Desulfuriwtion of INCO Semi-Blister Copper
by
Ioannis John Roumeliotis
Department of Mining and Metallurgical Engineering McGill University Montreal, Canada
A thesis submitted to the Faculty of Graduate Studies and Research in partial fulfillrnent of the requirements
for the degree of Master of Engineering
1. J. Roumeliotis
National Library 1*1 of Canada BiMiothèque nationale du Canada
Acquisitions and Acquisitions et Bibliographie Services services bibliographiques
395 Wellington Street 395. nre Wdlington OttawaON K l A M OüawaON K 1 A W cana& canada
The author has granted a non- exclusive licence allowing the National Library of Canada to reproduce, loan, distribute or sel copies of this thesis in microfonn, paper or electronic formats.
The author retains ownership of the copyright in this thesis. Neither the thesis nor substaatial extracts fiom it may be printed or otherwise reproduced without the author's permission.
L'auteur a accordé une licence non exclusive permettant a la Bibliothèque nationale du Canada de reproduire, prêter, distribuer ou vendre des copies de cette thèse sous la forme de microfiche/fïim, de reproduction sur papier ou sur format électronique.
L'auteur conserve la propriété du droit d'auteur qui protège cette thèse. Ni la thèse ni des extraits substantiels de celle-ci ne doivent être imprimés ou autrement reproduits sans son autorisation.
A bstract 1
The INCO finishing procedure represents the near final stages of copper production
at the Copper Cliff Smelter in Sudbury, Ontario, whereby semi-blister copper, at 4-6 wt %
Ni and 2-3 wt % S, is processed into blister copper. at 100 ppm S and 0.4 wt % Ni. in a
modified Pierce-Smith converter combining topblown oxygen injection and bottom-blown
nitropo stirring of the melt to accelerate semi-blister desulfurization. The procedure is
perfonned in two stages of equai duration: in the first, melt saturation with oxygen and suifisr
eiimination from 2-3 wt % S to 300 ppm is achieved by 45 minutes of oxygen top-blowing
and nitrogen bottom stimng; in the second stage, oxygen injection is terminated and sulfur
removal from 300 ppm to 30-100 ppm proceeds by the reaction of dissolved S and O under
a further 45 minutes of nitrogen stirring.
The apparent decrease in the rate kinetics of sulfbr elimination during second stage
finishing prompted an investigation into the possible causes irnpeding sulfùr removal. Two
possible causes were identified: the cessation of surface tension driven flow, or 'Marangoni
convection', upon oxygen saturation of the melt and surface coverage by nickel oxidation.
In this study 1 to 2 kg liquid charges of Cu - 1 wt % S. Cu - 3 wt % Ni and cathode copper
were impinged with an oxygen gas stream of 75 cm3/min from a gas lance 1.5 cm above the
melt surface to examine whether Marangoni convection can indeed be provoked in these
systems and to compare sulfw elimination between Cu-S and Cu-Ni-S melts. Marangoni
convection was not observed in these systems but surface oxidation did occur readily and
was found to impede sulfur elirnination; the effect king more pronounced in the Cu-Ni-S
melts.
Cu-S and Cu-Ni-S alloys were also exposed to the open atrnosphere to examine
desul furization of stagnant melts under air. Although surface oxidation irnmediately
occurred in these melts, it was found that at a particular concentration of S and O in the
liquid C u 4 alloy the melt periodically erupted with effervescence resulting in disintegration
of the oxidized surface layer and accelerated S removal. The Cu-Ni-S alloy which did not
undergo spontaneous bubbling maintained the integity of its slag layer and sulfur removal
was therefore gradual.
. . Résumé 11
La procédure d'affinage iNCO représente le stage une des dernieres étapes de la
production de cuivre à l'fierie Copper Cliff de Sudbury, en Ontario. Dans cette opération,
le cuivre semi-blister (c.-à-d. ayant des cloques en surface), à 4-6 % pds de Ni et 2-3 % pds
de S. est traité pour être transformé en cuivre blister contenant 100 ppm de S et 0,4 % pds
de Ni. Ce traitement a lieu dans un convertisseur Pierce-Smith modifié dans lequel on
insuffle de l'oxygène au haut du f o u et, au bas, de l'azote qui assure le mélange du métal en
fusion pour accélérer la désuifunsation du semi-blister. L'opération s'effectue en deux étapes
de durée égale (45 minutes). Au cours de la première, on sature le métal en h i o n d'oxygène
et on en réduit la teneur en souffre à 300 ppm en continuant à soumer l'oxygène par le haut
et l'azote par le bas pour assurer le mélange. À la seconde étape, on cesse d'injecter de
l'oxygène mais la réduction de la teneur en soufre, se poursuit jusqu'à 30 à 100 ppm. par
réaction de S et de O dissous grâce au mélange par l'azote.
La diminution apparente de la cinétique d'élimination du soufre au cours de la
seconde étape de l'affinage a donné lieu à une étude visant à déterminer les causes
susceptibles de nuire à cette élimination. Nous avons identifié deux causes possibles: la
cessation d'écoulement induit par la tension superficielle, ou convection de Marangoni, après
saturation en oxygène du métal fondu, et la formation d'une couche de nickel oxydé à la
surface. Dans le cadre de l'étude. des phases liquides à 1 kg - 2 kg de Cu à 1 % pds de S, de
Cu à 3 % pds de Ni et 1 % pds S, et de cuivre pur ont été bombardées d'un flux de gaz
d'oxygène de 75 cm3/min provenant d'une buse à gaz placée à 1,s cm au-dessus de la surface
du métal en fusion, afin de déterminer s'il était effectivement possible de provoquer la
convection de Marangoni dans ces systèmes et pour comparer les taux d'élimination du
soufie dans le Cu-S et le Cu-Ni-S en h ion . On n'a pas observe de convection de Marangoni
dans ces systèmes; par contre, l'oxydation en surface s'y produit facilement et affecte
l'élimination de soufie, cet effet étant plus prononcé dans le cas du CU-Ni-S en fiision.
On a aussi exposé les alliages C u 4 et Cu-Ni-S a i'air libre pour étudier le processus
de désulfkisation des bains stagnants à l'air. Même s'il y avait oxydation immédiate à la
surface de ces alliages en hision, il a été déterminé qu'une certaine concentration de S et de
O dans I'alliage liquide Cu-S provoquait périodiquement l'effervescence du métal fondu, ce
. . . Résumé U1
qui entrainait la désintégration de la couche superficielle oxydée et accélérait l'élimination
du S. Dans le cas de I'ailiage Cu-Ni-S, qui ne connaissait pas un tel bouillonnement spontané,
l'intégrité de la couche de scories étant maintenue. l'élimination du soufre se faisait moins
rapidement.
Ackno wledgements iv
This research program could not have been camied out without the financial support
of NSERC and iNCO which in the case of the latter was complemented by the indispensible
technical support provided by its s-, Dr. Sam Marcuson, Mike Humphries. and Jin Liu and
through the use of its analytical facilities at Copper Cliff.
Special thanks to the teaching staff of the Department of Mining and Metallurgical
Engineering at McGill University, including Department Chairman Prof. G. Dernopoulos for
his personal involvement in the course of this investigation. Prof. A. Laplante for his
discussion on statistical analyis and in conjunction with Florence Paray as CO-editor of the
uanslated abstract. and especially my supervisor Prof. Ralph Harris whose continued faith.
moral encouragment. technical assistance and discussions proved invaluable for the
completion of this study.
The technical staff of the Department of Mining and Metallurgical Engineering who
also deserve particular mention are H. Ward. M. Riendeau R. Paquette. H. Campbell and E.
Femandez for providing technical assistance and consultation beyond their duty
requirements. To former and fellow p d u a t e students. T. Brzezïnski. Y. Baik. R.
Sankanarayanan. H. Abulewufa, B. Handle. M. lkezawa T. Luganova-Shrenyakova and Qi
Xia. I would like to thank them al1 for providing a forum for moral support and technical
discourse while H. Abulewufa's contribution of his data acquisition equipment for use in this
study was additionaiiy appreciated.
Gratitude and recognition go to Claudia Cien and Richard Thesi for their tirne and
effort donated to transiating the abstract of this thesis to french. I would also like to thank
my immediate family, Eugenia, Ioanna, Dernosthenes and David for providing continued
encouragement throughout this research program and to Donatella Battista whose faith.
support and inspiration were indispensible for completing this work. Additional thanks also
go out to John Kappos. Sami Ramadan and other tnends for their moral support and other
intangible contributions.
Table of Contents v
Abstract ............ ........................... ...................................................................................... 1
Résumé .................. .... ....... .. ........................................... ii
Acknowledgements ......... ........... ..................................................................................... iv
Table of Contents .................... .. .................................................................................... v
List of Figures .................................................................................................................... vii
List of Tables ...................................................................................................................... xii
.................................................................................................................. Nomenclature xiii
Chapter 1 . 1.1 1.2 1.3
Chapter 2 . 2.1
Chapter 3 . 3.1
Introduction ....... .r............... ............................................................... The Smelter Flowsheet in 1992 ................................................................... The Smelter Flowsheet in 1993 ................................................................... Blister Copper Production fiom MK Concentrate ...................................... 1.3.1 Oxygen Flash Converting of MK Concentrate to Semi-Blister 1.3.2 Finishing of Semi-Blister to Blister ................................................ Researc h Objectives .....................................................................................
Literature Review ................................................................. Thermodynarnics and Thermochemistry of Copper Converting .............. .... 2.1 . 1 Conventional Coppet Converting ................................................... 2.1.2 Copper Converting at M C 0 ........................................................... Gas-Liquid Interactions ............................................................................... 2.2.1 Top Blown Gas Injection with High Momentum lets ..................... 2.2.2. Top Blow Gas Injection with Low Momentum Jets ..................... Interfacial Phenornena- ............. ... ............................................................ 2.3.1 Surface Active Solutes and Surface Tension .................................. 2.3 -2 The Role of Surface Active Solutes on Reaction Rates .................. 2.3.3 Surface Tension Driven Flow ......................................................... Oxidation Studies ........................................................................................
................................................................................................... Hypothesis
Experimental Methodology ................. ........................... ................. Experimental Program ................. ... .......................................................... Test Apparatus ............................................................................................. 3.2.1 Design Criteria ............................................................................... 3.2.2 Selection of Fumace Technology ...................................................
Parabolic Clamshell Heater ............................................................. Silicon Carbide Resistance Heating Fumace ..................................
3 .2.3 Reaction Vesse1 .............................................................................. 3.2.4 Gas Regulation System ...................................................................
Table of Contents vi
Chapter 1 . 4.1
Chapter 5 . 5.1
5 -2
Chapter 6 . Chapter 7 . Appendix A . References
Gas EvacuationNentiiation. ........................................................... Gas Delivery .................... ... .........................................................
............................................................................... Experimental procedure Test 1 - Test 6 ................................................................................. Test 7 - Test 9 ................................................................................
Elemental Analyses ...................................................................................... ...................................................................................... Charge Pre parat ion
3.5.1 In Situ Alloy Preparation .............................................................. 3.5.2 Master AIloy Preparation ................................................................ Selection of Experimental Conditions .................. .... ...............................
Results ............ .... .......................................................................... ................................................................................... Experirnental Results
. .......................... Test 1 : Desulfùrization of a Cu 3 wt % S Alloy Test 2: Desulfurization of a Cu . I wt % S Alloy with 66 cm'
................................................................................ O, /m in Test 3: Desulfurization of a Cu . 1 wt % S Alloy with 75 cm3
OJm in ................................................................................ Test 3: Desulfùrization of Cu . 3 wt % Ni . I wt % S Alloy with 75
cm3 O. /min ......................................................................... Test 5 . Test 6: Oxidation of Cathode Copper with 75 and 372 cm3
................................................................. OJm in. Test 7, Test 8: Desulfurization of Cu-1 wt % S Alloy Exposed to
Air ........................................................................ Test 9: Desulfurization of Cu - 3 w % Ni . 1 wt % S Alloy
................................................................... Exposed to Air .................................................................................... Discussion of Errors
................................................................................. ......... Discussion ... Discussion of Results ................................................................................... 5 . l . i Marangoni Convection ................................................................... 5.1.2 The Role of Surface Films on Mass Transfer ................................ 5.1.3 Melt Effervescence ......... .... ...................................................... Sumrnary
..........*................ ...................................... Conclusions ... Recommendations for Future W o r k .................................. ... ............ X-Ray /SEM Analyses ............................ .... ...................m..............*........
List of Figures vii
Chapter 1 Figure 1. The Copper Cliff Smelter flowsheet in 1992 operating separate nickel and
r i
copper production circuits- ........................ ,........- .-.-...--.--.-..
Figure 2.
Figure 3.
Figure 4.
The current Copper Cliff Smelter flowsheet after implernentation of process and equipment modifications in 1993' .........................................................
The W C 0 Multi-purpose vesse1 (MPV) for finishing of semi-blister to .......................................................................................................... blister'
Process curve of sulfiir for the W C 0 MPVL9. Stage 1 sulfur elimination is performed by oxygen top-blowing and enhanced by nitrogen stirring. In Stage II. oxygen injection is terminated while nitrogen agitation of the melt is continued ..................................................................................................
Chapter 2 Figure 5 . The Cu-S phase diagram showing the oxidation path of CU'S to blister Cu
during conventional converting according to Biswas and Davenporf'. The shaded region depicts the oprating zone of the MC0 finishing
..................................................................................................... procedure
Figure 6.
Figure 7.
Figure 8.
Figure 9.
The phase relations of the copper-rich region of the Cu-Ni-S phase diagram at 1473 K s h o w superimposed on the isoactivity line of Ni and S according to Larrain and Lee'9-3' ..................................................................................
The phase relations and various isotherms of the copper-rich corner of the Cu-Ni-O system according to T'askinenj6 and Kuxmann and Rieckejg. The mows trace the oxidation path followed by nickel during the INCO finishing pr~cedure '~ ....................................................................................
The composition and temperature changes experienced by the copper charge during a pilot plant test of the RJCO finishing procedure19 ....... .. ...........
(a) Dimpling of a Iiquid surface by a low momentum gas jet. (b) Increasing the jet momentum beyond a critical value results in splashing i-e. ejection of material fiom the impingement area. (c) At high jet momentum the gas penetrates the liquid resulting in a tower volume of ejected material. (d) Schematic depiction of the geometric model developed by wakelin6' and the ensuing dimensionless relationship ............................................................
Figure 10. Types of adsorption behaviour observed at liquid-metal interfaces (a) positive adsorption (b) negative adsorption (c) electrocapillary behaviour, according to ~ r imacomùe~ ..........................................................................
Figure I 1. Effect of (a) dissolved oxygen and (b) dissolved sulphur on the surface tension of liquid copper at various temperatures according to Monma and suto" ...........................................................................................................
m..
List of Figures Vl l l
Figure 12.
Figure 13.
Figure 14.
Figure 15.
Chapter 3 Figure 16.
Figure 17.
Figure 18.
Figure 1 9.
Figure 20.
Figure 2 1.
Figure 22.
Figure 23.
Figure 24.
Surface renewal by eddies at interfaces: (a) no surface active material present (b) in the presence of surface active material according to ~ichardson -.....
Mac-scale interfacial motion on the surface of liquid copper generated by (a) the impingement of an oxygen jet on the melt surface which leads to (b) radial spreading of the oxide patch at high velocity towards the regions of highest surface tension (c) ...........................................................................
(a) Micro-sale interfacial motion generated by the penetration of eddies at the gas-liquid interface with a solute composition exceeding that of the interface resulting in motion towards regions of higher interfacial tension according to BrirnacombeZ. (b) Macro-scale interfacial motion generated by the dissolution of a partially immersed solid resulting in liquid motion away fiom the solid-liquid interface when there is positive adsorption of the solute on the Iiquid surface and towards the solid-liquid interface when there is negative solute adsorption on the liquid surface according to
............................................................................................ ~rimacom bez
Variation of the sulfür dioxide pressure in equilibrium with Cu,,,. Cu,S, Cu.0 and the liquidus curve of coppep .................................................-.
Temperature versus total. normal cmiss ivi~ of heavily oxidized stainless steel and aluminum oxidelo3 .........................................................................
Sc hematic representation of the (a) profile and (b) plan view of the silicon .............. carbide resistance fiirnace designed and used in this investigation
The time-temperature profiles of an iron block heated to 1473 K in the clamshell radiation fiimace and to 1523 K in the Sic resistance fumace ....
W king d iagrarn for the S iC resistance fumace feaiuring two Omega CN9 1 1 1 series controllers which allowed for high thermal stability in the bath ........
Schematic representation of the (a) cross section of the reaction vessel. crucible and accessories and (b) plan view of the AI water jacket and its
............ access ports ................................ ... Schernatic representation of the test apparatus when the quartz reaction vesse1 and graphite receptacle were used ......................-..............................
Photograph of the test apparatus during operation .......................................
Broaâside and cross section of the cathode copper sheet. Elemental analyses were performed on the shaded regions .......................................................--
Cross section of crucible and solidified slag layer fiom Test 1 ....................
List of Figures ix
Figure 25.
Chapter 4 Figure 26.
Figure 27.
Figure 28.
Figure 29.
Figure 30.
Figure 3 1.
Figure 32.
Figure 33.
Figure 34.
Figure 35.
Regions of alloy ingot sampled for elemental deteminations ......................
The dissolved S and O concentration profile over time in Test 1. The vertical line coincides with the introduction of the O,-Nz gas mixture ont0
.................................... the melt surface at 1 70.6 cm3/min and .J& = 0.62
Photograph of the luminescent patch beneath the tip of the gas lance in Test 1 at the start of O,-N, gas blowing. The dark spot on the tube is a large droplet of material that had been ejected fiom the bath ...............................
(a) Schematic diagram of the region on the quartz tube most affected by the melt ejections. (b) Photograph of the ktured reaction vessel near its radial bottom ringed with droplets of copperkopper oxide ...................................
The time-temperature profile of the alloy melt in Test 1 relative to the sampling time. The horizontal Iine marks the bath setpoint temperature of 1 498 K .........................................................................................................
The dissolved S and O concentration profiles over time in Test 2. The vertical line coincides with the introduction of pure O, ont0 the melt surface at 66 cm3/min .......... .....,, ..........................................................................
The time temperature profile of the melt in Test 2 relative to the sampling time t = 0; the depression in the curve near 1400 K indicates liquefaction of the alloy charge while the horizontal Iine marks the bath setpoint temperature of 1523 K...- ............... .. ............................................................................
Photographs of the alloy surface and oxide film from Test 2 at (a) 1523 K and t = 70 minutes; a highly emissive solid or liquid oxide near the crucible wall is sumunded by the darker liquid alloy and (b) room temperature where the blistered alloy surface is partially covered by dark regions of oxidized copper.. ........................................................................................................
Photograph of the quartz reaction vessel, fiom Test 2, along its vertical ................................. length showing solidified droplets of ejected material
The dissolved S and O concentration profile over time for Test 3 at 1523 K. The vertical line coincides with the introduction of pure 0, ont0 the melt
................................................................................... surface at 75 cm3/min
The time temperature profile of the melt in Test 3 relative to the sampling time t = 0; the depression in the curve near 1400 K indicates liquefaction of the alloy charge while the horizontal Iine marks the bath setpoint temperature of 1523 K .....................................................................................................
List of Figures X
Figure 36.
Figure 37.
Figure 38.
Figure 39,
Figure 40.
Figure 4 1 .
Figure 42.
Figure 43.
Figure 44.
Figure 45.
Figure 46.
The dissolved S, O and Ni concentration profile over time in Test 4. The first and second vertical lines coincide respectively with the intrduction of pure O, ont0 the melt surface at 75 cm3/min and then at 372 crn3/min ........
Photograph of the melt surface in Test 4 covered by an emissive oxide film at 1523 K and t = 40 minutes. The dark region is the liquid metal surface that was exposed after a sample had been extracted fiom the melt ..............
The time temperature profile of the melt in Test 4 relative to the sampling time t = 0; the deptession in the curve near 1400 K indicates Iiquefaction of the alloy charge while the horizontal line marks the bath setpoint temperature of 1523 K ....................................................................................................
The dissolved O concentration profile over time in Test 6. The first and second vertical lines coincide respectively with the introduction of pure Oz ont0 the melt surface at 75 cm3/min and then at 372 cm3/min ....................
Photographs of the melt surface at 1523 K in (a) Test 6 covered by an emissive oxide layer afler 22 minutes of Oz blowing (Le. t-piiys = 32 minutes) and (b) Test 5 after 35 minutes of 0 blowing at 75 cm3/min; note the mirror image of the gas lance on the dark but reflective melt surface ....
The time temperature profile of the melt in Test 6 relative to the sampling time t = 0; the depression in the curve near 1400 K indicates liquefaction of the alloy charge while the horizontal line marks the bath setpoint temperature
Photograph of the melt surface in Test 8 covered by an emissive oxide at approximately t = O minutes. The darker spots are the exposed surface of the liquid alloy .................... ..,, ....... ... ............................ Photograph of the melt surface effervescing in Test 8 at t = 28 minutes .....
n i e dissolved S and O concentration profiles over time for Test 7 and Test 8. The dashed and solid vertical lines rspectively mark the occurrence and duration of effervescence in Test 7 and Test 8 ............................................
The time temperature profile of the melt in Test 7 relative to the sampling time t = 0; the plateau in the curve near 1400 K indicates Iiquefaction of the alloy charge while the horizontal line marks the bath setpoint temperature of
......................................................................................................... 1523 K
The tirne temperature profile of the melt in Test 8 relative to the sampling time t = 0; the plateau in the curve near 1400 K indicates liquefaction of the alloy charge while the horizontal line marks the bath setpoint temperature of 1523 K .........................................................................................................
List of Figures xi
Figure 37.
Figure 48.
Figure 49.
Chapîer 5 Figure 50.
Figure 5 1.
Figure 52,
Figure 53.
Figure 54.
Figure 55.
Appendk A Figure A 1.
Figure AS.
The S, O and Ni concentration profiles over time in Test 9. The vertical Iines coincide respectively with the introduction of pure O2 ont0 the melt surface at 75 cm3/min and submerged nitrogen injection at 2000
..................................................................................................... cm3/min..
Photograph of the melt surface in Test 9 covered by an oxide layer at t = 32 minutes .......................................................................................................
The time temperature profile of the melt in Test 9 relative to the sampiing tirne t = 0; the plateau in the curve near 1400 K indicates liquefaction o f the alloy charge while the horizontal iine marks the bath setpoint temperature of
The concentration profiles over time in Tests 1 and 2 adjusted to the time scale of Test 1. The vertical line coincides with the start of Oz delivery to both melts ....................................................................................................
The concentration profiles over time in Tests 3,4, and 6 adjusted to the time scale o f Test 3. The vertical line coincides with the start of O, delivery to al1 the melts .................... .. ...............................................................................
The concentration profiles over time in Tests 2 and 3 adjusted to the time scale of Test 3. The vertical line coincides with the start of O? delivery to both melts ....................................................................................................
The S concentration profiles over time in Tests 8 and 9. The sarnpling time in Test 8 was adjusted to the time scale of Test 9 when a similar S concentration is observed in both melts ............................................................
The sulfùr concentration profile fiom CS alloy blown with O at 75 cm3/min, 500 cm3/min and 1000 cm3/min and fiom CNS alloy blown with oxygen at 1000 cm3/min, according to RiouxfM ........................... ,.,. ............................
