DREF  Yarns  by  NOR*FAB  

NOR*FAB  Corporation  1032  Stanbridge  Street  

Norristown  PA  19404  USA  1-­‐800-­‐441-­‐9680  

¡  The  DREF  spinning  process  manufactures  yarns  composed  of  a  core  covered  completely  by  staple  fibers.  

¡  Allows  creation  of  hybrid  yarns-­‐combining  the  best  properties  of  core  yarn  and  sheath  fibers.  

¡  DREF  yarns  provide  the  best  durability  as  compared  to  other  core    spinning  processes  

¡  NOR*FAB  Corporation  operates  the  largest  collection  of  DREF  III  yarn  spinning  equipment  in  the  world.  

¡  Yarn  sizes  ranging  from  41  to  1000  tex.  

 

1.  Sliver    2.  Double  Apron  Drafting  arrangement      3.  Strand    4.  Spinning  drums    5.  Staple  Fibers    6.  Yarn    7.  Take  off  rollers  

Fiber  Sheath  Core  

¡  Glass  ¡ Wire  

§  Stainless  Steel  §  Brass  §  Inconel  

¡  OPF  (Oxidized  Pan  Fiber)    ¡  Aramids  

¡  Para-­‐Aramid  ¡  Meta-­‐Aramid  ¡  Novaloid  ¡  PBI®  (Polybenzimidazole)  ¡  Modacrylic  ¡  Acrylic  ¡  FR  Rayon  ¡  Rayon  ¡  Blend  of  above  fibers  

PBI®  is  a  registered  trademark  of  PBI  Performance  Products  Inc.  

 

Yarns  for:  ¡  Braiding  ¡  Knitting  ¡ Weaving    ¡ Wire  &  Cable  ¡  Cut  Resistance  ¡  Clutch  Facing  &  Brake  Linings  

¡  Thermocouple  Insulation  ¡  Aerospace  

¡  DREF  yarns  provide  superior  abrasion  resistance,  durability  and  strength.  

¡  Enables  the  development  of  individually  engineered  yarns  to  meet  customer  needs.  

¡  Superior  cut  resistance  as  compared  to  ring  spun  yarns  §  Allows  for  hardened  cores  such  as  fiberglass  and  wire  to  further  enhance  cut  resistance  

¡  Excellent  thermal  insulation  ¡  Outstanding  value  versus  lower  performing  yarns  

Fabric     Cut  Protection  (ASTM  1790-­‐97,  CPPT  (g)  

100%  Para-­‐aramid  ring  spun  fabric   700  g  

Hybrid  Ring-­‐Spun  /  DREF-­‐Spun  woven  fabric  with  hardened  core,  such  as  NOR*FAB  CutPro™  Style  10TT366  

3200  g  

Ø The  example  above  compares  Para-­‐Aramid  woven  fabrics  of  similar  weights  except  that  Style  10TT366  is  woven  with  DREF-­‐Spun  yarns  that  have  a  core  of  stainless  steel.    The  result  is  an  improvement  in  Cut  Resistance  of  450%.