Supporting Information
Highly stable semi-transparent MAPbI3 perovskite
solar cells with operational output for 4000 hours
M. Bodiul Islam,†,‡,§ M. Yanagida,† Y. Shirai,*,† Y. Nabetani‡ and K. Miyano†
†Global Research Center for Environment and Energy based on Nanomaterials Science (GREEN),
National Institute for Materials Science, 1-1 Namiki, Tsukuba, Ibaraki 305-0044, Japan
‡ Interdisciplinary Graduate School of Medicine and Engineering, University of Yamanashi, 4-3-11
Takeda, Kofu, Yamanashi 400-8511, Japan
§ Department of Glass and Ceramic Engineering, Rajshahi University of Engineering & Technology,
Rajshahi-6204, Bangladesh
1
Table S1 Summary of the studies on the operational stability of perovskite solar cells to compare with present
work.
Device Structure PCE (%)
Max. process temp. (C)
Stability Under ContinuousIllumination
ReferenceTime(h)
Temp.(C)
Retained Efficiency
( %)FTO/ meso-TiO2 + CH3NH3PbI3 /
Spiro-OMeTAD/Au 14.1 500 500 45 80 Nature. 2013, 499, 316.
FTO/ compact-TiO2/ Al2O3+ CH3NH3PbI3-
xClx /Spiro-OMeTAD/Au 12 500 1000 40 50 Nat. Commun. 2013, 4, 2885.
FTO/ compact-TiO2/meso-TiO2+CH3NH3PbI3-xClx /Spiro-OMeTAD/Au 5.9 480 335 40 60 Phys. Chem. Chem. Phys. 2014, 3918.
TiO2/(Meso-TiO2/ZrO2) +(5-AVA)xMA1-xPbI3/porous Carbon 12.8 450 1008 RT ~100 Science. 2014, 345, 295.
FTO/NiMgLiO/MAPbI3/PCBM/Ti(Nb)Ox/Ag 15 500 1000 50 90 Science. 2015, 350, 944.
FTO/ compact-TiO2/ CH3NH3PbI3-xClx /Spiro-OMeTAD/Ag ~12 450 120 85 40 J. Mater. Chem. A. 2015, 3, 8139.
FTO/ compact-TiO2/ Al2O3 +CH3NH3PbI3-
xClx /Spiro-OMeTAD/Au 13.1 500 350 RT 95 J. Phys. Chem. Lett. 2015, 6, 432.
FTO/ compact-TiO2/meso-TiO2 +CH3NH3PbI3-xClx /Spiro-OMeTAD/Au 11.1 470 360 RT 20 J. Mater. Chem. A. 2015, 3, 9194.
FTO/compact-TiO2/FA0.9Cs0.1PbI3/Spiro-OMeTAD/Ag 16.5 500 220 65 70 Adv. Energy Mater. 2015, 5, 1501310.
ITO/PEDOT:PSS/2D-Perovskite/PCBM/Al 12.5 150 2,250 RT ~100 Nature. 2016, 536, 312.
FTO/ compact-TiO2/meso-TiO2 + Cs5(MA0.17FA0.83)95Pb(I0.83Br0.17)3/
Spiro-OMeTAD/Au21.1 450 250 RT 85 Energy Environ. Sci. 2016, 9, 1989.
ITO/PEDOT/MAPbI3/PCBM/AZO/ITO 12.3 135 124 100 80 Adv. Mater. 2016, 28, 3937.
FTO/NiO/MAPbI3/PCBM/Au 8 400 300 45 64 J. Phys. Chem. C. 2016, 120, 27840.
FTO/ TiO2/MAPbI3/Spiro-OMeTAD/ MoO3/Al 14.8 450 144 85 85 ChemSusChem. 2016, 9, 2597.
FTO/ compact-TiO2/meso-TiO2 +FAPbBr3/Spiro-OMeTAD/Au 8.2 450 150 RT, 60 95, 80 Nano Lett. 2016, 16, 7155.