The S concentration profile over time in Test 8 compared to Rioux's testwork with CS alloy blown with oxygen at 75 cm3/min. The time scale in Test 8 is adjusted to Rioux's sarnpling time when a similar S concentration is observed in both melts. The vertical line indicates the start of Oz blowing at 75 cm3/min in Test 8 .........................................................
Qualitative identification o f slag components in Test 1 by X-ray d i fhc t ion ....................................................................................................
Qualitative identification of ejected material on the quartz reaction vesse1 in Test 1 by scanning electron microscopy .................. ,.. .............................
List of Tables xii
Chapter 2 Table 1 .
Chapter 3 Table 2.
Table 3.
Table 4.
Table 5.
Table 6.
Chapter 4 Table 7.
Table 8.
Table 9.
Table 10.
Table 1 1 .
Table 12.
Tabie 13.
Parameters of the experimental systern w d by Kikuchi6'-'" et al. according to ~ l y a s e p .................................................................................................
Dimensions of the reaction vesse1 and its accessories ........................ .... ......
Average elemental composition of WC0 cathode copper sheet ....,.............
Composition of HYCOR alumina crucible according to the manufacturer..
Elemental determinations for C S and CNS alloys ...-. ....-....-.........-......--.....
Experimental conditions used for desulfùrization and oxidation tests ........
Tabulated S and O assays fiom Test 1 conducted at 1498 K by blowing an Oz-N, gas mixture with Ja, = 0.62 at 170.6 cm3/min on liquid Cu - 3 wt??
- ,
S alloy .............................. : ..........................................................................
Tabulated S and O assays h m Test 2 conducted at 1 523 K by blowing pute O1 at 66 cm3/min on the surface of Iiquid CS alloy ....................... .. ...... ....
Tabulated S and O assays h m Test 3 conducted at 1 523 K by blowing pure O, at 75 cm3/min on the surface of a CS alloy charge .............................. ..
Tabulated S. O and Ni assays fiom Test 4 conducted at 1523 K with CNS alloy initially blown with pute Oz jet at 75 cmS/min and then at 372
Tabulated O assays fiom Test 6 conducted at 1 523 K by blowing a pure O, jet at 75 cm3/min on the surface of a cathode copper ...,........,-.-..... ., ...... .....
S and O determinations for Test 7 and Test 8. The time scale in Test 8 has been adjusted to coincide with the sampling time of Test 7 at t = 61 minutes where the S content of both meits is similar ............. .. .............................
Tabulated S, O and Ni assays fiom Test 9 for CNS alfoy melted under air and then blown with pure O2 a! 75 cm3/min and finally subjected to submerged N, injection at 2000 cm3/min ........ ... . . . .. . ... ... . .. .. . . . .. -. -....... .. -. ..... . . .
... Nomenclature Xl l l
Ab breviations atm CDN cm' cm3/m in g J K kg kg-mole EGj
kPa rn m3 nr in fMP v mt m tpd LV ~ r n j ivm3/hr OFC Pa S
Temp vol % Wt % X Y'-
atmospheres (multiply by IO1325 to attain value in Pa) Canadian cubic cenrimeters cubic cenrimeters per minute (divide by 6 x IO' to attain value m3/s) gt.am joules degrees Kelvin kilogram kilogram-mole kilojoules kilo-Pascals fmultiply by 1000 to attain value in Pa) meters cubic meters minutes Mzilti-Purpose Vessel mefric tonne metric tonne per day Newtons normal cubic meters normal cubic metres per hour Oxygen Flash Converting Pascal seconds Temperature composition in volume percent composition in weight percent mole fi-action year
Chernical Symbds A1203 alumina (aluminum oxi& CH, merhane (na rural gus) Co cobalt Cu copper C u 0 copper (II) oxide Cu,O copper ( I ) oxide CuS chalcocire Fe iron Ni nickel Ni0 nickel oxide Nz diatomic niirogen O, 0 2 monatom ic oxygen and diat O mie oxygen respect ively Si silicon SO- sulfitr dioxide
Nomenclature xiv
Dimensionless Numbers Fr Froude Ma Marangoni Re Reynolds Sc Schmidt Sh Shenvood
Superscripts b bulk phase 1 intedace
Su bscripts fa gas fl) liquid fs) solid 1. S reactants I or S
Symbol negative dope of sur$ace tension-solute concentration plot negative of gradient of solute concentration across liquidfilm sirt$iace activity coeffîcient change in quantity sudace concentration or adsorption fiactional suflace coverage by solute gus or 1 iquid viscosiîy chemical poten tial of reactant B sur$ace tension electrical potenrial activity of sofute or species concentration of reaciants concentration gradient inner diameter of lance diameter of caviw d@kivity of solute standard free energy of formation gravitational constant (9.81 ds') depth of bath depth of caviiy lance height inner diameter apparent rate constant
S.I. LIirits Typical Uni6 (~/m)/fkg-mo le/m3)
unitless unit dependent kg-mole/m2 unitless k g / d s v .V/m v
poise (g/cds)
dynekm
unitless kg-mole/m3 kg-mole/m3 m mm m mm m% Jkg-mool U/g-mole, k/ m/s' 131 mm m mm m mm m mm dependenr on the order of the reaction
Nomenclaf ure xv
Symbol S.I. Uni& Typical Uni& overall mass rransfer coeficient equilibrium adsorption coefficient momentum of gas jet flux pressure partial pressure universal gas constant (8.3 14 J/mole/K) radius of bath radius of reacrion areo spreading coeflcient t emperature axial gas velocity gas flowrare ar lance ourlet mole fiaction dissolved species dissolved species in copper adsorbed species on liquid surface
nus unitless N kg-mole/m2/s Pa Pa Jkg-mole/K m m rv/m K m/s m3/s unitless kg-moldm3 kg-mole/m3 kg-mole/m3
dyne (N x 16) g/m2/s atm. kPa atm J/g-mole/K mm mm dyne/crn "C cm4 cm3/s. cmJ/min
Chanter 1. Introduction
M C 0 3 Copper-Cliff Smelter in Sudbury, Ontario is a leading non-ferrous metals
producer with annual yields of 120.000 mt of copper and 1 15,000 mt of nickel. Over the
decades, the production flowsheet at the smelter has been modified continuously in response
to technological developments, economic demands and increased environmental
awareness". These factors combined led to a decrease in sulfûr dioxide (SO,) emissions
at the smelter from 2,000,000 mt/yr to 685,000 mt/yr between 1970 and 1985. In the mid
1 980's. the Ontario Ministry of the Environment initiated the "Countdown Acid Rain"'
program which required INCO to M e r reduce sulfhr dioxide emissions to 265,000 mt/year
by 1994. INCO responded to its new environmental obligations at Sudbury with the 'SO,
Abatement Project'? At a capital cost of CDNS540,000,000, the project was designed ro
lower SOI emissions by the target date. increase the efficiency of INCO's manpower 23d
energy resowces, reduce smelter operating costs, improve the converter workplace
environment and affect these changes without diminishing productivit$". Meeting these
goals involved substantial changes to the smelting and copper production circuits. Smelting
practice was improved with existing DUC0 flash h a c e techology and through
consolidation of NCO's mil1 resources while copper smelting and converting was enhanced
with technology borrowed from the ferrous industry Le.. melt stimng via bottom injection
of inert gas through porous plugs.
The puipose of this study is to examine copper converting practice at the Copper Cliff
Smelter and investigate the factors afTecting the kinetics of desulfwization in the finishing
stages of blister copper production. To better understand the rnetailurgy of INCO's
converting practice, it is instructive to examine the smelter circuit in some detail and the
major changes to the flowsheet between 1992 and 1993+.
1.1 The SmeCter Flowsheet in 1992
In 1992, the srnelter complex operated individual nickel (Ni) and copper (Cu) circuits
(see Figure 1) which processed 2800 mtpd of nickel concentrate at 1 1-1 2 wtYo Ni, 2-3 wt%
Cu, and 1 O00 mtpd of copper concentrate at 28-30 wt% Cu, 0.8- 1 .O wt% Ni'.'. Nickel
* The evolution of the smelter flowsheet prior to the pend 1992-1993 is docurnented in the referenccs cited".
Chapter 1. Introduction L
I Bessemer Motte
I
Sem i- - cuzs + n -Blister+ Conc. Cu
Flash Nickel Sul fide I Converter
f
Converters lac3,CJ I Hot Metal Car
Nickel Oxide
Markets & Refineries Copper Refinery
Figure 1. The Copper Cliff Smelter flowsheet in 1992 operating separate nickel and copper production circuitsf.
concentrate was either flash smelted in the INCO flash furnace or was partially oxidized in
multiple hearth roasters and then smelted in oxygen-fuel fired reverberatory fumaces to
produce a matte of 30-35 wt% CuNiCo*. Furnace mattes were blown with air in Pierce
Smith (PS) converters for partial sulfur elimination and almost complete iron removal,
through oxidation and slagging, producing a sulfûr deficient nickel-copper white metal, or
"Bessemer matte". containing 75 wt% Cu-Ni and 22 wtYo S. Converter slags were reverted
to the reverberatory furnaces for cleaning and disposal while the Bessemer matte was sent
for M e r processing.
Cu-Ni matte was cast into molds in the matte processing plant and slow cooled to
promote the segregation of its constituent phases into grains of copper sulfide and Cu-Ni
alloy within a matrix of nickel sulfide7. Solidification of the matte into physically and
chemically distinct phases allowed for its crushing, grinding and separation into concentrates * Prior to 1992 nickel concentrate was processed solely by reverberatory srnelting'"
Chapter 1. Introduction 3
of nickel sulfide, copper sulfde and a Ni-Cu alloy containing precious metals. The nickel
products undenvent funher roasthghefining procedures while the copper fraction, a nickel
bearing chalcocite (6-7 wP! Ni), was sent to the copper smelter for oxygen flash convefling
to semi-blister copper.
In the copper production circuit, concentrate fiom ore flotation was oxygen flash
smelted to matte at 45-50 wt?? CuNiCo. Both matte and semi-blister were blown to blister
copper in PS converters and then nansferred via hot metai cars to the copper refinery where
the metal was cast, solidified and subsequently electro-refined to cathode copper.
W C 0 strategy's to meet production and environmental goals called for fewer SO,
emission sources. elimination of process redundancy and inefficiency, intensification of
process rates and improvements in copper smelting and converting pra~tice""~". Sulfur
containment in 1992 was achieved principally through the rejection of pyrrhotite to the mil1
tailings during mineral processing of the mined ore. At the nickel smelter, large volumes of
weak SO, gas streams were generated by the Herreshoff roasters. reverberatory fùrnaces and
nickel converters. Process redundancy was identified in the practice of separating copper and
nickel during ore beneficiation and at the matte separation stage while production limits were
imposed on both metals production circuits due to the processing of nickel in the copper
circuit. The presence of nickel in copper matte from flash smelting and in semi-blister
copper fiom flash converting introduced a nurnber of metallurgical challenges to converting
practice8. During the finishing blows to blister, excessive oxidation of nickel and copper
near the ruyere Iine of the PS converters resulted in the formation of a solid oxide or 'mush'
that separated by gravity to the melt surface. Accumulation of 'mush' between successive
converter cycles reduced the production capacity of the converten while accretions of the
refiactory oxides on the myere line interfered with punching procedures and air flow as
shown by Bustos et al9. Matte from the nickel smelter was periodically transferred to the
copper converters to 'washout' i.e. reduce the accrued oxides of nickel and iron, into a Cu-Ni
matte and a fluid slag which were recycled to the nickel smelter. Ferro-silicon additions
were made to every third or fourth washout to create stronger reducing conditions and affect
a more thorough rernoval of the oxides.
Chapter 1. Introduction 4
Washout procedures highlighted important deficiencies in smelter practice.
Reduction of the slag by the iron sulfide in the rnatte released sulfur dioxide into the
workplace environment while asynchronous production schedules in copper converting and
nickel smelting delayed m s f e r s of nickel matte to the copper converters and recycling of
washout products to the nickel h a c e s and converters. These recycles were an
encumbrance to the nickel circuit because the large transfers of copper upset the
metai lurgicd chemistry of nickel production.
1.2 The Smelter Flowsheet in 1993
The process and equipment modifications made by 1993 resulted in the smelter
flowsheet shown in Figure 2'".10.'1 . Impiementation of new production methods has
aiiowed INCO to maintain production levels of copper and nickel, resolve its metallurgical
problems in copper production and meet target SO, emissions. Bulk Cu-Ni Concentrate
-- S 0 2 - - - -
Flash Furnaces I I
C X I I Converters
I Bessemer Matte
v I I I 8 Semi-Blister Cu fi
Matte Seprrration I Alloy &
I Slag Nickel Sulfide
Nickel Sulfides I & Blister Cu
I Hot Metal Car Nickel Oxide
Copper Refinery
Figure 2. The curreat Copper Cllff Smdter flowsbeet af'îer impltmtntation of p m w and equipment modifications in 1993'.
Chapter 1. Introduction 5
Rationalization of ENCO's mil1 resources under the "SO, Abatement Project" has
simplified ore processing to produce a bulk copper-nickel concentrate. Oxygen flash
smelting of the mil1 concentrate yields a matte at 45-50 WO CuNiCo which is transferred
to PS converters and blown with air to a Bessemer matte. Preliminary cooiing of the
Bessemer matte is conducted in the converten with nitmgen injected through the tuyere line.
Cooled matte is transferred to the matte processing plant where al1 Cu-Ni separation takes
place afier matte solidification and segregation into its constituent phases via comrninution.
magnetic separation and colurnn flotation. The products of matte separation are metallic Cu-
Ni alloy. and concentrates of nickel sulfide and copper sulfide. Nickel products are sent for
funher refining whereas the chalcocite (MK) concentrate, now the sole feed for copper
production. is steam dried and then flash converted to semi-blister copper in the recently
developed MK flash reactor. The use of column flotation during matte separation has
decreased the nickel content in the MK concentrate fiom 6-7 wt % Ni to 3-4 wtYo Ni and
consequently has reduced the arnount of metals recycle to the smelter fumaces. Finishing
of semi-blister to blister is performed. in modified PS converters. by oxygen top-blowving and
enhanced by bottom stimng of the melt with nitrogen. The high strength, low volume. SO,
gis streams tiom the flash fùmace and flash converter are directed to the SO, plant for su1 fur
fixation while the development of sulfur-fiee washouts using Cu-Ni alloy and ferrosilicon
have Iargely eliminated fbgitive SO1 emissions fiom the finishing stages. The new washout
procedures have the added benefits of not king dependent on matte from the smelting
furnaces and the recycled washout products are more amenable to processing in the bulk
smel ting and Bessemer convert ing units.
1.3 Blister Copper Production from MK Concentrute
1.3.1 Oxygen Flush Converting of MK Concenîtute to Semi-Blister
MCO's experimentation with oxygen flash converting (OFC) began in 1947 as an
extension ro its flash fumace research program for primary snelting of sulfides". Initial
OFC trials on cornrninuted MK concentrate without flux additives produced molten copper
Chapter 1. Introduction 6
in addition to various oxides of nickel, copper and iron. Significant nickel oxidation
observed in these experirnents presented a metallurgical barrier against commercial
application of OFC to MK concentrate at the time. OFC testwork renewed at MC03
research facilities in the late 1970's and early 1980's successfûlly smelted concentrates with
mineralogical and chemical compositions ranging fkom pure chalcopyrite to chalc~cite"-'~.~~.
An important result of these experiments was ihat nickel oxidation could be minimized by
practicinp OFC at hi& temperature and recovering al1 the nickel in sulfur saturated copper
or semi-blister.
Commercial ra le OFC of M K concentrate was impiemented at Copper Ciiff in 1985
using rnodified PS converters to process 250 mtpd of wet chalcocite cakes. at 74 wt% Cu,
4.2 wt% Ni. and 21 wtYo S into semi-blister copper at 2-3 wt% S and 4 4 % Ni. Ni0
formation and large temperature fluctuations were controlled by maintainhg 8% moisture
in the filter cakes and adjusting the oxygedfilter cake ratio accordingly. Desulfization of
semi-blister to blister in PS converten by submerged air injection via tuyeres yielded blister
copper at 100 ppm S and < 1% Ni.
The desire to increase energy eficiency and intensiQ process rates under the "SOz
Abatement Project" resulted in a new drying procedure for the MK concentrate and the
development of a new flash procedure and a flash reactor with a greater production
capacityiO.'". Current practice is to dry 725 mtpd of fine nickel containing chalcocite to
4 0.2% moisture in a Myren multi-coi1 strearn dryer operated at 483 K. T%e dried
concentrate is fed through two burners near each endwall of the MK flash reactor, a
cylindrical vesse1 18 m in length by 4.5 m in diameter, and flash converted to produce semi-
blister and a hi& strength S 0 2 gas strearn. Nitrogen sparging of the rnelt, via porous plugs
on the reactor bottom, enhances mixing conditions and allows for oxygen utilization
efficiencies of up to 90%. The semi-blister, a mixture of white metal and metallic copper.
with an aggregated S content of 2-3 wtYo S and 3-5 wt% Ni, is transferred to the Multi-
Purpose Vesse1 (MPV) for M e r desulfurization to blister while the SOL gas Stream is
directed to the acid plant for fixation to sulfùric acid.
Chapter 1. Introduction 7
L3.Z Finish h g of Semi-Blister ?O Blister
Although nickel oxidation was controlled during OFC it persisted in the finishing
procedures of 1992. Oxide production and accumulation in the converten were attributed
to the variable mixing conditions generated in the melt From submerged air injection via
tuyeres". in the vicinity of the tuyere line the injected air oxidized substantial quantities of
nickel and copper and only provided adequate agitation of the melt in this regi~n"-~~-"?
Under these mixing conditions the oxides could not be redigested sufficiently into the melt
and either separated out to the melt surface due to density differences or accreted on the
tuyeres and other converter surfaces. The use of air as the oxidizing gas also limited the
amount of sensible heat available for melting anode scrap.
Themodynarnic analyses of the temary Cu-Ni-S and Cu-Ni-O systems by MC0I9
indicated that under equilibrium conditions it was possible to selectively remove sulfûr as
S 0 2 with minimal nickel oxidation and subsequently separate nickel fiom the melt as Ni0
wi thout significant copper oxidationl l . MCO's pilot testwork on semi-blister melts top-
blown with oxygen and bottom stirred with nitrogen via a porous plug produced blister
copper at near chemical equilibriumH. Concurrent washout experiments developed a new
procedure using a Cu-Ni-Fe-Si alloy, with a Cu:Ni weight ratio of 3-4. to reduce oxide
accretions into a Cu-Ni alloy of the sarne Cu:Ni ratio as the washout medium. and a fayalite
slag containing 1 wt% Ni and 0.5 wt% Cu.
Industrial application of these procedures depended on vessels that could provide
uniform agitation of the melt and uninterrupted oxygen delivery. These requirements were
satisfied by the INCO MPV (see Figure 3). a tuyereless PS converter, 10.7 m in length by
4 m in diameter, retrofitted with an oxygen lance in each endwall and five porous plugs* with
a preset permeability to nitrogen in the reactor bottom. Natural gas bumen coupled to the
oxygen lances are fired during washouts to create reducing conditions and sustain the
reaction temperature at 1573 K. Two MPVs are operated at al1 times and altemate between
processing semi-blister or holding Cu-Ni alloy at temperature in preparation for later use in
washouts.
* A later modification to the MPV increased the number of porous plugs fiom five to six".
Chapter 1. Introduction 8
Figure 3. The lNCO Multi-purpose vesse1 (MPV) for fmisbing of semi-blister to blister1.
Desulfurization is performed by top-blowing oxygen at 5300 Nm3/hr while the melt
is stirred with nitrogen injected at a rate of 14 ~rn ' /hr /plu~. Tonnage oxygen, utilized near
85% efficiency, also provides excess heat for melting cold anode scrap. Disposable oxygen
probes monitor the oxidation state of the melt to determine the endpoint of blowing and
prevent overoxidation of the molten copper charge. Bottom stimng with nitrogen enhances
the process kinetics by providing unifonn mixing conditions in the bath. This method of
agitation was borrowed fiom the ferrous industry where it is applied to ladle refining
procedures to accelerate thermal and chemical homogenization of the melt and the kinetics
of the refining reactions". MCO's adaptation of bottom stimng to copper smelting and
converting represents the first application of this technology to commercial copper
produ~tion'~. ' '. The MPV converts 135 mt of semi-blister at 2-3 wtYo S. 3-5 wtYo Ni into blister at
0.6 wt% Ni, 70 ppm S. and 1 wt?! O at temperatures between 1493 K and 1573 K. About
25 mt of copper scrap is also added into the reactor during the converting procedure. Sulfur
Cha~ter 2. Introduction 9
Figure
Time (minutes)
4. Process curve of sulfur for tbe iNCO MPV'9J0. Stage 1 sulfur elimination is perCormed by oxygen top-blowing and enhanced by nitrogen stimhg. In Stage II, oxygen injection is terminated while nitrogen agitation of the melt is continued.
elimination fiom roughly 2 wtYo S to 70 ppm S, occurs in two stages (see Figure 4) of
approximately equal process time; the second stage having a lower rate of desulfù~ization'~".
A change in the rate of sulfùr elimination is observed to occur at a s u h r content of 300 ppm
which corresponds to oxygen saturation (roughly 1 wt% 0) and partial oxidation of the
nickel values in the melt. Industrial practice is to teminate the oxygen top blowing at 300
ppm S in the belief that the oxygen dissolved in the melt is more than suficient to oxidize
the remaining sulfur. Nitrogen bottom blowing through porous plugs is continued at that
sarne rate during the second stage of finishing. At the end of two finishing cycles, 150 t of
washout aIloy with a Cu:Ni ratio of 3 is transferred from the holding MPV to the finishing
MPV along with 15 mt of 15 wt% Si ferro-silicon. The oxy-fuel burners are fired at 70%
Chapter 1. Introduction 10
stoichiometric oxygen to maintain the process temperature at 1573K and create a reducing
atmosphere that minimizes alloy oxidation. The reduction process is assisted by nitrogen
injection into the bath and produces slag and excess alloy which are bled to the bulk smelting
circuit.
1.4 Research Objectives
A project was commissioned at McGill University in 1993 by INCO as part of an
effort to improve the process kinetics in second stage converting. Its purpose was to
determine if sulfur elimination is impeded by the formation of oxide impurities such as Ni0
since this species is themodynamicaily stable at oxygen saturation and at the concentration
of the impurity encountered industrially. The role of surface phenomena such as the
Marangoni effect during desulfùrization was also to be exarnined given the presence of two
surface active agents i.e. S and O in the melt.
The influence of nickel on desulfurization kinetics was to be evaluated by comparing
the rates of sulfur elirnination in copper-sulfur melts both in the presence and absence of Ni
in the bath. Surface phenomena were to be examined under quiescent melt conditions in
order to facilitate their observation and also provide an indirect evduation of bath mixing to
desulfiirization kinetics.
Chapter 2. Literature Review I I
Copper extraction fiom sulfide concentrates encornpasses pyrometallurgicd
procedures such as reverberatory srnelùng, INCO and Outokumpu flash srnelting, the
Isasmelt top-blown process, the Vanyukov bath smelting process and the Noranda and
Mitsubishi continuous processes. These production methods are differentiated by the s h a p
and size of the reactors, the delivery mechanism of concentrate, flux. reverts, recycle slag and
of aidoxygen mixtures to the melt during smelting and converting, the ancillary operations
applied after each process stage to recover valuable by-products, and in copper refining
procedures. Continuous copper production is m e r distinguished by the combination of
several process stages into one.
