Xylan 1053DF/399 Dark

General DescriptionXylan 1424 series fastener class coating mate-

rial is a waterborne/VOC-compliant, resin bonded,thermally cured, single film, dry lubricant. It isprimarily formulated for use on fasteners toprevent corrosion and facilitate make-up torque.

Xylan 1424 series is available in a wide rangeof colors.

Substrate InformationXylan 1424 coating can be applied to many

types of substrate material such as aluminum,brass, high alloy steels, carbon steel, stainlesssteel, titanium and zinc plating.

Use TemperatureXylan 1424 coating can be used continuously

from -58°F (-50°C) to +350°F (+176°C) and cansurvive up to +400°F (+204°C) intermittently.

If higher temperature service is required,please contact your Whitford representative forrecommendations.

Corrosion ResistanceXylan 1424 coating applied at 1 mil (25 micron)

dry film thickness, over zinc phosphated steelpanels, has exceeded 1500 hours of ASTM B-117salt fog test. With the same pretreatment, 30cycles DIN 50018 (2.0 liters SO2) Kesternich Testare achieved. Both with less than 15% red rust.

Xylan 1424 coatings will provide even bettercorrosion protection if used over a sacrificialprimer like Xylan 5211, Xylar 1, Xylar P51 or zincplating

Physical PropertiesPencil hardness 2 - 3 HDielectric strength 500 V/milCoefficient of friction .05 - 0.10VOC Content/Series Avg. 3 lbs/gal (360gms/l)

Torque ValuesThe low coefficient of friction of the coating

reduces the torque required to achieve thedesired tension preload. Whitford Corporationrecommends the use of direct tension indicatorsto determine proper make-up torque for each sizeor lot of fasteners used on a given application.

Chemical ResistanceXylan 1424 coatings will withstand most sol-

vents, waters, automotive fluids and fuels up to200°F. Xylan 1424 coatings are impervious to newwater base hydraulic fluids used in offshore oilproduction.

Application InstructionsPlease refer to the Whitford Product Data

Sheet for application information or contact yourWhitford representative for more information.

Non-Warranty:The information presented in this publication is based upon the research and experience of Whitford. No representation or warranty is made, however, concern-ing the accuracy or completeness of the information presented in this publication. Whitford makes no warranty or representation of any kind, express or implied, including withoutlimitation any warranty of merchantability or fitness for any particular purpose, and no warranty or representation shall be implied by law or otherwise. Any products sold byWhitford are not warranted as suitable for any particular purpose to the buyer. The suitability of any products for any purpose particular to the buyer is for the buyer to determine.Whitford assumes no responsibility for the selection of products suitable to the particular purposes of any particular buyer. Whitford shall in no event be liable for any special,incidental or consequential damages. Xylan is a registered trademark of Whitford.

Whitford Corporation, Box 80, Elverson, PA 19520Tel: (610) 286-3500 • Fax: (610) 286-3510 • website: whitfordww.com

XXYYLLAANN® 11442244 SSEERRIIEESSFastener Class Coatings: VOC-Compliant

1424Chemical Resistance

HCI (concentrated) @room temp.HCI (pH 2) room temp.HCI (pH 2) 125°FNaOH (50%) room temp.NaOH (12.5) room temp.NaOH (pH 9.5) 125°FMEK room temp.Toluene room temp.Castrol Hydraulic Fluid 200°F

Oceanic HK-540 200°F

Changes in 1424after 24 hrs exposure

NoneNoneNoneNoneNoneNoneSlight MarkSlight Mark

Gloss decrease: 25.6 to 24.1. No loss in coating integrity.

Gloss decrease: 29.9 to 10.3. Color lightened slightly. No loss in coating integrity.