65
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 31/35
Question (1): A 50 mm thick test plate done for a weld
procedure by FCAW is welded full thickness andreceives X-ray examination and mechanical tests,
including impact tests. Is the thickness test range
. . - .
ep y : es, excep w en no c oug ness s a
requirement the minimum thickness qualified is 5/8 in.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
66
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 32/35
Background: A WPS is supported by three PQRs. Two
PQRs are recorded on 12mm and 28.5mm thick couponsusing tensile, bend, and impact testing specimens. A third
PQR was made using 5mm thick plate using the same
,
tested.
WPS for welding 2.5 mm through 57 mm material
re uirin notch tou hness testin ? Reply (1): No.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
67
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 33/35
Background: A WPS is supported by three PQRs. Two
PQRs are recorded on 12mm and 28.5mm thick couponsusing tensile, bend, and impact testing specimens. A third
PQR was made using 5mm thick plate using the same
,
tested.
support welding base metal thicknesses of 4.8 mm
throu h 57 mm with or without notch tou hness? Reply (2): Yes.
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
68
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 34/35
Question (1): Do the provisions of QW-200.4(b) permit a
GTAW procedure qualification test weldment performedon a 13 mm thick coupon to support depositing a root
pass in a production joint of the qualified base metal
required?
- . . ..
30 เมษายน 53 ASME Section IX, WPS/PQR Prepared by
SCB
69
8/12/2019 4 Asme Sec Ix Wps Pqr Slide 36 to 70
http://slidepdf.com/reader/full/4-asme-sec-ix-wps-pqr-slide-36-to-70 35/35