In spite of the number of production routes copper pyrometallwgy is basically
separated into three process nages: smelting, converting and refining. Industriai interest to
optimize these stages has generated studies regarding the kinetics, thermodynarnics and
thermochemistry of copper extraction. Kinetic studies relevant to the present investigation
are those involving the oxijation of copper rnatte and copper-sulfur alloys by top-blowing
of oxygen-inert gas mixtures while submerged gas injection and vacuum refining procedures
are also considered here. The role of surface active elements and other surface phenornena
on reaction rates are alço examined fiom the perspective of the Cu-S-O, Cu-Ni-S and Cu-Ni-
O systems.
2.1 Thermodynamics and Tlrermochemisby of Copper Convettfng N C O k finishing procedure resembles the final part of the copper making stage of
most converting operations and therefore a brief review of conventional copper converting
is presented below to highlight the thermochemical considerations of the M C 0 process.
2.1.1 Con ventional Copper Con verting
Copper converting is usually regarded as the production of impure metallic or
'blister' copper by the seqxntial oxidation of iron sulfide and copper sulfide in smelter
matte. This procedure is most often performed in a Pierce-Smith converter (4 m ID x 9-1 1
Chapter 2. Literature Review 12
m length) by submerged injection of air or oxygen-e~ched air (23-26 vol. % 03 into the
melt at 500-700 Nm3/minute through water cooled tuyeres spanning the inner length of the
reactor. A typical converter cycle processes 200-500 mt of matte at 1473 K and produces
100-200 mi of blister copper with by-products of iron-silicate slag and effluent gas bearing
s u l h dioxide as surnrnarized by the unbalanced reaction":
The matte is converted in two distinct stages made autogenous by the exothermic oxidation
of its sulfide components of which the themodynamics and phase relationships have been
detailed el~ewhere""~. In the initial slag-forming stage iron sulfides are oxidized to FeO.
Fe,O, and S O while silica flux is added in with the iron oxides to increase their fluidity and
hence facilitate their removal during slag tapping procedures. The impure Cu,S or -white
metal' end product is subsequently oxidized in the copper-making stage to blister copper by
the overall reaction" : :
The phase relations of copper-making are described by the temary Cu-S-O system yet a
simplified representation of Cu2S oxidation to blister copper can be made with the binary Cu-
S phase diagram (Figure 5). The initial oxidation of Cu2S (Point A) produces SO, and a
sulfur deficient white metal containing 19.7 wt% S by the reaction":
C u 2 + xo, * Cu$, - + xso,
When the melt composition reaches the Cu-Cu$ miscibility gap (Point B) a blister copper
phase containing 1 wt?A S is produced which increases in proportion to the white meîal with
continued melt oxidation. Beyond this imrniscibility region (Point C) sulfur exists only as
a dissolved species in blister copper and its continued removal takes place by its reaction
with dissolved oxygen (Equation (4))". The relationship between the activity of sulfur and
'AG0 for Cu,S oxidation was derived fiom a linear regression of the thermodynamic values obtained ktween 1403 K and 2000 K using Outokumpu's HSC Chemistry Version 1.10 thermodynamic software.
oxygen is one that is mutuaily inversed and therefore at the endpoint of convening (Point D)
the blister copper contains 0.001-0.03 WO S and 0.1-0.8 wt %O. Although fùrther
desulfurization may take place with continued blowing the procedure is terminated to prevent
copper oxide formation by Equation (5)" .
1
900 1 I I
5 s 11 73
IO 15 20 Cu tus
Mass % S Figure 5. The Cu-S phase diagram showing the oxidation path of Cu,S to blister Cu
during conventioaal coaverting accorâing to Biswas and Davenport". The sbaded region depicts tbe operating zone of the INCO finishing procedure.
2.1.2 Copper Con verting a! INCO
As mentioned in Chapter 1, WC0 processes a sulfur-saturated copper melt (- 2 wt%
S) or 'semi-blister' containing significant nickel values (- 4 wt %Ni) into blister copper (100
ppm S , 0.6 wt% Ni) at 1523 K - 1573 K in a two stage procedure in which the first is
Chapter 2. Literature Review 14
operated with oxygen top-blowing and nitrogen stirring of the melt and the second with only
stimng of the bath by injected nitrogen. The procedure was developed on the basis of a
thermodynamic analysis conducted by INC0I9 which sought to minimize 'mush" formation
and maintain nickel levels in the final blister product within acceptable tolerances for
subsequent copper electro-refining. It was found that under equilibnum conditions, sulfur
cm be removed fiom semi-blister at elevated temperatures by oxidation to S R with minimal
nickel oxidation and significant oxygen dissolution in the meit. Upon cooling, the dissolved
oxygen reacts with dissolved nickel to f o m Ni0 which separates fiom the melt with minimal
copper oxidation and/or entrainment and thus lowers the nickel concentration of the melt to
desirable levels.
The relevant thermodynamic information relating to conversion of semi-blister can
be obtained from published literatwe on the C u-Ni-S"-j5 and Cu-Ni-O s y ~ t e m s ~ ~ ? Larrain
and Lee3' calculated the phase relationships and isoactivity lines for Ni and S in the Cu-Ni-S
system which were largely corroborated by Chuang and Chang5 and are shown
superimposed for the copper-rich region at 1473 K in Figure 6. Taskinen's" compilation of
various isothems in the Cu-Ni-O system in addition to Kwmann and Riecke's3' data are
presented in Figure 7 which reveal the strong temperature dependence of O and Ni
solubilities in copper.
iNCO determined the degree of Ni and S oxidation in the copper rich region of the
phase diagram by combining the activity data fiom the Cu-Ni-S diagram with the fiee
energies of formation5' of N i 0 and SO,:
t 'Mush' in the MC0 vernacular refers to a c i q slag layerldross consisting of copper oxides and nickel oxides that is fonned during conversion of semi-blister.
Chapter 2. Literature Review 15
Figure 6.
Figure 7.
W t % Nickel
Tbe phase rehtions of tbe copper-rich region of the Cu-Ni-S phase diagram at 1473 K sbown superimposed on the isoactivity line o f Ni and S according to Larrain and L d 9 ?
Tbc pbase rcîations and various isotherms o f the copper-rich corner of the Cu- Ni-O system according to ~ a s k i n e n ~ and Kuxmann and R ~ W L ~ Y Tbe a m s trace the oridation patb followeâ by nickel during the INCO finishimg procedure".
Clza~ter 2. Literature Review 16
If PSO, is assumed to be 0.20 atm (2 x 104 Pa) while Ps2 and Po+ are the equilibrium partial - pressures of sulfur and oxygen, then the sulfûr content of a semi-blister melt at 1473 K can
be reduced to below 0.2 wt % before Po* becomes sufficiently high to cause Ni0
fomiati~n'~. The Cu-Nb0 diagram shows that sulfur-fiee copper at 1573 K containing 3 wt
% Ni can dissolve upto 0.6 wt % oxygen (Point A) before any nickel oxidation takes place.
Continued oxygen dissolution at 1573 K increases the oxygen content and decreases the
nickel content of the copper. At point B the dissotved oxygen content of the copper reaches
1.1 wt% which is suficient to lower the nickel content of the meit to 0.6 ut %, without
oxidizing copper, by cooling the melr to the casting temperature of 1423 K ' ~ .
The composition and temperature profiles of the melt from a pilot plant test of the
finishing procedure are shomn in Figure 8. A holding period of 30 minutes was incorporated
into the MC0 conversion technique to approach equilibrium because early test results
indicated that some copper had oxidized in spite of vigorous melt stimng -<th nitrogen.
Cooling the charge to the casting temperature of 1423 K was accomplished by adding cold
anode scrap to the melt which was found to be more rapid than natural cooling and did not
affect the elimination of nickel as NiO.
t 8
Blowing Holding
, I
Time (miautes) Figure 8. The composition and temperature changes experienced by the copper charge
during a pilot plant test of the INCO finishing procedure".
Ch apter 2. Literature Review 17
2.2 Cas-Liquid Interactions A rate process involving two immiscible phases which are not in chemical
equilibriurn with each and are brought into contact can be regarded as the following series
of mass transport and chernical reaction steps between the reactant species of each phasej9.10:
1 ) Difbion of the reactant species h m the bulk of their respective phases and through a boundary layer to a gas-liquid or liquid-liquid interface.
2) Chernical reaction at the interface which includes absorption. adsorption, dissociation or activated complex formation.
3 ) Diffusion of the initial reactants and/or reactant products away fiom the interface-
The sum of the three steps determines the overall rate of reaction while the step providing
the most resistance is considered to be rate controlling. In higher temperature processes.
where near chemical equilibrium exists at the reaction interface, diffusion of a reactant in the
liquid and/or gas phase is ofien the rate limiting step while in lower temperature systems the
chemical reaction may exercise al1 or joint control over the process rate.
Mass transfer rates between two fluid phases such as in gas-liquid metal systems
depends on the physical properties of the phases, on dynamic conditions in the reaction
system and on the concentration driving force that is equivalent to the difference between the
equilibrium concentration and effective bulk concentration of the bulk liquida'. A reactant
gas species may contact a liquid metal either by difhsion through a stagnant gas phase or by
convection when it is part of a larninar or turbulent gas jet that is either blown ont0 the liquid
metal surface or is injected into the melt.
The mass flux of any system can be related generally to the kinetic and
thennodynamic influences of the system according to the following equation:
here n " is the mass or molar flux per unit area, kW is the overall m a s transfer coefficient and
Ch apter 2. Literature Review 18
AC is the concentration driving force in the liquid phase. Although useful kinetic data C ~ I I
be derived fkom diffusion controlled studies. indusaial pyromeiallurgical procedures usually
involve convective contact between the gas phase and the melt Ferrous and non-ferrous
processes both make use of submerged injection and top-blown procedures of which the
physical behaviour of the injected gas and the flow regimes established in these reacton have
been modelled at low ternperat~re~"~~. Combining this information with available thermo-
chemical data can yield mass transport relationships defined in terms of dimensionless 4 t .57& groups which consider the transport, dynamic and geometric properties of the system -
in togblown systems the gas jet impinging on the liquid may experience starvation
of its reactant species. When this condition arises the mean gas pressure in the bulk gas
above the liquid surface is reduced to a value less than the pressure in the jet. Therefore,
analysis of kinetic data must recognize whether starvation has occurred othemise mass
transfer coefficients may become unreliableS7.
2-21 Top Blown Gas Injection with High Momentuni Jets
Gas impingement on a liquid can generate several modes of flow between the phases
depending on the gas velocity and the angle and position of the lance above the liquid
surface. Molloy4' identified three main modes according to the observed surface effecrs:
dimpling, splashing and penetrating which are depicted in Figure 9 and show the change in
shape of the surface depression fiom a parabola or semi-circle to a U-shape with increasing
jet momennim". A low jet velocity or large lance height between the liquid and impinging
$as creates a dimple or slight depression on the liquid surface (Figure 9(a)). Increasing the
gas momentum by reducing the lance height or increasing the gas velocity leads to a critical
depth of depression which if exceeded results in the entrainment of liquid in the s h a c e
indent followed by its outward ejection signalling the start of spiashing (Figure 9(b)).
Further increases in gas momentum eventually results in deeper p e n e m i o n of the liquid
phase by the gas Stream which is accompanied by a reduction in the volume of ejected
material (Figure 9(c)). Two consequences of increased jet momentum account for this
Chapler 2. Literature Review 19
behaviour: an increased proportion of the gas jet is reflected back into itself while the
remaining portion of the reflected gas not entrained in the incoming jet follows a longer
trajectory dong the periphery or lip of the depression4'.
HL. depth of caviry Ho lance heighr M, jet momentum p, density of liquid phare g gravist k,!* jet constant for momentum transjër
Figure 9. (a) Dimpüng of a muid suriace by a low momentum gris jet. (b) Increasing the jet momentum beyond a critical value results in splashing i.e. ejection of material from the impingement area. (c) At high jet momentum tbe gas penetiates the liquid multing in a lower volume of ejected material. (d) Schematic depiction of the geometric mode1 developed by Wakelia and the ensuing dimensionkss relationshipu.
Although most industrial top-jetting processes operate in the splash or the penetration
regime investigators modelling these procedures at hi& temperature have operated under the
critical zone because flow patterns and interfaciai areas can be desfribed by reaction models
such as Higbie's Penetration Theoryu. In top blown batch processes such as iron
decarburization and copper desulfunzation by oxygen, m a s transport control altemates
between the gas phase when the impurity level in the liquid phase is high and the liquid
phase when the concentration dnving force in the bulk liquid drops to a small value.
Wakelinm and Loheu provided the basis for determining the gas-phase mass transfer
coefficient from low temperature models in which jets of air or CO2 with a momenturn of
0.08 N were blown on the surfaces of mercury and water. The Wakelin mode16' depicting
the geometry of the impingernent area shown Figure 9(d) was used to correlate the measured
Shenvood nurnber (Sh) to the Reynolds number (Re) and Froude number (Fr) a?:
Sh = a[Re(l + Fr)]" (9)
where a = 6.57 and n = 0.43 for air impinging on water. Schmitt and Wuth4' also developed
an empirical m a s transport relationship with the Shenvood nurnber for top-blomn systems
at hi& temperature when the jet momentum was 0.3 N and mass changes occurred only in
the liquid phase:
I l l . ( i s ~ ~ 0 . 6 7 ( , . / h 10.29 Sh = K'Sc 1.75[~e(l + K )] b b (10)
In the above equation K ' and K" are dimensionless constants, and rJh, is the ratio of the
bath's radius to its depth. The authors expressed the dimensionless groups in order of
dccreasing importance and found that the Schmidt nurnber, Sc, containing only the transport
properties of the metallurgical system, had the strongest effect on mass transport while the
dynamic and geometric factors were less influential.
2.2.2. Top BIown Ga Injection with Low Morncntum Jets
Rate measurement relationships developed for hi@ momentum gas jets cannot be
rxtrapolated to low momentum jets without incurring significant e m r . ~ l y m P 6 reviewed
Chapter 2. Literature Review 21
mass transfer studies by Kikuchi et ale6'-"' in which low momentum gas hpingement in low
and high temperature systems was investigated; in both cases the correlation of Sh to the
dimensionless groups were similar for the system parameters defmed in Table 1.
Table 1. Parimeters o f the experimeatal systcm used by ~ikuchi"-'~ et al. accordiog to ~ i y - i w .
Systems Investigated Re Sc H4d, f/d, do (X le m)
--
Low Temperature 13-1 500
Napthalene-N, Toluene-N, Acetic Acid-N2 Water-N,-NH,
High Temperature
Graphite-CO-COz 0.57-0.93 1 5 6 . 3 1.4-3.1 0.4- 1 -3
Liquid Fe-CO-CO, 0.57-0.9 0.8-1 -5 1.4-2.9 0.66- 1.3
At low temperature the effect of nitrogen impingement on the sublimation of napthalene or
the evaporation of toluene, water or acetic acid was expressed as6%
where rs is the radius of the reaction area and d is the inner diameter of the lance. The hi&
temperature oxidation of graphite and decarburization of iron by CO-COI gas mixtures
yielded the following respective re~ationships~~:
It was concluded that the gas-liquid reaction rate was controlled by resistance in the gas-
phase mass when the exponent for the Reynolds number was between 0.66 and 0.76~~.
Chapter 2. Literature Review 22
2.3 Inrerfcial Phenornena
2.3-1 Surjiace Active Solutes and Surjke Tension
Within a liquid. attractive forces are exerted on each molecule by its surrounding
neighbours. When the liquid is partitioned to create a gas-liquid interface. the surface atoms
lose half their neighbours and there is a tendency t~wards minimum surface area because of
a net inward aîiraction acting on the surface atorns7'. The work associated with surface area
rninimization or the surface tension (O) is governed by the strength of intermolecular
attractions in the liquid. Strong intermolecular attractions lead to hi@ surface tensions.
molar heats of vaporization, ùoiling points. and viscosities.
Strongly adsorbed solutes on the liquid surface, an applied potential or changes in
temperature can al1 affect the interactions between surface molecules". A surface active
solute can decrease the surface tension of a liquid with increasing solute concentration
(20/UCs>O) when it is positively adsorbed (rs > O). i.e.. when it is in excess on the surface
relative to the bulk (see Figure IO(@) while the converse (OulaC, < O) applies when the
solute is negatively adsorbed (rs c O) (see Figure 10(b)). Systems which exhibit
electrocapillary behaviour such as amalgam-electrolyte and liquid metal - fused salts
experience changes in interfacial tension as seen in Figure 100 when a potential is applied
at the interface.
Most swface active solutes in liquid metals adsorb positively on the melt surface.
The Group VIb elements, i.e. O, S. Se, and Te, are the most cornrnonly encountered solutes
lowering interfacial tension in ferrous and non-ferrous pyrometallurgical refining
procedures''. Elevating the temperature of a liquid metal solution containing a positively
adsorbed solute increases its swface tension. These effects are illustrated respectively for
oxygen and sulfur dissolved separately in liquid copper at various temperatures in Figure
1 1 (a) and Figure 1 l(b). Both figures also show that the effect of solute concentration on
surface tension becomes less pronounced at higher temperatures.
Chapter 2. Literature Review 23
Figure 10.
(Ji
ab
(J i
b
Solute Concentration
Solute Coircentration
(b)
- Pottatial (+) E, (O) Poteatirl - (cl
Types of adsorption behaviour obseived at liquid-metal interfaces (a) positive adsorption (b) negativt adsorption (c) ciectrocapillary behaviour, according to Brimacom ben.
Ch apter 2. Literature Review 24
[ O ) (wt %)
Monma & Suto
----- Bacs & Kellog
- - - O 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1.0 1.1 1.2 1.3
[S) (wt V o )
(b)
Figure 11. Effect of (a) dissofved oxygen and (b) dissolved sulphur on the surface tension of liquid copper nt various temperatures according to Moama and Suto".
Ch apter 2. Literature Review 25
The acc'mulation of s d a c e tension data for a liquid metal is u s d l y perfonned by
measuring the dimensions of a sessile liquid drop resting on a horizontal surface over a range
of solute compositions and temperature. Applying this data to the Langmuir and Gibbs
adsorption isotherms yields a relationship between the activity of the solute and the
depression in the surface tension of the liquid metal solution. in the simplest case of a single
chemisorbed solute, 1, the Langmuir adsorption isotherm describes the fractionai coverage
0, of the liquid surface as7':
where a, is the activity of the solute I and K ,is a temperature dependent equilibrium or
adsorption coefficient. The appropriate form of the Gibbs isotherm providing the surface
concentration or adsorption of the solute is7':
where a is the surface tension, r, and r, are the adsorptions of the bulk phase A and solute
B re~pectively~ X, represents the atom fraction of the two components in the bulk phase and
pH is the chernical potential of B. Under strong adsorption behaviour Equation (1 5) can be
where r," is the temperature independent adsorption at full coverage. Substituting for 8, from
Equation (1 4) and integrating yields in the limiting case of a pure so1vent7?
Chapfer 2. Litercrture Review 26
where d and o are the surface tensions of the pure metal and alloy. For a strongly adsorbed
solute. I;' can be obtained as the linear slope fiom a plot of a vs lm,.
Equilibrium surface concentrations on iiquid m e t . interfaces can be established
almost instantaneously. A simplified form of the diffusion equation:
where n is equal to the surface excess, C is a constant concentration gradient between the
interface and bulk liquid and D is the difi ivi ty of the solute. was used by Richardsonz to
demonstrate that the equilibrium surface concentration of oxygen in liquid iron is reached
within 10-' to IO*' second even when oxygen was present at one-tenth its bulk saturation
concentration.
The above treaunent considers ideal adsorption of a solute on a liquid metal surface
consisting of equivalent sites. Deviations fiom this behaviour arise when there are attractive
or repulsive interactions in the adsorbate or other competitively adsorbed solutes present.
Sun and Bel t~n '~ reported that in the liquid Cu-S system repulsive interactions in the
adsorbate led to more rapid than expected coverage of the liquid copper surface with
increasing sulfûr concentration. Negative deviations fiom ideaiity observed by Gallois and
Lupis7? in the liquid Cu-O were ascribed to attractive forces acting between the adsorbed
oxygen atoms. The contrasting behaviour of various adsorbates may be related to differences
in the structure of the surface layer and size of the adsorbed atoms but an adequate model to
corroborate these assumptions has yet to be developed. The traditional model describes
surface saturation of a liquid metal substrate as close-packed coverage by a monolayer of
doubly charged anions (e-g. O?-, S", Se") however for the Ag-O and Cu-O systems surface
saturation by oxygen ions is less than close-packed and more consistent with coverage by a
two dimensional ionic compound with the stoichiometry M;O (where M = metal a t ~ r n ) ~ " .
Surface interactions are M e r cornplicated when two or more solutes are present
together because the effects are generally not additive and may be influenced unpredictably
by other non-active solute elements. Chromiurn and carbon in liquid iron are two non-active
Chapter 2. Literuttîre Review 27
solutes individually but when present together at low concentrations result in lowered
interfacial tension". Belton proposed that the interactions between two competitively
adsorbed solutes may be addressed by introducing a coverage dependent surface activity
coefficient into Equation (14) leading to a more pneral f o m of the Langmuir isotherm":
2.3.2 The Role of Surface Active Solutes on Reaction Rates
interfacial phenomena are not considered to affect thexmodynamic equilibria between
different phases but are known to influence the rates of interfacial chernical reactions the
extent which depends on the nature of the solute, its surface activity and mass transpon
conditions in the liquid*.
Mass transfer in most pyrometallurgicai r e f ~ n g procedures takes place under strong
mixing conditions and in the absence of surface active elements agitation of the melt
produces eddies which transport elements of fluid h m the bulk to the interface resulting in
constant renewal of the liquid surface" (see Figure IZ(a)). At the interface. mass transport
to and from the fluid elernent can occur by unsteady-state diffusion until it is displaced by
another eddy. Depending on the level of melt agitation the residence time of the eddy at the
interface can range fiom 104 second for vigourous stimng to approximately 1 second for
more quiescent condition^'^. Non-reactive solutes strongly adsorbed on the liquid surfaces
can reduce mass tramfer coefficients by blocking reaction sites at the interface and inhibiting
chernical reaction of less surface active solutes and by lowering the rate of surface renewal.
Under strong mixing conditions, the eddy surface during its lifetime at the interface may
remain free of adsorbed material but under gentle stimng it may establish the equilibrium
concentration of the adsorbed solute and hence interrupt mass transfer and chernical reaction
at the interface. Areas of reduced surface tension created by the adsorbed solute also
diminish reaction rates by opposing eddy dispersal at the surface Le. surface renewai, with
a force equal to the difference of the two surface tensions (see Figure 1 2(b)). At higher
solute surface concentrations and under quiescent conditions the number, fRquency and area
Chapter 2. Literature Review 28
of surface clearings decreases which can arrest both diffusional and eddy processes.
Figure 12. Surface renewal by eddies at interfaces: (a) no surface active material present (b) in the presence of surîace active material according to ~ ichardson~.