FTO/compact-TiO2/meso-TiO2 + MAxFA1-xPb(IyBr1-y)3/Spiro-OMeTAD/Au
18.7 450 Outdoor3 months 11~35 ~100 Science. 2016, 354, 203.
FTO/compact-TiO2/meso-TiO2 + Rb5(Cs5(MA0.17FA0.83)95)95Pb(I0.83Br0.17)3/
Spiro-OMeTAD/Au21.6 450 500 85 95 Science. 2016, 354, 206.
ITO/TiO2-Cl/Cs0.05FA0.81MA0.14PbI2.55Br0.45/Spiro-MeTAD/Au 20.1 150 500 RT 90 Science. 2017, 355, 722.
Glass/FTO/LBSO/MAPbI3/NiO/FTO/glass 13.4 280 1000 25 93 Science. 2017, 356, 167.
ITO/NiO/Cs0.17FA0.83Pb(Br0.17I0.83)3(CsFa)/LiF/PCBM/SnO2/ZTO/ITO/LiF/Ag 14.5 300 1000 35 ~100 Nature Energy. 2017, 2, 17009.
ITO/NiOx/MAPbI3/PCBM/AZO/Ag 15.2 100 1000 85 73 ACS Omega. 2017, 2, 2291.
FTO/c-TiO2/TiO2/ 11.9 450 10,000 55 ~100 Nat. Commun. 2017,
2
(meso-TiO2/ZrO2)+ 2D/3D Perovskites/Carbon DOI: 10.1038/ncomms15684.FTO/SnO2/C60/BA0.09(FA0.83Cs0.17)0.91Pb
(I0.6Br0.4)3/Spiro-OMeTAD/Au 17.2 180 ~4000 50~60 ~80 Nat. Energy. 2017, 2, 17135.
FTO/c-TiO2/mp-TiO2/MA1-xGuaxPbI3/Spiro-OMeTAD/Au 19.0 500 1100 60 ~80 Nat. Energy. 2017, 2, 972
ITO/SnO2/(FA0.79MA0.16Cs0.05)0.97Pb(I0.84Br0.16)2.97/EH44/MoOx/Al 18.5 150 1000 30 94 Nat. Energy. 2018, 3, 68.
ITO/NiOx/MAPbI3/PCBM/AZO/ITO 12.8 100 4500 30 ~100 Present work
Semitransparent solar cell device
Table S1. Statistics of device parameters. Avg: average, Std: standard deviation.
Opaque
devicesNiOx HTL PTAA HTL
JSC
(mAcm-2)
VOC
(V)FF
(%)
JSC
(mAcm-2)
VOC
(V)FF
(%)
Avg 19.86 1.01 0.68 14.76 20.50 1.08 0.77 17.23
Std 0.85 0.02 0.02 0.39 0.42 0.01 0.01 0.57
3
Fig. S1 Photograph showing the glass encapsulation of solar cells.
4
Sealing Glass
Fig. S2 Transmission spectra of the sputtered ITO layers with different thickness.
Fig. S3 Histogram of the opaque devices with NiOx (red) and PTAA (green) HTL.
5
Fig. S4 Absorption spectra of PTAA (~25nm) and NiOx (~70nm) HTLs.
6
0 200 400 600 800 100002468
1012
Powe
r (mW
/cm̂
2)
Power (mW/ cm2) J max (mA/cm2) M.P. Point (V)
Time (h)
J max M.P. Point
13.5
14.0
14.5
15.0
15.5
16.0
0.68
0.70
0.72
0.74
0.76
0.78
0.80
Fig. S5 Long-term stability test of the semitransparent device with NiOx HTL under 1 SUN. The
device was kept at MPPT condition at constant temperature (~30 ).℃
Fig.S6 Long-term stability test of the semitransparent device with NiOx HTL under 1 SUN. The
device was kept at MPPT condition at various heat stresses in temperature controlled oven.