2K Etch Primer-process Data Sheet
Transcript of 2K Etch Primer-process Data Sheet
-
8/11/2019 2K Etch Primer-process Data Sheet
1/3
2K Etch PrimerTechnical Data Sheet
16.05.03 L2.03.01
Description Two component, chromate free, etching primer surfacer for
general use in refinishing cars and also light commercial vehicles.
For fast turn round work, only denibbing with Scotch Brite is
necessary prior to the application of topcoat.
3 : 2
2K Etch PrimerActivator Etch
Primer
Mixing Ratio
Chart orMixing Stick B
2 -3 x 1
1.5 - 1.8 mm2 - 3 bar
5 10 mins 1 hrs 20C
20 mins 60C
Product & Ancillary ItemsProduct Lesonal 2K Etch Primer
Activator Lesonal Activator Etch Primer
Chemical Basis 2K Etch Primer - Combination of polyvinyl butyral, and other special resins
Activator Etch Primer - Combination of organic solvents and phosphoric acid
Method of Use
Substrates Sound original finishes with the exception of thermoplastic acrylics
Steel
Zinc coated steel
Aluminium
Lesonal Polyester Body Filler
Lesonal Polyester Spraying Filler
Substrate Preparation Prior to commencing any sanding work, thoroughly cleanse the surface of any
grease or wax with Lesonal Degreaser SB. Apply using two cloths in a wipe on,
wipe off process.Original finishes - sanding with P280 grit dry or P600-P800 wet.
Steel remove all traces of rust and abrade thoroughly until a clean surface is
achieved. Any millscale should be removed by shot blasting.
Aluminium and zinc coated steel - abrade thoroughly with Scotch Brite 447 (Red).
Lesonal Polyester Body Filler - finish sand with P280 grit dry.
After sanding work is completed and just prior to the application of primer, degrease
again thoroughly with Lesonal Degreaser SB.
Mixing Ratio Use Mixing Ratio Chart or Mixing Stick B
3 volumes - 2K Etch Primer
2 volumes - Activator Etch Primer
Mix in a parallel sided mixing vessel and stir well before use.
-
8/11/2019 2K Etch Primer-process Data Sheet
2/3
2K Etch PrimerTechnical Data Sheet
16.05.03 L2.03.01
Spraying Viscosity When mixed as described the correct spray viscosity is achieved.
20-22 secs DIN Cup 4 at 20C
Pot Life After mixing the mixture must be used within 2 days at 20C.
Gun Set Up & Spraying Pressure Spray Gun Fluid Opening Spraying Pressure
LVLP (HR) Gravity Feed
HVLP Gravity Feed
Conventional Gravity Feed
1.8 - 2.0 mm
1.8 - 2.0 mm
1.5 - 1.8 mm
2.0 - 3.0 bar
0.7 bar
3.0 - 4.0 bar
Application Technique Apply two or three single coats; allow to dry until matt between each coat. Generally
this will take 5 - 10 minutes. (This time will be very much influenced by factors such
as temperature and air movement at the time of application.)
If the product is to be applied over a fresh synthetic finish, it is recommended that a
thin coat is applied first, and that care is taken in applying subsequent coats. Flash
off times between each coat should be also extended.
Build per Coat Sprayed 20 - 25 microns
Theoretical Usage
12 m2per litre at a layer thickness of 15microns (the practical material usage
depends on many factors, i.e. shape of the object, roughness of the surface,
application method and application circumstances)
Equipment Cleaning Use a nitrocellulose thinner.
Drying Times at 20C
Dry to sand
Dry to denib (with Scotch Brite)
Dry to recoat with Primer / Filler
1 hour
20 mins
15 mins
Infra red short wave equipment
Half power
Total time
5 mins flash off
7 mins low
12 mins
When recoating with a topcoat, it is always necessary to at least denib the product
with Scotch Brite.
Recommended Sanding Grades Method Sandpaper Grade
Wet, by hand or machine
Dry, by hand
Dry, by machine
P800 - P1000
P400 - P500
P400 - P500
-