Darken and ~urkdogan '~ reviewed a number of gas-liquid systems where there is
strong chemisorption and found that the interfacial reaction rate was usual ly proportional to
the reciprocal activity of the interfering solute and that the limiting behaviour was consistent
with Langmuir adsorption with interfacial reaction occurring at vacant sites. nie apparent
rate constant, k,, for such an interfacial reaction in the presence of one chemisorbed solute
is described by7?
where at high surface coverage, i.e. K,a, >> 1, or when the concentration of a surface active
solute approaches bulk saturation equation 20 reduces to":
Chapter 2. Literature Review 29
Ln a multicomponent system having a nurnber of interfenng solutes with a fraction
of sites available oniy for reaction, Belton proposed a generalized f o m of the rate equation7':
where p represents the fraction of s d a c e available for reaction. 13elton7' approximated the
apparent rate constant for the adsorption of nitrogen in liquid u o n in the presence of oxygen
and sulfùr from Fruehan and ~artonik's" data by combining equations (19) and (21)
yielding under the assumption that y; = 1 :
Fruehan and Martoniks' aiso found that the kinetics of the same reaction can be increased
with the addition of chromium. a non-surface active solute. because of its ability to suppress
sulfur activity7'.
2.3.3 Surface Tension Driven Flow
Surface tension gradients in other instances can lead to surface turbulence which may
increase the rate of interfacial reaction kinetics. James Thomson correctly identified this
phenornenon in 1855 while investigating the motion of alcohol droplets on the surface of
wateP3. Surface tension driven flow or "Marangoni convection9' arises when a shear stress
develops dong a liquid surface and changes the motion of fluid dong the interface in the
direction of highest interfacial tension resulting in increased heat and mass transport. This
shear stress r,, expressed dong a direction x, asM:
Chapter 2. Literature Review 30
- do - a a d ~ au d~ do.@ $ - - - * + * - + - - ar dx ac dr a* dx
(24)
develops fiom gradients of temperature T, concentration of a surface active solute C in the
liquid or electrical potential $ between two liquids. however. in many systems the effect of
temperature is small unless the temperature gradients at the interface are very large7'.
Following Thomson's early experiments, Marangoni convection has since k e n recognized
to maintain foam film stability against hydrodynamic drainages5. influence the size. shape.
and properties of weldss6. enhance the rates of gas-liquid metal reactions that are transport
controlled in the liquid phase. i.e.. copper desu l fü r i za t i~n~~-~~ , nitrogen absorption in liquid
irons'. and cause local refractory corrosion in steelmaking fumaces by slag film motion above
the slag levelu.
Brimacombe and Weinberga9 Arst recorded the occurrence of interfacial motion in
liquid metals when a low momentum (< 6 x 10" N) oxygen jet was impinged on the surfaces
of liquid copper and tin. An oxide patch observed on the rnelt surface directly beneaih the
pas lance was seen to move radially outward fiom the center of the bath to the periphery of C
the liquid surface at hi& velocity (see Figure 13). The interfacial motion was attributed to
localized surface tension gradients between the oxide and surrounding metal caused by the
non-unifonn transfer of oxygen at the interface. Similar behaviour has been reported by
Lange and WilkenW for a number of low and high temperature two phase systems while
Barton and Bnmacombe's9' measurements of oxygen absorption in liquid copper credited
Marangoni convection with increasing mass transfer coefficients by an order of magnitude.
Other local sources of solutes are capable of invoking surface tension flow on b t h
the micro and macro-scale. In stirred melts, eddies carrying a positively adsorbed surface
active solute fiom the bulk phase to the melt surface can lead to micro-scale interfacial
motion due to the lower surface tension of the eddy fluid element relative to the surrounding
interface7' (Figure 14(a)). Convective motion can also occur fiom the dissolution of a
partially irnmersed solid b e c a w of resulting longitudinal surface tension gradients which
lead to movement away fiom the interface if the solute is positively adsorbed (ï, > 0) and
towards the interface if the solute is negatively adsorbed (î, < O)" (Figure 14(b)).
Chapter 2. Literature Revie w 3 I
Figure 13. Macmscale interfiacial motion o n the surface o f liquid copper geaemted by (a) the impingemeat o f an oxygen jet on the melt surface which leads to (b) radial spreading of the oxide patch a t high velocity towards the regions o f highest surface tension (c).
I
C;
" Liquid
D q q . ? p . 3 0 i l 5 r )
c - O
Figure 14. (a) Micro.sca14 interfacial motion genemted by tbe penetration o f eddies at the gas-liquid interface with a solute composition exceeding that o f the interface resulting in motion towards regions o f higher interfacial tension, according to ~ r i r n a c o m b e ~ . (b) Macrolscllie interfacial motion gcnernted by the dissolution o f a partial ly immersed solid rcsulting in liquid molion away from the solid- liquid interface when thete is positive adsorption o f the d u t e on the liquid surface and towards thc solid-liquid interface when tbere is aegative solute adsorption on the liquid surface according to rimac combe?
Chapter 2. Literature Review 32
Prediction of the onset of interfacial motion has been attempted with limited success
using hydrodynarnic stability analysis on gas-liquid systems involving aqueous and organic
soiutions by examining the ratio of the destabilizing interfacial tension force resulting from
mass transfer to viscous forces i.e. the Marangoni numberz:
In liquid metai systems where interfacial tension, liquid density and adsorption effects are
much greater it is more convenient to evaluate interfacial movement in terms of an initial
spreading coefficient, S. which in the case of oxygen blown on a liquid metal surface is
expressed asz:
where S must be positive for oxide movement to ocçur.
2.4 Oxidution Studies
Rate deteminations for the desulfûrization or oxidation of copper-sulfür melts are
often perforrned by thermogravirnetry, whereby the mass of the charge is recorded as a
function of time, by on-line analyses of the exiting reaction gases. through periodic chemical
analyses of the melt or by a combination of these methods. A cornmon observation in many
of these studies is the removal of sulfùr in two or three distinct stages: a slow and sometimes
variable initial desulfùrization stage followed by a dominant stage of relatively rapid sulfiir
elimination and ending with a final stage of decelerated desulfurization.
Ajench and Toguri" measured the oxidation rates of liquid copper sulfide by
thermogravimetry under gas diffusion control conditions and saw three distinct regions in
the desulfiirization cuve of Cu$ as it progressed to liquid Cu. An initial stage of variable
weight loss was attributed to the tirne required for the diffusing oxygen gas to esbblish
steady-state conditions. in the second stage as the melt composition entered the CL+,, - Cu,S,,,
miscibility gap region desulfunzation (weight loss) proceeded at a constant rate. When the
Chapter 2. Literature Review 33
copper sulfide phase was eliminated th2 meft continued to lose weight at a slower rate
although past a critical point continued oxygen delivery to the melt resulted in a net weight
increase due to copper oxide formation. Throughout the desulfunzation procedw the
composition of both liquid phases was assumed to be invariant and equilibriurn conditions
maintained through continuous mixing of the sulfide phase by the settling motion of the
denser liquid copper droplets. The mass-time curves of iron bearing matte oxidized under
similar conditions by Asaki et aL9' foliowed a similar path although the initial stage was
characterized by a m a s gain due to oxidation of the iron to iron oxide.
Fukunaka et al.93 bubbled &-O, gas mixtures into molten copper containing 0.74
ut% S and 0.01 wt % O at 1523 K and, as with Ajersch and Toguri". described an initial
penod of slow suliùr removal, followed by an intewai of rapid sulfw elimination that ended
with a period of decelerated desulfurization. in both the first and third stages. the slower
desulfûrization rate coincided with significant oxygen dissolution in the melt. Gas flowate
( 1 x 10'' m'k to 2 x 10" mS/s). oxygen partial pressure of the gas Stream (1 0 kPa ro 30 kPa)
and lance immersion depth in the melt (0.018 m to 0.033 m) were al1 varied to determine
their effect on the rate of desulfunzation. Higher gas flowrates and oxygen partial pressures
in the injected gas increased the rate of the second stage and shortened the duration of the
initia1 stage while changes in the lance immersion depth negligibly afTected these rates. in
the vicinity of the lance. it was assumed that oxygen was conswned by the two elementary
reactions:
and that equilibrium was reached between the sulfùr dioxide in the gas bubbie and the
composition of the melt. A mode1 describing mass transfer around a single gas bubble
suggested desulfûrization was controlled by mass tmnsfer in the $as boundary layer and
therefore the rates of the above reactions were detemined by the rate of oxygen supply into
the melt. The authors also observed some desulfurization during melting of the copper alloy
Chapter 2. Literaiure Review 34
which made the starting concentration of sulfùr a variable between each test. ~ h n o ' ~
confinned that considerable desul furization and deoxidation can occur fiom Cu-S-O al10 ys
during melting or solidification. Alloys of varying O and S concentrations were inductively
melted between 1373 K and 1573 K under a vacuum or an argon atmosphere (PA, = 6.5 kPa
to 10 1 -6 kPa) or were solidified and then remelted under argon ( P , = 1.33 kPa to 102 kPa)
and then chemically analyzed for O and S. In al1 circumstances. the observed weight change
ratio between sulfur and oxygen was very close to one indicating suifur and oxygen were
eliminated as S02. Under vacuum melting, the rates of sulfur and oxygen removal could be
expressed as a first order rate equation while their rate constants could be determined with
respect to the inverse of temperature. However under an inert atmosphere. desulfunzation
and deoxidation showed a dependence on dissolved S and O concentrations but not on argon
pressure. Most S and O elimination was believed to take place during melting or
solidification of the alloy when the equilibrïum S O pressure becomes much higher than the
applied argon pressure. These findings agreed with Floe and Chipman'sg5 solubility study
of sulfur dioxide in rnolten copper and Knacke and ~ r o b s t ' s ~ work conceming the
solidification of copper melts saturated with SO,. Floe and Chipman arrived at an expression
relating the equilibrium pressure of SO, to temperature and the sulfbr and oxygen
concentration of the melt9':
Ohno applied this equation at a nurnber of soiute concentrations in the temperature range of
1373 K to 1573 K to demonstrate that SO, formation is favourable even at low solute levels.
In Knacke and Probst'sW experiments, copper melts cooled at various rates (0.2
Wmin to 5 Wmin) continuously expelled sulfûr dioxide until the liquidus temperature
( 1 353K) cf copper was reached; M e r cooling to 100 K below the melting point of copper
resulted in a sudden evolution of the remaining gas. Ohno wimessed a similar phenornenon
in the form of vigorous boiling during alloy solidification and referred to the equilibrium
diagram presented by Knacke and Probst showing the variation of the sulfùr dioxide pressure
Literature Review
in equilibriurn with solid copper. copper sulfide, copper oxide and the liquidus c w e of
copper (see Figure 15). huing liquefaction of a Cu-S-O alloy, the pressure of sulfùr dioxide
increases to above 600 kPa and then drops dong the liquidus curve of copper with increasing
temperature: during solidification the solutes are concentrated in the remaining molten
materiai and the pressure of SO, increases similarly.
Temperature (K)
Figure 15. Variation of tbe sulfur dioxide pressure in equilibrium witb Cu,,,, Cu,S, Cu,O and the liquidus cuive o f copper?
In Rottrnan and Wuth's9' top blown conversion expenments. gas jets of varying
oxygen composition were delivered through a lance fitted with a laval-type nozzle onto 2kg
bath of molten copper matte (65 wt?! Cu. 14 wtYo Fe and 21 WWO S) at temperatures up to
1873 K. By fixing the lance position at 0.07 m above the unstirred melt the oxidizing gas
exited at super-sonic velocities with suficient momentum to stir the liquid phase without
invoking splashing. Under these conditions the authors concluded the rate-controlling step
during conversion was diffision of the reaction gases through the viscous sub-layer of the
impinging gas jet. Mass changes in the melt revealed two periods of desulfurization each
proceeding at a distinct rate. In the first period constant oxygen dissolution into the melt was
Chapter 2. Literature Revie w 36
accompanied by simultaneous reaction of oxygen diffusing through the gas boundary layer
at the gis-liquid interface. ï h e authon postulated that sulfur was removed by the reaction
of the dissolved oxygen with sulfûr in the liquid phase in conjunction with the direct reaction
of oxygen in the gas phase at the gas-liquid interface. When the melt became saturated with
oxygen (- 0.6 wtYo O). the desulfùrization rate increased to roughly twice the rate observed
in the first period and was accompanied by slag formation and increased turbulence in the
gas phase due to SOZ evolution at the melt surface. Although slag coverage reduced the - surface area available for reaction, a comparison of the oxidation rates of white metal and
iron bearing matte showed no significant difference. indicating mass transfer was taking
place primarily in the vicinity of the surface depression caused by the gas jet.
Top-blown conversion experiments were also perfonned Bryukvin et al?* at 1473 K - 1673 K using synthesized Cu$ melts (5 x 1 O-' - 2 x 10') kg), instead of matte. and oxygen-
nitrogen gas mixtures (12 - 30 vol.% 02) blown at a fixed rate of 1.67 x IO4 m'ls. Two
distinct regions were observed in the mas-time curve of the melt samples: an initial stage
of comparatively low mass loss followed by a secondq stage of accelerated mass toss.
Although the desuliùrization rate generally increased with reaction zone temperature and
oxygen partial pressure, the initial stage was more influenced by temperature whereas the
secondary stage was more a!Tected by gas composition. The transition to secondary stage
desulfùrization occurred. as with Rottrnan and Wuth, at a certain degree of melt oxidation
although this value was not specified. Increased rates of mass loss in the secondary stages
were attributed to metdlization of the melt and evolution of dissolved oxygen from the bath
through the decomposition of oxysuifide phases. The reaction kinetics were found to be zero
order with respect to the sulfur concentration of the melt but not to the temperature and
oxygen partial pressure of the gas jet. The desulfurization mechanism in both stages was
correlated to activation energies calculated for the primary and secondary oxidation stages
at different bath temperatures. At 1473 K, the higher activation energy of the first stage was
associated wi th chemisorption of oxygen ont0 the melt surface whereas the lower activation
energy of the second stage was characteristic of diffusion. tn experiments performed at
1673K, the difference between the activation energies was less pronounced implying that the
Chapter 2. Literature Review 37
distinction between the two stages is diminished at higher temperatures and mass fransfer
becomes dependent on the mixing conditions of the melt.
J~ i lkanen~~ sou@ to determine the phenomenology of oxidation of molten copper
sulfide at 1423 K - 1623 K. Temperature. gas velocity. oxygen partial pressure were varied
in addition to the Cu:S molar ratio of Cu$ which ranged between 1 -875 to 2.30. Gas
velocity was maintained at less than 2 d s to avoid forming a depression on the melt surface.
The mass-time c w e s of the sulfide oxidation indicated two stages of desuifurization; the
first was related to oxygen and copper saturation of the melt by the reactions:
OZ@) + [S1 = q@) (30)
3 ;O2@] - + [SI = [O1 + SOZ@) (31)
Upon saturation of the melt, conversion proceeded to the second stage by the reaction:
which was assurned to occur in several steps: oxygen adsorption (Equation (33)) followed
by the formation of an intermediate activated complex as proposed by Byerley et al.Iw
(Equation (34)) which then reacted with dissolved oxypn to produce sulfbr dioxide
(Equation (35)) that was subsequently released into the gas phase.
SulfÙr removal increased with gas velocity and oxygen partial pressure yet its relation to
temperature was less obvious; a positive temperature dependance on the rate of
desulfurization was noted during the second stage at zero top blowing velocity but this
dependence becarne negative at a value between O and 1 rnls (NTP). It was concluded that
the conversion of copper sulfide to metallic copper was controlled jointly by the rate of rnass
transfer of the oxidizing gas to the melt surface and the kinetics of the chernical reaction.
Chapter 2. Literature Review 38
Radioisotope experirnents by Morland, Mathew and Hayes'" indicated that formation
of an activated complex may be rate-controlling only in the chernical reaction sequence of
SO, generation fiom a copper sulfide melt. The reaction kinetics were determined by
measuring the transfer rate of the radioisotope Sj5 fiom molten copper sulfide to gas mixtures
of SOfiO/CO, in equilibriurn with the melt under conditions that ensured the results would
be independent of gas flowrate over the melt surface, melt size. and the isotope concentration
in the original melt. The authoa concluded that S O generation was controlled by the
formation and decomposition of the activated complex SO' according to the reaction:
SO], = SO' = M, + [O],
However their estimated reaction rate for copper sulfide oxidation in air at 1523 K was
relatively hi& at 1 mol S02 me%-' suggesting to the authon that reaction rates in real systerns
are mass transport controlled.
Contrasting the activated complex hypotheses was an electrochemical mode1
proposed by Alyaser and Bnma~ornbe~~.", in due consideration of the ionic nature of the
sulfide melt. to describe desulfirization of Culs baths top-blown with 02-NZ gas mixtures.
The experiments consisted of varying oxygen partial pressure (0.2 to 0.78 vol. %). gas
f l o m t e (1.67 x IO-' to 6.67 x IO-' m3/s), bath temperature (1473 K to 1573 K) and mixing
conditions in the bath. DesulfÛrization was reported to occur at two distinct rates that were
controlled by the transfer of oxygen in the gas phase to the melt surface. These rates
increased with oxygen partial pressure and the rate of gas delivery to the melt surface but
were negligibly afîected by temperature. In the first stage, oxygen dissolution was
accompanied by simultaneous partial desulfization of the melt according to the reaction:
The transition to the second stage upon oxygen saturation of the melt resulted in a higher rate
of sulfur removal than the preceding stage due to the reaction of oxygen at the melt surface
in conjunction with the overall bath reaction:
Chapter 2. Literature Review 39
The negligible liquid phase resistance to mass transfer was attributed to the ionic nature of
the melt and to agitation provided by Marangoni convection and spontaneous sulfur dioxide
eruptions fiom the melt, the latter phenornenon having also been previously reported by
Barton and Brimacombe'" in surfactant snidies involving the dissolution of solid Cu,S in
copper rnelts.
2.5 Hypotlresis The review of the relevant literature regarding copper converting and oxidation
suggests that surface phenornena may be responsible for decreasing the rate of sulfur removal
at the end of oxygen blowing in the INCO finishing procedure. It is hypothesized that upon
oxygen saturation of the melt there is a cessation of Marangoni convection at the melt surface
and that surface blockage by solid Ni0 formation or by oxygen andlot sulfbr adsorption may
be reducing the number of available reaction sites for sulfür elimination.
Chapter 3. Experimental Methodology 40
3.1 Experimental Program The hypothesis presented in Chapter 2 attributed the reduction in mass tnuisfer rates
during second stage converting to blocking of the melt surface through the formation of
nickel oxide (NiO) and a decrease in melt agitation fiom the cessation of surface tension
dnven flow upon oxygen sahiration of the melt. To test this hypothesis the rates of oxygen
dissolution/sulfur removal were measured for cathode C u Cu - 1 wt % S and Cu- 3 wt % Ni
- I wt % S melts at 1523 K when top blown with O?-N, gas mixtures at various oxygen
partial pressures and gas flowrates.
Top-blowing of 02-Nz ont0 moiten cathode copper was carried out to observe the
occurrence of surface tension dnven flow in a quiescent bath when only one surface active
agent (oxygen) was present and to provide a cornparison to the measured oxygen solubilities
of Cu-S and Cu-Ni-S melts tested under similar conditions.
3.2 Test Apparutus
3.2.1 Design Criteria
Melting of a Cu-S alloy under a vacuum or an inert atrnosphere has k e n shown to
result in sipificant sulfur evolutionw while surface tension driven flow has k e n attributed
to concentration gradients in addition to thermal and electrical gradients". To minimize
premature s u l h losses, meIt oxidation, and possible thermal contributions to surface tension
driven flow it was desired to rapidly reach the process temperature of 1523 K under an inert
atmosphere and maintain good temperature control in the bath at the setpoint temperature.
Uncertainty in the observation of any surface phenomenon could be reduced M e r by
visually recording the melt surface under quiescent bath conditions.
3.2.2 Selection of Furnace Technology
Parabolic Clamshell Heater
Induction melting of metallic charges was not considered because electro-magnetic
stimng of the bath was believed to mask the occurrence of surface tension dnven flow and
Chapter 3. Experimental Methodology 41
also upon MCO's suggestion not to consider desulfùxization of inductively stirred meits
since it was felt this had been done previousiy.
Radiative heating of the copper charge was then attempted with a Research
incorporated parabolic clamshell heater mode1 4068. The fumace consisted of twenty-four.
2000 W. infia-red larnps veriically mounted and assembleci in a hexagon comprising of four
iarnps per side. The lamps, c o ~ e c t e d in a three-phase, delta-senes configuration with a
480V drop across each phase, provided a combined power output of 48,000 W. Infia-red
radiation ernitted by the lamps was directed to a focal point at the center of the fumace cavi-
by a parabolic aluminum reflector positioned behind each larnp. These reflectors were
cooled with water flowing at 3 x IO4 m3/s through a copper tube atiached to their anterior
surface.
Although the radiation fumace could achieve rapid heating rates. several technical
deficiencies rendered its use impractical. To reach the setpoint temperature of 1523 K the
furnace was operated at 100% of its raîed power which reduced the usehl iifetime of the
lamps to several hours and made the duration of experiments unpredictable. Under these
operating conditions the calculated heat losses fiom the fumace to the cooiing water
amounted to about 24.000 W. or half of the power output of the larnps, which consequently
limited the charge temperature to 1473 K.
The upper temperature limit was also affiected by the surface emissivity of the
crucible holding the charge material. An iron block heated in an alumina crucibie sheathed
in stainless steel reached a temperature 30 K - 40 K higher than what was possible in an
unsheathed crucible. This observation stemmed fiom an increase in the total, normal surface
emissivity of the cmcible surface from about 0.4 for alumina to 0.8 for the oxidized stainless
steel sheath at 1473 KIo3 (see Figure 16).
At the elevated test temperatures the alumina fiberboard used to insulate the furnace
degraded and released oxide parùcuiates which deposited ont0 the larnps and reflecton.
Disassembly of the heating unit was then required after each experiment to polish the
reflecton to a mirror finish so as to maintain maximum heating efficiency in the fumace.
Ch apter 3. Experimental Methodology 42
/ \ - '. \, ' J, H c a v i l y Oridized j S t a i a l c s s Stee l .
, \
Temperature (K)
Figure 16. Temperature versus total, normal emissiviîy of heavily oxidized stainless steel and aluminum oxidetm.
Silicon Carbide Resistance Hearing Furnace
FoIlowing a major failure of the clamshell heater, a resistance fumace using silicon
carbide (Sic) heating elements t a s designed and built at McGill University. Six cylindrical
S C elements (OD = 0.0254 m x overall length = 0.914 m) each with a heated length of 0.5
m were al igned horizontally in a fumace charnber (inner volume of 0.1 1 m') tvhich was
constructed from silica bricks and insulated on the exterior with alumina-silicate fiberboard
followed by a thin layer transite board (see Figure 17). The fûmace assembly was enclosed
in a cubical M e made of slotted steel angle which was fastened with bolts and reinforced
at each corner with gusset plates.
The Sic heating rods were arranged in two opposing sets of three elements to create
a heating zone 0.284 m wide and 0.152 m high. Connected in a 3-phase, mye-senes
configuration with a voltage drop of 208V across each phase, the elements yielded a
combined power output of 18,000 W.
Chapter 3. Experimental Methodology 43
Figure I f . Schematic represenîation of the (a) profile and (b) plan view of the silicon carbide resistance furnace designed and used in tbis investigation.
Although heating was less rapid with the Sic fumace than the clamshell fumace this
deficiency was compensated by the former's ability to reach a higher melt temperature and
maintain it with greater control over a prolonged period (see Figure 1 8). High temperature
stability was accomplished with two Omega mode1 CN9111 controllen comected in series
and atiached to individual R-type thermocouples immersed in the melt and placed behind a
heating element (see Figure 19). With upper limits of the element and bath controllers set
respectively at 1623 K and 1523 K, power delivery to the furnace was at first regulated by
the element controller but as the melt approached the setpoint temperature this function was
assumed by the bath controller.
Chapter 3. Experimental Method- 44
Due to the modular design of the S i c furnace it was possible to increase the power
of the himace by inserting additional elements into the heating chamber and to replace any
failed individual components without any major disassembly of the heating unit.
Time (minutes)
Figure 18. The time-temperature profiles of an iron block heated to 1473 K in the clamshell radiation fumace and to 1523 K in the SIC rosistance furnace.
Chapter 3. Experimental Methodology 45
/ - - * 2.. 4 - 4 r
n to 11 1 2 s t o l 1 r i 2
I r L N w P N w
CS91 11A CS91 1 1 Coatroikr
A P \ 1 T C 8 I I 0 4 3 7 6 5 4 3
='-% P T C
Bath DA Unit
(6) Sic Hea ting Elemeats
Wye-Series
Figure 19. Wiring diagram for the Sic resisîance furnace featuring two Omega CN9lll series controller which allowed for high thermal stabiliîy in the bath.
3.2.3. Reaction Vessel
Cathode copper or copper alloy contained in an alumina crucible was inserted into
a transparent, cylindrical quartz tube which was sealed on one end with a full radial bottom.
The open end of the tube was made gas-tight with an annular, water-cooled top constnicted
of aluminum that had viton O-rings embedded in its intenor wall (see Figure 20(a)). On the
horizontal surface of the cooling jacket (see Figure 20@)) a nurnber of access ports equipped
with swagelok fittings accommodated a gas lance, an exhaust tube, a themocouple, an
oxygen probe, a sarnpling tube, and a quartz window (see Table 2 for the dimensions of the
reaction vesse1 and its accessories).
Ch apter 3. Experimental Methodolo$y 46
O-Ring Water Inlet -
Inclined M i r r o r
I
-
n
Quartz Tube
Alumina Crucible 1
Copper Charge- -U) Silica Brick
1- Aluminum Water Jacket Quartz Window
- Oxygen Probe U I
Water Inlet
Figure 20. Schemaîk mpresentation of the (a) cross section o f the reaction vessel, crucible and accessories and (b) phn view of the Al water jacket and its access ports.
Table 2. Dimensions of the reaction vesse1 and its accessories.
1 tem tD OD LengthMeigbt m (mm) m (mm) m (mm)
Hycor AI,O, Crucibie 0.07 (70) 0.08 (80) 0.15 (152)
Higb Density AI,O, Crucible 0.068 (68) 0.072 (72) 0.148 (148)
Quartz Reaction Vesse1 0.155 (155) 0.161 (161) 0.61 (610)
Aluminum Water Jacket 0.165 (165)
Mul l i te Cas Lance 0.006 (6.4) 0.01 (9.5) 0.6 1 (6.1 )
R-type TIC witb Sheath - 0.01 (9.5) 0.6 1 (6.1 )
Flexible Exhaust Tube 0.008 (7.94) 0.013 (1 2.7) variable
Quartz Sampling Tube@) 0.003 (3) 0.005 ( 5 ) variable
Quariz Window - 0.013 ( 1 2.7) -
Ch apter 3. Experimental Methodolow 47
A mullite lance supplied inert gas to the reaction vessel during alloy melting and later
introduced O& gas mixîures ont0 the melt surface for either oxygen dissolution andlor
desulfunzation. Prior to melting of the alloy a flexible exhaust tube in conjunction with a
vacuum pump evacuated the reaction vessel of air but in the heating stage served to vent the
effluent gases. An R-type thermocouple sheathed in alumina was immersed into the melt and
regulated the bath temperature while a submerged oxygen probe monitored dissolved oxygen
levels in the alloy. Both the thermal and oxygen level readouts of the bath were recorded by
a data acquisition unit over the duration of the experiment. Quartz tubes inserted through
the sampling port withdrew copper samples from the melt by applying suction at the exposed
end with a mbber bulb pump. The quartz window, in addition to the transparent walls of the
reaction vessel. permitted visual observation of the melt surface. A rnirror positioned above
the quartz window at a 45" inclination to the horizontal plane reflected the image of the melt
surface into the lens of a video carnera that was close-circuited to a television monitor. The
complete test apparatus is shown in Figure 21 and Figure 22.
Shut-Off Valv PressureNacuum
Vacuum Pum
Controllers
Figure 21. Sehematic represenbation of the test appamtus when the quartz mction vesse1 and grapbite rieceptacle were use&
Chapter 3. Experimen ta1 Methodology 48
Figure 22. Photograph of the test apparatus during operation.
Corrosive attack of the experimental equipment by molten copper oxide precipitated
several modifications to the test apparatus. HYCOR dumina crucibles used initiaily for
containing the alloy charge were replaced with high density alumina crucibles due to the
permeability of the former to copper oxide. The susceptibility of the high density crucibles
to thermal and physical shock required that they be placed in a graphite receptacle (Test 3
to Test 6) in case of failure. Surface eruptions from the melt necessitated an extension to the
crucible wall to prevent contact and subsequent reaction of melt droplets with the quartz
tube. On-line monitoring of the oxygen levels was abandoned afier the second test because
of electronic noise in the oxygen readings and the vulnerability of the probes to corrosive
attack by the melt.
The test apparatus was again altered in later tests (Test 7 to Test 9) because of the low
sulfùr elirnination observed in preceding experiments. This effect was amibuted partly to a
reduced oxygen potential in the gas phase resulting from the oxidation of the graphite
Chapter 3. Experimental Methodology 49
crucible to carbon monoxide. The quartz reaction vessel was dropped from use in preference
of the charge k i n g melted in the open atmosphere while the aluminurn water jacket
remained as a support for the gas lance, thennocouple and mirror. The use of HYCOR
alumina crucibles was resurned due to their lower cost and greater durability while the
graphite receptacle was replaced with a larger HYCOR alurnina crucible (ID x OD x L =
0.14 m x 0.167 m x 0.22 m) that was partially filled with silica sand to contain copper spills.
3.2.4 Gas Regdation System
Cas EvacuatiodVentiIation
The exhaust tube of the cooIing jacket was connected in parallel to a ventilation hood.
a vacuum pump and a pressure gauge as shown in Figure 21 and Figure 22. Air was
evacuated fiom the tube prior to heating by shutting the flow line to the ventilation hood and
engaging the rotary vacuum pump until the pressure in the quartz vessel had dropped to 10'
to IO-' atmosphere. The vacuum line was then closed. the pump was disengaged and the
evacuated reaction vessel was then backfilled with nitrogen. When the heating cycle was
initiated the ventiiation line was opened and the heated gases exited into the fùme hood.
Gus Delivery
Gases fiom the nitrogen and oxygen cylinders were directed by individual two-way
valves to either a high flowrate rotameter or to a drying cylinder leading into a low flowrate
rotameter. The gases exiting the low flow rotameters were regulated with precision metering
valves and then mixed in the desired proportions upon exiting the flowtubes before being
channelled into the gas lance above the melt.
3.3 Experimental procedure
Test I - Test 6
P io r to melting of the charge, water flow to the cooiing jacket was set at 125-1 60
cm% and the reaction vessel was either evacuated and backfilled with ultra-high p h t y N1
five times or continuously flushed with nitrogen until seven reactor vessel volumes were
displaced. Upon completion of this cycle the data acquirer was activated and power was
Chapter 3. Experimental Methodology 50
delivered to the fimace. As the charge was heated, the reaction vesse1 was continuously
supplied with nitrogen at a rate of 50-80 cm3/s while the exhaust port was leA open to
accommodate for the expansion of the heated gis. At the setpoint temperature of 1523 K.
two or three samples were exmcted fiom the melt to provide a reference composition for 0.
S and Ni at the start of the experiment. AAer the initiai sarnples were taken, top-blowing
with an O N N L gas mixture and video recording of the melt surface was initiated. The melt
was then sampled at intervals of 10 to 15 minutes for the dwation of the test (90 to 240
minutes).
Test 7 - Test 9
ï h e charge was melted in the furnace chamber under a fumehood and exposed to the
open atmosphere. When the alloy had liquified samples were extmcted for a period of 160
minutes in Test 7, 135 minutes in Test 8 and 90 minutes in Test 9 while the charge was
exposed to air. In each test oxygen was top-blown ont0 the melt at 75 cm3/min for
approximately 50 minutes with continued sampling of the melt. In Test 9 the melt was
subjected to a stage of submerged nitrogen injection at 2000 cm5/min.
3.4 Eiemental Analyses
Elemental analysis for sulfur and oxygen in the copper alloys and test samples were
conducted by the Technical Services depamnent at MCO's Copper Cliff Smelter while
nickel determinations were performed at the Department of Mining and Metallurgical
Engineering of McGill University.
Sulfur anaiysis was determined with a Leco IR 332 combustion anaiyzer in which a
copper sample weighng 0. lg to 1 g was induction melted in a red heat environment in the
presence of oxygen and an iron accelerator. The resulting oxygen and sulfur dioxide Stream
was delivered to an infra-red detector that quantified the sulfur content of the copper sample.
The accuracy of the detector under normal operating conditions was stated to be * 2%, or 1
standard deviation. The unit was calibrated twice with an iron standard of known sulfiir
composition pnor to the commencement of analysis and was recalibrated afler 10 to 20
analyses had k e n perfonned.
Chapter 3. Experimental Methodolugy 51
Oxygen analysis of the copper samples was perfomed with a Leco RO 1 16 analyzer
in which a copper sample of m a s 0.1 g to 1 .O g was placed in a graphite crucible and
combusted in an electrode fumace in the presence of nitrogen. The oxygen in the copper
after having reacted with the carbon in the crucible to produce carbon monoxide gas (CO,,,)
was carried by the nitrogen stream to an infra-red ce11 which quantified the oxygen level of
the copper sample through an evaluation of the CO,,, concentration in the gas stream. The
accuracy of the analyzer was similarly r d at * 2%. or I standard deviation and caiibration
was carried out at the same fiequency as with the S analyzer.
The quantification of nickel levels in the copper samples was evaluated with an
Elmer Atomic Absorption Spectrometer Mode1 3 1 10. A copper sample of approximately O. 1
e was dissolved in an acid solution consisting of 10 cm3 of hydrochloric acid and 5 cm' of C
nitric acid. The copper-acid solution was diluted in a 500 cm3 flask with distilled water
which was then aspirated into the AA unit and b m e d in the presence of an acetyleneiair
flame. The nickel composition of the copper was then correlated to the absorbance of the
flame as established through a series of standard solutions of known nickel compositions.
3.5 Charge Preparation WC0 semi-blister copper fiom the MK flash reactor analyzes at 2-3 wt % S and 3-5
nt % Ni. To reduce the time of the laboratory-scale experiments, the initial sulfbr content
of the Cu-S and Cu-Ni-S alloys was lowered to 1 wt % and the nickel content in the Cu-Ni-S
dloy was reduced to 3 wt %. Thus. while oxidation experiments were perfonned on cathode
copper. desulfurization tests were carried out on two copper alloys: Cu - 1 WO S and Cu-
3 wt % Ni - l wt% S which were respectively designated CS and CNS alloys.
Experimental alloy charges were prepared fiom cathode copper sheet (0.70 m x
0.80m x 0.0 1 m) supplied by iNCO in addition to -1 00 mesh nickel (Ni) powder (99.99 wt
% purity) and -325 mesh copper(i) sulfide (Cu$) powder (99+ wt % purity) purchased fiom
Sigma-Aldrich. The Cu2S powder analyzed by Sigma-Aldrich at 76.2 wt % Cu and 23.4 wt
% S indicated an excess of sulfür with respect to the stoichiometric compound. The
Ch apter 3. Experimental Methodology 52
composition of the cathode copper (see TabIe 3) was determined by emission spectroscopy
and was performed on 10 regions selected randomly across the cathode sheet (see Figure 23).
Each elementd assay was derived from 30 determinations i.e. 3 assays from each of the 10
surveyed areas.
Table 3. Average elemental composition OC INCO cathode copper sbeet.
Element Composition' Element ~omposition' (wt %) (wt %)
Ni 0.04795 * 0.0 1 53 Sn 0.003 7 * 0.00 1 8
Co 0.0 1 903 * 0.0033 Mn <0.0040
Si 0.0 126 * 0.00047 Cd <0.0017
P 0.0 1 22 a 0.00084 AI <0.0008
Mg 0.00833 * 0.0025 Bi <0.0008
Fe 0.0079 0.001 8 S <0.0004 *standard deviation calculated on the bais of the population.
Figure 23. Broadside and cross section o f the cathode copper sheet Ekmenîal analyses were perfonned on the sbaded regioos.
Chapter 3. Experimental Methodology 53
3.5.1 I n Situ Alloy Preparation
Preparation of a Cu-3 wt % S alloy was first attempted in a HYCOR alumina crucible
by heating measured amounts of cathode copper and CuzS powder under U.H.P. N2 prior to
desulfurization of the melt. In this experiment significant evolution of sulfur dioxide (SO,)
gas occurred during the alloy preparatory stage while the formation of a viscous secondary
phase was observed on the melt surface after oxygen blowing had cornmenced. The
rneasured sulfbr content in the melt at the start of oxygen blowing had dropped to
approximately 1 wt?4 as a result of the initial S 0 2 evolution while the fiozen slag layer, at
1.5 cm thickness (see Figure 24) was considered to be the reaction product of the molten
charge with components or impurities of the crucible. The crucible composition (see Table
4) consisted predominantly of alumina at 88.3 wt % followed by silica at 1 1.2 wt % and
minor arnounts of other oxides. However a qualitative analysis of the slag phase by X-ray
diffraction (see Appendix A) detected the presence of amorphous copper oxides (Cu0 and
Figure 24. Cross section of crucible and solidified slag layer from Test 1.
Chapter 3. Experimental Methodo Cogy 54
Cu@) and some CuzS but not of any crucible compounds. From these analyticai results the
slag layer was believed to have formed by the oxidation of the Cu2S powder and therefore
in situ alloy preparation was abandoned d e r the first desulfurization test. Alloy charges
used in subsequent tests were taken fiom master alloys that had been prepared in advance.
NaO, 0.12 1 C a 0 0.02
Table 4. Composition of HYCOR alumioa crucible according to the manufacâurer..
3. S. 2 Mas fer A floy Preparation
Two copper alloys at 1 wtYo S (CS alloy) and 3 wt % Ni - 1 wt % S (CNS alloy) were
Compound Composition (wt O ! )
prepared through induction melting of cathode copper and Cu$ powder, and Ni powder (for
the CNS alloy) in a sealed, cylindrical graphite crucible (OD x n> x Height = 9.2 cm x 7.7
Compound Composition (As Impurity) (wt %)
cm x 1 9.1 cm). The proportions of the alloy feed materials were determined by a m a s
balance of the elements where it was assurned that metallic losses were negligible and s u l h
recovery was 90 wt %.
The sealed cmcible was inserted into the induction fiiniace chamber and packed with
coarse silica granules to minimize oxidation of the graphite with the outside atmosphere. A
removable centerpiece on the lid of the crucible allowed the charge to be monitored
periodicdly as it was heated. Upon liquefaction, the charge was kept molten for roughly 40
minutes to allow adequate time for dissolution of the powdered material and homogenization
of the melt. Power delivery to the induction coils was then suspended and the alloy was left
to cool and solidifi in the cnicible. The resulting cylindrical ingot was removeà, massed and
then sandbiasted to remove any foreign and oxide particdates fiom its extenor surfaces. The
ingot was sectioned dong its vertical axis and drill sarnples were extracteci h m four regions
(see Figure 25) for 0, S and Ni detenninations (see Table 5).
Chapter 3. Experimentul Methodology 55
Table 5. Elemenîal determinations for CS
CS Alloy - -
Sam pled O S Reg ion (wt %) (wt %)
1 0.00 1 0-82 k 0.0 1
ad CNS alloys.
CNS Alloy
O S Ni (wt O h ) (wt Y.) (wt @/O)
0-046 1.23 2.86 * O. 162
Average 0.014*0.010m 0.81*0.012* 1 0.02410.013' 1.17*0.071' 3.02*0.20'
'Standard deviation calculated on the ba is of the sample population
+Standard deviation calculaied on the pouled average from the deviation o f each analysis which is based on two determinations per region
Figure 25. Regions of alloy ingot sampled for elemenîal determiaaîions.
Chapter 3. Experimental Methodolw 56
3.6 Selection of Experimentd Conditions Nine experiments were performed at 1523 K+ to investigate the effect of gas flowrate.
PO2 of the gas strearn and the presence of Nckel in the melt on desulfunzation (see Table 6).
The test conditions were selected on the basis of pnor works and h m the observations made
in each test.
The gas flowates used in the testwork were initially selected to result in low
momentum gas streams, which, upon impingement on the melt surface. would not
appreciably stir the bath or infiuence the occurrence of surface tension driven flow. Due to
the similarity in the kinematic viscosities of water and Iiquid copper it was assurned that a
water mode1 of the system could provide a reasonable assessment of the level of stirring
attributed to the momentum of the gas stream. Water soluble food dye was introduced under
the gas Stream and its dispersion was observed under the various gas flowrates. It was found
that at an air flowrate of 100-200 cm3/min no appreciably mixing of the food dye occurred.
Tests 1 through 3 were performed using the copper-sulfùr alloy under different gas
flowates and compositions in order to detemine the effect of these variables on the rate of
desulfiuization. Tests 3 through 6 were conducted under similar conditions with different
alloy charges although the gas flowratte was increased in the later stages of Tests 4.5 and 6.
a cornparison was drawn between the desulfiirization rates of the copper-sulfbr (CS)
alloy used in Test 3 and the copper-nickel-sulfur (CNS) alloy used in Test 4. a further
evaluation was made of the dissolved oxygen levels in these ailoys which were contrasted
against that for cathode copper (Test 5 and Test 6).
The sarnples of Test 5 were not assayed on account of the failure of the crucible
containing the copper charge. The final tests in the experimental program (Tests 7 through
9) were designed to assess desulfunzation under conditions where the two alloy charges were
melted under air. Reproducibility of the testwork was also verified through Test 7 and Test
8 which were carried out with a CS alloy charge under the same experimental conditions.
'The setpoint tempcranire in Test 1 was lowered to 1498 K because the rnelt temperature according to the data acquirer readings had exceeded 1550 K.
Chapter 3. Experimental Methodolom 57
Table 6. Experimental conditions uscd for desulhrization and oxidation tests.
Test Melt Alloy/ Charge Stage Gris Lance .%$ -?s, Temp. Charge Mass Flowrate Position*
K (g) (cm3/min) (cm) (atm) (atm)
573 CS
573 CNS
1573 CS
1573 CNS
1
1
1
1 II
1 II
1 II
1 II
1 I 1
1 II III
169.4
13 I
7 5
75 372
75 372
7 5 372
Air 75
Air 7 5
Air 7 5
2000
'In situ alloy preparation of a Cu - 3 wt% S alloy tt Graphite receptacle used as spill container
Charges melteâ under an open atmosphere and consequently no flowrate is stated in Stage 1. + Distance of the lance tip from the meit suriace.
Chapter 4. Results 58
4.1 Experimerttal Resulls
Test 1: Desul/ui&on of a Cu - 3 wt% S Alloy
The first test of the experimental program anempted to produce a copper alloy of 3
wt % S, in situ, by melthg 0.3 kg (302.0 g) of Cu2S powder and 1.7 kg (1696.0 g) of cathode
copper in a HYCOR alumina crucible under Ntrogen gas and subsequently desulfunze this
alloy at 1323 Kr with an 02-N2 gas mixture. During liquefaction of the alloy components.
much sui fur was evolved fiom the melt as was evident by a strong odour of Sol in the off-
gas fiom the reaction vesse1 and this was confirmed by the initial melt analysis of 1.2 1 wt %
S. Oxygen-nitrogen gas injection for 7 1 -5 minutes at 1 70.6 cm5/min and .% = 0.62
decreased the sulfur content of the melt by a M e r 10 % to 1.07 wt % S while the dissolved
oxygen concentration increased by an order of magnitude fiom 0.02 wt % to O. 1 1 wt % (see
Table 7 and Figure 26).
Table 7. Tabuiatd S and O assays from Test 1 coaducted at 1498 K by blowing an 0,- N, gas mixture witb 9% = 0.62 at 170.6 cm3/min on Iiquid Cu - 3 wt% S alioy.
Sampling Time (SI lolM Experimental Condition O/ w t %
0.00 1 -2 1 r 5 e-5 0.020 * 0.005 Melt Hornogenization
10.5 - - 0, introduced at 105.6 cm5/min -
22.3 1 . 1 7 * 0.0 12 1 0.050 r 0.009 O2 blown at 105.6 cm3/min 38.6 0.975 r 5 e-3 0.085 * 0.0 12 O2 blown at 1 05.6 crnS/min 55.3 1.12 0.126 * 0.009 O2 blown at 105.6 cm3/min 71.7 1 .O9 0.094 1 O, blown at 105.6 cm3/min 81 .O 1 .O7 0.1 1 I 0.027 O, blown at 105.6 c&in
Pooled Std. Deviations 9.3 e-3 7.5 e-3 M ~ x y g e n assays performed at McGill University Visual recording of the melt surface was terminated less than 10 seconds afier the
start of oxygen blowing due to the failure of the heat shield in front of the video camera.
This brief record of the melt surface showed a luminescent patch beneath the tip of the gas
lance (see Figure 27) but contrary to reports of Marangoni convection in copper r n e l t ~ ~ ' ~ . ~ ' ,
1 The bath controller setpoint was lowered to 1498 K because the output temperature fiom the data acquirer was often in excess of 1550 K (see Figure 29).
Chapter 4. Results 59
it did not spread radially outwards at high velocity; instead some material was ejected fiom
this region. Inspection of the quartz reaction vesse1 at experiment's end revealed fine
particles uniformiy distributed in a circular band (see Figure 28) near the sealed radiai bonom
of the quartz tube; dong the horizontal tube length the distribution pattern and size of the
particles was more randornized. in some regions large droplets of ejected matenal (- 0.5 cm)
caused hctures dong the vertical length of the quartz tube.
Following several minutes of 02-N2 gas blowing a slag layer formed on the melt
surface which thickened over time and eventually enveloped the tip of the gas lance. Upon
melt solidification this layer measured 1.5 cm in thickness (Figure 24 in C hapter 3) while X-
ray diffraction determined that it consisted mostly of Cu,O, Cu0 and some Cu,S.
Penetration of the crucible wall by copper oxide resulted in contact b e ~ e e n the melt and the
radial bonom of the reaction tube leading to its failure and termination of the experiment.
Time (minutes)
Figure 26. The dissoived S aad O coacentratioa profik ovcr time in Test 1. The vertical line coincides with the introduction of the O,-N, gas mixtun onto the melt s u a c e at 170.6 cm3/min and .Po, = 0.62.
Chapter 4. Resulis 60
Figure 27. Photogmpb of the luminescent patch beneath the tip of the gas lance in Tut 1 at the start of O,-N, gas blowing. The dark spot on tube is a iarge dmpkt of material that bad been ejected from the bath.
Figure 28. (a) Schematic of the region on the quartz tube most affected by the melt ejcctions. (b) Pbotograph of the fracturai reactioa vusel aear its radial bottom ringed m t b dropkts of copper/copper o d e .
Chapter 4. Results 61
Tlme (minutes)
Figure 29. The tirne-temperature prof* of the alloy melt in Test 1 relative to the sampling n'me. The horizonîal lime marks the bath setpoint tempenature of 1498K. The data during melîing of tbe alloy charge coukl not be rotrieved from tbe DA unit.
Test 2: Desulfuization of Cu - I wt % S Alloy with 66 cm) Ojmin
Slag formation in Test 1 was initially attributed to the reaction of the melt with the
porous crucible and to an excessive rate of oxygen delivery. Therefore in Test 2, a 1 kg
(1014.5 g) section of CS master alloy was melted under nitrogen in a high density dumina
crucible and the oxygen flowrate was reduced to 66 cm3/min while .-/8- was increased to 1.
At 1523 K pure oxygen was introduced ont0 the liquid alloy surfice for 156 minutes. Under
these blowing conditions the sulfbr content of the bath was reduced to 0.62 wt % or by about
40 % (see Table 8 and Figure 30). The dissolved oxygen content increased tiom 0.23 - 0.47
wt % to a maximum level of O. 16 - 0.165 wt % (see Table 8 and Figure 30). An attempt to
monitor the oxygen level in the bath with a submerged oxygen probe failed because the tip
of the probe was consurned by the melt. Although the temperature readings fiom the data
acquirer were ofien in excess of 1523 K (see Figure 3 l), the bath temperature controller
consistently displayed 1523 K and therefore no changes were made to the setpoint
temperature in the controller.
Chapter 4. Results 62
Throughout the expriment the melt surface remained fiee of the type of slag
coverage observed in Test 1 and the characteristic dark surface of the liquid copper was
clearly visible; however a thin, emissive, oxide film collected near the crucible wall (see
Figure 32a) \*hich after melt solidification appeared as darkened regions on the blistered
copper surface (see Figure 32b). Some limited swirling motion of this film did take place
but the flow pattern and velocity were not characteristic of Marangoni convection. The only
surface phenornenon observed war some intermittent bubbling on the melt surface. As in
Test 1. there was evidence of material ejection fiom the melt which appeared as finely
dispersed droplets dong the vertical length of the cooled reaction tube (see Figure 33).
Despite using a high dewity alumina crucible, the container failed and its contents seeped
onto the quartz reaction vesse1 resulting in irreparable damage to the tube.
Table 8. Tabulated S and O assays from Test 2 conductd at 1523 K by blowing pure O2 at 66 cmJ/min on the sudace o f liquid CS alloy.
Sampling Time [sl [O! Experimental Strige wt O/ O/
0.00 1 .O3 I O. 1 8 0.047 * 0.024 Melt Homogenization 3.30 1.0710.19 0.023&0.011 Melt Homogenization
6.77 - - Oz introduced at 66 cm5/min
1 5.63 1 -06 I 0.0 1 4 0.05 O2 blown at 66 cm'lmin 29.73 0.99 0.1 1 O, blown at 66 cm3/min 4 1.40 0.97 O. 1 O, blown at 66 cm5/min 45.57 0.92 0.064 O2 blown at 66 cm3/min 7 1 -40 0.93 0.068 O2 blown at 66 cm3/min 86.82 0.87 i 0.01 4 O. 133 * 0.04 O, blown at 66 cm3/min 89.45 0.87 I O 0.1 34 * 0.008 0, blown at 66 cm3/min 99.72 0.79 - O blown at 66 cm3/min 101.48 0.835 * 0.007 O. 139 * 0.0 1 0, blown at 66 cm3/min 1 14.82 0.79 0.144 * 0.01 8 O, blown at 66 cm3/min 132.98 0-7 15 *O-007 O. 139 O, blown at 66 cm5/min 144.73 0.68 O. 165 O= blown at 66 cm3/min I 63-48 0.62 i 0.0 14 0. 1 58 * 0.004 O, blpwn at 66 cml/min
Pooled Std. Deviation 0.087 0.020
Chapter 4. Results 63
Figure 30.
Figure 31.
Time (min utes)
The dissolvecl S and O concentration profiles over time in Test 2. The vertical line coincides with the intmâuction of pure O, onto the melt surface at 66
Time (minutes)
The time temperatun prnfik of the mdt in Test 2 mlaiive to the sampling timc t = 0; t he depmion in the cuive near 1400 K indicrites liqucfaction of tbe nlloy charge whik the horizontal Une marks the bath sctpoint tempcmturt of 1S23K.
Chapter 4. Results 64
Figure 32. Photographs of the alloy surface and oxide film fmm Test 2 at (a) 1523 K and t = 70 minutes; a highly emissive solid or liquid oxide near the crucible wall is surrounded by the darker liquid alloy and (b) m m temperature where the blistered alloy surface is partially covered by dark regions of oxidized copper.
Figure 33. Photograph of the qua* mction vcsscl, fmm Test 2, along i îs verocal kngth showing solidifid droplets of ejected material.
Chapter 4. Results 65
Test 3: Desurfurization of Cu - I wt % S Aîfoy with 75 cm' Ojmin
Due to the loss of two quartz reaction vesmls by contact with the melts in Test 1 and
Test 2, the high density alumina crucible used to contain the copper alloy charge was placed
within a graphite spi11 receptacle (see Figure 21 Chapter 3) while a 15 cm alurnina d l
extension was added to the lip of the alumina crucible to shield the quartz tube from melt
ejections. As in Test 2, a 1 kg (1009 g) section of CS master alioy was melted to a setpoint
temperature of 1523 K under nitmgen . The liquid alloy was sampled three times over a
period of 2 1 minutes while still under nitrogen and then impinged with pure oxygen at 75
cm5/min for approximately 205 minutes. Afier 130 minutes of oxygen blowing there was
no discemable change in the suifur content of the bath however the oxygen content increased
to about 0.8 - 0.9 wt % (see Table 9 and Figure 34). An additional 75 minutes of oxygen
blowing reduced the sulfur content to 0.84 wt % while the dissolved oxygen level increased
Table 9. Tabulated S and O assays from Test 3 conducted at 1523 K by biowing pure O, a t 7 5 cm3/min on the surface of a CS alloy charge.
Sarnpling Time [SI [O! Experimental Condition
Melt Homogenization Melt Homogen ization Melt Homogenization
22.58 - - O, introduced at 75 m'/min
32.00 0.956 0.006 O2 blown at 75 cm3/min 46.15 1.01 0.028 O, blown at 75 cm3/min 52.92 1 .O6 - 0, blown at 75 cm3/min 66.12 1 0.0 12 0, blown at 75 cm3/min 68.00 1 .O4 0.022 0, blown at 75 cm3/min 77.50 1 .O6 0.0 19 O, blown at 75 cm3/min 88.33 0.993 0.022 O2 blown at 75 cm3/min 91.10 1 .O4 - O, blown at 75 cm3/min 103.78 1 .O5 0.039 O2 blown at 75 cm3/min 1 15.83 1 .O5 0.093 O, blown at 75 cm3/min 1 26.33 1 .O6 - O2 blown at 75 cm3/min 147.17 1 .O8 - O, blown at 75 cm3/min 1 59.33 I .O6 0.082 O, blown at 75 cm3/min
Ch apter 4. Ressulis 66
Table 9. Conrinucd Sampling Time [SI (01 Experimental Conditions
O/ wt O/
1 69.33 1 - 0: blown at 75 cm3/min 182.08 0.985 - O, blown at 75 cm3/min 197.67 0.97 - O2 blown at 75 cm3/min
O2 blown at 75 cm3/min 0' blown at 75 cm2/min Or blown at 75 cm3/min
328.00 0.84 1 - O, b~own at 75 cm5/min
Time (minutes)
Figure 34. The dissolved S and O concentration profile over time for Test 3 at 1523 K. The verlical line coincides witb the introduction o f pure 0, onto the melt surface at 75 cm3/min.
Although observation of the bath did not reveal any high speed motion of oxide away
from the region below the lance tip, within 15 minutes of oxygen injection, the melt surface
was covered by an emissive, oxide layer. Neither the melt nor the oxide penetrated the
crucible.
As in previous tests the bath temperature indicated by the data acquirer usually
exceeded the setpoint temperature of 1523 K displayed by the bath temperature controller
(see Figure 35).
Chapter 4. Results 67
Time (minutes) The time temperature profile of the melt in Tcst 3 tcliitive to tbe sampling time t = 0; the depression in the curve near 1400 K indicatcs liquefaction of the alloy cbmrge wbiie tbe horizontal line marks tbe bath setpoint tempemture of 1S23K.
Test 4: Desurfurit~tion of Cu - 3 wt % Ni - 1 wt % S Alhy witk 75 c d O/min
tn Test 4. a 1.1 kg ( 1 093 g) charge of CNS master ailoy was melted under nitrogen
in the crucible configuration w d in Test 3. Upon reaching 1523 K the melt was top-blown
with oxygen at 75 cm3/min over a p e n d of 21 0 minutes and at 372 cm3/min for 33 minutes.
The elemental assays for this test are presented in Table 10 and Figure 36. The concentration
profile of the copper alloy over time remained almost constant with respect to sulfür while
the scatter in the oxygen measurements precludes any assessrnent in the change of the oxygen
concentration below the levelO.O1 wt %. Nickel determinations appear constant at 3 wt % - 3.5 wt % for most of the duration of oxygen blowing at 75 cm3/min; the values decrease near
the end of this period and again after the oxygen flowrate was increased to 372 cm3/min.
Dissolved oxygen levels also dropped with increased oxygen delivery to the melt while sulfur
levels remained constant.
No evidence of Marangoni convection appeared in the visual record of the
experiment and as in Test 3 the liquid surface had become almost completely covered by an
ernissive oxide layer within 15 minutes of oxygen injection (see Figure 37). As in previous
Chapter 4. Results 68
tests, the temperature from the data acquirer consistently exceeded the setpoint value of
1523 K displayed by the bath controller (see Figure 38).
Table 10. Tabulated S. 0 and Ni assays from Tat 4 conducted at 1523 K with CNS alloy initialh. blown with pure 0, jet at 75 cm3/min and then at 372 cm3/min.
Sampling Time [Sj (01 [Nil Experimental Stage t % Wt a/ Wt O/
0.00 1.13 0.004 * 0.004 Melt Homogenization 26.17 1-16 3.1 8 Melt Homogenization
28.33 O2 introduced at 75 cc/min
0, blown at 75 cm3/min 0, blown at 75 cm3/min 0, blown at 75 cm3/min Ot blown at 75 cm3/min O1 blown at 75 cm3/min O2 blown at 75 cmS/min 0, blown at 75 cm3/min 0, blown at 75 cm3/min O2 blown at 75 cm3/min O2 blown at 75 cm3/min 0, blown at 75 cm3/min O2 blown at 75 cm3/min 0, blown at 75 cm3/min 0, blown at 75 cm3/min O2 blown at 75 cm3/min 0, blown at 75 cm3/min O2 blown at 75 cm3/min O2 blown at 75 cm3/min O2 blown at 75 cm3/min O2 blown at 75 cm3/min
- 0, blown at 75 cm3/min
238.80 - - - 0, introduced at 372 cm3/min
246.00 1.13 0.006 2.59 O2 blown at 372 cm3/min 255.17 1.1 1 - - 0, blown at 372 cm3/min 261 -57 1.12 <O.OO 1 2.61 0, blown at 372 cm3/min 267.50 1.15 <O.OO 1 - 0, blown at 372 cm3/min 277.17 1.15 <o.oo 1 3.39 0.. blown 37- 3 -
' Oxygen determinations <0.001 wt % were plotted as zero on subsequent plots of the melt concentration profile versus time.
Chapter 4. Results 69
O 30 60 90 120 1SO 180 210 240 270
Time (minutes)
Figure 36. The dissoked S, O and Ni concentration profile over time in Test 4. The first and second vedcal lin- coiacide respectively witb the introduction of pure O, oato the melt surface at 75 cm'lmin and tben at 372 cm'lmin.
Figure 37. Photogmpb of the melt surface in Test 4 covered by an emissive oxide film at 1523 K and t = 40 minutes The dark ngion b the muid metal surface that was exposed after a sampie bad been extractcd from the melt.
Chapter 4. Results 70
Time (minutes)
Figure 38. The time temperature prof* of the melt in Test 4 relative to the sampliag time t = 0; the depression in the curve near 1400 K indicrites liquef'action of the alloy cbaqge whik the horizontal üne marks the bath secpoint tempemture o f 1523K.
Test 5, Test 6: Oxidation of Cathode Copper with 75 and 3 72 c d Oyrnin
In Test 5 and Test 6 cathode copper was melted under nitrogen in the sarne crucible
configuration used in Test 3 and Test 4 and subsequently impinged with pure oxygen at a
flowrate of 75 crn3/min for 191 minutes and at 372 cm3/min for 20 minutes at 1523 K. The
objectives were to compare the level of oxygen dissolution in cathode copper versus
measurements made for the CS and CNS alloys and observe whether Marangoni convection
would occur more readily under the influence of only one surface active agent i.e. oxygen.
The crucible in Test 5 failed at the start of the experiment which resulted in contact of the
melt with the graphite spi11 receptacle and hence deoxidation of the copper. This was
evident by a dark and highly reflective melt surface observed for the duration of the
experiment (see Figure 40b). As a result of this event the samples fiom Test 5 were not
analyzed and the experiment was repeated as Test 6 with a copper charge weighing 1 kg
(1 O68 g).
Ch apter 4. Results 11
The oxygen concentration profile of the copper melt over t h e in Test 6 is tabulated
in Table 1 1 and graphically depicted in Figure 39. During oxygen blowing at 75 cm'lmin,
the oxygen determinations were widely rattered between 0.00 1 wt % and 0.0 1 wt %; at the
higher oxygen flowrate of 372 cm3/min the dissolved oxygen level increased to between
0.285 wt % and 0.373 wt % afier 20 minutes of blowing.
Table 11. Tabuhtd O ossoys fmm Test 6 conducted at 1523 K by blowing s pu- Oz jet at 75 cm3/min on the surface o f a catbode copper.
Sampling Time (01 Experimental Condition t '/a
0.00 0.009 Melt Homogenization 7.12 0.03 1 Melt Homogenization 8.78 O2 introduced at 75 cc/min 17.95 0.006 O, blown at 75 cm3/min 28.22 0.005 O2 biown at 75 cm3/min 37.48 0.093 O2 blown at 75 cm3/min 49.1 2 0.0008 O2 blown at 75 cm3/min 57.95 0.00 15 O2 blown at 75 cm3/min 67.85 0.0036 O2 blown at 75 cm3/min 78.03 0.0 1 8 O2 blown at 75 cm3/min 87.63 0.00 1 8 O2 blown at 75 cm3/min 97.95 0.0088 O2 blown at 75 cm3/min 107.78 0.00 19 O, blown at 75 cm5/min 1 17.53 0.0036 O2 blown at 75 cm3/min 128.20 0.003 OS blown at 75 cm3/min 1 37.53 0.0032 OS blown at 75 cm3/min 147.95 0.0026 O2 blown at 75 cm3/min 157.57 0.0033 O2 blown at 75 cm3/min 1 67.37 0.0089 OS blown at 75 cm3/min 177.37 0.0039 0, blown at 75 cm3/min 1 87.3 7 0.028 O2 blown at 75 cm3/min 197.3 7 0.002 O2 blown at 75 cm3/min 199.95 O, introduced a t 372 cm3/min 207.45 0.373 O b l o m at 372 cm3/min 213.38 0.289 O, blown at 372 cm31min 220.62 0.309 O2 blown at 372 cm3/min 227.28 0.392 O2 blown a t 372 cm3/min 234.35 0.285 O2 blown at 372 cm3/min 239.42 0.3 16 O,
Chapter 4. Results /L
in contras to Test 5, the surface of Test 6 became covered by an emissive, oxide layer within
10 minutes of oxygen injection (see Figure 40a). Marangoni convection was not observed
in either of these experiments and as in previous tests the melt temperature values frorn the
Time (minutes)
data acquirer and the bath controller display often differed (see Figure 41).
Figure 39. The dissoIved O concentration p m f k over time in Test 6. The first and second vertical lines coincide respectively with the i n t d u c t i o n of pure O, onto the melt surface a t 75 cms/min and then a t 372 cm3/min.
b
0.04 - -
0.03 h * œ
s w - 0.02 P.
Figure 40. ~ h o t o g i ~ h s of the acit surface a t 1523 K in (a) Test 6 covered by an emhrive oxide hyer afbr 22 minutg of O* bloning (Le. t = 32 minutes) and @) Tut S after 35 minuta of 4 blowiag a t 75 cm3/min; note the mirror image of the gas lance on the dark but rentctive melt sudace.
11 1
i ; 1
1 I
: 1 t 1 1 l I
I 1
i -- , 1: A
1 I $ '
1 1 I
1 I ' 1 1 -- ': 1
1
' I * I 1
1 1 I
1: I 1 1
I l 1 , 1
1
0.01 & : I i * 9 1 I 1
1 1 I I
a 1 I
, i * * 1 i ! 1
1 I 8 I
' O ; * r ~ r * ' ? 1 1 * i n .
1 . . , . 4 O r ' : : : g - n - x - l - l - rn -
b * CI
w s
"0.2 - P.
--0.1
. O O 30 60 90 120 150 180 210 240
Chapter 4. Results 73
A
z V
O L a CI a L Q)
;
Figure 41.
Time (minutes)
The time tempemture profik o f the melt in Test 6 reiative to the sampling time t = O; the depression in the curve near 1400 K indimates iiquefactioa of the alloy charge whik the horizonîal line marks the bath seîpoint tempemture of ISUK.
Test 7, Test 8: Desulfurization of Cu-l wt % S Alloy Eyosed to Air
In Test 7 and Test 8, CS master alloy charges, weighing respectively 0.83 kg (83 1 g)
and 0.89 kg (891g), were melted in HYCOR alumina crucibles under air with the objectives
of measuring sulfw eiimination of stagnant melts exposed to the open atmosphere and
verimng the reproducibility of experimental results. In both tests the crucibles were placed
within a larger HYCOR dumina spi11 receptacle which was partially filled with silica sand.
The rnelt su'ace in both tests becarne partially covered with an oxide layer from the
onset of sampling which was initiated just prior to the melt reaching 1523 K (see Figure 42).
In both tests, the melt spontaneously effervesced (see Figure 43), Le., enipted with bubbles
and vigorously agitated the bath for 10-20 minutes, which destroyed the oxidized surface
layer and accelerated sulfur elimination. A penod of melt quiescence followed this
effervescent episode after which the melt enipted for a second time. These eruptions sprayed
material fiom the melt ont0 the interior fûmace chamber and ont0 the fiberfhx insulation
cover located 44 cm above the melt surface. The composition profiles over time of Test 7
Ch opter 4. Results 74
and Test 8 are tabulateci in Table 12 and presented in Figure 44 which also marks the onset
of effervescence in both tests. The sarnpling tirne in Test 8 was adjusted to coincide with
time scale of Test 7 when the melt assays are almost identical at about 0.16 wt % S. Oxygen
impinged on the melt surfaces of both tests at 75 cm3/min did not appear to affect oxygen
dissolution or sulfur elimination fiom the melts (see Figure 55, CIiapter 5) and both tests
showed thermal deviations fiom the setpoint temperatures which were unrelated to the
surface eruptions. The source of these deviations remained undetennined.
Similar reports of effervescence were made by ri ou^'^ in desulfurization tests of CS
alloy charges top blown with oxygen at 75 cm3/min, 500 cm3/min and 1000 cm3/min. The
charges were melted in the experimental apparatus used in this study and under the same
crucible configuration and conditions used in Test 7 and Test 8 of this study. Rioux also did
not observe any instances of Mamgoni convection in any of the tests.
Table 12. S and O determinations for Test 7 and Test 8. The time s a l e in Test 8 bas been adjusted to coincide with the sampling time of Test 7 at t = 61 minutes where the S content of both melts is simiia
Time Test 7 Test7 Test7 [SI [O1 Temp.
wt O/o wt @/O K 0.00 0.06 1 1 400 10.00 0.445 1459
20.00 0.089 1493 30.00 0.425 1517 3 1-67 0.136 1521 37.57 41 -13 0.274 1529 45.50 50.05 0.234 1517 55.50 61.00 0.1 64 1528 62.67 68.34 70.42 0.393 1524 75.50 82.05 0.045 1522 83.17 93.50
Test8 Test8 Test 8 Pl 101 Temp.
wt O/ wt @/O K
Chapter 4. Results 75
Table 12. Conrinued Time Test 7 Test 7 Test 7
[SI 101 Temp. wt O/ wt O/O K
93 -53 0.25 1524 104.00
109.10 0.062 1527
I 16.00 123.55 0.23 5 1512 125.84 126.95 137.88 0.044 1534 139.02 0.246 - 140.95
148.67 158.15 162.05 0.6 1 5 1529 168.00
pp - -
Test 8 Test 8 Test 8 Pl Pl Temp. t O/ wt @/O K
Figure 42. Photograph of the melt sudacc in Test 8 covered by an emissive oxide at approximately t = O minutes. Tbe darker spots are the exposed surface of the liquid alloy.
Chapter 4. Results
Figure 43. Pbotograpb of the melt surface effervescing in Test 8 at t = 2s
Time (minutes)
minutes.
Figure 44. The dissolved S and O concentration profiles over time for Test 7 and Test 8. The dashed and solid vertical lines respectively mark the occurrence and duration of effervescence in Test 7 and Test 8.
Chapter 4. Results / /
-90 -60 -30 O 30 60 90 120 150 180 210 240
Time (minutes)
Figure 45. The time temperature profiie of the melt in Test 7 relative to the sampling time t = 0; the plateau in the curve near 1400 K indicates liquefaction of the alloy charge whik the horizontal üne marks the bath sesetpoint temperature of 1S23K.
-90 -60 -30 O 30 60 90 120 150 180 210 240
Time (minutes)
Figure 46. The time temperihim pmllk of the meit in Tut 8 relative to the umpling time t = 0; the plateau in the curve near 1400 K indicates liquefaction of the alby cha* w h k the horbontal üne marks the bath setpoint temperaturr of lS23K.
Chapter 4. Results 78
Tes? 9: Desu&urization of Cu - 3 wt % Ni - I wt % S Alloy Exposed tu Air
The same conditions and crucible configuration which were used in both Test 7 and
Test 8 were applied in Test 9 to measure sulfbr elimination fiom a 1 kg (1035.0 g) melt of
CNS master alloy. The concentration profile of the melt (see Table 13 and see Figure 47)
shows a gradua1 decrease of sulfbr over time and no greater degree of oxygen dissolution
over the copper-sulfur melts in Test 7 and Test 8; nickel assays do not show any obvious
trend and are above the mean alloy concent ra to~ No spontaneous eruptioos were observed
and the melt surface always remained covered by an oxide layer (see Figure 48). Submerged
niaogen stirring of the bath did not affect the nickel and oxygen levels in the bath. but the
increased melt agitation did result in greater sulfur removal. The time temperature profile
of the bath, s h o w in Figure 49, displayed deviations h m the setpoint temperature of 1523
K at periodic intervals.
Table 13. Tabuiated S, O and Ni assays from Test 9 for CNS aUoy melttd under air and tben blowa with pure O, at 75 cm3/min and finally subjected to submeaed N, injection at 2000 cm3/min.
Sarnpling Time [SI 1 0 1 [Nil Temp Experimenîal Condition ,,,t O/ *t O/ O/ K
0.00 0.673 0.1 19 3 .O 1 1418 Melt exposed to air 10.57 0.465 0.146 1472 Melt exposed to air 20.82 0.046 0.191 4.39 1502 Melt exposed to air 30.07 0.329 0.2 1 1522 Melt exposed to air
1530 Melt exposed to air 1520 Melt exposed to air
45.20 0.309 0.228 5 .O3 15 18 Melt exposed to air 49.88 0.292 O. 195 1515 Melt exposed to air 59.95 0.2 1 1 O. 192 153 1 Melt exposed to air 6 1 -23 0.282 O. 187 4.84 1531 Melt exposed to air 69.82 0.25 0.232 1517 Melt exposed to air 72.73 0.23 0.266 1513 Melt exposed to air 79.90 0.223 0.265 1523 Melt exposed to air 89.73 0.064 0.3 16 1530 Melt exposed to air 91.73 0.181 0.276 4.1 7 1523 Melt exposed to air
92.73 Oz introduced at 75 cm3/min
Chapter 4. Results 79
Table 13. Continucd
Sampling Time [SI Pl [Nil Temp Experimenîal Condition O/ O/ ID/ K
1 10.72 O. 1 73 0.3 73 4.78 1536 O2 blown at 75 cm3/min 120.02 0.4 1 5 1514 O, blown at 75 cm3/min 121.68 0.193 0.3 8 1509 O2 blown at 75 cm3/min 130.73 0.161 0.426 2.46 1520 O, blown at 75 cm3/min 143.73 N, iniection at 2000 cm3/min 147.15 0.02 0-3 66 3.85 1508 N, injection at 2000 cm3/min 152.05 0.143 0.502 1507 Nz injection at 2000 cm3/min 153.52 0.002 0.467 15 10 N, injection at 2000 cm3/min 160.20 0.00 1 0.469 3.21 1 53 1 N2 injection at 2000 cm3/min 169.85 0.003 0.542 1 52 1 Nz injection at 2000 cm3/min
1 3 1>24 N- u e c t ~ o n at 7000 . . . <
Time (minutes)
Figure 47. The S. O and Ni concentratka proNe over time in Test 9. The vertical lines coincide respectively with t k iiitmduetioa of pare oryga ont0 the mdt surlace at 7s cm3/min and submerged nitmgen injection at 2000 cm31min.
Chapter 4. Resulis 80
Figure 48. Photograpb o f tbe melt surCace in Test 9 covered by an oxide layer at t = 32 minutes.
Time (minutes)
Figure 49. The time temperriture protik of the melt in Test 9 relative to the sampliag timt t = 0; the plateau in the cuwe near 1400 K indiates liquefaction of the alloy charge while the borizontrrl line marks the bath setpoint temperatum of 1523K.
Chapter 4. Results 81
4.2 Discussion of Errors Severai sources of uncertainty can be identified and related to the scatter in the data
plots. These include the error introduced by the analytical method, uncertainty fiom the
sampling procedure. i.e., with respect to the depth and position of the sampling point and the
size of each sample, and contamination of the quartz sampling tubes. The error of analysis
for S and O assays, according to INCO, was within 2 % of the detennination; uncertain@ due
to contamination of the sampling tubes could not be easily identified while evaluation of the
sampling error. by the sirnultanmus exiracrion of two samples at the same depth and position
in the melt, could not be perfomed accurately due to technical constraints on the test
apparatus. To minimize the sampling error, al1 attempts at sampling were directed to the
bottom of the melt however this may have also introduced an additional source of uncertainty
by stimng the melt. Having two unknown quantities it was not possible to sepvate the
contribution of each error source in the computation of the sample variance or standard
deviation. Other sources of error which were not considered in this analysis included the
accumulated mass loss fiom the melt due to sampling, which did not exceed more than 5-6%
of the initial charge mass, the periodic adjustments made to the gas rotameters to maintain
the desired gas flowrate and with respect to comparisons and the difference in the charge
masses between the experiments since this was usudly less than 10%. Statistical anomalies
in the elemental determinations, especially those of oxygen, may have been caused by the
oxidation of the sample during its transfer to the quench bath or the withdrawal of oxidized
surface material rather than bulk liquid fiom the melt.
The standard deviation of the S and O detenninations applied in Tests 2-9 are mostly
based on the pooled average of the sample standard deviations calculated fiom Test 2 while
the values calculated in Test 1 were applied only to that experiment. This approach was used
because the calculated deviation for S was higher in Test 2 over Test 1 while the standard
deviation for oxygen in Test 1 was based on elemental determinations perfomed at McGill
University rather than at MCO. The sarnple standard deviation for oxygen at low
concentration (~0.01 wt % 0) was estimated h m one result in Test 4 to be 0.004 wt% since
Chupter 4. Resu Its 82
a similar calculation could not be performed fiom the assays in Test 2. The standard
deviation of oxygen detenninations between 0.01 wt % and 1 wt % was taken as 0.020 wt
% fiom while readings above 1 wt % O were not plotted with an assumed standard deviation.
In al1 tests the standard deviation of the sulfur assays between 0- 1 wt % and - 1 wt % was
assurned tu be 0.087 wt %; S assays below this range were not plotted with a standard
deviation because no repeat deteminations were performed on low sulfur samples which
were near the lirnit of the analytical method.
The results of the nickel detenninations in Test 4 and Test 9 are dificult to assess
because repeateâ analysis of the samples consistently registered values higher than the mean
concentration of the CNS master alloy iagot with almost no variance. The nickel standard
solutions used for the a d y s i s were reproduced several tirnes without affecting the elemental
deterzninations. Hence the hi& nickel readings may have arisen from contamination of the
samples by the oxidized surface layer of the melts or the influence of an unaccounted minor
element in solution with the melt sarnples; interference from dissolved copper was not
considered because the relevant atomic absorption literature precluded that possibility . Satisfactory regression analyses could not be performed on ploned data due to the
high standard deviation of analysis in many of the sarnples following Test 1 . The calculated
standard deviation of the sulfur assays was 0.087 wt % and represented almost 10 % of the
initial sulfûr concentration whereas the standard deviation of the Iow oxygen measurements
almost matched the elemental determination. As a result of the large uncertainty in the
plotted data and therefore the nurnerous possibilities regarding the seiection of a best fit
curve attempts at regression analyses of the data were abandoned.
Chapter 5. Discussion 83
5.1 Discussion oflesulrs
S. 1.1 Marangoni Convection
The hypothesis presented in Chapter 2 presumed that sulfur removal fiom a copper-
nickel-sulfur melt might be impeded by the cessation of Marangoni convection upon oxygen
saturation of the melt and nickel oxide formation blocking the melt surface. Marangoni
convection was not observed in any of the experiments performed at the selected oxygen
flowrates. SIag accumutation on the melt surface in Test 1 obstructed surface observations
yet in Test 2. where a lower oxygen flowrate and a CS aIloy prepared in advance were used
to prevent excessive slag formation, the melt surface remained highly visible and no
instances of Marangoni convection were observed. Instead, a thin oxide film was seen
swirIing at low velocity on the melt surface but this motion could be attributed to the
impinging gas glancing against oxidized particles. However, sulfur removal. in the absence
of the slag layer. proceeded more rapidly in Test 2 over Test 1 in spite of the reduced gas
flowrate (see Figure 50).
Due to the absence of Marangoni convection in Test 2. the oxygen flowrate in Test
3 (CS melt) was increased to 75 cm3/min while the test crucible was cemented to a wall
extension and placed in a graphite receptacle intended to prevent melt spills and ejections
from darnaging the quartz reaction vessel. Test 4 and Test 6 were similarly conducted with
charges of CNS alloy and cathode copper respctiveiy. The results of these three tests (see
Figure 5 1 ) revealed that oxygen dissolution was greatest in the CS alloy of Test 3 and while
some sulfur removal took place in Test 3 none occurred in Test 4. No instances of
Marangoni convection were witnessed in any of these three experiments but al1 the melts
expenenced surface oxidation, although not to the extent seen in Test 1. The effectiveness
of the slag layer against the transfer of reactants or reaction products to and fiom the gas-
liquid interface was made evident fiom the results of Test 2 and Test 3 (see Figure 52) where
a greater degree of sulfur elimination was achieved in the former using a lower oxygen
flowrate and where the observed surface oxidation was much less and partially in the fonn
of a fluid film rather than a solid layer.
Chapter 5. Discussion 84
Figure 50. The concentrsition profiles over time in Tests 1 and 2 adjusted to the time scale of Test 1. The vertical line coincides with the start of O, delivery to botb melts.
Test 3 Test 4 T r a i 6
I
Tfme (minutes)
Figure 51. The concentration profdes over time ia Tests 3,4, and 6 adjustd to the tirne sale in Test 3. The ve-1 üne coincides with tbe start of O, d e l b e y to aU the melb.
Ch apter 5. Discussion 85
Time (minutes)
Figure 52, The coneeatmtioa profiles over time in Tests 2 and 3 adjusted to the time sale of Test 3. The vertical line coincides witb the start of O, delivery to botb melts,
5.1.2 The Role of Surface Films on Mass Transfer
Surface oxidation and hence the rninor arnount of desulfkization in Test 3 and Test
4 can be related to the blowing conditions and lack of melt agitation. Oxygen saturation of
copper melts is typically in the range of 1 wt % at 1523 K and even higher for Cu-Ni melts
according to the Cu-Ni-O phase diagram'926 (see Figure 7. Chapter 2) because nickel
suppresses the activity coefficient of oxygen to about 0.7 at 1523 K" and hence increases
oxygen activity. In Tests 1 - 6 the recorded oxygen values were much below oxygen
saturation with the CNS alloy showing the least tendency to dissolve oxygen and the greatest
likel i hood to oxidize its metallic components.
Thermodynarnics predicts that nickel oxidizes more readily than either copperios or
sulfur; this was observed in Test 4 when the dissolved oxygen and nickel content of the melt
had dropped as the oxygen flowrate was increased fiom 75 cm3/min to 372 cm3/min,
presumably due to increased nickel oxidation, while the sulfur level remained unafKected.
nie iow oxygen flowrates impinged on the melt surfaces did not induce any melt agitation
Chapter 5. Discussion 86
and in turn would have led to low rates of surface renewal thereby established and
maintained large concentration gradients of oxygen between the melt surface and the bulk
liquid. As previously mentioned in Chapter 2, ~ichardson" estimated that an iron melt
containing one-tenth its saturation level of dissolved oxygen, would attain surface saturation
with a monolayer of the dissolved species within milliseconds. If surface saturation is
readily established in a stagnant melt then surface oxidation becomes thermodynamically
favourable and the surface concentration gradients needed to drive Marangoni convection
are dissipated. Some support to these arguments are also found in the observations made in
Test 5. The cmcible containing the cathode copper had failed almoa irnmediately bringing
the melt into partial contact with the graphite cmcible for the duration of the experiment: the
copper k ing continuously deoxidized was not subject to the surface coverage observed in
Test 3. 4 and 6 and yet Marangoni convection did not take place. If the melt had k e n
sufficiently stirred then rapid surface renewal may have maintained suficient surface
concentration gradients but under the prevailing bath conditions this may not have occurred.
5.1.3 Melt Effervescence
The difficulty in achieving substantial sulfur removal fiom Tests 1 through 4.
prompted Tests 7 and 8, and 9. using CS and CNS alloy charges respectively, to be melted
under air in order to measure desulfkization of unperturbed melts exposed to the open
atmosphere. Knacke and Probn's% diagram (see Figure 1 5, Chapter 2) indicated that melting
of a Cu-S alloy would lead to large s a l e sulfùr evolution during melting or solidification and
therefore the initial meit assays were not unexpectedly below 0.5 wt% S. Two conclusions
relating to the earlier tests can be drawn: meiting of the alloy charges under ultra-high purity
nitrogen in Tests 2. 3 and 4 was necessary to prevent significant desulfùrization prior to
oxygen injection and evidence of melt ejections in these earlier tests can be partly attributed
to SOz evolution during solidification of the charges upon completion of the tests. Although
the melts in Tesis 7 - 9 experienced surfaçe oxidation, oxygen absorption and sulfur removal
occurred to a greater extent in these tests over previous attempts with oxygen blowing at low
flow-rates. Desulfurization of the exposed melts was expected to be gradua1 in these
Chapter 5. Discussion 87
experiments. However in Tests 7 and 8 spontaneous effervescence for a 20 minute penod
caused disintegration or digestion of the oxidized surface layer and accelerated sulfur
elimination; the CNS alloy charge in Test 9 did not experience turbulent eruptions and
therefore suifUr elimination progressed gradually and to a iesser extent than in the CS melts
(see Figure 53). At the time of the eruptions, the alloys had fully liquified and therefore the
phenornenon could not be attributed solely to the melting process since several periods of
effervescence were witnessed over the duration of the experiment separated by intervals of
melt quiescence. Effervescence is believed to occur when the melt has reached a certain
degree of oxygen super-saturation; the effervescence stops when the level of super-saturation
or the 'driving force" for SO, evolution is insuflicient to nucleate bubbles.
T i m e (minutes)
Figure 53. Tbe S coacentmtion profiles over time in Tests 8 and 9. Tbe srimpling time in Test 8 was adjusted to the time scale of Test 9 when a similar S concentration is observed in both melts.
Effervescence in C u 4 alloy melts was also witnessed by rio^'^ while exarnining
the efiect of jet momentum on desulfurization fiom CS and CNS alloys melted in the test
apparatus of this study and in similar conditions to Tests 7,8 and 9. In Rioux's experiments,
a pure oxygen gas Stream was delivered ont0 the melt surface from a gas lance 1 cm above
Chapter 5. Discussion 88
the bath at 75 cm3/& 500 cm3/min and 1ûûû cm3/min for the CS alloy and at 1000 cm3/min
for the CNS alloy. The results of Rioux's experiments, reproduced in Figure 54 without
alteration, show more rapid sulfür removal with increased oxygen delivery to the CS melt
whereas sulfûr elimination fiom the CNS alloy was slower than for the CS alloy blown at the
same oxygen flowrate. A comparison of Rioux's CS alloy expenment blown with 75 cm'
O Jmin to the concentration profiles over time of Test 8 show a fair degree of similarity (see
Figure 5 5 ) and indifates that this modest injection of oxygen contributed linle if anything to
the ensuing desulfurization. According to Rioux, increasing the gas flowmte accelerated the
onset of effervescence in the CS melts but did not provoke Marangoni convection; it should
be noted however that the turbulent conditions created on the melt surface at higher jet
momentun could have precluded witnessing such an eventuality. Some bubbl ing observed
by Rioux in the CNS melt was subdued compared to the eruptions of the CS alloy blown at
the sarne oxygen flowrate; this result was probably due to the rapid coverage of the melt
surface by Ni0 which also proceeded to consume the durnina sheath of the bath
thermocouple and premahirely ended the test.
O 20 40 60 80 100 120 140 160
Time (minutes)
Figure 54. The S concentration profile fmm CS aUoy blown with 4 at 75 em3/min, 500 cm3/min and 1000 cm3/min and fmm CNS alloy bloua with osygen at 1000 cm3/min, according to ~ioux'".
Chapter 5. Discussion 89
Time (minutes)
Figure 55. The S concentration profile over time in Test 8 compared to Rioux's testwork with CS alloy blown with oxygen at 75 cm3/min. Tbe time scak in Test 8 is adjusteâ to Rioux's sampling time whcn a similar S concentration is observed in both melts. The vertical line indicates the start of O blowing at 75 cm'lmin in Test 8.
This study failed to correlate the cessation of Marangoni convection as a factor in
diminished sulfur elimination fiom Cu-Ni-S melts or observe surface tension driven flow in
any of the copper and copper alloy melts used in this testwork. The causes of slow sulfbr
removal obsewed in this investigation can be atûibuted to the low oxygen flowrates used in
the expenments which did not provide a sufficiently hi& rate of oxygen delivery to the melt
or in turn agitate the liquid charges. As a consequence of melt quiescence large
concentration gradients may have developed between the bath and the bulk liquid leading to
surface oxidation and elimination of the surface concentration driving force required for
Marangoni convection. in this regard, nickel oxidation in the copper-nickel-sulfur melts
proved to be more effective in reducing or preventing desulfunzation over the copper
oxidation in the conesponding copper-sulfur melts. In the absence of Marangoni convection,
melt effervescence was the only observed surface phenomenon that may have led to
Chapter 5. Discussion 90
accelerated sulfùr elimination h m the copper-sulfur melts; again nickel oxidation may have
been responsible in suppressing this phenomenon and hence sulfur removal fiom the CNS
liquid alloy. Under the conditions of low oxypn blowing and open amosphere
desulfurization the progress of sulfur elimination and oxygen dissolution should be
considered in ternis of resistance to mass transfer through an oxide layer rather than as a rate
phenomenon.
Rioux' s findings also corroborated that nickel oxidation impedes su1 fur elimination
from semi-blister melts even under increased melt agitation. Although effervescence was
observed in the stagnant melts of CS alloy exposed to air in this study. Rioux demonstrated
that its onset could be accelerated with more rapid oxygen delivery to the melt but also be
suppressed by nickel oxidation on the melt surface. It is this author's opinion that as a result
of nickel oxidation a correlation between the cessation of Marangoni convection and reduced
sulfur elimination in WC0 semi-blister copper cannot be satisfactorily established. Under
both quiescent and agitated conditions in the melt. rapid surface coverage by nickel oxidation
precludes the observation of Marangoni convection on the melt surface. The high degree of
turbulent mixing required to dismpt this laye- which is already achieved in the iNCO
finishing converter by bottom blown gas injection, would create metallodynamic conditions
where Marangoni convection could not be observed or its contribution to desulfurization be
quantified.
Chapter 6. Conclusions 91
Test I CO Test 6: Oxidation by a Low Momentam Oxygen Stream
1 ) Marangoni convection was not obsexved in any of the melts impinged with oxygen
at 66 cm3/min and 75 cm5/min. Instead the CS and CNS alloy undenvent oxidation
fonning either a panially fluid film, as in Test 2. or a solid layer, as in Tests 3.4 and
6. on the fiee surface.
7) Stagnant metailodynamic conditions in the melts helped sustain large concentration
gradients between the gas-liquid interface and the bulk fluid by providing a low rate
of surface renewal which made conditions favourable for the formation of oxide on
the surface.
3 ) The surface slags fonned in Tests 3, 4 and 6 impeded the transfer of reactants or
reaction pmducts to and fiom the gas-liquid interface. This effect was most
pronounced in the CNS alloy melt whereby no discemable sulfùr elimination was
recorded.
Test 7 to Test 9: Oxidation of CS and CNS Liquid AUoy in Air
4) Sulfur elimination and oxygen dissolution in CS and CNS alloy melted under air
proceeded more rapidly and to a greater degree than similar charges impinged with
oxygen at low flowrates.
5) Increased sulfùr elimination over earlier tests was attributed partly to the sudden
evolution of SO, fiom the alloys, in the fom of effervescence, in the course of
melting them under air. Additional periods of effervescence experienced by the CS
alloy charges disrupted the oxidized surface layer resulting in more rapid sulfur
elimination as compared to a similarly tested CNS alloy melt which did not undergo
any effervescence or eruptions thereby leaving the slag layer intact.
Chapter 6. Conclusions 92
6 ) The onset of effervescence in liquid CS alloy is believed to occur when the melt
achieves a ceriain degree of oxygen super-saturation. The effervescence stops when
the level of super-saturation or the 'driving force' for SO, evolution is insufficient
to nucleate bubbles but will reappear periodically if the melt continues to absorb
oxygen until sufficient super-saturation is again reached. Once suficient S has been
removed such that the necessary super-saturation can no longer be attained the
effervescence ceases since the dissolved oxygen concentration cannot exceed its level
of saturation with respect to the Cu-O system,.
7) It is believed that the uiability of the systems to achieve this level of super-saturation
once sulfur is low enough and dissolved oxygen is high enough, that the oxygen
content of the meit cannot be increased M e r and the mechanism of desulfûrization
changes to one in which there is no longer any S 0 2 bubble nucleation as seen during
effervescence. Consequently, desulfurization becornes slower in accord with the
iNCO observations during the second stage of the finishing procedure.
8) The Marangoni aspect of the hypothesis in Chapter 2 was not confirmed but a
discovery was made about the nature of the desulhinzation process in Cu-S b a h .
Le.. perïodic effervescence.
Cha~ter 7. Recommendations for Future Work 93
Expenments have already k e n conducted by ~ ioux ' " as an extension to this
investigation which examined the effect of gas jet momentum or the rate of oxygen delivery
to the melt on the desulfùrization of CS and CNS alloy melted under air.
It would be of interest to this author to M e r quanti@ the onset of effervescence in
copper-sulfur melts by more accurate measurement of the sulfitr and oxygen levels prior to
bubbling since this phenornenon, to the knowledge of this author, has not k e n previously
reported in copper melts. Rioux's assays did not involve oxygen determinations due to time
and resource constraints whiIe the scatter in the experimental data of this investigation did
not provide an accurate indication to the onset of bubbling. Furthemore. it would be
necessaq to investigate whether the type of crucible used during expenmentation may have
contributed to effervescence.
Appendix A. X-Ray /SEM Analyses 94
Figure Al. Qualitative identifkt ioa of siag components in Test 1 by X-ray diffraction.
Figure M. Qualitative identi!kation of ejectd material on the quartz mction vusel in Test 1 by scaaning ekctmn micmscopy.
References 96
C.A. Landolt, A. Fritz, S.W. Marcuson, R.B. Crowx, J. Miszczak, -ber M a h g a iNCO's C-r Cl ff S e , Proceedings of the Copper 91-Cabre 91 International Symposium. Vol. W.- PyTometallurgy of Copper, August 18-21, 1991. Ottawa, Canada, hternational Symposium Organired by the Metallurgical Sociev of Canadian Institute of Mining, Metallurgy and Petroleum, Chilean Institute of Mining Engineers, ami Minerals, Metals and Materials Society of the AIME, ed. C. Diaz et al., Pergamon Press, Toronto, New York, 199 1, pp 1 5-29.
C.A. Landolf A Dutton, A. Fritz and S. Segsworth, Nickel a d C o p r S m CO'S Copper C l i f f , Extractive Metallwgy ofcopper, Nickel and Cobalt:
Proceedings of the Paul E Queneau Inrernational Syrnposium. Vol. II: Copper and Nickel Smelter Operations /sponsored by the &action and Processing Division of TMS and the Me fdurgïcal Society o f l e Canadian Institute of Mining, MeralZurgy and Petroleum (CIAQ, ed. C.A. Landolt, TMS, Minerals, Metals. Matenals. Warrendale, PA. 1 993, pp 1497- 1 528.
Ontario Govenunent, -, Ontario Ministry of the Environment. Toronto. 1987.
M.C. Bell, LA. Blanco. H. Davies and P. Gamtsen. Taking- S<IT2 Abatement Proiect, CIM Bulletin, Vol. 83. No. 933. 1990, pp 47-50.
LA. Blanco and C.A. Landolt, m2 A b a t e b ! c o a t s ff Smeltet, Prescnted at the 73rd SCC/40th SCGCH Conference, Halifax.
Nova Scotia. July 1 5-20, 1990.
C.A. Landolt, A. Dutton, J.D. Edwards, and RN. McDonald. u- Conservation a d Productiwty at Cop-per CI ff . . i , JOM, Vol. 44, No. 9, 1992, pp 50-54.
J.R. Boldt Jr.. The Winning of Nickel, Longmans Canada Ltd., Toronto, 1967, pp 275-283.
R.J. Neal and R.A. Reyburn, Practice at a e Copper Cl= -1ter of M C 0 Metals Co-, Copper and Nickel Converters: Proceedings of a Symposium on Converter Operating Practices Sponsored by the TMS-AIME Pyrometallurgy Committee ar the 108th AIME Annual Meeting in New Orleans, Louisiana, February 19-21, 1979, ed. R.E. Johnson, Metallurgical Society of MME, New York, 1979, pp 135-143.
. . A.A. Bustos, G.G. Richards, N.B. Gray and J.K. Brimacombe, Ph- rn NQnferrous Processa, Meta/[. Trans. B, Vol. 1 SB, 1 984, pp 77-89.
P.E. Queneau and S.W. Marcwn, Pyr- at C o p ~ e r Cliff - A Half
References 97
C e n u of Pro-, JOM, Vol. 48, No. 1, 1996, pp 14-2 1.
. . S. W. Marcuson C. Di= and K Davies, Bottom Sti- Process for Producine Blister COB, JOM, Vol. 46, No. 8, 1994, pp 61-63.
G.S. Victorovich, Ox for Product on of Co-, Ektractive Metullurgy of Copper. Nickel and Cobalt: Proceedings of the Paul E. Queneau International Symposium, Vol. 1: Fundamental Aspects, sponsored by the Ex~ruction and Processing Division of TMS and the Metallurgical Society of the Canadian Insiitute of Mining, Metaflurgy and Petroleum (CZW, eds. R.G. Reddy and R.N. Weizenback TMS. Minerals, Metals, Materials, Warrendale, PA, 1993, pp 50 1 -529.
. . M.C. Bell. J.A. Bianco, H. Davies and R. Sridhar, m n Flash Smelting in a Converta, JOM, Vol. 30, 1978, pp 9-14.
H. Davies. S. Marcuson, G. Osborne, and A. Wmer, Conv-mite Concentrate at RVCO's Port Colbourne Pilot P u Erfractive Metahrgy ofCopper. Nickel and Cobalt: Proceedings of the Paul E. Queneau International Symposium. Vol. I.- Fundamental Aspects~ponsored by the Extraction and Processing Division of TMS and rhe Metallurgical Society of the Canadian Institute of Mining, Merallurgy and Petroleum (CIW, eds. R.G. Reddy and R.N. Weizenbach, TMS. Minerals, Metals, Matenals, Warrendale, PA. 1993, pp 623-637.
. . . . J.K. Brimacombe, S.E. Meredith and R.G.H. Lee, Pressure 1- of Air UUp
a Pierce-Smith Converter, Metall. Trans. B, Vol. 15B. 1984. pp 243-250.
. . E.O. Hoefele and J.K. Brimacombe, -es in Sub-d Gas In!ection, Metall. Trans. B, Vol. 1 OB. 1979, pp 63 1 -648.
G.N. Oryall and J.K. Bnmacombe, J'he Physical Rehavior of a Gas Ipjected ilv into
. . , Metall. Trans. B, Vol. 7B, 1 976, pp 39 1-403.
. . N.J. Themelis. P. Tarassofi and J. Szekely, $&-J.quid Mo- T ~ f e r in a
r Converter, Tram Met. Soc. Aime, Vol. 245, 1969, pp 242592433.
C. Diaz. S. Marcuson. H. Davies and R. Stratton-Crawley, ConverSipD of N i c u Sulfùr-Con- C o p ~ e r to Blister . .
, Proceedings of Copper 87. Vol. 4. P'ometallurgy of Copper, Organized by the Metallurgical Sociew of the Canadian Institute of Mining and Metall urgy, the Chilean Institute of Mining Engineers, the University of Chile, eds. C . Diaz et al., Facultad de Ciencias Fisicas y Matematicas, Universidad de Chile, Santiago, Chile, 1987- 1988, pp 293-304.
Private communication with S.W. Marcuson, Sept. 1993.
References 98
A.K. Biswas and W .G. Davenport, Extractive Metallurgy af Copper, 3 rd ed., Peqarnon. Tanytown, N.Y., 1 994. pp 194- 1 99.
H.H. Kellogg, -emical P r e e s of the Svsem CU-S at Elevated -mm, Can. Metal. Q., Vol. 8, No. 1, 1969, pp 3-23.
. . A. Yazawa and T. Azakami, J l e r r n o ~ i o f n t m a u n t i e s Dunrlp
r Smeltiu, Can. Metal. Q., Vol. 8, No. 3. 1969, pp 257-261.
* .
G.K. Sigworth and J.F. Elliot, Ihe The- CS of Dih&.Lugud Cpp~er AI~Q~s. Can. Metal. Q., Vol. 1 3, No. 3 , 1974, pp 455-46 1 .
A. Yazawa. J h e m o d ~ d e r a t j o n s o f Cop~er Smeltirg, Can. Metal. Q-. Vol. 13. No. 3, 1974, pp 443-453.
. . J.F. Elliot. Phase Relatio- in the P ~ e t a l l u r ~ v of Copw, Merall. Tram. B. 1976. Vol. 7B, pp 17-33.
H. Jaikanen and M.H. Tikkanen. ~ l i b r i u m Studies on Hiph-Copper Matta. Scand J. MetaZiurgv. Vol. 8, No. 2. 1979, pp 64-66.
R.C. Sharma and Y.A. Chang, A T h e m o d w i c A u s i s of the CoggwSuifUL Svstem, .Wetall. Trans. B, 1980, Vol. 1 lB , pp 575-583.
R. Schmid: A T h e r m o d m i c Advsis of the Cu-O Svstem with an Associatd Solution Model, Metall. Trans. B. 1983, Vol. 14B, pp 473-48 1.
J.M. Lamin, S.L. Lee. H.H. Kellogg, T h e r r n o w c Promies of Copper-Sulfur Melts, Can. Metal. Q.. Vol. 18, No. 4, pp 395-400.
C.B. Alcock. Principles of Pyrometallurgy, Academic Press, New York, 1976, pp 1 70- 1 79.
J.M. Larrain and S.L. Lee, J h e ~ o d ~ c Proyrties of Cppper-Nickel-Su Melt~, Can. Metal. Q., Vol. 19, No. 2, 1980, pp 183-1 90.
S.L. Lee. J.M. Lanain, and H.H. Kellogg, T h e m o d ~ c Properties of Molta SuIfides. Part III. The Svstem Cu-Ni-S, MetaII- Trans. B, Vol. 1 1 B, 1980, pp 25 1- 255.
. . . . . . . W.J. Schlitt, R.H. Craig, and K.J. Richards, Miribility ci& D m
en Cu-Ni& Mefull. Trans., Vol. 4, 1973, pp 1994-1996.
References 99
Y. Chuang and Y .A. Chang, E x t e h o Model to Te- etal-Sulfbr Melts. Cu,Ni-S, Merall. Tram B, Vol. 13B. 1982, pp 379-385.
. . . . - . . P. Taskinen. L i o u i d u s U b n a a d Solution The-CS in Cppper-Rich
n Al lqys, Acta Polyrechnica Scandinmica. Chemistry Including Metailurgy Series, No. 145, Helsinki, 45 pp.
A.D. Kulkarni and R.E. Johnson Studies of Llqyid Co~per Allog . .
b~ Electro&ve Force Methpd- Part II. The Cu - Ni - O & Cu-Ni Svstem , Metall. Trans.. Vol. 4, 1973, pp 1 723- 1 727-
U. Kuxmann and J. Riecke, Die Gle&ggwichte Z w i s c k N i c w Sauersloffin
Schiacken, Erzmetall. 25, 1972, pp 395-404.
G. Astarita Mass Transfer wiih Chernical Reaction, Elsevier Publishing, New York. 196% pp 1.
. . . . F. Ajerch and J.M. Toguri, O x i d m e s of U u i d C o g w r d Liquid Co- Sulfi&, Mefull. Trans.. Vol. 3, 1972, pp 2 187-2 193.
P. Schmitt and W. Wuth, pulass T m f e r in ~ o m e t a i l ~ c d Top Blo- Svstem, Heaf and Mass Transfer in Merallurgical Systems. eds. D.B. Spalding and N.H. Afgan, MacGraw-Hill, 198 1, pp 27 1-280.
. . . . A. Chattejee and A.V. Bradshaw, Break-UD of a Liquid Surface bv an Imeineine Gas Jet, J. Iron and Steel Inst.. Vol. 2 1 0, Part 3, Mar. 1972, pp 1 79- 1 87.
. . N.A. Molloy, Imoinninp Jet Flow in a Two-Pke Svstm-c Flow P a m , J. lron and Steel Inst., Oct. 1970, Vol. 208, Part 10. pp 943-950.
K. Li, A Model Studv of S D ~ , J. bon and Steel Inst., Nov. 1960, Vol. 196, pp 275-29 I .
. * R.B. Banks and D.V. Chandrasekhara, Investfeatl~ndthe Penetration of a m-Veloc i tv Gas Jet Tho& a I.iqu1d Surface . . , J. Fluid Mech., Vol. 15, No.
- 3. 1963, pp 13-34.
. . . . F.R. Cheslak, J.A. Nicholls and M. Sichel, Cavities Forrned on LLgyid S e e s bv aseous Jets, J: Fhid Mech., Vol. 36, No. 1, pp 55-63.
E.T. Turkdogan, -CS of G- on S w e of . . w, Chem
Eng. Sei, Vol. 21,1966, pp 1133-1 144.
References 1 00
F. Tanaka, R. imai, T. Yanagiya and A. Fuwa, E ~ Q V B a h c e &&sis on Formation of Cavitv and S w bv TopRlowi~@as Jet Metallurgicd Review of MMIJ. Vol. 1 2, NO. 2, 1995, pp 46-59.
. . . . E. Kimura, F u n d d R e m of UE M e c h w m in Mitsubishi Co- -, ISIJ International. Vol. 23. 1983, pp 522-529.
* - R. Li and R.L. Harris. beraction of Gas Jets with Mode1 Process I . i b , Pyrometallurgy '95,Paper.s Presented ut the "Pyrometaflurgy '95" Conference / Organized by the hsfiruiion of Mining and Mefallurgy in Association with the insrirute of Materials, and Held in Cambridge, Engfand. fiom IO ta 12 Juiy, 1995. The Institution of Mining and Metallurgy, London. 1995. pp 107- 123.
. . A.H. Castillejos and J.K. Brimacombe. m e n t of Phvsical Chc tens t ics of Bubbles in Gas-Lwid P lumsJar t II. . .
Idocal Progefiies of Turbulent A ir-Water Plumes in V e r t i c u e c t e d Je& Metail. Trans. B, Vol. 1 88, 1987, pp 65967 1.
- * *
J. Liow and N.B. Gray, Re- Gas m ~ o n in a Peirce-Sm Convrrter. Water M o d u , Metall. Trans. B, Vol. 2 1 B, 1990, pp 987-996.
. . . . I.F. Taylor. J.K. Wright and N.B. Gray, M i ~ R e s u I t L ~ From Reactive G ~ s Jn i ect ion, The Howard Worner International Symposium on lnjection in Pyrometallurgy. eds. M. Nilmani and T. Lehner, Melbourne, Australia The Minerals. Metals and Materials Society, 1996, pp 163- 174.
N.P. Bacon, J.H. Chesters and I.M.D. Halliday, Flow Pa- in T-sied S ha?=, J. Iron and Steel Inst.. July 1960, pp 286-292.
K. D. Peaslee and D. G. C. Robertson, Mode1 Studies of S D ~ W a v d Flows Within Stee Fu-, Steehaking Conference
Proceedings, Vol. 77 199% bon & Steel Soc of AIME, Warrendale, PA, pp 7 1 3-722.
. . D.G.C. Robertson, -on of the- Phases, EPD Congress 1995 : Proceedings of a Symposium isponsored by the fitraction and Processing Division, held ut the TMS Annual Meeting in Las Vegas. Nevada, Febmary 12- 16. 1995, ed. G. W. Warren, TMS, Warrendale, Pa., 1995, pp 347-36 1.
A. Chaîte jee and A.V. Bradshaw, m e -ce of Re-ce on M~ISS . . sfer to a L i q ~ d Mes, Metall. Trans., Vol. 4, 1973, pp 1359-1364.
. . R.J. Fmehan, m s T m f e r Between Me-ted O-, Metals Technology, Vol. 7, Part 3, March 1980, pp 95-1 01.
References 101
J.K. Brimacombe, ES. Stratigakos and P. Tarassoff. ms T d x a S u b w e d Gas Jet and a I .iqUid, Metall. Tram, Vol. 5. 1974. pp 763-
771.
W.G. Davenport. D.H. Wakelin and A.V. Bradshaw, w t i o n n f BoWubbles anQ Jets with I .iQYidS, Heat and M a s Transfer in Process MetaZlurgy: Proceedings
of a Symposium Held by the John Percy Research Group in Process Metallurgv. Imperia1 College, London, 19 and 20 Aprii 1966, ed. A.W.D. Hills. The Institution of Mining and Metallurgy. London, 1967, pp 207-245.
W.F. Porter, F.D. Richardson and L N . Subramanian, & Across I n t d c e s m t e d bv Bubblg Heat and Mass TranFfr in Process Metallurgv: Proceedings of a Symposium HeZd by the John Percy Research Group in Process Metallurgy, Imperial College, Loniion, 19 and 20 Aprif 1966, ed. A. W.D. Hills. The institution of Mining and Metallurgy, London. 1967, pp 79-1 15.
. . - . . N.J. Themelis and P.J. Mackey, Sol id-Liauid Gas-l ,auidract ions in a B&
eactor? Proceedings of the Savard'Lee International Symposium on Bath Smelting: Proceedings of an International Symposium / Sponsored Jointly by the Minerals, Metals & Materials Socieîy, the Iron & Steel Society and the MetallurgicaZ Society of CIM, eds. J.K. Brimacombe and P.J. Mackey, G.J.W. Kor, C. Bickert and M.G. Ranade. The Minerals, Metals and Materiais Society, Warrendale, Pa., 1992. pp 353-375.
. . K. Mori and M. Sano, Jnteractions Between l f i e ç a i . ? Scaninject: International Conference on Injection Metallurgy Luka. Sweden, June 9-10, 1977/ Organized Jointly by MEFOS, Jernkontoret, MEFOS, Lulea. Sweden 1977, pp 348-354.
8 M n s e w c h t e n A u f - b n H. Lohe, von C l d e n & F l u s - o b e m .. . .- , Chem. Ing. Tech., Vol. 38, pp. 309-3 14.
J. Szekely and N.J. Themelis, Rate Phenomena in Proce-rc Melallurgy. Wiley- Interscience. New York, 197 1, pp 724-728.
A.H. Alyaser, Oxidation Kinetics of Molen Copper Sulphide, Master's Thesis, The University of British Columbia 1993,220 pp.
S. Taniguchi, A. Kikuchi and S. Maeda, Mgdel on WSSligpS in G s Retew an
. . . . Jet of Gas a n d d lron , Testu-to-Hugane, 1976, Vol. 62, No. 2, pp 19 1-200.
. . . . S . Taniguchi, A. Kikuchi and S. Maeda, of m n of CirpDhite bv tk
References 102
ImoinmnP Jet of G a , Testu-to-Hagane, 1977, Vol. 63, No. 7, pp 1071-1080.
S. Taniguchi, A. Kikuchi, T. Tadaki and S. Maeda, Numerical -sis on the G e " - * .
s T d e r Retwe- Jet of Gas -id I ro~ , Testu-to- Hagane, 1979, Vol. 65. No. 13, pp 1830-1873-
S. Taniguchi, A. Kikuchi. T. Tadaki and S. M d Fluid Flow md Mass T ~ f e r in . - the Ch-muid Iron Svstem th a Laboratorv-Scak Induct Metallurgical Applications of Magnetohydrodynamics : Proceedings of a Symposium of the Internotional Union of nieoretical and Applied iMechanics held ut Trinify College. Cambridge. WK, 6-10 Seprember 1982, eds. H.K. Moffat and M.R.E. Proctor. The Metals Society, London, 1984.
F. W. Richardson Physical Chemistry of Melts in Metallurgy, Academic Press. New York, 1974, pp 426-439.
. . J.K. Brimacombe, Interfacial Turbulence in w-, Physical Chemistry of Process Metallurgy , Papers Presented al the July 1 973 Conference / The Richardson Conference. eds. J. H. E. Jeffes and R. J. Tait, The institution of Mining and Metallurgy. London, 1974. pp 1 75- 1 85.
K. Monrna and H. Suto, Effects of Dissolved sulphiir. Oxvg~n- Selen Tellurium on the Surface Tension of J.iquid CO-
. . , Tram JIM. Vol- 2. 1961 pp 148-153.
G.R. Belton, m e 1- Between S t r o u Adsapion of Solutes and Interfacd . . . . inetics at the Liawd Metal Surfacg, Can. Metul. Q., Vol. 2 1, No. 2. 1982, pp 137-
143.
G.R. Belton, Ad-e Gibbs AdSprption Isothemudlnterfacial uid Metal Svstem, - Metall. Trans. B, Vol. 7B. 1976,35-42.
S. Sun and G.R. Belton, n e Effect of Sulfur on & I n t e r f a Rates of Reaction of . . CO, md CO with LI QUI^ CO=, Metaii- and Mai. Tram B, Vol. 29, 1998, pp 296- 298.
. . B. Gallois and C.H. Lupis, mec t of Oxvgen on the Surfâce T a i o n of Liaud -, Metail. Trans. B, Vol. 1 ZB, 1 99 1, pp 549-557.
. . . G. Bernard and C.H.P. Lupis, S u r f & i h s ~ Silver WYS. Part L
Ilos, Meral/. Trans., Vol. 2, 197 1, pp 299 1 -2998.
F.D. Richardson, h t e w P h e n a n d Proce=, Can. Metal- Q.,
Vol. 2 1, No. 2. 1982, pp 1 1 1-1 19.
. . L.S. Darken and E.T. Turkdogan, Adsolption Kinetics at Elevated Te-, Heterogeneou Kinetics ut Elevated Temperatures : Proceedings of a n International Conference in Metallurgy and Materials Science Held at the Universis. of Pennsylvania, eds. G.R. Belton and W.L. Worrell. Plenum Press, New York. 1970. pp 25-95.
Tjuo . . . R.J. Fmehan and L.J. Martonik, ne Rate of A bsomtion of h d t o hqrrid iron
X- S u k MetaII. Tram. B, Vol. 1 1 B, 1980. pp 6 15-622.
R.J. Fruehan and L.J. Martonik, ~ g ~ Q . h 2 h U d of Nitr-ot Fe-Cr and-vs Co- SulfiiE
* . - - . Merall. Tram. B, Vol. 12B, 198 1 . pp 379-384.
L.E. Scriven and C.V. Steding, The -ffkct~, Nature, Vol. 1 87- 1 960, PP 186-1 88.
K. Mukai, w o n i Fffect in lron and S t e e l m w Processes, ISfJ International. Vol. 32, No. 1 , 1992. pp 19-25.
F o m , Van Nustrand's Scientific Encyclopedia. 8th ed.. ed. D.M. Considine, Van Nostrand Reinhold, Toronto. 1 995. pp 1 300- 1 30 1 .
P . Sahoo. T. Debroy and M.J. McNallan, -ce Tension of B b v y Metal- Surfacc . . ve Solute S-er Conditions Relev Met-, Metall.
Trans. B, Vol. 19B, 1988 pp 483-49 1 .
. . . . A.H. Alyaser and J.K. Brimacombe, Oxidation m e t ~ c s of Molten Co-gper S U U , Metall. and Mat. Trans. B, Vol. 26, 1 995, pp 2540.
N. Hirashima, R.T.C. Choo, LM. Toguri and K. Mukai, n e Effect of S m Movemmts on Nitro id Iran, Metall. T r a m B. Vol. 26B. 1995, pp 97 1-980.
. . J.K. Brimacombe and F. Weinberg, Observations of Su*e Movem- of Liauid
r and Th, Metall. Trans., Vol. 3, 1972, pp 2298-2299.
K.W. Lange and M. Wilken, m i T-l P ~ ~ ~ I E I U in S v s t m , Con. Meral. Q., Vol. 22, No. 3, 1983, pp 326.
R.J. Barton and J.K. Brimacombe, w e of Surface Tension-Driven Flow on b . . . . m, MetafI. Trans. B, Vol. 8B, 1977,
References 1 O4
2. Asaki, S. Ando, and Y. Kondo, of Molten C o a ~ e r m, Metali. Tram- B. Vol. 29B. 1988, pp 47-52.
. - . . Y. Fukunaka, K. Nishikawa H.S. Sohn, and 2. Asaki, Desulfunlationtics of
olten C o v r b- B u b w , Metal' Trans. B, Vol. 22B, 1991, pp 5-1 1.
Reiichi Ohno, Des . . S o w o n
Induction Meltirg, Metall. Trans. B, Vol. 22B, 199 1. pp 405-41 6.
. . . . . . C.F. Floe and J. Chipman, Effect of Impynt~es on the Solubd~v of Subhur Dioxid~ in Molten Co-, Trans. AIME, 1942, Vol. 147, pp 28-38.
. . O. Knacke and H. Probst. m e Evolution of Gases in Cogper on S o m , Metallurgical Chernistry, ed. O. Kubaschewski, Her Majesty's Stationary Office, London. 1972, pp 527-3 1.
G. Rottmann and W. Wuth, Conversion of Copwr Matte bv use of the Top-Blowiu T-, Copper Metallurgy: Practice and Theory: Paprs Presented at a Meeting Orgoniaid by rhe Institurion of Minïng and Metallurgy, With nie Cooperation of the Centre Belge d'hformation du Cuivre. and Held in Brussels. Belgium, on I I Febmury 197.5. ed. M.J. Jones. Institution of Mining and Metallurgy, London, 1975. pp 49-52.
. . V.A. B r y h i n . 0.1. Tsybin, L.I. Blokhina. and G.N. Zviadadze. 8n InvesUgUon of . . . .
e Oxidation Kinetics of a C o p ~ e r SuIfide Melt with O x m , Russ. Metall. (Engl. Trans.). No. 5 , 1978, pp 24-28.
. . . . H. Jalkanen, a s of Molten C w u s Su- m d Co-, Scand. J. Metallurgy, Vol. 10, 198 l , pp 257-262.
J.J. Byerley, G.L. Rempel, and N. Takebe, h t e M o n of Copger S u e s w i b Copper O+ in the Mol ten Stak, Metall. Trans., Vol. 5, 1 974, pp 250 1 -2506.
. . P.T. Morland, S.P. Matthew, and P.C. Hayes, m e t i c s of S3' bebetween ~ 2 / C 0 / C 0 , Gas Mianires @ Co- S a d e M & m , Metali. Tram. B. Vol. 22B, 1991 pp 21 1-21 7.
R.J. Barton and J.K. Brimacombe, Qterfacial Turwence D w , Solid C ~ ~ m o l t e n COI>=, Metall. Trans. B, Vol. 78, 1976, pp 144-145.
References 105
1 03. F.P. incropera, lntrodmion to Heat Transfer, 2nd ed., Wiley, New York, 1 !HO, pp 681.
. . 104. D. Riow, n e m e c t of 0- Jet M o m o n Rate of Desulfurization of
er Co-, B. Eng. Research Projec~ McGill University, 1 998,32 pp.
105. A. Yazawa and S. Nakazawa, -ns Between Co12pe- esses f i o m c Viewboim, Sulfide SmeZfing '98: Czment
und ~ u & e Prof tices, ~ roceed in~ i of the ~yrn&siurn Held at the 1 998 TMS Annuaf Meeting, San Antonio, Texas, Februmy 16-1 9. 1 998 with addtionui pyrometul~urgy papers presented at the 199 7 TMS Annuai Meeting, Orlando, Floriaiz, February 1 O- 13, 1997, eds. J.A. Asteljoki and R.L. Stephens, TMS, Wanendale, Pa., 1998, pp 39- 48.